CN107556613A - A kind of ornamental flower greenhouse gardening method - Google Patents
A kind of ornamental flower greenhouse gardening method Download PDFInfo
- Publication number
- CN107556613A CN107556613A CN201710779240.XA CN201710779240A CN107556613A CN 107556613 A CN107556613 A CN 107556613A CN 201710779240 A CN201710779240 A CN 201710779240A CN 107556613 A CN107556613 A CN 107556613A
- Authority
- CN
- China
- Prior art keywords
- light conversion
- film
- greenhouse gardening
- light
- conversion agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to agricultural greenhouse field of planting, more particularly to a kind of ornamental flower greenhouse gardening method.A kind of ornamental flower greenhouse gardening method, a kind of ornamental flower greenhouse gardening method, this method uses greenhouse gardening, described plastic house is provided with conversion film, conversion film includes film resin, modified additive and light conversion agent, described light conversion agent is the 0.5 ~ 1.0% of film resin quality, and the chemical general formula of light conversion agent is Zn 9‑x‑y TbNa(PO4)7F:xEu2+,yMn2+, x span is 0.02≤x≤0.04, and y span is 0.03≤y≤0.05.Optimal feux rouges and blue light ratio of the present invention according to needed for the red palm in growth course, helps peasant to improve working condition, can improve quality, the yield of plant, while can shorten growth period, makes its increase income, produces significant economic benefit and social benefit.
Description
Technical field
The present invention relates to agricultural greenhouse field of planting, more particularly to a kind of ornamental flower greenhouse gardening method.
Background technology
Modern proportion of crop planting has used the means such as substantial amounts of agricultural chemicals, chemical fertilizer, hormone medicine and transgenosis, therefore
Also many diseases are brought for the mankind, there is data to show that agricultural chemicals and chemical substance trigger the possibility of cancer very big, steroids
Human developmental may also be triggered precocious for medicine and transgenosis and some destabilizing factors, while agricultural chemicals and chemical fertilizer are also to other
Biology brings destructive strike.
Existing organic healthy food plantation with common plastic house plastic sheeting and applies the implantation methods such as organic fertilizer substantially
Based on, early investment fund is big, and plant maintenance cost is high, and volume increase is general, so existing organic healthy food yields poorly, price
It is expensive, large-scale promotion can not be realized substantially.
Conversion film be it is a kind of by add light conversion agent realize light change film, it can will to plant growth be harmful to purple
Outer light is converted into the blue violet light useful to crop and blood orange light, or the non-absorbent green glow of plant and green-yellow light are converted into feux rouges.
I.e. by changing the light quality through conversion film, promote absorption of the plant to nutrients such as nitrogen, phosphorus, potassium, zinc, improve in blade
Photosynthate content raises, and promotes plant growth, while plays a part of reducing pest and disease damage.
The content of the invention
First purpose of the present invention is to provide a kind of ornamental flower greenhouse gardening method, and second purpose of the invention is to carry
For the preparation method of above-mentioned conversion film；Optimal feux rouges and blue light ratio of the present invention according to needed for the red palm in growth course,
Help peasant to improve working condition, quality, the yield of plant can be improved, while growth period can be shortened, make its increase income, produce
Significant economic benefit and social benefit.
In order to realize first above-mentioned purpose, present invention employs following technical scheme：
A kind of ornamental flower greenhouse gardening method, a kind of ornamental flower greenhouse gardening method, this method uses greenhouse gardening, described
Plastic house be provided with conversion film, conversion film includes film resin, modified additive and light conversion agent, and described light conversion agent is film
The 0.5 ~ 1.0% of resin quality, the chemical general formula of light conversion agent is Zn 9-x-y TbNa(PO4)7F: xEu2+, yMn2+, x value model
Enclose for 0.02≤x≤0.04, y span is 0.03≤y≤0.05.
Preferably, the conversion film is made up of following component by mass percentage：
Film resin 96 ~ 99%
Light conversion agent 0.5 ~ 1.0%
Light stabilizer 0.1 ~ 0.5%
Antioxidant 0.1 ~ 0.5%
Lubricant 0.2 ~ 2.0%.
