CN107587141A - It is applicable the low bubble cleaning agent that steel product exempts from secondary rinsing - Google Patents
It is applicable the low bubble cleaning agent that steel product exempts from secondary rinsing Download PDFInfo
- Publication number
- CN107587141A CN107587141A CN201711000568.3A CN201711000568A CN107587141A CN 107587141 A CN107587141 A CN 107587141A CN 201711000568 A CN201711000568 A CN 201711000568A CN 107587141 A CN107587141 A CN 107587141A
- Authority
- CN
- China
- Prior art keywords
- cleaning agent
- steel product
- low bubble
- exempting
- secondary rinsing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of low bubble cleaning agent for being applicable steel product and exempting from secondary rinsing, it is made up of the raw material of following weight percents：Citric acid 3~4%, nonionic surfactant 7~8%, EDTA 4Na0.4~0.5%, NaOH1~2%, sodium gluconate 3~4%, triethanolamine 0.5~0.7%, water surplus, the organic acid is citric acid, the surfactant is nonionic surfactant RQ 129, the complexing agent is EDTA 4Na, the bases is NaOH, the organic salt is sodium gluconate, and the solubilizer is triethanolamine.The present invention is aqueous cleaning agent, nonflammable explosive, is nontoxic free of contamination environmental type cleaning product, average detergency is 99.99, and average scavenging period is 2min, 40 DEG C of cleaning temperature, metal corrosion test result is 0 grade, has larger market competition potentiality.
Description
Technical field
The invention belongs to equipment cleaning field, is related to metal cleaning, and especially a kind of applicable steel product exempts from secondary rinsing
Low bubble cleaning agent.
Background technology
In recent years, as the horizontal development of world industry, cleaning technique have the development advanced by leaps and bounds, the requirement to cleaning
More and more higher, cleaning technique develop and are used widely in multiple fields such as electronic information, Aero-Space, machineries, are to determine
Determine the guarantee of properties of product.
According to retrieval, patent document related to the application as follows is found, specific disclosure is as follows：
1st, a kind of low bubble cleaning agent and preparation method thereof (CN104313614A), cleaning agent raw material is following by weight including
Component：Dodecyl sodium sulfate 0.3~5.0%, alkylolamides 1.0~3.6%, diethanol amine 5~8%, zinc sulfate 0.2~
3.0%th, glucolactone 10~12%, sodium carbonate 3~6%, dipropylene glycol methyl ether 0.3~1.2%, fluorohydrocarbon base are modified
Polysiloxanes 0.1~0.3%, sodium hydroxide 0.9~2.0% and deionized water 50~79%.
2nd, water base low bubble cleaning agent in metal surface used for hot spraying and preparation method thereof (CN104789915A), its raw material composition
Including A, B amount component, by volume 4 during preparation：1 mixing, wherein component A includes by weight：Ethylenediamine tetra-acetic acid 4-8 parts,
Polyethers 11-18 parts, trihydroxy ethylamine 10-15 parts, octadecenic acid 1-4 parts, dichloromethane 5-10 parts, vinyl bis-stearamides
10-17 parts, alkyl benzene calcium sulfonate 5-8 parts, the double pungent primary alkyl zinc salt 2-4 parts of sulphur phosphorus, BTA 12-15 parts, antioxidant 4-6
Part, defoamer 6-8 parts, water 75-80 parts；B component includes by weight：Sodium carbonate 14-16 parts, butanediol 3-8 parts, gluconic acid
Sodium 5-7 parts, triethylamine urea 6-8 parts, polyoxyethylene aliphatic alcohol ether 17-19 parts, alkanolamide 3-6 parts, water 40-55 parts.
The application and above-mentioned patent document disclosure are had any different technical characteristic, and its constituent and using effect are also deposited
In very big difference.
The content of the invention
It is an object of the invention in place of overcome the deficiencies in the prior art, there is provided a kind of suitable for the clear of various metals material
Wash, the low bubble cleaning agent for being applicable steel product and exempting from secondary rinsing that cleaning performance is good, foam is few, client can be needed according to oneself by
Various metals material is put together cleaning, avoids the troublesome applicable steel product of cleaning caused by single cleaning agent from exempting from secondary drift
The low bubble cleaning agent washed.
The present invention solves its technical problem and takes following technical scheme to realize：
A kind of low bubble cleaning agent for being applicable steel product and exempting from secondary rinsing, is made up of the raw material of following weight percents：
Moreover, the nonionic surfactant is RQ-129.
