CN107586076B - Preparation method for concrete - Google Patents
Preparation method for concrete Download PDFInfo
- Publication number
- CN107586076B CN107586076B CN201710987891.8A CN201710987891A CN107586076B CN 107586076 B CN107586076 B CN 107586076B CN 201710987891 A CN201710987891 A CN 201710987891A CN 107586076 B CN107586076 B CN 107586076B
- Authority
- CN
- China
- Prior art keywords
- parts
- mud
- concrete
- fibre
- construction waste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of preparation method for concrete, the concrete is made of the material of following parts by weight: 35-40 parts of cement, 15-20 parts of mud, 15-20 parts of cinder, 8-12 parts of construction waste, 5-8 parts of reinforcing fibre, 2-3 parts of waterproof additive;The reinforcing fibre is made of the material of following parts by weight: 5-8 parts of glass fibre, 2-3 parts of polypropylene fibre, 2-3 parts of plastic-steel fabric, 5-6 parts of Corvic;Preparation method is the following steps are included: (1) construction waste is handled;(2) mud deodorization;(3) reinforcing fibre is prepared;(4) waterproof additive (5) mixing is prepared.
Description
Technical field
The invention belongs to technical field of concrete preparation, more particularly, to a kind of preparation method for concrete.
Background technique
Concrete is one of the present age most important civil engineering material.It is by cementitious material, granular aggregat, water and
The additive and admixture being added when necessary are prepared by a certain percentage, through uniform stirring, closely knit molding, one made of maintenance hardening
The artificial stone material of kind.Cement concrete is needed using to a large amount of natural sand, rubble during preparation, but these resource categories
It is long-term to exploit and use natural sand and rubble in non-renewable resources, it will being gradually reduced for these non-renewable resources is caused,
It will even influence whether ecological environment, irreversible destruction is caused to ecology.
Summary of the invention
The present invention for overcome the deficiencies in the prior art, provides one kind and makes full use of resource, energy-saving and environment-friendly to be used for coagulation
The preparation method of soil.
To achieve the goals above, the invention adopts the following technical scheme: a kind of preparation method for concrete;It is described
Concrete is made of the material of following parts by weight: 35-40 parts of cement, 15-20 parts of mud, and 15-20 parts of cinder, construction waste 8-12
Part, 5-8 parts of reinforcing fibre, 2-3 parts of waterproof additive;The reinforcing fibre is made of the material of following parts by weight: glass fibre
5-8 parts, 2-3 parts of polypropylene fibre, 2-3 parts of plastic-steel fabric, 5-6 parts of Corvic;Preparation method the following steps are included:
(1) construction waste is handled: recycled concrete aggregate being cut into bulk by cutting machine, and by drilling machine in bulk
The different location of concrete is punched;By discarded brick, tile is ground into the particle of 80 mesh by stone crusher;It later will be upper
It states construction waste and is mixed to form construction waste A together;
(2) mud deodorization: from river, lake, pond, sedimentation basin, after the place such as moat obtains mud, in the ratio of 1:1.5
Calcium oxide is launched into mud, and carries out standing for 24 hours;Manually mud was stirred using rake every 20-30 minutes during standing
Disorderly;After for 24 hours, mud is dried, so that mud natural air drying;
(3) prepare reinforcing fibre: Corvic be heated to 140 DEG C to soften Corvic, it is backward soft
Glass fibre, polypropylene fibre, plastic-steel fabric are added in the Corvic of change;Continue to be heated to 160 DEG C, sustained response
It after 10-15min, is cooled to room temperature, reinforcing fibre is made;
(4) it prepares waterproof additive: calcium stearate being put into the ratio of 1:21 into ethanol solution, is melted to calcium stearate
After change, then water-reducing agent is put into ethanol solution, calcium stearate, dispersing agent, magnesium lime, swelling agent, obtained waterproof after mixing
Additive;
(5) it mixes: by cement, through step (2) treated mud, cinder, through step (1) treated construction waste,
Through reinforcing fibre made from step (3), put into through waterproof additive made from step (4) into concrete mixer, to stirring
Water is added in machine, starts blender, stirs to get concrete.
