CN107585850A - A kind of purifying agent for polluted water and preparation method thereof - Google Patents
A kind of purifying agent for polluted water and preparation method thereof Download PDFInfo
- Publication number
- CN107585850A CN107585850A CN201711047127.9A CN201711047127A CN107585850A CN 107585850 A CN107585850 A CN 107585850A CN 201711047127 A CN201711047127 A CN 201711047127A CN 107585850 A CN107585850 A CN 107585850A
- Authority
- CN
- China
- Prior art keywords
- parts
- purifying agent
- polluted water
- water
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of purifying agent for polluted water and preparation method thereof.The purifying agent for polluted water zeolite powder is 80 150, and Na2Fe04 is 70 100 parts, and poly- propionamide is 1 10 parts, and ferric sulfate is 5 15 parts, and activated carbon is 5 30 parts, and calcium hydroxide is 10 20 parts, and sodium metasilicate is 20 60 parts, and copper sulphate is 1 10 parts, 15 parts of peromag.Purifying agent for polluted water purifying agent for polluted water provided by the invention provided by the invention can be purified preferably to water quality, with good environment protecting, siliceous in the purifying agent for polluted water, ferrate flocculent agent and calcic, the NEW TYPE OF COMPOSITE cleanser of magnesium ion, it overcomes existing inorganic water purification agent, flocculant goes the low deficiency of ammonia nitrogen phosphorus waste water effect, using silicon, calcium, magnesium, oxonium ion in water purification agent significant synergy complementation, reach and realize the purpose of the nuisances such as the synchronous ammonia nitrogen phosphorus removed in waste water, it is that a kind of performance is more excellent, noresidue toxin；The green phosphor high efficiency composition cleanser of non-secondary pollution.
Description
Technical field
The invention belongs to new energy and environmental protection and energy saving technical field, more particularly to a kind of purifying agent for polluted water and its preparation side
Method.
Background technology
China is the country of a water resources shortage, and insufficient total amount, spatial and temporal distributions are uneven, pollution is more serious.Cause
The factor that China's water resource lacks is a lot, such as water resource waste phenomenon is serious, water resource pollution aggravates, the management body of water resource
Make unsound.The water resource pollution in China is also mainly manifested in rivers and is constantly discharged into the dirts such as sewage, waste oil, waste liquid, chemicals
Thing is contaminated, surface water and groundwater all receives serious pollution, the river course around cities and towns, these pitch-black smelly pollutions of pond waters
Thing not only influences urban, produces stink, and can produce harm to human body through various channels.Therefore, accelerate at sewage
The paces of reason are very urgent.
The content of the invention
In view of the problems of prior art, it is an object of the invention to provide a kind of dirt that can be effectively improved water quality
Water scavengine agent.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of purifying agent for polluted water, including following parts by weight group
Point:Polymeric aluminium ferrum silicate is 80-200, and Na2Fe04 is 30-80 parts, and poly- propionamide is 5-15 parts, and ferric sulfate is 10-30 parts, living
Property charcoal is 5-10 parts, and calcium hydroxide is 20-30 parts, and sodium metasilicate is 10-25 parts, and copper sulphate is 1-10 parts, peromag 15-30
Part.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the purifying agent for polluted water includes following parts by weight of component：80 parts of polymeric aluminium ferrum silicates, 30 parts of ferric acid
Sodium, 5 parts of poly- propionamides, 10 parts of ferric sulfate, 5 parts of activated carbons, 20 parts of calcium hydroxides, 10 parts of sodium metasilicate, 1 part of copper sulphate, 15 parts of mistakes
Magnesia.
Further, the purifying agent for polluted water includes following parts by weight of component：200 parts of polymeric aluminium ferrum silicates, 80 parts of high ferros
Sour sodium, 15 parts of poly- propionamides, 30 parts of ferric sulfate, 10 parts of activated carbons, 30 parts of calcium hydroxides, 25 parts of sodium metasilicate, 10 parts of copper sulphate, 30
Part peromag.
Further, the purifying agent for polluted water includes following parts by weight of component：90 parts of polymeric aluminium ferrum silicates, 40 parts of ferric acid
Sodium, 8 parts of poly- propionamides, 20 parts of ferric sulfate, 7 parts of activated carbons, 25 parts of calcium hydroxides, 18 parts of sodium metasilicate, 6 parts of copper sulphate, 18 parts of mistakes
Magnesia.
