CN107596947A - Enamel glass stirrer - Google Patents
Enamel glass stirrer Download PDFInfo
- Publication number
- CN107596947A CN107596947A CN201711088189.4A CN201711088189A CN107596947A CN 107596947 A CN107596947 A CN 107596947A CN 201711088189 A CN201711088189 A CN 201711088189A CN 107596947 A CN107596947 A CN 107596947A
- Authority
- CN
- China
- Prior art keywords
- parts
- lining bottom
- bottom glaze
- paddle
- butyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of enamel glass stirrer, including puddler and paddle；The outer wall of the puddler and paddle has been covered each by glass lining bottom glaze；The glass lining bottom glaze is composed of the following components：Alundum (Al2O3), silica, 1-hydroxy ethylidene-1,1-diphosphonic acid, 4 bromide, di-n-butyl phosphite salt, alkali formula calcium molybdate zinc, phosphorus zinc chromate, nanometer silicon carbide, azodiisobutyronitrile, calcine trautwinite, N vinyl pyrrolidones, normal-butyl sodium naphthalene sulfonate.The outer wall of enamel glass stirrer of the present invention, its puddler and paddle covers special glass lining bottom glaze, has corrosion-resistant, abrasion-resistant, oxidation resistant performance.
Description
Technical field
The present invention relates to enamel glass stirrer.
Background technology
Enamel glass stirrer is conventional chemical industry equipment, and the puddler and paddle outer wall of enamel glass stirrer typically cover
There is glass lining bottom glaze, the performance of glass lining bottom glaze directly affects the using effect of enamel glass stirrer.
The content of the invention
It is an object of the invention to provide a kind of enamel glass stirrer, it is special that the outer wall of its puddler and paddle covers
Glass lining bottom glaze, have corrosion-resistant, abrasion-resistant, oxidation resistant performance.
To achieve the above object, the technical scheme is that designing a kind of enamel glass stirrer, including puddler and stir
Mix leaf；The outer wall of the puddler and paddle has been covered each by glass lining bottom glaze；The glass lining bottom glaze is by following components group
Into：Alundum (Al2O3), silica, 1-hydroxy ethylidene-1,1-diphosphonic acid, 4 bromide, di-n-butyl phosphite salt, alkali formula molybdic acid
Calcium zinc, phosphorus zinc chromate, nanometer silicon carbide, azodiisobutyronitrile, calcine trautwinite, NVP, normal-butyl naphthalene
Sodium sulfonate.
Preferably, the glass lining bottom glaze is composed of the following components by weight：
15 parts of alundum (Al2O3)s,
40 parts of silica,
2~3 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids,
3~5 parts of 4 bromides,
1~3 portion of di-n-butyl phosphite salt,
2~3 parts of alkali formula calcium molybdate zinc,
1~3 part of phosphorus zinc chromate,
2~4 parts of nanometer silicon carbides,
1~2 part of azodiisobutyronitrile,
1~3 part of calcining trautwinite,
2~4 parts of NVPs,
4~6 parts of normal-butyl sodium naphthalene sulfonates.
Preferably, the glass lining bottom glaze is composed of the following components by weight：
15 parts of alundum (Al2O3)s,
40 parts of silica,
2.3 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids,
3.5 parts of 4 bromides,
1.3 portions of di-n-butyl phosphite salt,
2.3 parts of alkali formula calcium molybdate zinc,
1.3 parts of phosphorus zinc chromates,
2.4 parts of nanometer silicon carbides,
1.2 parts of azodiisobutyronitriles,
1.3 parts of calcining trautwinites,
2.4 parts of NVPs,
4.6 parts of normal-butyl sodium naphthalene sulfonates.
The advantages of the present invention are：A kind of enamel glass stirrer is provided, its puddler and paddle it is outer
Wall covers special glass lining bottom glaze, has corrosion-resistant, abrasion-resistant, oxidation resistant performance.