The present invention improves resource utilization by effectively reducing the use of sandstone raw material using construction waste as raw material;And
Since construction waste has played use, to effectively reduce building waste to appropriation of land and to soil, the pollution of water body, pole
Big degree improves ecological environment;And different processing is carried out according to different building wastes, give full play to construction waste
Value improves resource utilization;Concrete block is cut into bulk, and hardness is larger, can enhance the secured intensity of pile foundation;Brick and watt
The intensity of piece is lower, to be crushed, is sufficiently mixed with cement, is relatively made for bulk, can more be fully utilized, mention
The utilization rate of high building rubbish;After particle is made simultaneously, the usage amount of cement can be reduced, to save construction cost;And pass through
Drill to concrete block, during concrete formation and solidification, guarantee cement can through hole enter to coagulation
In soil block, enhances the firmness of the connection between concrete block and cement, effectively improve the intensity of concrete;Mud is passing through dispensing
After calcium oxide, the peculiar smell in mud will be effectivelyed removed, and prevent from containing peculiar smell in last concrete obtained.
Mud is used in the present invention, cinder, the materials such as construction waste prepare cement concrete, to effectively reduce day
The use of right sand and rubble, effectively reduces the waste to non-renewable resources, prevents resource from irreversible shortage occur;Its
Secondary also to prevent mud, cinder, these waste materials of construction waste pollute ecological environment or living environment, without independent again
These waste materials are handled, ecological environment is not only strengthened, also effectively reduce the processing cost to waste material, municipal administration is reduced and throws
Enter;Reinforcing fibre is polymerized by multiple fiber, for comparing single fiber, has the characteristic and high intensity of multiple fiber
Toughness, effectively improve be made after concrete tension, bending resistance, shearing strength.
Further, the waterproof additive is made of the material of following parts by weight: 5-10 parts of water-reducing agent, calcium stearate 3-
5 parts, 3-5 parts of dispersing agent, 2-3 parts of magnesium lime, 1-2 parts of swelling agent;It can be reduced in concrete preparation process by water-reducing agent
Water consumption, calcium stearate and swelling agent can increase the swelling volume of concrete effectively when concrete is hardened, to prevent from mixing
Solidifying soil it is really up to the mark and there is a situation where dry and cracked, joint filling effectively is carried out to cement;To by water-reducing agent, calcium stearate, swelling agent it
Between cooperation, effectively realize the reduction of water consumption, while the case where cracking will not be caused because water consumption is very few again.
Further, the magnesium lime is the lime stone of the ingredient containing following mass percent: CaO >=49%, H2O
≤ 0.5%, MgO >=3.8%, SiO2≤1.5%,S≤0.035%。
In conclusion the invention has the following advantages: using mud, cinder, the materials such as construction waste prepare water
Cement concrete reduces the waste to non-renewable resources, prevents resource from irreversible shortage occur;Secondly it can also prevent from becoming silted up
Mud, cinder, these waste materials of construction waste pollute ecological environment or living environment, without again individually to these waste materials into
Row processing, not only strengthens ecological environment, also effectively reduces the processing cost to waste material, reduces municipal administration investment.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention.
Fig. 2 is the enlarged drawing in Fig. 1 at B.
Fig. 3 is the cooperation schematic diagram of power-assist component and paddle.
Fig. 4 is the cross-sectional view of Fig. 3.
Specific embodiment
In order to make those skilled in the art better understand the present invention program, below in conjunction in the embodiment of the present invention
Attached drawing, technical solution in the embodiment of the present invention carry out clear, complete description.