Preferably, the composition of described film resin be low density polyethylene (LDPE), linear polyethylene, high density polyethylene (HDPE),
One kind or any in polyvinyl chloride, polypropylene, polyamide, polystyrene, polyethylene terephthalate, polyvinyl acetate
Several combinations.
Preferably, the described light stabilizer includes 2-（2- hydroxy-5-methyl base phenyl）BTA, (2,2,6,
6- tetramethyl -4- piperidines) imines, the double -2,2,6,6- tetramethyl piperidines alcohol ester of decanedioic acid, 4- hydroxyl -2,2,6,6- tetramethyls -1-
One kind or any several combinations in piperidine alcohols, succinic acid.
Preferably, described antioxidant includes 2,4,6- tri-butyl-phenols, antioxidant 2246, antioxidant 300, antioxygen
One kind or any several combinations in agent 1010, irgasfos 168, dilauryl thiodipropionate.
Preferably, described lubricant includes Tissuemat E, vinyl bis-stearamides, zinc stearate, stearic acid season
One kind or any several combinations in Doutrate, polyethylene glycol and aluminate coupling agent.
The preparation method of above-mentioned conversion film, this method comprise the following steps：
1）Prepared by light conversion agent, with high-purity Zn3(PO4)2、TbPO4·H2O、NaF、Eu2O3And MnCO3For raw material, according to chemical formula
Zn 9-x-y TbNa(PO4)7F: xEu2+, yMn2+, x span is 0.01≤x≤0.03, y span for 0.02≤
The stoichiometric proportion of y≤0.05 weighs each raw material；Then it is well mixed after the raw material of acquisition is fully ground, and mixing acquisition
Compound is put into corundum crucible, and then corundum crucible and mixture are put into high temperature process furnances together and carry out calcination, calcination temperature
Spend for 1200 DEG C, calcination time is 6 hours, and sintering atmosphere is 5% hydrogen and 95% nitrogen mixture, sample after the completion of calcination
Room temperature is cooled to stove, finally taking-up acquisition sintered body progress ball milling, crushing, washing, drying can obtain the light conversion agent；
2）Prepared by masterbatch, the light conversion agent, modified additive and film resin are added in mixer and are stirred, to be mixed uniform
Afterwards, by the extruder extruding pelletization that extrusion temperature is 130~200 DEG C, screw speed is 100~500r/min, it is made described
Light conversion master batch；
3）Then the light conversion master batch is diluted with film resin and uniformly mixed, be blow molded by blow moulding machine described in being made and turn light
Film.
Conversion film in the present invention, the light conversion agent synthesis technique that it is used is simple, and active ingredient is uniformly dispersed, and cost is far low
In traditional light conversion agent, stability is good, and emission spectrum matches with photosynthesis of plant spectrum, improves the absorption to sunshine
With conversion efficiency, matching improves.Pass through one kind in modifying agent, light stabilizer, antioxidant, lubricant or any several groups
Close, improve light conversion agent turns light effect, improves photostability, strengthens its antioxygenic property under air and illumination,
Its service life is extended, optimizes film translucency, while improves its processing characteristics, it is scattered in conversion film to improve it
Degree.Light conversion agent provided by the invention turns light efficiency height, can fully absorb the black light in sunshine, and it is changed simultaneously
For blue light and feux rouges, the growth of plant can be effectively facilitated；The light conversion agent is in black light（365nm）Excite down bright with two
Aobvious emission peak, respectively positioned at 652nm red light district and positioned at 470nm blue light region.Light conversion agent provided by the invention can be with
By adjusting Eu2+And Mn2+The doping ratio of ion, effectively adjust the ratio of feux rouges and blue light, when feux rouges reaches it is most strong when, its
The ratio of feux rouges and blue light is just at 7:3, the conversion film for being highly suitable for red palm plantation uses.Provided by the present invention for
The ratio of the conversion film of red palm plantation, feux rouges and blue light is adapted to the demand of red palm field planting and nursery stage light source, can improve red
The speed of growth of the palm.