Embodiment
With reference to embodiment, the embodiment of the present invention is further described.Following examples are only used for more
Add and clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied is：
A kind of enamel glass stirrer, including puddler and paddle；The outer wall of the puddler and paddle has been covered each by warding off
Glass ground-coat enamel；The glass lining bottom glaze is composed of the following components：Alundum (Al2O3), silica, 1-hydroxy ethylidene-1,1-diphosphonic acid, tetramethyl
Base ammonium bromide, di-n-butyl phosphite salt, alkali formula calcium molybdate zinc, phosphorus zinc chromate, nanometer silicon carbide, azodiisobutyronitrile, calcining
Trautwinite, NVP, normal-butyl sodium naphthalene sulfonate.
Preferably, the glass lining bottom glaze is composed of the following components by weight：
15 parts of alundum (Al2O3)s,
40 parts of silica,
2~3 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids,
3~5 parts of 4 bromides,
1~3 portion of di-n-butyl phosphite salt,
2~3 parts of alkali formula calcium molybdate zinc,
1~3 part of phosphorus zinc chromate,
2~4 parts of nanometer silicon carbides,
1~2 part of azodiisobutyronitrile,
1~3 part of calcining trautwinite,
2~4 parts of NVPs,
4~6 parts of normal-butyl sodium naphthalene sulfonates.
Preferably, the glass lining bottom glaze is composed of the following components by weight：
15 parts of alundum (Al2O3)s,
40 parts of silica,
2.3 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids,
3.5 parts of 4 bromides,
1.3 portions of di-n-butyl phosphite salt,
2.3 parts of alkali formula calcium molybdate zinc,
1.3 parts of phosphorus zinc chromates,
2.4 parts of nanometer silicon carbides,
1.2 parts of azodiisobutyronitriles,
1.3 parts of calcining trautwinites,
2.4 parts of NVPs,
4.6 parts of normal-butyl sodium naphthalene sulfonates.
The outer wall of enamel glass stirrer of the present invention, its puddler and paddle covers special glass lining bottom glaze, has
Corrosion-resistant, abrasion-resistant, oxidation resistant performance.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (3)
1. enamel glass stirrer, it is characterised in that including puddler and paddle；The outer wall difference of the puddler and paddle
Covered with glass lining bottom glaze；The glass lining bottom glaze is composed of the following components：Alundum (Al2O3), silica, hydroxy ethylidene two
Phosphonic acids, 4 bromide, di-n-butyl phosphite salt, alkali formula calcium molybdate zinc, phosphorus zinc chromate, nanometer silicon carbide, azo two are different
Butyronitrile, calcine trautwinite, NVP, normal-butyl sodium naphthalene sulfonate.
2. enamel glass stirrer according to claim 1, it is characterised in that the glass lining bottom glaze by weight by with
The following group packet into：
15 parts of alundum (Al2O3)s,
40 parts of silica,
2~3 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids,
3~5 parts of 4 bromides,
1~3 portion of di-n-butyl phosphite salt,
2~3 parts of alkali formula calcium molybdate zinc,
1~3 part of phosphorus zinc chromate,
2~4 parts of nanometer silicon carbides,
1~2 part of azodiisobutyronitrile,
1~3 part of calcining trautwinite,
2~4 parts of NVPs,
4~6 parts of normal-butyl sodium naphthalene sulfonates.
3. enamel glass stirrer according to claim 2, it is characterised in that the glass lining bottom glaze by weight by with
The following group packet into：
15 parts of alundum (Al2O3)s,
40 parts of silica,
2.3 parts of 1-hydroxy ethylidene-1,1-diphosphonic acids,
3.5 parts of 4 bromides,
1.3 portions of di-n-butyl phosphite salt,
2.3 parts of alkali formula calcium molybdate zinc,
1.3 parts of phosphorus zinc chromates,
2.4 parts of nanometer silicon carbides,
1.2 parts of azodiisobutyronitriles,
1.3 part calcines trautwinite,
2.4 parts of NVPs,
4.6 parts of normal-butyl sodium naphthalene sulfonates.