Embodiment 1
A kind of concrete is made of the material of following parts by weight: 35 parts of cement, 15 parts of mud, and 15 parts of cinder, construction waste
8 parts, 5 parts of reinforcing fibre, 2 parts of waterproof additive;Wherein, the reinforcing fibre is made of the material of following parts by weight: glass fibers
5 parts, 2 parts of polypropylene fibre, 2 parts of plastic-steel fabric, 5 parts of Corvic of dimension;Wherein, the waterproof additive is by following weight
The material composition of part: 5 parts of water-reducing agent, 3 parts of calcium stearate, 3 parts of dispersing agent, 2 parts of magnesium lime, 1 part of swelling agent;Wherein, described
Water-reducing agent is polycarboxylate water-reducer;Wherein, the magnesium lime is the lime stone of the ingredient containing following mass percent:
90.47%CaO, 0.5%H2O, 8%MgO, 1%SiO2, 0.03%S;Wherein, the swelling agent is by calcium oxide, and calcium sulphoaluminate, water is with 1:
1.5:2 ratio be mixed to get.
Above-mentioned concrete is prepared by following preparation method, specifically includes the following steps:
(1) construction waste is handled: recycled concrete aggregate being cut into bulk by cutting machine, blocky concrete can be not advise
Then shape, but control is in the range of volume is less than 8 cubic centimetres;Later by drilling machine in the different positions of blocky concrete
It sets and is punched, the aperture of punched hole is 0.5cm;Later by discarded brick, tile is ground into 80 purposes by stone crusher
Particle;The construction waste after above-mentioned process is mixed to form construction waste A together later;(2) mud deodorization: from river, lake, pond
The pool, sedimentation basin after the place such as moat obtains mud, launch calcium oxide into mud in the ratio of 1:1.5, and carry out for 24 hours
It stands;Manually mud was confused using rake every 20-30 minutes during standing;After for 24 hours, mud is dried, is made
It obtains mud natural air drying and forms mud block;
(3) it prepares reinforcing fibre: taking glass fibre 5kg, polypropylene fibre 2kg, plastic-steel fabric 2kg, Corvic
5kg;Corvic is heated to 140 DEG C in the boiler later so that Corvic is softened, backward softening after
Corvic in be added glass fibre, polypropylene fibre, plastic-steel fabric;Continue heating boiler and makes boiler heating extremely
160 DEG C, after material sustained response 10-15min in boiler;10h is stood, so that the material in boiler and boiler is cooled to often
Reinforcing fibre is made in temperature;(4) it prepares waterproof additive: taking calcium oxide 1kg, calcium sulphoaluminate 1.5kg, water 2kg, by blender
Swelling agent is made after mixing;Take feed ethanol solution 36kg, water-reducing agent 5kg, calcium stearate 3kg, dispersing agent 3kg, magnesium lime
2kg, swelling agent 1kg obtained above;The ethanol solution of above-mentioned acquirement is put into reaction pot later, later again into reaction pot
Calcium stearate is put into, blender is started, so that calcium stearate melts in ethanol solution;Backward reaction pot in be added diminishing
Agent, calcium stearate, dispersing agent, magnesium lime, swelling agent, and reaction pot is heated to 70 DEG C, start blender later, to material
Waterproof additive is made after mixing and dissolving;
(5) it mixes: taking cement 70kg, mud 30kg, cinder 30kg, through step (1) treated construction waste 16kg,
Through reinforcing fibre 10kg made from step (3), through waterproof additive 4kg made from step (4), water 25kg;It is taken later by above-mentioned
The cement obtained, mud, cinder, construction waste, reinforcing fibre, waterproof additive, water are put into concrete mixer, are started
Blender obtains concrete after mixing evenly.
As shown in Figure 1, the concrete mixer includes rack 1, teeter chamber 2, agitating device and driving device;Institute
It states teeter chamber 2 to be made of stainless steel, and rotationally sets up on the rack, the agitating device is set in teeter chamber, the stirring
Device includes that agitating shaft 31 and the paddle 32 on agitating shaft can stir specifically, the paddle 32 is helical form setting
When mixing axis rotation, it is stirred to indoor material is stirred;The driving device includes the first driving part 4, for driving the
The actuator 5 of one driving part rotation and the second driving part 6 being sequentially connected with first driving part, when actuator 5 is dynamic
When making, first driving part 4 drives the teeter chamber to rotate, and second driving part 6 then drives agitating device to compare
Teeter chamber is rotated backward, and guarantees to mix between cement and other materials sufficiently, concrete quality obtained is high;And with biography
In the case that system blender reaches identical mixing effect, the energy consumption of mixing plant can be reduced to original 50%, thus not changing
In the case where stirring efficiency, good energy-saving effect is reached.
