CN107573737A - A kind of automobile Secondary Anticorrosion - Google Patents
A kind of automobile Secondary Anticorrosion Download PDFInfo
- Publication number
- CN107573737A CN107573737A CN201710926324.1A CN201710926324A CN107573737A CN 107573737 A CN107573737 A CN 107573737A CN 201710926324 A CN201710926324 A CN 201710926324A CN 107573737 A CN107573737 A CN 107573737A
- Authority
- CN
- China
- Prior art keywords
- parts
- styrene
- nitrocotton
- aerosil
- drier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of automobile Secondary Anticorrosion, is prepared from the following raw materials in parts by weight：Including 20~26 parts of butyl glycol ether, 10~15 parts of carbon black, 5~9 parts of dispersant, 0.1~1 part of drier, 2~7 parts of superfine talcum powder, 0.5~1 part of aerosil, 15~19 parts of high hydroxyl content acrylic resin, 2.5~4.2 parts of nitrocotton, 2~4 parts of aluminium powder, 6~11 parts of modified rosin resin, 7~9 parts of organobentonite, 95% 3~5 parts of ethanol, 37~48 parts of phenolic aldehyde insulating varnish, 0.3~0.7 part of formamide, 11~16 parts of boron sikicate aluminum, 6~11 parts of styrene, 9~14 parts of aramid fiber short fibre, 3.1~6.5 parts of styrene series thermoplastic elastomer, 1.4~3.0 parts of cobalt iso-octoate catalyst；It is an advantage of the invention that：Increase the practicality and durability of paint.
Description
Technical field
The present invention relates to a kind of automobile Secondary Anticorrosion, belong to paint technology field.
Background technology
The appearance of automobile must smear paint, and it mainly plays a part of to protect and decorated, traditional paint generally existing
Smell weight, easily come off, be perishable, it is not environmentally friendly enough the problems such as, can not meet requirement of the consumer to paint, because
This increases the practicality and durability of paint, to improve the antiseptic property of automobile, it is necessary to improve the formula of original paint.
The content of the invention
It is an object of the invention to provide a kind of automobile Secondary Anticorrosion.
The problem to be solved in the present invention is traditional paint generally existing smell weight, easily comes off, be perishable, not environmentally friendly enough
The problems such as.
To realize the purpose of the present invention, the technical solution adopted by the present invention is：
A kind of automobile Secondary Anticorrosion, is prepared from the following raw materials in parts by weight：Including 20~26 parts of butyl glycol ether, carbon black
10~15 parts, 5~9 parts of dispersant, 0.1~1 part of drier, 2~7 parts of superfine talcum powder, 0.5~1 part of aerosil, height
15~19 parts of hydroxy radical content acrylic resin, 2.5~4.2 parts of nitrocotton, 2~4 parts of aluminium powder, 6~11 parts of modified rosin resin, have
7~9 parts of machine bentonite, 95% 3~5 parts of ethanol, 37~48 parts of phenolic aldehyde insulating varnish, 0.3~0.7 part of formamide, boron sikicate aluminum
11~16 parts, 6~11 parts of styrene, 9~14 parts of aramid fiber short fibre, 3.1~6.5 parts of styrene series thermoplastic elastomer is different pungent
Sour 1.4~3.0 parts of Co catalysts.
Above-mentioned anti-corrosion automobile coating, is prepared from the following raw materials in parts by weight：Including 21 parts of butyl glycol ether, carbon black 11
Part, 5 parts of dispersant, 0.1 part of drier, 3 parts of superfine talcum powder, 0.6 part of aerosil, high hydroxyl content acrylic resin
15 parts, 2.7 parts of nitrocotton, 2 parts of aluminium powder, 6 parts of modified rosin resin, 7 parts of organobentonite, 95% 3 parts of ethanol, phenolic aldehyde insulation is clearly
39 parts of paint, 0.3 part of formamide, 11 parts of boron sikicate aluminum, 6 parts of styrene, 9 parts of aramid fiber short fibre, styrene series thermoplastic elastomer
3.2 parts, 1.5 parts of cobalt iso-octoate catalyst.
