CN107572863A - A kind of building adhisive powder - Google Patents
A kind of building adhisive powder Download PDFInfo
- Publication number
- CN107572863A CN107572863A CN201710852965.7A CN201710852965A CN107572863A CN 107572863 A CN107572863 A CN 107572863A CN 201710852965 A CN201710852965 A CN 201710852965A CN 107572863 A CN107572863 A CN 107572863A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- building
- haloflex
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of building adhisive powder, according to the number of parts by weight, includes the raw material of following number：12 20 parts of sepiolite powder, 12 20 parts of diatomite, 28 parts of borax, 4 10 parts of calcium sulfate, 37 parts of methylcellulose, 3 10 parts of haloflex, 5 10 parts of alum, 35 parts of rosin, 8 10 parts of oxidized starch, 57 parts of zinc oxide, 0.9 1.5 parts of ammonium chloride, 8 12 parts of phosphoric anhydride, 57 parts of iron oxide yellow, 9 11 parts of lignin, 25 parts of defoamer.Rubber powder adhesion strength provided by the invention is high, scrubbing resistance, not shedding when low temperature uses, it is not cracked, can fully it be dissolved in cold water, raw material sources are extensive, simple production process, it is readily transported, long-term storage is never degenerated, and easy to use, cost is low, it is widely used in building coating and carton manufacturing, production process is without waste water, waste gas, pollution-free.
Description
Technical field
The invention belongs to chemical building field of material technology, and in particular to a kind of building adhisive powder.
Background technology
Building gelatine powder is to be directed to cement base material series building special product, has excellent amalgamation with cement, uses the glue
The adhesive mortar that powder is prepared can significantly improve cementitiousness and itself tension, anti-pendant intensity, water-fast, freeze-thawing resistant, heat-resistant aging
Can be prominent, water-keeping thickening has good workability, can be dissolved completely in using cement in the mortar lotion of backbone, not reduced after solidification
The intensity of cement, cementation and cracking resistance are both kept, there is good, film forming, pliability, weather resisteant and stably again
Property, after drying, erosion of the acid air to wall can be effectively prevented, is not pulverized easily after by humidity, deliquescence, is widely used in gluing
Tie mortar, in anticracking grout materials for wall, and Easy dosing, it is easy to use, directly add water to stir during use, the ratio of mud
20% or so, it is that can be used to place 5-10 minutes, and the material prepared was once preferably finished in 30 minutes, bonds thickness 1-3 millimeters,
The Kilograms Per Square Meter of dosage about 5.The raw material that production this product uses has：Mashed sweet potato starch, haloflex, ethanol, activity
Silicon powder, precipitated calcium carbonate, hydroxyethylmethylcellulose, monoxone, soda ash, aqueous tackifier powder.This product has cold water or temperature
The characteristics of water speed is molten, it can be used in mixed way, have with materials such as dry powder, light calcium carbonate powder, sierozem power, land plaster, white cement, black cements
Stronger cementitiousness, tension, anti-pendant, water-fast, freeze-thawing resistant, heat-resistant aging, water-keeping thickening have good workability, and dispensing letter
Single, easy to use, cost is cheap.But there is bad adhesion in the building adhisive powder of existing market length sale, easily produce crack etc. and lack
Fall into, while also pollute environment, or even contact can cause damage the building adhisive powder having to the body of builder for a long time.
The content of the invention
It is an object of the invention to provide a kind of building adhisive powder.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of building adhisive powder, according to the number of parts by weight, include the raw material of following number：Sepiolite powder 12-20 parts, diatom
Native 12-20 parts, borax 2-8 parts, calcium sulfate 4-10 parts, methylcellulose 3-7 parts, haloflex 3-10 parts, alum 5-10 parts,
Rosin 3-5 parts, oxidized starch 8-10 parts, zinc oxide 5-7 parts, ammonium chloride 0.9-1.5 parts, phosphoric anhydride 8-12 parts, iron oxide yellow 5-7
Part, lignin 9-11 parts, defoamer 2-5 parts.
Preferably, a kind of described building adhisive powder, according to the number of parts by weight, includes the raw material of following number：Hai Pao
12 parts of stone flour, 12 parts of diatomite, 2 parts of borax, 10 parts of calcium sulfate, 7 parts of methylcellulose, 10 parts of haloflex, 10 parts of alum,
3 parts of rosin, 10 parts of oxidized starch, 5 parts of zinc oxide, 0.9 part of ammonium chloride, 8 parts of phosphoric anhydride, 7 parts of iron oxide yellow, 11 parts of lignin,
2 parts of defoamer.
Preferably, a kind of described building adhisive powder, according to the number of parts by weight, includes the raw material of following number：Hai Pao
15 parts of stone flour, 15 parts of diatomite, 6 parts of borax, 6 parts of calcium sulfate, 4 parts of methylcellulose, 6 parts of haloflex, 8 parts of alum, pine
It is fragrant 4 parts, 9 parts of oxidized starch, 6 parts of zinc oxide, 1 part of ammonium chloride, 10 parts of phosphoric anhydride, 6 parts of iron oxide yellow, 10 parts of lignin, defoaming
4 parts of agent.