Specifically, first driving part 4 includes driving link 41, driven member 42, driving member 43, reduction 44 and defeated
Part 45 out, the actuator 5 are that firsthand motor, the driving link 41 are the skin being connected with the motor output shaft on the market
Belt wheel, the driven member 42 are rotatablely connected with the driving link, and preferred, realize transmission connection using belt between the two;Institute
Stating driven member 42 also is belt pulley, and one end of belt is set on driving link, and the other end is set on driven member;The driving member
43 be to be coaxially disposed, and driven member 42 is the gear being connected on driving member 43 with the driven member 42, the reduction setting
It is 3, and reduction is the gear that diameter is less than driven member, the output is the metalwork of an annular, the metalwork inner wall
Above evenly spaced that multiple latches are distributed with, output is disposed around outside multiple reduction, and the latch phase of reduction and output
Engagement;Preferably, the driving member 43 and driven member 42 are movably set in outside the agitating shaft 31, can be carried out with respect to agitating shaft
Rotation, and not will drive agitating shaft and rotate together;Preferably, correspond on agitating shaft on the position of driving member 43 and driven member 42
It is respectively equipped with a protrusion, the position of driving member 43 and driven member 42 is defined respectively by the protrusion.
Specifically, second driving part 6 includes the input tooth 61 with the driven member synchronization action, with the input
The deceleration tooth 62 that tooth 61 is sequentially connected and the output tooth 63 with deceleration tooth transmission connection, the output tooth 63 and institute
Agitating shaft 31 is stated to be connected;Specifically, the input tooth is the gear being connected on driven member, and position is to correspond to and driving member
The other side on, the deceleration tooth 62 includes two gears being fixed together, and being relatively large in diameter for one of gear is another
The diameter of a gear is smaller;And the gear being relatively large in diameter is meshed with output tooth, the lesser gear of diameter and output tooth phase
Engagement;The output tooth is gear, and exports tooth and be connected with agitating shaft, can drive stirring when to exporting tooth rotation
Axis rotation.
Further, the rack 1 be equipped with a positioning seat 11, the positioning seat be by it is stainless steel welded at direction frame
Frame;The actuator may be provided on the positioning seat 11;Preferably, which is preferably direct current generator, can a period of time into
Row rotates forward, and is inverted for a period of time, more uniform for the stirring of concrete;Specific to rotate forward, the time of reversion is according to reality
Demand is formulated, therefore is not specifically limited;It when actuator rotates forward, is rotated clockwise, is driven by belt driven transmission part
Part follows driven member to be rotated clockwise, and driving output rotates counterclockwise, and teeter chamber is driven to rotate counterclockwise;And output
It is realized and is slowed down by reduction;Inputting tooth simultaneously follows driven member to rotate clockwise, and driving deceleration tooth rotates counterclockwise, and subtracts
Fast tooth driving output tooth rotates clockwise, and drives agitating shaft to rotate clockwise, so that teeter chamber and agitating shaft can be same
It realizes and rotates backward under the driving of actuator;When actuator reversion, above-mentioned component is rotated backward.
