CN107556892A - A kind of super-thin steel structure fire-proof paint and its production method - Google Patents
A kind of super-thin steel structure fire-proof paint and its production method Download PDFInfo
- Publication number
- CN107556892A CN107556892A CN201710965199.5A CN201710965199A CN107556892A CN 107556892 A CN107556892 A CN 107556892A CN 201710965199 A CN201710965199 A CN 201710965199A CN 107556892 A CN107556892 A CN 107556892A
- Authority
- CN
- China
- Prior art keywords
- parts
- super
- steel structure
- thin steel
- proof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of super-thin steel structure fire-proof paint, is made up of following raw material according to parts by weight：Diethylene glycol ether acetate：5 15 parts；Alkyd resin：15 25 parts；APP：38 56 parts；Melamine：5 10 parts；Pentaerythrite：20 30 parts；20 40 parts of talcum powder, solvent：25 parts, a kind of production method of super-thin steel structure fire-proof paint, the production method of the super-thin steel structure fire-proof paint comprises the following steps：S1；Stirred under normal pressure；S2：Grinding；S3 is packed.Super-thin steel structure fire-proof paint is domestic earliest ultrathin fire-proof product, and route of employing new technology develops.It is expanded foamed to meet fire, forms spongy charring layer, prevents heat from protecting steel construction ground not soften within a certain period of time to base material transmission and collapse.
Description
Technical field
The present invention relates to super-thin steel structure fire-proof paint technical field, specially a kind of super-thin steel structure fire-proof paint
And its production method.
Background technology
Super-thin steel structure fire-proof paint is widely used in large-scale industrial and mineral steel-structure factory building, various gymnasium, exhibition center master
Body steel structure fireproof protection.Super-thin steel structure fire-proof paint is domestic earliest ultrathin fire-proof product, road of employing new technology
Line develops.It is expanded foamed to meet fire, forms spongy charring layer, prevents heat from being protected within a certain period of time to base material transmission
Steel construction ground, which does not soften, to collapse.Super-thin steel structure fire-proof paint characteristic, easily construct, be nontoxic, coating is thin, and fire protecting performance is tall and erect
More, any surface finish, good decorating effect, film ageing-resistant performance is excellent, it is firm it is durable, not efflorescence for many years can be kept.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of ultra-thin steel structure proposed is prevented
Fiery coating and its production method.
To achieve the above object, the present invention provides following technical scheme：
A kind of super-thin steel structure fire-proof paint, it is made up of following raw material according to parts by weight：
Diethylene glycol ether acetate：5 parts；
Alkyd resin：15 parts；
APP：38 parts；
Melamine：5 parts；
Pentaerythrite：20 parts；
Talcum powder：20 parts；
Solvent：2 parts
Preferably, the alkyd resin.
Preferably, the APP particle diameter is 800 mesh.
Preferably, a kind of production method of super-thin steel structure fire-proof paint, the super-thin steel structure fire-proof paint
Production method comprises the following steps：
S1：Stirred under normal pressure：Diethylene glycol ether acetate：5 parts；15 parts of alkyd resin；APP：38 parts；Trimerization
Cyanamide:5 parts；20 parts of pentaerythrite；20 parts of talcum powder；Solvent：2 parts are stirred 30 minutes to 50 minutes,
S2：Enter grinder and be ground to fineness 90um
S3:Packaging：S2 product is packed according to specification requirement.
A kind of super-thin steel structure fire-proof paint provided by the invention, the super-thin steel structure fire-proof paint not only have compared with
Good fire protecting performance, and be that a kind of cost is cheap, excellent performance, full-featured super-thin steel structure fire-proof paint.
Embodiment
Based on the embodiment in the present invention, those of ordinary skill in the art are obtained under the premise of creative work is not made
The every other embodiment obtained, belongs to the scope of protection of the invention.
Embodiment 1
A kind of super-thin steel structure fire-proof paint, it is made up of following raw material according to parts by weight：
Diethylene glycol ether acetate：6 parts；
Alkyd resin：16 parts；
APP：39 parts；
Melamine：56 parts；
Pentaerythrite：21 parts；
Talcum powder：21 parts；
Solvent：23 parts；
Preferably, the alkyd resin.
Preferably, the APP particle diameter is 800 mesh.
