CN107556663A - A kind of microlite PVC floor and preparation method - Google Patents
A kind of microlite PVC floor and preparation method Download PDFInfo
- Publication number
- CN107556663A CN107556663A CN201710946752.0A CN201710946752A CN107556663A CN 107556663 A CN107556663 A CN 107556663A CN 201710946752 A CN201710946752 A CN 201710946752A CN 107556663 A CN107556663 A CN 107556663A
- Authority
- CN
- China
- Prior art keywords
- parts
- substrate
- microlite
- pvc
- finished product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of microlite PVC floor and preparation method, it is mainly made up of a microlite PVC substrates and the decoration musculus cutaneus posted in substrate surface, the tongue and groove of conventional floor installation is formed with least long side side of substrate, described substrate is made up of the microlite PVC raw materials of following parts by weight：30 50 parts of 100 150 parts of polyvinyl chloride resin, 200 300 parts of microlite powder, bamboo charcoal and bamboo powder compound, 1 10 parts of stabilizer, 2 12 parts of diatomite, 3 15 parts of ACR auxiliary materials, 2 10 parts of paraffin, 5 15 parts of stearic acid；Described preparation method includes：a）Substrate manufacture：Carry out dispensing in proportion, be put into mixer and be mixed evenly after all dispensings are mixed, then at a temperature of 160 200 DEG C, mould extrusion molding is utilized by extruding machine, and after being cut off and cooled down with guillotine, substrate finished product；b）Veneer：From wood skin, on the surface of substrate finished product with carrying out covering skin without aldehyde glue, you can.
Description
Technical field
The present invention relates to a kind of microlite PVC floor and preparation method, belong to chemical building material technical field.
Background technology
Polyvinyl chloride（PolyVinyl Chloride, abbreviation PVC）, yield is only second to polyethylene, is currently the most important ones
One of versatile material, have a extensive future, be becoming increasingly popular by composite prepared by matrix of PVC.
Existing PVC is widely used in flooring material, common are PVC wood plastic composite floor, and this floor is by PVC and wood
Powder composite material foaming is handled, and obtained composite floor board has good foam structure, passivation crack tip and can effectively be prevented
The expansion of crackle, so as to significantly improve the shock resistance of material and ductility, and greatly reduce the density of product.
At present, for microlite as the new high-tech product in architectural pottery field, it picks yo, elegant and poised, tool with sparkling and crystal-clear
Have imitative bag reason, painted level, the exterior decorative effect of superb craftsmanship, and it is not contaminated, be readily cleaned, be inherent excellent
Good physical and chemical performance, it is already present in the making of glass-ceramic clad plate product；Even it is used to make microlite
PVC foam flooring product, it is steady that it can solve the problem that existing imitative plastic decorative board material has not high product strength, short life, physical dimension
The technical problems such as qualitative poor, tool chemical toxicity.
The content of the invention
It is an object of the invention to overcome the shortcomings of the prior art, and offer is a kind of simple and reasonable for structure, and installation makes
With convenient, properties of product stabilization, intensity height, cheap, the simple microlite PVC floor of manufacture craft and preparation method.
To achieve the above object, the present invention uses following technical scheme：A kind of microlite PVC floor, it is mainly micro- by one
Spar PVC substrates and the decoration musculus cutaneus posted in substrate surface are formed, and conventional floor is formed with least long side side of substrate
The tongue and groove of installation, described substrate are made up of the microlite PVC raw materials of following parts by weight：Polyvinyl chloride resin 100-150 parts, crystallite
Stone powder 200-300 parts, bamboo charcoal and bamboo powder compound 30-50 parts, stabilizer 1-10 parts, diatomite 2-12 parts, ACR are auxiliary
Expect 3-15 parts, paraffin 2-10 parts, stearic acid 5-15 parts.
As preferred：Being offered on described substrate broadside end face along long side uniform has a plurality of insertion duct；It is described
Substrate be made up of the raw material of following parts by weight：125 parts of polyvinyl chloride resin, 250 parts of microlite powder, bamboo charcoal and bamboo powder compound 40
Part, 5 parts of stabilizer, 6 parts of diatomite, 10 parts of ACR auxiliary materials, 7 parts of paraffin, 10 parts of stearic acid, and added less according to being actually needed
Measure toner.
As preferred：The bottom surface of the substrate is provided with a plurality of horizontal shallow grooves perpendicular to long side；The substrate
Upper surface is also formed with rough surface, and the decoration musculus cutaneus for being formed with wood skin with being covered without aldehyde glue on the rough surface and being formed.
A kind of preparation method on microlite PVC floors as described above, described preparation method comprise the following steps：
a）Substrate manufacture：Dispensing is carried out in proportion, is put into mixer and mix after all dispensings are mixed
It is even, then at a temperature of 160-200 DEG C, mould extrusion molding is utilized by extruding machine, and cut off with guillotine and cold
But after, substrate finished product；
b）Veneer：From wood skin, on the surface of substrate finished product with carrying out covering skin without aldehyde glue, you can.