In order to reduce the abrasion between paddle and teeter chamber, we are in the paddle 32 and 2 inner wall of teeter chamber
Between be provided with assisting device for reducing frictional force between the two;Specifically, the assisting device includes being spaced apart
Multiple power-assist components 7, which includes cover 71 and is set to and covers intracorporal rolling member 72, and the rolling member is steel ball,
It is the receiving portion 711 of the upper outlet body 71 including tubular, the interconnecting piece 712 being connected with the paddle and for connecting the receiving
The tapered portion 713 in portion and interconnecting piece, described accommodation section 711 may be configured as tubular, and the diameter of receiving portion 711 should be set as big
In the diameter of rolling member;The diameter that the diameter of the interconnecting piece 712 is less than rolling member is arranged, and the two sides of interconnecting piece are respectively to extension
It stretches to form two flanges, two flanges are connected by screw with paddle 32, so that cover can be dismantled with respect to paddle 32;
In order to facilitate in rolling member merging cover, we are symmetrically arranged with two open slots 714 on the interconnecting piece, which is
The setting of " V " character form structure, which extends in the tapered portion 713;Further, the rolling member 72 to
Small part is pierced by the cover 71, so that rolling member is in contact with stirring chamber interior walls;Specifically, 711 lower surface of receiving portion is set
There are circular opening 715 and multiple annular material leakage channels 716, the width in the material leakage channel 716 is preferably 1.5cm;The rolling
Part lower part may pass through the opening, to extend out to the outer surface lower part of cover;It is spaced between the multiple annular material leakage channel 716
Uniformly, and centered on the center of the opening, the radius in multiple annular material leakage channels 716 successively increases outward;As preferred
, the evenly spaced material leakage through slot 717 that multiple bar shapeds are distributed on 711 side wall of described accommodation section, and the width of material leakage through slot 717
Degree is set as 2cm.
Screw can not be dismantled in order to prevent, we are respectively provided with a flexible layer in the interconnecting piece 712 on outer surface
91, which is made of rubber material;And 92 both ends of screw are bolted with seal cap 93 respectively, the seal cap 93 is by stainless
Steel is made, and inner wall is equipped with internal screw thread, and lower part is flaring structure setting, and flaring structure here refers to seal cap lower part
Opening diameter is greater than the diameter of cap body part.
Embodiment 2
A kind of concrete is made of the material of following parts by weight: 40 parts of cement, 20 parts of mud, and 20 parts of cinder, construction waste
12 parts, 8 parts of reinforcing fibre, 3 parts of waterproof additive;Wherein, the reinforcing fibre is made of the material of following parts by weight: glass fibers
8 parts, 3 parts of polypropylene fibre, 3 parts of plastic-steel fabric, 6 parts of Corvic of dimension;Wherein, the waterproof additive is by following weight
The material composition of part: 10 parts of water-reducing agent, 5 parts of calcium stearate, 5 parts of dispersing agent, 3 parts of magnesium lime, 2 parts of swelling agent;Wherein, described
Water-reducing agent is polycarboxylate water-reducer;Wherein, the magnesium lime is the lime stone of the ingredient containing following mass percent:
85.47%CaO, 0.4%H2O, 13.1%MgO, 1%SiO2, 0.03%S;Wherein, the swelling agent is by calcium oxide, calcium sulphoaluminate, water
It is mixed to get with the ratio of 1:1.5:2.
Above-mentioned concrete is prepared by following preparation method, specifically includes the following steps:
(1) construction waste is handled: recycled concrete aggregate being cut into bulk by cutting machine, blocky concrete can be not advise
Then shape, but control is in the range of volume is less than 8 cubic centimetres;Later by drilling machine in the different positions of blocky concrete
It sets and is punched, the aperture of punched hole is 0.5cm;Later by discarded brick, tile is ground into 80 purposes by stone crusher
Particle;The construction waste after above-mentioned process is mixed to form construction waste A together later;(2) mud deodorization: from river, lake, pond
The pool, sedimentation basin after the place such as moat obtains mud, launch calcium oxide into mud in the ratio of 1:1.5, and carry out for 24 hours
It stands;Manually mud was confused using rake every 20-30 minutes during standing;After for 24 hours, mud is dried, is made
It obtains mud natural air drying and forms mud block;
(3) it prepares reinforcing fibre: taking glass fibre 8kg, polypropylene fibre 3kg, plastic-steel fabric 3kg, Corvic
6kg;Corvic is heated to 140 DEG C in the boiler later so that Corvic is softened, backward softening after
Corvic in be added glass fibre, polypropylene fibre, plastic-steel fabric;Continue heating boiler and makes boiler heating extremely