Beneficial effects of the present invention：Rubber powder adhesion strength provided by the invention is high, scrubbing resistance, not shedding when low temperature uses,
It is not cracked, can be fully dissolved in cold water, raw material sources are extensive, simple production process, are readily transported, and long-term storage is never degenerated,
Easy to use, cost is low, is widely used in building coating and carton manufacturing, and production process is without waste water, waste gas, pollution-free.
Embodiment
The present invention is described in further detail with reference to specific embodiment.
Embodiment 1
A kind of building adhisive powder, according to the number of parts by weight, include the raw material of following number：12 parts of sepiolite powder, diatomite
12 parts, 2 parts of borax, 4 parts of calcium sulfate, 3 parts of methylcellulose, 3 parts of haloflex, 5 parts of alum, 3 parts of rosin, oxidized starch 8
Part, 5 parts of zinc oxide, 0.9 part of ammonium chloride, 8 parts of phosphoric anhydride, 5 parts of iron oxide yellow, 9 parts of lignin, 2 parts of defoamer.
Embodiment 2
A kind of building adhisive powder, according to the number of parts by weight, include the raw material of following number：20 parts of sepiolite powder, diatomite
20 parts, 8 parts of borax, 10 parts of calcium sulfate, 7 parts of methylcellulose, 10 parts of haloflex, 10 parts of alum, 5 parts of rosin, oxidation shallow lake
10 parts of powder, 7 parts of zinc oxide, 1.5 parts of ammonium chloride, 12 parts of phosphoric anhydride, 7 parts of iron oxide yellow, 11 parts of lignin, 5 parts of defoamer.
Embodiment 3
A kind of building adhisive powder, according to the number of parts by weight, include the raw material of following number：12 parts of sepiolite powder, diatomite
12 parts, 2 parts of borax, 10 parts of calcium sulfate, 7 parts of methylcellulose, 10 parts of haloflex, 10 parts of alum, 3 parts of rosin, oxidation shallow lake
10 parts of powder, 5 parts of zinc oxide, 0.9 part of ammonium chloride, 8 parts of phosphoric anhydride, 7 parts of iron oxide yellow, 11 parts of lignin, 2 parts of defoamer.
Embodiment 4
A kind of building adhisive powder, according to the number of parts by weight, include the raw material of following number：15 parts of sepiolite powder, diatomite
15 parts, 6 parts of borax, 6 parts of calcium sulfate, 4 parts of methylcellulose, 6 parts of haloflex, 8 parts of alum, 4 parts of rosin, oxidized starch 9
Part, 6 parts of zinc oxide, 1 part of ammonium chloride, 10 parts of phosphoric anhydride, 6 parts of iron oxide yellow, 10 parts of lignin, 4 parts of defoamer.
Above content is only to design example and explanation of the invention, affiliated those skilled in the art
Various modifications or supplement are made to described specific embodiment or is substituted using similar mode, without departing from invention
Design or surmount scope defined in the claims, protection scope of the present invention all should be belonged to.
Claims (3)
1. a kind of building adhisive powder, it is characterised in that according to the number of parts by weight, include the raw material of following number：Sepiolite powder 12-
20 parts, diatomite 12-20 parts, borax 2-8 parts, calcium sulfate 4-10 parts, methylcellulose 3-7 parts, haloflex 3-10 parts are bright
Alum 5-10 parts, rosin 3-5 parts, oxidized starch 8-10 parts, zinc oxide 5-7 parts, ammonium chloride 0.9-1.5 parts, phosphoric anhydride 8-12 parts, oxygen
Change iron oxide yellow 5-7 parts, lignin 9-11 parts, defoamer 2-5 parts.
A kind of 2. building adhisive powder according to claim 1, it is characterised in that according to the number of parts by weight, including following part
Several raw materials：12 parts of sepiolite powder, 12 parts of diatomite, 2 parts of borax, 10 parts of calcium sulfate, 7 parts of methylcellulose, haloflex
10 parts, 10 parts of alum, 3 parts of rosin, 10 parts of oxidized starch, 5 parts of zinc oxide, 0.9 part of ammonium chloride, 8 parts of phosphoric anhydride, iron oxide yellow 7
Part, 11 parts of lignin, 2 parts of defoamer.
A kind of 3. building adhisive powder according to claim 1, it is characterised in that according to the number of parts by weight, including following part
Several raw materials：15 parts of sepiolite powder, 15 parts of diatomite, 6 parts of borax, 6 parts of calcium sulfate, 4 parts of methylcellulose, haloflex 6
Part, 8 parts of alum, 4 parts of rosin, 9 parts of oxidized starch, 6 parts of zinc oxide, 1 part of ammonium chloride, 10 parts of phosphoric anhydride, 6 parts of iron oxide yellow, wood
10 parts of quality, 4 parts of defoamer.