Embodiment
Embodiment 1
It is prepared by light conversion agent：With high-purity Zn3(PO4)2、TbPO4·H2O、NaF、Eu2O3And MnCO3For raw material, according to chemical formula
Zn8.47TbNa(PO4)7F: 0.03Eu2+, 0.5Mn2+Stoichiometric proportion weigh each raw material；Then by the raw material of acquisition in agate
It is well mixed, and the mixture of acquisition is put into corundum crucible after being fully ground in Nao mortars, then by corundum crucible and mixed
Compound is put into high temperature process furnances together carries out calcination, and calcination temperature is 1200 DEG C, and calcination time is 6 hours, and sintering atmosphere is
5% hydrogen and 95% nitrogen mixture, sample is cooled to room temperature with stove after the completion of calcination, finally takes out and obtains sintered body progress
Ball milling, crushing, washing, drying can obtain the light conversion agent.
Conversion film is blown：（1）70 parts of acrylic resin, 10 parts of light conversion agent, 2- are weighed by weight percentage（2- hydroxyls -5-
Aminomethyl phenyl）3 parts of BTA, 2 parts of tri-butyl-phenol, 15 parts of Tissuemat E；（2）Above-mentioned material is uniformly mixed in plasticator
Close, heating-up temperature is 160 DEG C, is then fabricated to light conversion master batch using granulating extruder；（3）Weigh by weight percentage and turn light mother
Grain 10 parts, 90 parts of acrylic resin, blown film, heating-up temperature are 170 DEG C on inflation film manufacturing machine after being well mixed.
Embodiment 2
It is prepared by light conversion agent：With high-purity Zn3(PO4)2、TbPO4·H2O、NaF、Eu2O3And MnCO3For raw material, according to chemical formula
Zn8.86TbNa(PO4)7F: 0.04Eu2+, 0.06Mn2+Stoichiometric proportion weigh each raw material；Then by the raw material of acquisition in agate
It is well mixed, and the mixture of acquisition is put into corundum crucible after being fully ground in Nao mortars, then by corundum crucible and mixed
Compound is put into high temperature process furnances together carries out calcination, and calcination temperature is 1200 DEG C, and calcination time is 6 hours, and sintering atmosphere is
5% hydrogen and 95% nitrogen mixture, sample is cooled to room temperature with stove after the completion of calcination, finally takes out and obtains sintered body progress
Ball milling, crushing, washing, drying can obtain the light conversion agent.
Conversion film is blown：（1）80 parts of acrylic resin, 6 parts of light conversion agent, 2- are weighed by weight percentage（2- hydroxy-5-methyls
Base phenyl）2 parts of BTA, 2 parts of tri-butyl-phenol, 10 parts of Tissuemat E；（2）Above-mentioned material is uniformly mixed in plasticator
Close, heating-up temperature is 160 DEG C, is then fabricated to light conversion master batch using granulating extruder；（3）Weigh by weight percentage and turn light mother
Grain 10 parts, 90 parts of acrylic resin, blown film, heating-up temperature are 170 DEG C on inflation film manufacturing machine after being well mixed.
Embodiment 3
It is prepared by light conversion agent：With high-purity Zn3(PO4)2、TbPO4·H2O、NaF、Eu2O3And MnCO3For raw material, according to chemical formula
Zn8.75TbNa(PO4)7F: 0.03Eu2+, 0.04Mn2+Stoichiometric proportion weigh each raw material；Then by the raw material of acquisition in agate
It is well mixed, and the mixture of acquisition is put into corundum crucible after being fully ground in Nao mortars, then by corundum crucible and mixed
Compound is put into high temperature process furnances together carries out calcination, and calcination temperature is 1200 DEG C, and calcination time is 6 hours, and sintering atmosphere is
5% hydrogen and 95% nitrogen mixture, sample is cooled to room temperature with stove after the completion of calcination, finally takes out and obtains sintered body progress
Ball milling, crushing, washing, drying can obtain the light conversion agent.
Conversion film is blown：（1）72 parts of acrylic resin, 8 parts of light conversion agent, 2- are weighed by weight percentage（2- hydroxy-5-methyls
Base phenyl）2 parts of BTA, 3 parts of tri-butyl-phenol, 15 parts of Tissuemat E；（2）Above-mentioned material is uniformly mixed in plasticator
Close, heating-up temperature is 160 DEG C, is then fabricated to light conversion master batch using granulating extruder；（3）Weigh by weight percentage and turn light mother
Grain 10 parts, 90 parts of acrylic resin, blown film, heating-up temperature are 170 DEG C on inflation film manufacturing machine after being well mixed.