Present invention also offers a kind of preparation method of purifying agent for polluted water to comprise the following steps：Weigh following parts by weight group
Point：Polymeric aluminium ferrum silicate is 80-200, and Na2Fe04 is 30-80 parts, and poly- propionamide is 5-15 parts, and ferric sulfate is 10-30 parts, living
Property charcoal is 5-10 parts, and calcium hydroxide is 20-30 parts, and sodium metasilicate is 10-25 parts, and copper sulphate is 1-10 parts, peromag 15-30
Part, said components are crushed and are uniformly mixed, and carry out drying process.
Embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
The invention provides a kind of purifying agent for polluted water, including following parts by weight of component:Polymeric aluminium ferrum silicate is 80-200, high
Sodium ferrite is 30-80 parts, and poly- propionamide is 5-15 parts, and ferric sulfate is 10-30 parts, and activated carbon is 5-10 parts, calcium hydroxide 20-
30 parts, sodium metasilicate is 10-25 parts, and copper sulphate is 1-10 parts, peromag 15-30 parts.
Inventor has carried out the screening experiment of substantial amounts of component and dosage early stage, is found surprisingly that, technology of the invention
Scheme is by reasonably matching and the combination of each component is with the effect that significantly purifies water and easily manufactured, purification
Quickly.
And Na2Fe04 is decomposed quickly to purification of water quality by Ferric Sulfate Hydrafe in said components, and water can be killed
Matter bacterium, so as to reduce its action period；Poly- propionamide helps solidifying ability synergistic purification water quality；Using physical absorption and chemical oxygen
Change synergy, making to purify water becomes apparent and thoroughly；Therefore it is ingenious in design, there is physical cleaning and chemicals collaboration to make
With coagulation effect is obvious, and purification is quick thorough, suitable for large-scale promotion application.
In addition, the pH after the medicament aquation of the present invention can be controlled in 7.5-9.5, and it can gradually form closely to have and be sustained
The calcium hydroxide of oxygen, magnesium silicate, the compound mineralization state deposit based on potassium silicate.Therefore, not only can be in rapid subsidence sewage
Particle suspensions and various objectionable impurities, while there is the sustained release oxygen-supplying function to water-bed shale, and can be formed after settling
The bed mud of tight structure, it can be applied to the processing of dyeing waste water, municipal pollution landscape water, cities and towns inland river black and odorous water.The present invention
It is a kind of siliceous, ferrate flocculent agent and calcic, the NEW TYPE OF COMPOSITE cleanser of magnesium ion, it overcomes existing inorganic water purification agent, wadding
The low deficiency of ammonia nitrogen phosphorus waste water effect is gone in solidifying agent, using silicon, calcium, magnesium, oxonium ion in water purification agent significant synergy complementation,
Reach and realize the purpose of the nuisances such as the synchronous ammonia nitrogen phosphorus removed in waste water, be that a kind of performance is more excellent, noresidue poison
Element；The green phosphor high efficiency composition cleanser of non-secondary pollution.
It is introduced below by specific embodiment.
Embodiment 1
A kind of purifying agent for polluted water, including following parts by weight of component：80 parts of polymeric aluminium ferrum silicates, 30 parts of Na2Fe04s, 5 parts poly-
Propionamide, 10 parts of ferric sulfate, 5 parts of activated carbons, 20 parts of calcium hydroxides, 10 parts of sodium metasilicate, 1 part of copper sulphate, 15 parts of peromags.
Embodiment 2
A kind of purifying agent for polluted water, including following parts by weight of component：200 parts of polymeric aluminium ferrum silicates, 80 parts of Na2Fe04s, 15 parts
Poly- propionamide, 30 parts of ferric sulfate, 10 parts of activated carbons, 30 parts of calcium hydroxides, 25 parts of sodium metasilicate, 10 parts of copper sulphate, 30 parts of peroxidating
Magnesium.
Embodiment 3
A kind of purifying agent for polluted water, including following parts by weight of component：90 parts of polymeric aluminium ferrum silicates, 40 parts of Na2Fe04s, 8 parts poly-
Propionamide, 20 parts of ferric sulfate, 7 parts of activated carbons, 25 parts of calcium hydroxides, 18 parts of sodium metasilicate, 6 parts of copper sulphate, 18 parts of peromags.
Comparative example 1
Without addition sodium metasilicate, polymeric aluminium ferrum silicate and Na2Fe04 in this comparative example, remaining component and match with reality
The technical scheme applied in example one is identical.