160 DEG C, after material sustained response 15min in boiler;10h is stood, so that the material in boiler and boiler is cooled to room temperature,
Reinforcing fibre is made;(4) it prepares waterproof additive: taking calcium oxide 1kg, calcium sulphoaluminate 1.5kg, water 2kg is mixed by blender
Swelling agent is made afterwards;Take feed ethanol solution 105kg, water-reducing agent 10kg, calcium stearate 5kg, dispersing agent 5kg, magnesium lime
3kg, swelling agent 2kg obtained above;The ethanol solution of above-mentioned acquirement is put into reaction pot later, later again into reaction pot
Calcium stearate is put into, blender is started, so that calcium stearate melts in ethanol solution;Backward reaction pot in be added diminishing
Agent, calcium stearate, dispersing agent, magnesium lime, swelling agent, and reaction pot is heated to 70 DEG C, start blender later, to material
Waterproof additive is made after mixing and dissolving;
(5) it mixes: taking cement 80kg, mud 40kg, cinder 40kg, through step (1) treated construction waste 24kg,
Through reinforcing fibre 16kg made from step (3), through waterproof additive 6kg made from step (4), water 40kg;It is taken later by above-mentioned
The cement obtained, mud, cinder, construction waste, reinforcing fibre, waterproof additive, water are put into concrete mixer, are started
Blender obtains concrete after mixing evenly.
The structure of concrete mixer is in the same manner as in Example 1, repeats no more.
Embodiment 2
A kind of concrete is made of the material of following parts by weight: 38 parts of cement, 18 parts of mud, and 18 parts of cinder, construction waste
10 parts, 7 parts of reinforcing fibre, 2.5 parts of waterproof additive;Wherein, the reinforcing fibre is made of the material of following parts by weight: glass
6 parts of fiber, 2.5 parts of polypropylene fibre, 2.5 parts of plastic-steel fabric, 5.5 parts of Corvic;Wherein, the waterproof additive by
The material of following parts by weight forms: 8 parts of water-reducing agent, 4 parts of calcium stearate, 4 parts of dispersing agent, 2.5 parts of magnesium lime, 2 parts of swelling agent;
Wherein, the water-reducing agent is polycarboxylate water-reducer;Wherein, the magnesium lime is the stone of the ingredient containing following mass percent
Lime stone: 87.47%CaO, 0.4%H2O, 11.31%MgO, 0.8%SiO2, 0.02%S;Wherein, the swelling agent is by calcium oxide, sulphur aluminium
Sour calcium, water are mixed to get with the ratio of 1:1.5:2.
Above-mentioned concrete is prepared by following preparation method, specifically includes the following steps:
(1) construction waste is handled: recycled concrete aggregate being cut into bulk by cutting machine, blocky concrete can be not advise
Then shape, but control is in the range of volume is less than 8 cubic centimetres;Later by drilling machine in the different positions of blocky concrete
It sets and is punched, the aperture of punched hole is 0.5cm;Later by discarded brick, tile is ground into 80 purposes by stone crusher
Particle;The construction waste after above-mentioned process is mixed to form construction waste A together later;(2) mud deodorization: from river, lake, pond
The pool, sedimentation basin after the place such as moat obtains mud, launch calcium oxide into mud in the ratio of 1:1.5, and carry out for 24 hours
It stands;Manually mud was confused using rake every 20 minutes during standing;After for 24 hours, mud is dried, so that becoming silted up
Mud natural air drying forms mud block;
(3) it prepares reinforcing fibre: taking glass fibre 6kg, polypropylene fibre 2.5kg, plastic-steel fabric 2.5kg, polyvinyl chloride
Resin 5.5kg;Corvic is heated to 140 DEG C in the boiler later, so that Corvic is softened, it is backward
Glass fibre, polypropylene fibre, plastic-steel fabric are added in Corvic after softening;Continue heating boiler and makes boiler liter
Temperature is to 160 DEG C, after material sustained response 15min in boiler;10h is stood, so that the material in boiler and boiler is cooled to
Reinforcing fibre is made in room temperature;(4) it prepares waterproof additive: taking calcium oxide 1kg, calcium sulphoaluminate 1.5kg, water 2kg, by stirring
Swelling agent is made after machine mixing;Take feed ethanol solution 84kg, water-reducing agent 8kg, calcium stearate 4kg, dispersing agent 4kg, magnesia stone
Grey 2.5kg, swelling agent 2kg obtained above;Later by the ethanol solution of above-mentioned acquirement investment reaction pot, Xiang Fanying again later
Calcium stearate is put into pot, starts blender, so that calcium stearate melts in ethanol solution;Backward reaction pot in be added subtract
Aqua, calcium stearate, dispersing agent, magnesium lime, swelling agent, and reaction pot is heated to 70 DEG C, start blender later, to object
Waterproof additive is made after mixing and dissolving in material;
(5) it mixes: taking cement 76kg, mud 36kg, cinder 36kg, through step (1) treated construction waste 20kg,
Through reinforcing fibre 14kg made from step (3), through waterproof additive 5kg made from step (4), water 40kg;It is taken later by above-mentioned
The cement obtained, mud, cinder, construction waste, reinforcing fibre, waterproof additive, water are put into concrete mixer, are started
Blender obtains concrete after mixing evenly.
