CN107572878A - 一种隔热防火仿石涂料及其制备方法 - Google Patents
一种隔热防火仿石涂料及其制备方法 Download PDFInfo
- Publication number
- CN107572878A CN107572878A CN201710723074.1A CN201710723074A CN107572878A CN 107572878 A CN107572878 A CN 107572878A CN 201710723074 A CN201710723074 A CN 201710723074A CN 107572878 A CN107572878 A CN 107572878A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- heat
- insulating
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种隔热防火仿石涂料，由以下组份合成：水性弹性羟基丙烯酸树脂15‑20份，天然大理石碎石15‑20份，空心玻璃微珠15‑20份，天然彩色云母片15‑20份，羟乙基改性疏水纤维素0.2‑0.3份，成膜助剂1‑1.5份，水性异氰酸酯1‑6份，防霉防腐剂0.2‑0.6份，去离子水0.6‑12份，防火材料10‑15份，其它助剂0.2‑0.3份，还公开了这种涂料的制备方法，本发明具有天然石材效果，同时兼具保温、隔热、防火、防裂功能，综合性的解决了目前外墙建筑涂料的装饰性、节能性、防火性、防裂性、环保性等现实问题，为多功能性装饰材料的完美结合。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种隔热防火仿石涂料及其制备方法。
背景技术
随着我国经济持续快速的增长，基础设施的大量建设，人们生活水准的提高和环保意识的逐渐增强，要求建筑涂料除了具有保护作用以外，还要具有某些特殊的功能，比如装饰性、环保性等，形成了建筑涂料的高装饰性兼功能化的新观念。同时，随着高分子化学、生物科学等涂料基础学科的交叉与进步，建筑涂料功能化也得到了新的发展。近年来，国外功能建筑涂料发展迅速，出现了很多新的涂料品种，主要有防水涂料、弹性功能涂料、防锈防腐蚀涂料、防静电涂料、防霉防虫涂料、防火涂料、仿石涂料和隔热涂料等。
对于建筑外墙涂料，外观上，许多建筑外立面完工后不久就发生严重退色、污染，甚至起鼓、脱落，导致建筑物整个外立面色差明显，颜色不均匀，影响了楼房、小区甚至整个城市的美观。功能方面，目前市场上应用广泛的的天然石岩片漆，虽然装饰效果美观，但缺乏隔热防火性能。
发明内容
为解决以上装饰性和功能性难以兼顾的问题，本发明提供一种隔热防火仿石涂料及其制备方法。
为了实现上述目的，本发明采用以下技术方案：
一种隔热防火仿石涂料及其制备方法，包括以下按质量份计的原料：
水性丙烯酸树脂 15-20份，
改性纤维素 0.2-0.3份，
成膜助剂 1-1.5份，
成碳剂 1-6份，
去离子水 0.6-12份，
骨料 10-75份，
助剂 0.2-0.3份。
优选地，水性丙烯酸树脂是由水性丙烯酸弹性树脂和水性羟基丙烯酸树脂按重量比为1-3:1-5混合而成。
优选地，所述改性纤维素是由羟乙基纤维和羟甲基纤维按重量比为1-10:1-10混合而成。
优选地，成膜助剂是由十二碳醇酯、丙二醇丁醚和丙二醇甲醚按重量比为1-2:1-2:1-2混合而成。
优选地，所述成碳剂为水性异氰酸酯，起固化作用，使得漆膜更坚固。
优选地，所述骨料包括大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩中的一种或多种。所述大理石碎石优选为天然大理石碎石，其粒径为0.1-0.6μm；所述空心玻璃微珠的粒径为0.1-0.3μm；所述彩色云母片优选为天然彩色云母片，其粒径为0.5-1.0μm；所述超细珍珠岩的粒径为0.1-0.3μm。
进一步优选地，所述骨料由大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩按重量比为1-2:1-2:1-2:1-2混合而成。
优选地，所述助剂包括分散剂、消泡剂、pH调节剂和防霉防腐剂中的一种或多种。
