CN107556957A - A kind of coated metallic plate - Google Patents
A kind of coated metallic plate Download PDFInfo
- Publication number
- CN107556957A CN107556957A CN201710925412.XA CN201710925412A CN107556957A CN 107556957 A CN107556957 A CN 107556957A CN 201710925412 A CN201710925412 A CN 201710925412A CN 107556957 A CN107556957 A CN 107556957A
- Authority
- CN
- China
- Prior art keywords
- parts
- metallic plate
- bonded adhesives
- coated metallic
- toughener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention proposes a kind of coated metallic plate, including substrate, and one layer of bonded adhesives is respectively coated in the tow sides of substrate, and the thickness of bonded adhesives is 0.2 0.6mm, pastes a strata ethylene glycol terephthalate film layer on the bonded adhesives on two sides respectively；The preparation method of the bonded adhesives is：Count in parts by weight and 50 70 parts of polyester resin, 25 35 parts of epoxy resin, 38 parts of toughener, 26 parts of dispersant, 15 parts of defoamer, 10 12 parts of acetone, 6 10 parts of aluminum oxide stir at a temperature of 70 90 DEG C, adhesive effect is good, improves product quality.
Description
Technical field
The present invention relates to a kind of metallic plate, specifically a kind of coated metallic plate.
Background technology
At present, household appliances shell, the chromatic metallic plate of Discussion on architecture decoration are typically laminated using colored in the prior art
Steel plate and colored pre-coated steel plate.Colored laminate steel in existing coated metallic plate includes substrate, and the substrate can be by cold rolling
The steel plates such as plate, electrolytic galvanized sheet, heat zinc coating plate, aluminium plating zinc plate are made.There is chemical treatment layer on two faces of substrate.Substrate
The outer application adhesive layer of front chemical treatment layer.Adhesive layer is mainly acrylic resin.Poly- terephthaldehyde is posted on adhesive layer
Sour glycol ester and polyvinyl chloride (PET/PVC) composite film.It is various by being carried out at the PET/PVC composite films back side
Printing treatment, realize colored laminate steel surface detail pattern.But because PET/PVC composite membranes are subsequently as at rubbish
Chlorine and dioxide gas can be produced during reason melting, environment is polluted.And PET/PVC composite membranes rapidoprint and life
Production. art reason, cost are very high.
The content of the invention
The present invention proposes a kind of coated metallic plate regarding to the issue above, and adhesive effect is good, improves product quality.
Specific technical scheme is as follows：
One layer of bonded adhesives is respectively coated in a kind of coated metallic plate, including substrate, the tow sides of substrate, and the thickness of bonded adhesives is
0.2-0.6mm, a strata ethylene glycol terephthalate film layer is pasted respectively on the bonded adhesives on two sides；
The preparation method of the bonded adhesives is：
Count polyester resin 50-70 parts, epoxy resin 25-35 parts, toughener 3-8 parts, dispersant 2-6 parts, disappear in parts by weight
Infusion 1-5 parts, acetone 10-12 parts, aluminum oxide 6-10 parts stir at a temperature of 70-90 DEG C.
Further, the ratio of weight and number of the polyester resin and epoxy resin is 2:1.
Further, the toughener is polyformaldehyde toughener.
Further, the dispersant is maleic acid-acrylic acid copolymer.
Further, the defoamer is 2,2,4- trimethyl -1,3- pentanediol mono isobutyrates.
Beneficial effects of the present invention are：Adhesive effect of the present invention is good, improves product quality.
Embodiment
To make technical scheme become apparent from clearly, below the present invention is described further, it is any to this
The scheme that the technical characteristic progress equivalencing of inventive technique scheme and conventional reasoning are drawn each falls within the scope of the present invention.
Embodiment one
One layer of bonded adhesives is respectively coated in a kind of coated metallic plate, including substrate, the tow sides of substrate, and the thickness of bonded adhesives is
0.2-0.6mm, a strata ethylene glycol terephthalate film layer is pasted respectively on the bonded adhesives on two sides；
The preparation method of the bonded adhesives is：
Count in parts by weight by 60 parts of polyester resin, 30 parts of epoxy resin, 5 parts of toughener, dispersant 2-6 parts, 4 parts of defoamer,
11 parts of acetone, 8 parts of aluminum oxide stir at a temperature of 70-90 DEG C.
Further, the ratio of weight and number of the polyester resin and epoxy resin is 2:1.
Further, the toughener is polyformaldehyde toughener.
Further, the dispersant is maleic acid-acrylic acid copolymer.
Further, the defoamer is 2,2,4- trimethyl -1,3- pentanediol mono isobutyrates.
Embodiment two
One layer of bonded adhesives is respectively coated in a kind of coated metallic plate, including substrate, the tow sides of substrate, and the thickness of bonded adhesives is
0.2-0.6mm, a strata ethylene glycol terephthalate film layer is pasted respectively on the bonded adhesives on two sides；
The preparation method of the bonded adhesives is：
Count 50 parts of polyester resin, 25 parts of epoxy resin, 3 parts of toughener, 2 parts of dispersant, 1 part of defoamer, third in parts by weight
10 parts of ketone, 6 parts of aluminum oxide stir at a temperature of 70-90 DEG C.
Further, the ratio of weight and number of the polyester resin and epoxy resin is 2:1.
Further, the toughener is polyformaldehyde toughener.
Further, the dispersant is maleic acid-acrylic acid copolymer.
Further, the defoamer is 2,2,4- trimethyl -1,3- pentanediol mono isobutyrates.
Embodiment three
One layer of bonded adhesives is respectively coated in a kind of coated metallic plate, including substrate, the tow sides of substrate, and the thickness of bonded adhesives is
0.2-0.6mm, a strata ethylene glycol terephthalate film layer is pasted respectively on the bonded adhesives on two sides；
The preparation method of the bonded adhesives is：
Count 70 parts of polyester resin, 35 parts of epoxy resin, 8 parts of toughener, 6 parts of dispersant, 5 parts of defoamer, third in parts by weight
12 parts of ketone, 10 parts of aluminum oxide stir at a temperature of 70-90 DEG C.
Further, the ratio of weight and number of the polyester resin and epoxy resin is 2:1.
Further, the toughener is polyformaldehyde toughener.
Further, the dispersant is maleic acid-acrylic acid copolymer.
Further, the defoamer is 2,2,4- trimethyl -1,3- pentanediol mono isobutyrates.
Claims (5)
1. a kind of coated metallic plate, it is characterized in that, including one layer of bonded adhesives is respectively coated in substrate, the tow sides of substrate, is bonded
The thickness of glue is 0.2-0.6mm, pastes a strata ethylene glycol terephthalate film layer on the bonded adhesives on two sides respectively；
The preparation method of the bonded adhesives is：
Count polyester resin 50-70 parts, epoxy resin 25-35 parts, toughener 3-8 parts, dispersant 2-6 parts, disappear in parts by weight
Infusion 1-5 parts, acetone 10-12 parts, aluminum oxide 6-10 parts stir at a temperature of 70-90 DEG C.
2. a kind of coated metallic plate as claimed in claim 1, it is characterized in that, the parts by weight of the polyester resin and epoxy resin
Number is than being 2:1.
3. a kind of coated metallic plate as claimed in claim 1, it is characterized in that, the toughener is polyformaldehyde toughener.
4. a kind of coated metallic plate as claimed in claim 1, it is characterized in that, the dispersant is copolymerized for maleic-acrylic acid
Thing.
5. a kind of coated metallic plate as claimed in claim 1, it is characterized in that, the defoamer is 2,2,4- trimethyls -1,3-
Pentanediol mono isobutyrate.