It is an advantage of the invention that：The crosslink density of this formula is good, and coating late hardness is high, mechanical performance, and ageing properties are excellent
It is different, and be not easy peeling after drying and do not break；Modified rosin resin has the function that increase adhesive force, adds the short fibre of aramid fiber
Dimension so that formula paint has certain compression strength after drying.
Embodiment
With reference to embodiment, the present invention is further illustrated.
A kind of embodiment 1, automobile Secondary Anticorrosion of the present invention, is prepared from the following raw materials in parts by weight：Including ethylene glycol fourth
21 parts of ether, 11 parts of carbon black, 5 parts of dispersant, 0.1 part of drier, 3 parts of superfine talcum powder, 0.6 part of aerosil, high hydroxyl
15 parts of content acrylic resin, 2.7 parts of nitrocotton, 2 parts of aluminium powder, 6 parts of modified rosin resin, 7 parts of organobentonite, 95% ethanol
3 parts, 39 parts of phenolic aldehyde insulating varnish, 0.3 part of formamide, 11 parts of boron sikicate aluminum, 6 parts of styrene, 9 parts of aramid fiber short fibre, styrene
3.2 parts of based thermoplastic elastomer, 1.5 parts of cobalt iso-octoate catalyst.
A kind of embodiment 2, automobile Secondary Anticorrosion, is prepared from the following raw materials in parts by weight：Including 26 parts of butyl glycol ether,
14 parts of carbon black, 8 parts of dispersant, 0.4 part of drier, 6 parts of superfine talcum powder, 0.9 part of aerosil, high hydroxyl content propylene
19 parts of acid resin, 4.2 parts of nitrocotton, 4 parts of aluminium powder, 10 parts of modified rosin resin, 8 parts of organobentonite, 95% 5 parts of ethanol, phenol
45 parts of aldehyde insulating varnish, 0.7 part of formamide, 15 parts of boron sikicate aluminum, 11 parts of styrene, 13 parts of aramid fiber short fibre, polystyrene heat
6.0 parts of thermoplastic elastic, 2.8 parts of cobalt iso-octoate catalyst.
Claims (2)
1. a kind of automobile Secondary Anticorrosion, it is characterized in that：It is prepared from the following raw materials in parts by weight：Including butyl glycol ether 20~26
Part, 10~15 parts of carbon black, 5~9 parts of dispersant, 0.1~1 part of drier, 2~7 parts of superfine talcum powder, aerosil 0.5
~1 part, 15~19 parts of high hydroxyl content acrylic resin, 2.5~4.2 parts of nitrocotton, 2~4 parts of aluminium powder, modified rosin resin 6
~11 parts, 7~9 parts of organobentonite, 95% 3~5 parts of ethanol, 37~48 parts of phenolic aldehyde insulating varnish, 0.3~0.7 part of formamide,
11~16 parts of boron sikicate aluminum, 6~11 parts of styrene, 9~14 parts of aramid fiber short fibre, styrene series thermoplastic elastomer 3.1~6.5
Part, 1.4~3.0 parts of cobalt iso-octoate catalyst.
2. a kind of automobile Secondary Anticorrosion according to claim 1, it is characterized in that：It is prepared from the following raw materials in parts by weight：
Including 21 parts of butyl glycol ether, 11 parts of carbon black, 5 parts of dispersant, 0.1 part of drier, 3 parts of superfine talcum powder, aerosil
0.6 part, 15 parts of high hydroxyl content acrylic resin, 2.7 parts of nitrocotton, 2 parts of aluminium powder, 6 parts of modified rosin resin, organobentonite
7 parts, 95% 3 parts of ethanol, 39 parts of phenolic aldehyde insulating varnish, 0.3 part of formamide, 11 parts of boron sikicate aluminum, 6 parts of styrene, the short fibre of aramid fiber
9 parts of dimension, 3.2 parts of styrene series thermoplastic elastomer, 1.5 parts of cobalt iso-octoate catalyst.