进一步优选地，所述分散剂是LBD-1。
进一步优选地，所述消泡剂是聚醚改性聚硅氧烷。
进一步优选地，所述pH调节剂是BS168。
进一步优选地，所述防霉防腐剂是季胺盐衍生物，如卡松。
本发明还提供了上述涂料的制备方法，包括以下步骤：
1)将去离子水加入反应釜，依次加入改性纤维素，成膜助剂分散均匀骨料，；
2)加入水性丙烯酸树脂和助剂，分散均匀；
3)检验合格后包装。
优选地，所述步骤(1)的分散转速为400-600转/分钟，分散时间为10-30min，步骤(2)的分散转速为600-800转/分钟，分散时间为5-20min。
本发明的有益效果：
1、本发明同时具有保温、隔热、防火、防裂功能，综合性的解决了目前外墙建筑涂料的节能性、环保性、防火性、防裂性等现实问题，为多功能性装饰材料的完美结合；
2、本发明具有天然石材效果，装饰性能突出；
3、本发明中的骨料由大理石碎石、空心玻璃微珠、彩色云母片和超细珍珠岩复配而成，根据需要调节配比，不仅可以使涂料的仿石效果更加逼真，同时还可以增加色彩的保色性和美观度；
4、本发明的生产工艺简单，易于操作，设备投入低，易于推广应用。
具体实施方式
实施例1
一种隔热防火仿石涂料，包括以下按质量份计的原料：
水性丙烯酸树脂 20份，
改性纤维素 0.2份，
成膜助剂 1份，
水性异氰酸酯 1份，
去离子水 10份，
骨料 67.5份，
LBD-1 0.3份。
水性丙烯酸树脂是水性丙烯酸弹性树脂和水性羟基丙烯酸树脂按重量比为1:1混合而成，改性纤维素是羟乙基纤维和羟甲基纤维按重量比为1:1混合而成，成膜助剂是十二碳醇酯、丙二醇丁醚和丙二醇甲醚按重量比为1:1:1混合而成。骨料由大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩按重量比为1:1:1:1混合而成。
上述隔热防火仿石涂料的制备方法，包括以下步骤：
1)将去离子水加入反应釜，依次加入改性纤维素，成膜助剂分散均匀骨料，按400r/min的速度搅拌10min；
2)加入水性丙烯酸树脂和助剂(分散剂、消泡剂、pH调节剂和防腐防霉剂)，按600r/min的速度分散20min；
3)检验合格后包装。
实施例2
一种隔热防火仿石涂料，包括以下按质量份计的原料：
水性丙烯酸树脂 18.3份，
改性纤维素 0.24份，
成膜助剂 1.2份，
水性异氰酸酯 2份，
去离子水 3份，
骨料 75份，
聚醚改性聚硅氧烷
0.26份。
水性丙烯酸树脂是水性丙烯酸弹性树脂和水性羟基丙烯酸树脂按重量比为1:5混合而成，改性纤维素是羟乙基纤维和羟甲基纤维按重量比为1:10混合而成，成膜助剂是十二碳醇酯、丙二醇丁醚和丙二醇甲醚按重量比为1:2:2混合而成。骨料由大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩按重量比为1.5:1:1:1.5混合而成。
上述隔热防火仿石涂料的制备方法，包括以下步骤：
1)将去离子水加入反应釜，依次加入改性纤维素，成膜助剂分散均匀骨料，按400r/min的速度搅拌15min；
2)加入水性丙烯酸树脂和助剂(分散剂、消泡剂、pH调节剂和防腐防霉剂)，按600r/min的速度分散15min；
3)检验合格后包装。
实施例3
一种隔热防火仿石涂料，包括以下按质量份计的原料：
水性丙烯酸树脂 17份，
改性纤维素 0.26份，
成膜助剂 1.4份，
水性异氰酸酯 3份，
去离子水 5份，
骨料 73.1份，
BS168 0.24份。
水性丙烯酸树脂是水性丙烯酸弹性树脂和水性羟基丙烯酸树脂按重量比为3:1混合而成，改性纤维素是羟乙基纤维和羟甲基纤维按重量比为5:1混合而成，成膜助剂是十二碳醇酯、丙二醇丁醚和丙二醇甲醚按重量比为2:1:1混合而成。骨料由大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩按重量比为2:2:1:1混合而成。
上述隔热防火仿石涂料的制备方法，包括以下步骤：
1)将去离子水加入反应釜，依次加入改性纤维素，成膜助剂分散均匀骨料，按400r/min的速度搅拌20min；
2)加入水性丙烯酸树脂和助剂(分散剂、消泡剂、pH调节剂和防腐防霉剂)，按600r/min的速度分散10min；
