CN107574997A - A kind of antistatic floor manufacture craft - Google Patents
A kind of antistatic floor manufacture craft Download PDFInfo
- Publication number
- CN107574997A CN107574997A CN201710837142.7A CN201710837142A CN107574997A CN 107574997 A CN107574997 A CN 107574997A CN 201710837142 A CN201710837142 A CN 201710837142A CN 107574997 A CN107574997 A CN 107574997A
- Authority
- CN
- China
- Prior art keywords
- raw material
- water
- drying
- agent
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antistatic floor manufacture craft, it includes following steps：A, raw material are chosen；B, roll；C, salt acid soak；D, impregnation；E, rinse；F, dry；G, drying process；H, press；I, mortise；J, paint and mat formation；K, aldehyde jelly is removed in floor surface brushing water-tight corrosion-proof：The water-tight corrosion-proof removes aldehyde jelly, containing water-base resin, Antisepticize and mildew preventive, insect-proof agent, anti-termite agent, except formaldehyde agent, coalescents, antifreezing agent and water.
Description
Technical field
The present invention relates to technical field of floor, more particularly, it relates to a kind of making work of antistatic floor
Skill.
Background technology
So-called electrostatic is exactly a kind of in macroscopically temporal persistence electric charge somewhere immobilising electric charge in other words.Work as electricity
Lotus is gathered on some object or is formed electrostatic during surface, and electric charge is divided into two kinds of positive charge and negative electrical charge, that is to say, that
Electrostatic phenomenon is also classified into two kinds of i.e. positive electrostatic and negative electrostatic.Positive electrostatic is formed when positive charge is gathered on some object,
Negative electrostatic is formed when negative electrical charge is gathered on some object, but either positive electrostatic still bears electrostatic, works as static electrification
Object contacts zero potential object (ground connection object) or electric charge transfer can all occur when having the object of potential difference with it, is exactly us
It is daily to see Spark Discharges.Such as northern wintry weather is dried, human body easily takes electrostatic, when contact other people or metal
Will Discharge Phenomena during electric conductor.People has the picotement of electric shock, and night can see spark, and this is chemical fibre clothes and people
On body friction human body band the reason for positive electrostatic.
Electrostatic harm among production, life is serious and immaterial, and can never ignore, how practical and effective
Elimination its harm be just when moderns are of interest, and prevent that electrostatic most efficient method from being the antistatic aids chosen, prevent quiet
Electric floor is one of most effective and best antistatic aids, is widely used so far.
Traditional antistatic floor, which is called, does static dissipation floor, is a kind of floor, when it be grounded or connected to it is any relatively low
During potential point, electric charge is set to dissipate, to reach the purpose of antistatic, it is basically divided into the straight flooring of antistatic and prevented quiet
The major class of electrical activity floor two, for the Workplace of special trade, it can have the function that pre- antistatic causes accident.It is anti-quiet
Electric straight flooring is generally divided into static-electricity proof tile, PVC antistatic floors and antistatic floor etc..Anti-static movable floor then one
As divided according to base material with surface lining difference, base material has base steel, aluminium base, composite base, particieboard base (wooden base), calcium sulfate
Base etc.；Surface lining has static-electricity proof tile, melamine (HPL), PVC etc.；There are plastic floor of electrostatic precention, OA networks in addition
Floor etc., relatively common is ceramic antistatic floor, Full-steel antistatic floor, three kinds of aluminium alloy type antistatic floor.
Above product is because it is because of the deficiency in manufacture craft, and specific aim is too strong, and portioned product is even more only a small number of raw
Business men is produced, it is impossible to is widely used in all trades and professions, more leisure opinion comes into life staying idle at home, ensures health.Due to by technique
Level limitation, traditional antistatic floor are made by materials such as ceramics, all steel, aluminium alloys, and shortcoming is numerous, such as：Itself weight
Have an impact to load-bearing, pollution resistance is poor, not wear-resisting, short life, is easily deformed, complexity etc. of constructing；A series of critical defect is led
It is special population service to have caused traditional antistatic floor and can only rest on specific occasion, and ignore numerous people to health,
The urgent yearning of environmental protection life.
The content of the invention
It is an object of the invention to effectively overcome the shortcomings of above-mentioned technology, there is provided it is a kind of can antistatic floor making work
Skill, the antistatic floor produced by such a manufacture craft, caused by electrostatic production accident, life health can be avoided
Problem, it is widely used in various places, there is the advantages of light, easy cleaning, facilitate installing/dismounting, be durable in use.