Measure of merit
The purifying agent for polluted water for determining above-described embodiment and comparative example preparation respectively is put into water body, and COD is removed respectively
Rate and heavy metal copper ion concentration measure.
Test result is as shown in table 1.
Table 1
| COD clearances (%) | Heavy metal ion (mg/L) | Percent of decolourization (%) | |
| Embodiment 1 | 89.3 | 0.62 | 94.5 |
| Embodiment 2 | 88.9 | 0.63 | 95.2 |
| Embodiment 3 | 91.2 | 0.58 | 94.9 |
| Comparative example 1 | 54.3 | 1.52 | 62.3 |
Data in table 1 can be seen that the middle heavy metal that technical scheme can be preferably gone in water removal
Simultaneously for COD, (COD refers under conditions of certain strict copper ion, and the reducing substances in water is additional strong
In the presence of oxidant, be oxidized and the quantity of oxidant consumed when decomposing) clearance it is also higher, can be preferably to water quality
Purified, there is good environment protecting, and in flocculation process, the flco of formation is big, and sinking speed is fast, improves effect
Rate, it is observed that the bed mud of sedimentation is more close compared to the bed mud structure after existing commercially available other purifying agent for polluted water processing.Therefore
The present invention can quickly realize the target of water body treating：Water is clear, it is not smelly, without wawter bloom phenomenon.
Embodiment described above only expresses the several embodiments of the present invention, and its description is more specific and detailed, but simultaneously
Can not therefore it be construed as limiting the scope of the patent.It should be pointed out that come for one of ordinary skill in the art
Say, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection of the present invention
Scope.Therefore, the protection domain of patent of the present invention should will be defined by appended right.
Comprise the following steps present invention also offers a kind of preparation method of purifying agent for polluted water and weigh following parts by weight of component：
80 parts of polymeric aluminium ferrum silicates, 30 parts of Na2Fe04s, 5 parts of poly- propionamides, 10 parts of ferric sulfate, 5 parts of activated carbons, 20 parts of calcium hydroxides,
10 parts of sodium metasilicate, 1 part of copper sulphate, 15 parts of peromags, and each component is well mixed, obtain the purifying agent for polluted water.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (5)
1. a kind of purifying agent for polluted water, it is characterised in that including following parts by weight of component:Polymeric aluminium ferrum silicate is 80-200, high ferro
Sour sodium is 30-80 parts, and poly- propionamide is 5-15 parts, and ferric sulfate is 10-30 parts, and activated carbon is 5-10 parts, calcium hydroxide 20-30
Part, sodium metasilicate is 10-25 parts, and copper sulphate is 1-10 parts, peromag 15-30 parts.
2. a kind of purifying agent for polluted water according to claim 1, it is characterised in that including following parts by weight of component：80 parts of polymerizations
Aluminium iron silicate, 30 parts of Na2Fe04s, 5 parts of poly- propionamides, 10 parts of ferric sulfate, 5 parts of activated carbons, 20 parts of calcium hydroxides, 10 parts of silicic acid
Sodium, 1 part of copper sulphate, 15 parts of peromags.
3. a kind of purifying agent for polluted water according to claim 1, it is characterised in that including following parts by weight of component：200 parts of polymerizations
Aluminium iron silicate, 80 parts of Na2Fe04s, 15 parts of poly- propionamides, 30 parts of ferric sulfate, 10 parts of activated carbons, 30 parts of calcium hydroxides, 25 parts of silicic acid
Sodium, 10 parts of copper sulphate, 30 parts of peromags.
4. a kind of purifying agent for polluted water according to claim 1, it is characterised in that including following parts by weight of component：90 parts of polymerizations
Aluminium iron silicate, 40 parts of Na2Fe04s, 8 parts of poly- propionamides, 20 parts of ferric sulfate, 7 parts of activated carbons, 25 parts of calcium hydroxides, 18 parts of silicic acid
Sodium, 6 parts of copper sulphate, 18 parts of peromags.
5. a kind of preparation method of purifying agent for polluted water, it is characterised in that comprise the following steps：Weigh following parts by weight of component：It is poly-
Conjunction aluminium iron silicate is 80-200, and Na2Fe04 is 30-80 parts, and poly- propionamide is 5-15 parts, and ferric sulfate is 10-30 parts, activated carbon
For 5-10 parts, calcium hydroxide is 20-30 parts, and sodium metasilicate is 10-25 parts, and copper sulphate is 1-10 parts, and peromag 15-30 parts will
Said components are crushed and are uniformly mixed, and carry out drying process.