The present invention is the improvement to prior art, and it has simple and reasonable for structure, and easy to install, properties of product are steady
Calmly, the features such as intensity is high, cheap, and manufacture craft is simple.
Brief description of the drawings
Fig. 1 is the floor panel structure schematic diagram of the present invention.
Embodiment
Below in conjunction with accompanying drawing, the present invention will be described in detail：Shown in Fig. 1, a kind of microlite PVC of the present invention
Floor, it is mainly made up of a microlite PVC substrates 1 and the decoration musculus cutaneus 2 posted in substrate surface, in substrate 1 to the youthful and the elderly
The tongue and groove 3 of conventional floor installation is formed with flank side surface；Being offered on the described broadside end face of substrate 1 along long side uniform has
A plurality of insertion duct 4, the section in this duct can be square, triangle, circle or ellipse；The bottom surface of the substrate 1
It is provided with a plurality of horizontal shallow grooves 5 perpendicular to long side；The upper surface of the substrate 1 is also formed with rough surface, and coarse at this
The decoration musculus cutaneus 2 for being formed with wood skin with being covered without aldehyde glue on surface and being formed.
Substrate of the present invention is made up of the microlite PVC raw materials of following parts by weight：Polyvinyl chloride resin 100-150 parts are micro-
Spinel powders 200-300 parts, bamboo charcoal and bamboo powder compound 30-50 parts, stabilizer 1-10 parts, diatomite 2-12 parts, ACR
Auxiliary material 3-15 parts, paraffin 2-10 parts, stearic acid 5-15 parts.
Substrate of the present invention is preferably made up of the raw material of following parts by weight：125 parts of polyvinyl chloride resin, crystallite stone flour
40 parts of 250 parts of end, bamboo charcoal and bamboo powder compound, 5 parts of stabilizer, 6 parts of diatomite, 10 parts of ACR auxiliary materials, 7 parts of paraffin, stearic acid
10 parts, and add a small amount of toner according to being actually needed.
A kind of preparation method on the microlite PVC floors, described preparation method comprise the following steps：
a）Substrate manufacture：Dispensing is carried out in proportion, is put into mixer and mix after all dispensings are mixed
It is even, then at a temperature of 160-200 DEG C, mould extrusion molding is utilized by extruding machine, and cut off with guillotine and cold
But after, substrate finished product；
b）Veneer：From wood skin, on the surface of substrate finished product with carrying out covering skin without aldehyde glue, you can.
The technology that the present invention does not address is the structure and dispensing on existing conventional floor, as toner can be according to actual need
Select or do not select, and in the case of selection, addition is a small amount of.Other embodiments of the invention can be from above disclosure
Technical scheme in, as carried out any selection, selection or replacement in open number range, and any of existing known technology is replaced
Change etc. and to obtain, and those skilled in the art and any creative work need not be paid can obtain.
Claims (4)
1. a kind of microlite PVC floor, it is mainly by a microlite PVC substrates and the decoration musculus cutaneus group posted in substrate surface
Into being formed with the tongue and groove of conventional floor installation at least long side side of substrate, it is characterised in that described substrate is by following
The microlite PVC raw materials composition of parts by weight：Polyvinyl chloride resin 100-150 parts, microlite powder 200-300 parts, bamboo charcoal and bamboo powder
Compound 30-50 parts, stabilizer 1-10 parts, diatomite 2-12 parts, ACR auxiliary material 3-15 parts, paraffin 2-10 parts, stearic acid 5-
15 parts.
2. the microlite PVC floor according to claim 1, it is characterised in that along length on described substrate broadside end face
While offering uniform has a plurality of insertion duct；Described substrate is made up of the raw material of following parts by weight：125 parts of polyvinyl chloride resin,
40 parts of 250 parts of microlite powder, bamboo charcoal and bamboo powder compound, 5 parts of stabilizer, 6 parts of diatomite, 10 parts of ACR auxiliary materials, paraffin 7
Part, 10 parts of stearic acid, and add a small amount of toner according to being actually needed.
3. microlite PVC floor according to claim 2, it is characterised in that the bottom surface of the substrate is provided with a plurality of hang down
Directly in the horizontal shallow grooves of long side；The upper surface of the substrate is also formed with rough surface, and with without aldehyde glue on the rough surface
Cover the decoration musculus cutaneus for being formed with wood skin composition.
A kind of 4. preparation method on microlite PVC floors as described in claim 1 or 2 or 3, it is characterised in that described system
Comprise the following steps as method：
a）Substrate manufacture：Dispensing is carried out in proportion, is put into mixer and mix after all dispensings are mixed
It is even, then at a temperature of 160-200 DEG C, mould extrusion molding is utilized by extruding machine, and cut off with guillotine and cold
But after, substrate finished product；
b）Veneer：From wood skin, on the surface of substrate finished product with carrying out covering skin without aldehyde glue, you can.