Present invention employs following technical scheme：A kind of antistatic floor manufacture craft, it includes following steps：
A, raw material are chosen：Sawdust or edges of boards, slab, crotch material, stalk are chosen as raw material；
B, roll：Sawdust or edges of boards, slab, crotch material, stalk are rolled, it is ensured that roll the smooth of rear entirety；
C, salt acid soak：Raw material are put into hydrochloric acid solution of the concentration less than 36%, soak 6~10h, during immersion, really
Raw material are protected all to be immersed in hydrochloric acid solution；
D, impregnation：Raw material after salt acid soak are put into phenolic resin glue, 6~10h are soaked, hereafter by raw material
Taken out out of phenolic resin glue；
E, rinse：Raw material are rinsed with water, clean the impurity on raw material；
F, dry：Raw material naturally dry after rinsing, avoids direct sunlight raw material during drying；
G, drying process：, it is necessary to which processing is dried after raw material rinsing, drying, 10~12h are dried with 60~80 DEG C,
The moisture of feed stock material is evaporated, its water content is no more than 9% is advisable；
H, press：Raw material are put into mould, pressing and forming, form sheet material；
I, mortise：According to the specification on floor, the male tenon and female groove being adapted once are processed on sheet material；
J, paint and mat formation：Paint spraying is carried out to the sheet material of mortise, spray painting is completed after paint dries, according to public affairs
Tenon and the fitting relation of female groove are mated formation；
K, aldehyde jelly is removed in floor surface brushing water-tight corrosion-proof：The water-tight corrosion-proof removes aldehyde jelly, containing water-base resin,
Antisepticize and mildew preventive, insect-proof agent, anti-termite agent, the percent by weight except formaldehyde agent, coalescents, antifreezing agent and water, wherein each component
It is respectively than content：Water-base resin 5-90 parts, Antisepticize and mildew preventive 0.01-30 parts, insect-proof agent 0.01-20 parts, anti-termite agent
0.01-15 parts, except formaldehyde agent 0.01-20 parts, coalescents 0.01-30 parts, antifreezing agent 0.01-15 parts, water 5-95 parts.
Further, the step C is：Raw material are put into the hydrochloric acid solution that concentration is 30%, soak time is
6h。
Further, the step C is：Raw material are put into the hydrochloric acid solution that concentration is 25%, soak time is
10h。
Further, the step G is：Drying process：, it is necessary to which processing is dried after raw material rinsing, drying, with
60 DEG C of drying 10h, the moisture of feed stock material is evaporated, it is 8% to make its water content.
Further, the step G is：Drying process：, it is necessary to processing be dried, with 80 after sheet material rinsing, drying
DEG C drying 12h, evaporates the moisture of feed stock material, it is 6% to make its water content.
Further, the step H comprises the following steps：H1, raw material are put into designed mould；H2, conjunction
Mould, raw material are pressed；H3, after feed stock material curing molding, depanning, that is, form sheet material.
Beneficial effect using above technical scheme is：
The antistatic floor made by the technique of the present invention, can be widely applied to various places, has good conduction
Property, available for antistatic, no matter avoid because of production accident, life health caused by electrostatic the problems such as, or meet consumer
, all can be exhaustive in the demand such as attractive in appearance, comfortable, environmentally friendly；With light, easy cleaning, facilitate installing/dismounting, long-lived
Advantage, traditional antistatic floor is surmounted, computer room, rubber and plastic sheeting production plant, inflammable can be used in
The special occasions such as explosive place, also have the advantages that moistureproof, fire-retardant, anti-corrosion, substitute completely it is original it is too thick and heavy, pollution resistance is poor,
Not wear-resisting, short life, be easily deformed, complexity of constructing etc. the defects of antistatic floor.
Antistatic floor produced by the invention, there is the function that water-tight corrosion-proof removes aldehyde.
Embodiment
With reference to embodiment, the present invention will be further described：
Embodiment：
A kind of antistatic floor manufacture craft, it includes following steps：
A, raw material are chosen：Sawdust or edges of boards, slab, crotch material, stalk are chosen as raw material；
B, roll：Sawdust or edges of boards, slab, crotch material, stalk are rolled, it is ensured that roll the smooth of rear entirety；
C, salt acid soak：Raw material are put into hydrochloric acid solution of the concentration less than 30%, 6 h are soaked, during immersion, it is ensured that be former
Material is all immersed in hydrochloric acid solution；
D, impregnation：Raw material after salt acid soak are put into phenolic resin glue, 6~10h are soaked, hereafter by raw material
Taken out out of phenolic resin glue；
E, rinse：Raw material are rinsed with water, clean the impurity on raw material；
F, dry：Raw material naturally dry after rinsing, avoids direct sunlight raw material during drying；
G, drying process：, it is necessary to which processing is dried after raw material rinsing, drying, with 60 DEG C of drying 10h, former material is evaporated
Moisture inside material, it is 8% to make its water content.