A kind of production method of super-thin steel structure fire-proof paint, the production method bag of the super-thin steel structure fire-proof paint
Include following steps：
S1：Stirred under normal pressure：Diethylene glycol ether acetate：6 parts；16 parts of alkyd resin；APP：39 parts；Trimerization
Cyanamide:56 parts；21 parts of pentaerythrite；21 parts of talcum powder；Solvent：23 parts；Stir 30 minutes to 50 minutes,
S2：Enter grinder and be ground to fineness 90um
S3:Packaging：S2 product is packed according to specification requirement.
Embodiment 2
A kind of super-thin steel structure fire-proof paint, it is made up of following raw material according to parts by weight：
Diethylene glycol ether acetate：8 parts；
Alkyd resin：20 parts；
APP：40 parts；
Melamine：6 parts；
Pentaerythrite：23 parts；
Talcum powder：24 parts；
Solvent：3 parts；
Preferably, the alkyd resin.
Preferably, the APP particle diameter is 800 mesh.
A kind of production method of super-thin steel structure fire-proof paint, the production method bag of the super-thin steel structure fire-proof paint
Include following steps：
S1：Stirred under normal pressure：Diethylene glycol ether acetate：8 parts；20 parts of alkyd resin；APP：40 parts；Trimerization
Cyanamide:6 parts；23 parts of pentaerythrite；24 parts of talcum powder；Solvent：3 parts；Stir 30 minutes to 50 minutes,
S2：Enter grinder and be ground to fineness 90um
S3:Packaging：S2 product is packed according to specification requirement.
Embodiment 3
A kind of super-thin steel structure fire-proof paint, the formula of the super-thin steel structure fire-proof paint is by including following parts by weight
Component be made：
Diethylene glycol ether acetate：15 parts；
Alkyd resin：25 parts；
APP：56 parts；
Melamine：10 parts；
Pentaerythrite：30 parts；
Talcum powder：40 parts；
Solvent：5 parts；
Preferably, the alkyd resin.
Preferably, the APP particle diameter is 800 mesh.
A kind of production method of super-thin steel structure fire-proof paint, the production method bag of the super-thin steel structure fire-proof paint
Include following steps：
S1：Stirred under normal pressure：Diethylene glycol ether acetate：15 parts；Alkyd resin：25 parts；APP：56 parts；Three
10 parts of poly cyanamid；30 parts of pentaerythrite；40 parts of talcum powder；Solvent：5 parts；Stir 30 minutes to 50 minutes,
S2：Enter grinder and be ground to fineness 90um,
S3:Packaging：S2 product is packed according to specification requirement.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
- A kind of 1. super-thin steel structure fire-proof paint, it is characterised in that：It is made up of following raw material according to parts by weight：Diethylene glycol ether acetate：5-15 parts；Alkyd resin：15-25 parts；APP：38-56 parts；Melamine：5-10 parts；Pentaerythrite：20-30 parts；Talcum powder：20-40 parts；Solvent：2-5 parts.
- A kind of 2. super-thin steel structure fire-proof paint according to claim 1, it is characterised in that：By following raw material according to weight Measure part composition：Diethylene glycol ether acetate：5 parts；Alkyd resin：15 parts；APP：38 parts；Melamine：5 parts；Pentaerythrite：20 parts；Talcum powder：20 parts；Solvent：2 parts.
- A kind of 3. super-thin steel structure fire-proof paint according to claim 1, it is characterised in that：The alkyd resin.
- A kind of 4. super-thin steel structure fire-proof paint according to claim 1, it is characterised in that：The APP particle diameter For 800 mesh.
- A kind of 5. super-thin steel structure fire-proof paint according to claim 1, it is characterised in that：The diethylene glycol ether Acetate.
- A kind of 6. production method of super-thin steel structure fire-proof paint as claimed in claim 1, it is characterised in that：The ultra-thin shaped steel The production method of structure fire coating comprises the following steps：S1：Stirred under normal pressure：Diethylene glycol ether acetate：5 parts；15 parts of alkyd resin；APP：38 parts；Melamine: 5 parts；20 parts of pentaerythrite；20 parts of talcum powder；Solvent：2 parts are stirred 30 minutes to 50 minutes；S2：Enter grinder and be ground to fineness 90um；S3：Packaging：S2 product is packed according to specification requirement.