CN107601981A - Plant's exterior wall modified anticracking cement mortar - Google Patents
Plant's exterior wall modified anticracking cement mortar Download PDFInfo
- Publication number
- CN107601981A CN107601981A CN201710839473.4A CN201710839473A CN107601981A CN 107601981 A CN107601981 A CN 107601981A CN 201710839473 A CN201710839473 A CN 201710839473A CN 107601981 A CN107601981 A CN 107601981A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- exterior wall
- plant
- cement mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses plant's exterior wall modified anticracking cement mortar, includes following raw material by mass parts：35 40 parts of cement；15 20 parts of kaolin powder；7 10 parts of perlite；8 12 parts of quartz sand；15 17 parts of slag powders；59 parts of cement waterproof agent；48 parts of flyash；35 parts of aluminium powder；25 30 parts of water.Kaolin powder raw material wide material sources, the heat-insulation and heat-preservation of perlite is good, and the cracking resistance of slag powders is good, along with cement waterproof agent, it is added in cement, when cement setting hardens, volumetric expansion therewith, aluminium powder light weight, quartz sand is hard, wear-resisting, stable chemical performance, and powdered coal ash is extensive, it is cheap, for architectural engineerings such as foggara, pond, water towers.
Description
Technical field
The present invention relates to cement mortar, more particularly to plant's exterior wall modified anticracking cement mortar.
Background technology
Cement mortar is used for the places such as architectural engineering, such as builds a house.Common cement mortar main component be exactly cement and
Sand, traditional cement mortar as plastering material there is the shortcomings of crack, hollowing, adhesive property difference, secondly setting and hardening
Speed is slow, and when especially winter constructs, cement mortar easily ftractures, and influences construction progress.It is accordingly, it is desirable to provide a kind of new
Technical scheme solve the above problems.
The content of the invention
To solve the above problems, the present invention provides a kind of plant's exterior wall modified anticracking cement mortar.
The technical solution adopted by the present invention：
Plant's exterior wall modified anticracking cement mortar, include following raw material by mass parts：
Cement 35-40 parts；
Kaolin powder 15-20 parts；
Perlite 7-10 parts；
Quartz sand 8-12 parts；
Slag powders 15-17 parts；
Cement waterproof agent 5-9 parts；
Flyash 4-8 parts；
Aluminium powder 3-5 parts；
Water 25-30 parts.
Slag is put into pulverizer after fully crushing, then fully polished through flour mill, 70-90 DEG C of heating-up temperature is cold
But after, through 120-140 mesh nets, after sieving, it is stand-by that slag powders are obtained.
It is an advantage of the invention that：Kaolin powder raw material wide material sources, the heat-insulation and heat-preservation of perlite is good, the anticracking of slag powders
Property is good, along with cement waterproof agent, is added in cement, when cement setting hardens, volumetric expansion therewith, and aluminium powder light weight, stone
Sand is hard, wear-resisting, and stable chemical performance, powdered coal ash is extensive, cheap, is built for foggara, pond, water tower etc.
Build engineering.
Embodiment
Following embodiments are merely to illustrate the present invention, but can not limit protection scope of the present invention.
Embodiment 1
Plant's exterior wall modified anticracking cement mortar, include following raw material by mass parts：
35 parts of cement；
15 parts of kaolin powder；
7 parts of perlite；
8 parts of quartz sand；
15 parts of slag powders；
5 parts of cement waterproof agent；
4 parts of flyash；
3 parts of aluminium powder；
25 parts of water.
Slag is put into pulverizer after fully crushing, then fully polished through flour mill, 70 DEG C of heating-up temperature, cooling
Afterwards, through 120 mesh nets, after sieving, it is stand-by that slag powders are obtained.
Embodiment 2
Plant's exterior wall modified anticracking cement mortar, include following raw material by mass parts：
37 parts of cement；
18 parts of kaolin powder；
8 parts of perlite；
11 parts of quartz sand；
16 parts of slag powders；
7 parts of cement waterproof agent；
6 parts of flyash；
4 parts of aluminium powder；
27 parts of water.
Slag is put into pulverizer after fully crushing, then fully polished through flour mill, 80 DEG C of heating-up temperature, cooling
Afterwards, through 130 mesh nets, after sieving, it is stand-by that slag powders are obtained.
Embodiment 3
Plant's exterior wall modified anticracking cement mortar, include following raw material by mass parts：
40 parts of cement；
20 parts of kaolin powder；
10 parts of perlite；
12 parts of quartz sand；
17 parts of slag powders；
9 parts of cement waterproof agent；
8 parts of flyash；
5 parts of aluminium powder；
30 parts of water.
Slag is put into pulverizer after fully crushing, then fully polished through flour mill, 90 DEG C of heating-up temperature, cooling
Afterwards, through 140 mesh nets, after sieving, it is stand-by that slag powders are obtained.
Kaolin powder raw material wide material sources, the heat-insulation and heat-preservation of perlite is good, and the cracking resistance of slag powders is good, along with cement
Waterproofing agent, it is added in cement, when cement setting hardens, volumetric expansion therewith, aluminium powder light weight, quartz sand is hard, wear-resisting, changes
Stable performance is learned, powdered coal ash is extensive, cheap, for architectural engineerings such as foggara, pond, water towers.
Claims (2)
1. plant's exterior wall modified anticracking cement mortar, it is characterised in that include following raw material by mass parts：
Cement 35-40 parts；
Kaolin powder 15-20 parts；
Perlite 7-10 parts；
Quartz sand 8-12 parts；
Slag powders 15-17 parts；
Cement waterproof agent 5-9 parts；
Flyash 4-8 parts；
Aluminium powder 3-5 parts；
Water 25-30 parts.
2. plant's exterior wall according to claim 1 modified anticracking cement mortar, it is characterised in that：Slag is put into
After fully being crushed into pulverizer, then fully polish through flour mill, 70-90 DEG C of heating-up temperature, after cooling, through 120-140 mesh nets,
After sieving, it is stand-by to obtain slag powders.