H, press：H1, raw material are put into designed mould；Raw material are pressed by H2, matched moulds；H3、
After feed stock material curing molding, depanning, that is, sheet material is formed；I, mortise：According to the specification on floor, once add on sheet material
Work goes out the male tenon and female groove being adapted；
J, paint and mat formation：Paint spraying is carried out to the sheet material of mortise, spray painting is completed after paint dries, according to public affairs
Tenon and the fitting relation of female groove are mated formation；
K, aldehyde jelly is removed in floor surface brushing water-tight corrosion-proof：The water-tight corrosion-proof removes aldehyde jelly, containing water-base resin,
Antisepticize and mildew preventive, insect-proof agent, anti-termite agent, the percent by weight except formaldehyde agent, coalescents, antifreezing agent and water, wherein each component
It is respectively than content：Water-base resin 5-90 parts, Antisepticize and mildew preventive 0.01-30 parts, insect-proof agent 0.01-20 parts, anti-termite agent
0.01-15 parts, except formaldehyde agent 0.01-20 parts, coalescents 0.01-30 parts, antifreezing agent 0.01-15 parts, water 5-95 parts.
Claims (6)
1. a kind of antistatic floor manufacture craft, it is characterised in that it includes following steps：
A, raw material are chosen：Sawdust or edges of boards, slab, crotch material, stalk are chosen as raw material；
B, roll：Sawdust or edges of boards, slab, crotch material, stalk are rolled, it is ensured that roll the smooth of rear entirety；
C, salt acid soak：Raw material are put into hydrochloric acid solution of the concentration less than 36%, 6~10h are soaked, during immersion, it is ensured that be former
Material is all immersed in hydrochloric acid solution；
D, impregnation：Raw material after salt acid soak are put into phenolic resin glue, soak 6~10h, hereafter by raw material from phenolic aldehyde
Taken out in resin glue；
E, rinse：Raw material are rinsed with water, clean the impurity on raw material；
F, dry：Raw material naturally dry after rinsing, avoids direct sunlight raw material during drying；
G, drying process：, it is necessary to which processing is dried after raw material rinsing, drying, with 60~80 DEG C of 10~12h of drying, evaporation
The moisture of feed stock material, its water content is no more than 9% is advisable；
H, press：Raw material are put into mould, pressing and forming, form sheet material；
I, mortise：According to the specification on floor, the male tenon and female groove being adapted once are processed on sheet material；
J, paint and mat formation：Paint spraying is carried out to the sheet material of mortise, spray painting is completed after paint dries, according to male tenon and mother
The fitting relation of groove is mated formation；
K, aldehyde jelly is removed in floor surface brushing water-tight corrosion-proof：The water-tight corrosion-proof removes aldehyde jelly, prevents containing water-base resin, anti-corrosion
Mould dose, insect-proof agent, anti-termite agent, the percent by weight content except formaldehyde agent, coalescents, antifreezing agent and water, wherein each component
Respectively：Water-base resin 5-90 parts, Antisepticize and mildew preventive 0.01-30 parts, insect-proof agent 0.01-20 parts, anti-termite agent 0.01-15 parts,
Except formaldehyde agent 0.01-20 parts, coalescents 0.01-30 parts, antifreezing agent 0.01-15 parts, water 5-95 parts.
A kind of 2. antistatic floor manufacture craft according to claim 1, it is characterised in that：The step C is：By former material
Material is put into the hydrochloric acid solution that concentration is 30%, soak time 6h.
A kind of 3. antistatic floor manufacture craft according to claim 1, it is characterised in that：The step C is：By former material
Material is put into the hydrochloric acid solution that concentration is 25%, soak time 10h.
A kind of 4. antistatic floor manufacture craft according to claim 1, it is characterised in that：The step G is：At drying
Reason：, it is necessary to which processing is dried after raw material rinsing, drying, with 60 DEG C of drying 10h, the moisture of feed stock material is evaporated, makes it
Water content is 8%.
A kind of 5. antistatic floor manufacture craft according to claim 1, it is characterised in that：The step G is：At drying
Reason：, it is necessary to which processing is dried after sheet material rinsing, drying, with 80 DEG C of drying 12h, the moisture of feed stock material is evaporated, contains it
Water is 6%.
A kind of 6. antistatic floor manufacture craft according to claim 1, it is characterised in that：The step H includes following
Step：H1, raw material are put into designed mould；Raw material are pressed by H2, matched moulds；H3, treat feed stock material
After curing molding, depanning, that is, sheet material is formed.