Moreover, the composition and percentage by weight of the cleaning agent are：
A kind of preparation method for being applicable steel product and exempting from the low bubble cleaning agent of secondary rinsing, method and step are as follows：
(1) EDTA-4Na is first added to the water dissolving；
(2) again by citric acid, sodium gluconate, NaOH, triethanolamine, RQ-129 be sequentially added into dissolving in (1),
Stir；
(3) cleaning temperature of the cleaning agent is controlled at 40~60 DEG C.
Moreover, for the copper alloy of non-refractory, cleaning temperature is less than 45 DEG C.
Advantages of the present invention and beneficial effect：
1st, this cleaning agent is answered nonionic surfactant, organic acid, complexing agent, bases, organic salt, solubilizer
Match somebody with somebody, adjust corresponding proportion, the cleaning agent blended adapts to the degreasing degreasing of various metal materials and low foaming feature, cleaning temperature
Then general control is 40~60 DEG C (copper alloy non-refractory, temperature general control is below 45 DEG C).
2nd, the present invention is aqueous cleaning agent, nonflammable explosive, is nontoxic free of contamination environmental type cleaning product,
Average detergency is 99.99, equal with the cleaning agent (98.66%) and commercially available cleaning agent (98.87%) that are not added with citric acid composition
It is significantly increased, average scavenging period is 2min, and 40 DEG C of cleaning temperature, metal corrosion test result is 0 grade, has larger city
Field competition potential.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not limit
Qualitatively, it is impossible to which protection scope of the present invention is limited with this.
Embodiment 1
A kind of low bubble cleaning agent for being applicable steel product and exempting from secondary rinsing, is made up of the raw material of following weight percents：
A kind of preparation method for being applicable steel product and exempting from the low bubble cleaning agent of secondary rinsing, method and step are as follows：
(1) complexing agent is first added to the water dissolving；
(2) solubilizer, organic salt, bases, organic acid, surfactant are sequentially added into dissolving in (1) again, stirred
Mix uniformly；
(3) cleaning temperature of the cleaning agent is controlled at 40 DEG C.
Moreover, for the copper alloy of non-refractory, cleaning temperature is less than 40 DEG C.
Embodiment 2
A kind of low bubble cleaning agent for being applicable steel product and exempting from secondary rinsing, is made up of the raw material of following weight percents：
A kind of preparation method for being applicable steel product and exempting from the low bubble cleaning agent of secondary rinsing, method and step are as follows：
(1) complexing agent is first added to the water dissolving；
(2) solubilizer, organic salt, bases, organic acid, surfactant are sequentially added into dissolving in (1) again, stirred
Mix uniformly；
(3) cleaning temperature of the cleaning agent is controlled at 60 DEG C.
Embodiment 3
A kind of low bubble cleaning agent for being applicable steel product and exempting from secondary rinsing, is made up of the raw material of following weight percents：
A kind of preparation method for being applicable steel product and exempting from the low bubble cleaning agent of secondary rinsing, method and step are as follows：
(1) complexing agent is first added to the water dissolving；
(2) solubilizer, organic salt, bases, organic acid, surfactant are sequentially added into dissolving in (1) again, stirred
Mix uniformly；
(3) cleaning temperature of the cleaning agent is controlled at 30-40 DEG C.
This product is adapted to steel product, removes surface grease, machines grease, and grease viscosity is larger, and high pressure is (8-10 big
Atmospheric pressure) cleaning showers, secondary rinsing is not needed after cleaning, because ironware rinsing can add water, easily causes corrosion.Clearly
Wash 2-3 minutes, 30-40 DEG C of temperature.
Comparative experimental data
Claims (5)
- A kind of 1. low bubble cleaning agent for being applicable steel product and exempting from secondary rinsing, it is characterised in that：By the original of following weight percents Material composition：
- 2. the low bubble cleaning agent according to claim 1 for being applicable steel product and exempting from secondary rinsing, it is characterised in that：It is described non- Ionic surface active agent is RQ-129.
- 3. the low bubble cleaning agent according to claim 1 or 2 for being applicable steel product and exempting from secondary rinsing, it is characterised in that：Institute The composition and percentage by weight for stating cleaning agent be：
- 4. the preparation method for being applicable steel product and exempting from the low bubble cleaning agent of secondary rinsing described in claim 1, it is characterised in that： Method and step is as follows：(1) EDTA-4Na is first added to the water dissolving；(2) citric acid, sodium gluconate, NaOH, triethanolamine, RQ-129 are sequentially added into dissolving in (1), stirring again Uniformly；(3) cleaning temperature of the cleaning agent is controlled at 40~60 DEG C.
- 5. the preparation method according to claim 4 for being applicable steel product and exempting from the low bubble cleaning agent of secondary rinsing, its feature It is：For the copper alloy of non-refractory, cleaning temperature is less than 45 DEG C.