CN107556907A - A kind of high-temperature titanium alloy pipe - Google Patents
A kind of high-temperature titanium alloy pipe Download PDFInfo
- Publication number
- CN107556907A CN107556907A CN201710810402.1A CN201710810402A CN107556907A CN 107556907 A CN107556907 A CN 107556907A CN 201710810402 A CN201710810402 A CN 201710810402A CN 107556907 A CN107556907 A CN 107556907A
- Authority
- CN
- China
- Prior art keywords
- titanium alloy
- titanium
- temperature
- alloy pipe
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-temperature titanium alloy pipe, the titanium alloy tube includes titanium alloy body, is sprayed on the high-temperaure coating of the external wall surface of the titanium alloy tube, the titanium alloy body is using made of titanium magnesium alloy, the high-temperaure coating is sprayed on the titanium alloy tube external surface again that drying obtains using silester based high-temp-resistant coating, and the material composition and its mass percent that the silester based high-temp-resistant coating includes are:Ethyl polysilicate 35% 40%, silica flour 18% 25%, aluminum oxide 8% 12%, coalescents 4% 8%, remaining is water.Through the above way, the present invention sprays silester based high-temp-resistant coating on the outer wall of common titanium magnesium alloy pipe, after drying high-temperaure coating is formed on the outer wall of titanium magnesium alloy pipe, enable titanium magnesium alloy pipe used above at 600 DEG C, the intensity and inoxidizability of titanium magnesium alloy pipe are improved simultaneously, and it is low to prepare cost.
Description
Technical field
The present invention relates to titanium alloy tube to prepare technical field, more particularly to a kind of high-temperature titanium alloy pipe.
Background technology
Titanium alloy belongs to alloy in lightweight, has the characteristics that specific strength is high, specific modulus is high, structural behaviour is excellent, titanium alloy is close
Degree is only the 58% of steel, therefore is widely used in the fields such as oil, chemical industry, space flight.
Existing titanium alloy temperature in use is typically below 600 DEG C, when titanium alloy is in more than 650 DEG C of temperature, its intensity
Difference, inoxidizability deficiency, so tubing made of existing titanium alloy with temperature typically can only less than 600 DEG C, and use
It is higher that high-temperature titanium alloy prepares cost.
The content of the invention
The present invention solves the technical problem of a kind of high-temperature titanium alloy pipe is provided, adhere on common alloy of titanium outer wall
Have painting high-temperaure coating, common alloy of titanium pipe is used at a higher temperature, at the same improve titanium alloy tube intensity and
Inoxidizability, and it is low to prepare cost.
In order to solve the above technical problems, one aspect of the present invention is:A kind of high-temperature titanium alloy pipe, institute are provided
Stating titanium alloy tube includes titanium alloy body, is sprayed on the high-temperaure coating of the external wall surface of the titanium alloy tube, the titanium alloy
Body is that the high-temperaure coating is to be sprayed on the titanium using silester based high-temp-resistant coating using made of titanium magnesium alloy
Drying obtains again on alloy outer surface of tube body, material composition and its quality that the silester based high-temp-resistant coating includes
Percentage is:Ethyl polysilicate 35%-40%, silica flour 18%-25%, aluminum oxide 8%-12%, coalescents 4%-8%, remaining is
Water.
In a preferred embodiment of the present invention, the drying temperature after the silester based high-temp-resistant coating spraying is
180-200℃。
In a preferred embodiment of the present invention, the thickness of the high-temperaure coating is 8-20mm.
In a preferred embodiment of the present invention, the highest of the high-temperaure coating is resistant to temperature as 1950 DEG C.
The beneficial effects of the invention are as follows:The present invention sprays silester based high-temp-resistant on the outer wall of common titanium magnesium alloy pipe
Coating, high-temperaure coating is formed on the outer wall of titanium magnesium alloy pipe after drying, enables titanium magnesium alloy pipe used above at 600 DEG C,
The intensity and inoxidizability of titanium magnesium alloy pipe are improved simultaneously, and it is low to prepare cost.