The structure of concrete mixer is in the same manner as in Example 1, repeats no more.
Obviously, described embodiment is only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment should fall within the scope of the present invention.
Claims (3)
1. a kind of preparation method for concrete, it is characterised in that: the concrete is made of the material of following parts by weight: water
35-40 parts of mud, 15-20 parts of mud, 15-20 parts of cinder, 8-12 parts of construction waste, 5-8 parts of reinforcing fibre, waterproof additive 2-3
Part;The reinforcing fibre is made of the material of following parts by weight: 5-8 parts of glass fibre, 2-3 parts of polypropylene fibre, and plastic-steel fabric
2-3 parts, 5-6 parts of Corvic;Preparation method the following steps are included:
(1) construction waste is handled: recycled concrete aggregate being cut into bulk by cutting machine, and by drilling machine in blocky coagulation
The different location of soil is punched;By discarded brick, tile is ground into the particle of 80 mesh by stone crusher;It is built later by above-mentioned
It builds waste material and is mixed to form construction waste A together;
(2) mud deodorization: from river, lake, pond, sedimentation basin, after the place such as moat obtains mud, in the ratio of 1:1.5 to silt
Calcium oxide is launched in mud, and carries out standing for 24 hours;Manually mud was confused using rake every 20-30 minutes during standing;To
After for 24 hours, mud is dried, so that mud natural air drying;
(3) prepare reinforcing fibre: Corvic be heated to 140 DEG C to soften Corvic, soften backward
Glass fibre, polypropylene fibre, plastic-steel fabric are added in Corvic;Continue to be heated to 160 DEG C, sustained response 10-
It after 15min, is cooled to room temperature, reinforcing fibre is made;
(4) it prepares waterproof additive: calcium stearate is put into the ratio of 1:21 into ethanol solution, melt to calcium stearate
Afterwards, then into ethanol solution water-reducing agent, dispersing agent, magnesium lime, swelling agent, obtained waterproof additive after mixing are put into;
(5) it mixes: by cement, through step (2) treated mud, cinder, through step (1) treated construction waste, through step
Suddenly reinforcing fibre made from (3) is put into concrete mixer through waterproof additive made from step (4), into blender
Water is added, starts blender, stirs to get concrete.
2. a kind of preparation method for concrete according to claim 1, it is characterised in that: the waterproof additive by
The material of following parts by weight forms: 5-10 parts of water-reducing agent, 3-5 parts of calcium stearate, 3-5 parts of dispersing agent, 2-3 parts of magnesium lime, swollen
Swollen dose 1-2 parts.
3. a kind of preparation method for concrete according to claim 2, it is characterised in that: the magnesium lime be containing
There is the lime stone of the ingredient of following mass percent: CaO >=49%, H2O≤0.5%, MgO >=3.8%, SiO2≤ 1.5%, S≤
0.035%.