3)检验合格后包装。
实施例4
一种隔热防火仿石涂料，包括以下按质量份计的原料：
水性丙烯酸树脂 18份，
改性纤维素 0.28份，
成膜助剂 1.3份，
水性异氰酸酯 4份，
去离子水 9份，
骨料 67.2份，
卡松 0.22份。
水性丙烯酸树脂是水性丙烯酸弹性树脂和水性羟基丙烯酸树脂按重量比为3:5混合而成，改性纤维素是羟乙基纤维和羟甲基纤维按重量比为10:1混合而成，成膜助剂是十二碳醇酯、丙二醇丁醚和丙二醇甲醚按重量比为2:2:1混合而成。骨料由大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩按重量比为1.5:1.5:1.5:1.5混合而成。
上述隔热防火仿石涂料的制备方法，包括以下步骤：
1)将去离子水加入反应釜，依次加入改性纤维素，成膜助剂分散均匀骨料，按600r/min的速度搅拌25min；
2)加入水性丙烯酸树脂和助剂(分散剂、消泡剂、pH调节剂和防腐防霉剂)，按800r/min的速度分散7min；
3)检验合格后包装。
实施例5
一种隔热防火仿石涂料，包括以下按质量份计的原料：
水性丙烯酸树脂 20份，
改性纤维素 0.3份，
成膜助剂 1.5份，
水性异氰酸酯 6份，
去离子水 12份，
骨料 60份，
LBD-1 0.1份，聚醚改性聚硅氧烷 0.2份。
水性丙烯酸树脂是水性丙烯酸弹性树脂和水性羟基丙烯酸树脂按重量比为1:5混合而成，改性纤维素是羟乙基纤维和羟甲基纤维按重量比为10:1混合而成，成膜助剂是十二碳醇酯、丙二醇丁醚和丙二醇甲醚按重量比为1:2:2混合而成。骨料由大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩按重量比为2:2:2:2混合而成。
上述隔热防火仿石涂料的制备方法，包括以下步骤：
1)将去离子水加入反应釜，依次加入改性纤维素，成膜助剂分散均匀骨料，按500r/min的速度搅拌30min；
2)加入水性丙烯酸树脂和助剂(分散剂、消泡剂、pH调节剂和防腐防霉剂)，按700r/min的速度分散5min；
3)检验合格后包装。
将本发明实施例1-5的隔热防火仿石涂料分别涂刷在40cm×40cm，厚度为(5±0.2)mm的胶和板上，涂层厚度为0.5mm。涂层干后在500℃恒温箱干燥板小时后检测其防火、隔热等理化性能，其结果如表1和2所示。
表1实施例1-5的理化性能
表2实施例1-5的防石涂料的防火性能
Claims (10)
1.一种隔热防火仿石涂料，其特征在于，包括以下按质量份计的原料：
2.根据权利要求1所述的隔热防火仿石涂料，其特征在于，所述水性丙烯酸树脂是水性丙烯酸弹性树脂和水性羟基丙烯酸树脂按重量比为1-3:1-5混合而成。
3.根据权利要求1所述的隔热防火仿石涂料，其特征在于，所述改性纤维素是羟乙基纤维和羟甲基纤维按重量比为1-10:1-10混合而成。
4.根据权利要求1所述的隔热防火仿石涂料，其特征在于，所述成膜助剂是十二碳醇酯、丙二醇丁醚和丙二醇甲醚按重量比为1-2:1-2:1-2混合而成。
5.根据权利要求1所述的隔热防火仿石涂料，其特征在于，所述成碳剂为水性异氰酸酯。
6.根据权利要求1所述的隔热防火仿石涂料，其特征在于，所述骨料包括大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩中的一种或多种。
7.根据权利要求6所述的隔热防火仿石涂料，其特征在于，所述骨料由大理石碎石、空心玻璃微珠、彩色云母片、超细珍珠岩按重量比为1-2:1-2:1-2:1-2混合而成。
8.根据权利要求1所述的隔热防火仿石涂料，其特征在于，所述助剂包括分散剂、消泡剂、pH调节剂和防腐防霉剂中的一种或多种。
9.根据权利要求1-8中任一项所述的隔热防火仿石涂料的制备方法，其特征在于，包括以下步骤：
1)将去离子水加入反应釜，依次加入改性纤维素，成膜助剂分散均匀骨料；
2)加入水性丙烯酸树脂和助剂，分散均匀；
3)检验合格后包装。
10.根据权利要求9所述的隔热防火仿石涂料的制备方法，其特征在于，所述步骤(1)的分散转速为400-600转/分钟，分散时间为10-30min，步骤(2)的分散转速为600-800转/分钟，分散时间为5-20min。