Embodiment
It is described in detail with reference to presently preferred embodiments of the present invention, so that advantages and features of the invention can be more easy to
In being readily appreciated by one skilled in the art, apparent clearly defined so as to be made to protection scope of the present invention.
Embodiment one:
A kind of high-temperature titanium alloy pipe, the titanium alloy tube include titanium alloy body, are sprayed on the external wall surface of the titanium alloy tube
High-temperaure coating, the titanium alloy body is that the high-temperaure coating is to use silester using made of titanium magnesium alloy
Based high-temp-resistant coating is sprayed on the titanium alloy tube external surface, dries what is obtained through 180 DEG C again, and the silester base is resistance to
The material composition and its mass percent that high-temperature coatings include be:Ethyl polysilicate 35%, silica flour 20%, aluminum oxide 10%, into
Film auxiliary agent 5%, water 30%.
Wherein, the highest of the high-temperaure coating is resistant to temperature as 1950 DEG C.
Preferably, the thickness of the high-temperaure coating is 12mm.
Embodiment two:
A kind of high-temperature titanium alloy pipe, the titanium alloy tube include titanium alloy body, are sprayed on the external wall surface of the titanium alloy tube
High-temperaure coating, the titanium alloy body is that the high-temperaure coating is to use silester using made of titanium magnesium alloy
Based high-temp-resistant coating is sprayed on the titanium alloy tube external surface, dries what is obtained through 185 DEG C again, and the silester base is resistance to
The material composition and its mass percent that high-temperature coatings include be:Ethyl polysilicate 37%, silica flour 22%, aluminum oxide 8%, film forming
Auxiliary agent 6%, water 27%.
Wherein, the highest of the high-temperaure coating is resistant to temperature as 1950 DEG C.
Preferably, the thickness of the high-temperaure coating is 15mm.
Embodiment three:
A kind of high-temperature titanium alloy pipe, the titanium alloy tube include titanium alloy body, are sprayed on the external wall surface of the titanium alloy tube
High-temperaure coating, the titanium alloy body is that the high-temperaure coating is to use silester using made of titanium magnesium alloy
Based high-temp-resistant coating is sprayed on the titanium alloy tube external surface, dries what is obtained through 200 DEG C again, and the silester base is resistance to
The material composition and its mass percent that high-temperature coatings include be:Ethyl polysilicate 40%, silica flour 18%, aluminum oxide 10%, into
Film auxiliary agent 7%, water 25%.
Wherein, the highest of the high-temperaure coating is resistant to temperature as 1950 DEG C.
Preferably, the thickness of the high-temperaure coating is 18mm.
Present invention is disclosed a kind of high-temperature titanium alloy pipe, and it is resistance to that silester base is sprayed on the outer wall of common titanium magnesium alloy pipe
High-temperature coatings, high-temperaure coating is formed on the outer wall of titanium magnesium alloy pipe after drying, titanium magnesium alloy pipe is made more than 600 DEG C
With, while the intensity and inoxidizability of titanium magnesium alloy pipe are improved, and it is low to prepare cost.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (4)
1. a kind of high-temperature titanium alloy pipe, it is characterised in that the titanium alloy tube includes titanium alloy body, is sprayed on the titanium alloy
The high-temperaure coating on tube wall surface, the titanium alloy body are that the high-temperaure coating is using made of titanium magnesium alloy
It is sprayed on the titanium alloy tube external surface what drying again obtained using silester based high-temp-resistant coating, the silicic acid second
The material composition and its mass percent that ester group high-temperature resistant coating includes be:Ethyl polysilicate 35%-40%, silica flour 18%-
25%th, aluminum oxide 8%-12%, coalescents 4%-8%, remaining is water.
2. high-temperature titanium alloy pipe according to claim 1, it is characterised in that the silester based high-temp-resistant coating spraying
Drying temperature afterwards is 180-200 DEG C.
3. high-temperature titanium alloy pipe according to claim 1, it is characterised in that the thickness of the high-temperaure coating is 8-
20mm。
4. high-temperature titanium alloy pipe according to claim 1, it is characterised in that the highest of the high-temperaure coating is resistant to temperature
For 1950 DEG C.