A kind of ornamental flower greenhouse gardening method, this method use greenhouse gardening, and described plastic house, which is provided with, turns light
Film, the present invention are set the red palm A without using film plantation, the red palm B planted using commercial membrane and turned using prepared by embodiment 1 ~ 3
The red palm C, D, E of light film plantation carry out red palm growth indexes experiment.Experiment is single factor design scheme, is meaned except film
Different or whether there is film, other condition is basically identical, if so these indexs there were significant differences, be all to be made by the difference of film
Into, test data table 1 below.
Table 1：Influence of the different conversion films to " enthusiasm " morphological index
Claims (7)
1. a kind of ornamental flower greenhouse gardening method, this method uses greenhouse gardening, and described plastic house is provided with conversion film,
It is characterized in that the conversion film includes film resin, modified additive and light conversion agent, described light conversion agent is film resin quality
0.5 ~ 1.0%, the chemical general formula of light conversion agent is Zn 9-x-y TbNa(PO4)7F: xEu2+, yMn2+, x span for 0.02≤
X≤0.04, y span are 0.03≤y≤0.05.
2. a kind of ornamental flower greenhouse gardening method according to claim 1, it is characterised in that by mass percentage should
Conversion film is made up of following component：
Film resin 96 ~ 99%
Light conversion agent 0.5 ~ 1.0%
Light stabilizer 0.1 ~ 0.5%
Antioxidant 0.1 ~ 0.5%
Lubricant 0.2 ~ 2.0%.
A kind of 3. ornamental flower greenhouse gardening method according to claim 2, it is characterised in that：The composition of film resin is
It is low density polyethylene (LDPE), linear polyethylene, high density polyethylene (HDPE), polyvinyl chloride, polypropylene, polyamide, polystyrene, poly- to benzene two
One kind or any several combinations in formic acid glycol ester, polyvinyl acetate.
A kind of 4. ornamental flower greenhouse gardening method according to claim 2, it is characterised in that：The light stabilizer includes
2-（2- hydroxy-5-methyl base phenyl）Double-the 2,2,6,6- four of BTA, (2,2,6,6- tetramethyl -4- piperidines) imines, decanedioic acid
Methyl piperidine alcohol ester, 4- hydroxyl -2,2,6,6- tetramethyl -1- piperidine alcohols, one kind in succinic acid or any several combinations.
A kind of 5. ornamental flower greenhouse gardening method according to claim 2, it is characterised in that：Antioxidant includes 2,4,6-
In tri-butyl-phenol, antioxidant 2246, antioxidant 300, antioxidant 1010, irgasfos 168, dilauryl thiodipropionate
A kind of or any several combinations.
A kind of 6. ornamental flower greenhouse gardening method according to claim 2, it is characterised in that：Lubricant includes polyethylene
One kind in wax, vinyl bis-stearamides, zinc stearate, stearic acid pentaerythritol ester, polyethylene glycol and aluminate coupling agent
Or any several combinations.
7. one kind prepares the preparation method of the conversion film described in claim 1 ~ 6, it is characterised in that this method includes following step
Suddenly：
1）Prepared by light conversion agent, with high-purity Zn3(PO4)2、TbPO4·H2O、NaF、Eu2O3And MnCO3For raw material, according to chemical formula
Zn9-x-y TbNa(PO4)7F: xEu2+, yMn2+, x span is 0.01≤x≤0.03, and y span is 0.02≤y
≤ 0.05 stoichiometric proportion weighs each raw material；Then it is well mixed after the raw material of acquisition is fully ground, and mixing acquisition
Compound is put into corundum crucible, and then corundum crucible and mixture are put into high temperature process furnances together and carry out calcination, calcination temperature
Spend for 1200 DEG C, calcination time is 6 hours, and sintering atmosphere is 5% hydrogen and 95% nitrogen mixture, sample after the completion of calcination
Room temperature is cooled to stove, finally taking-up acquisition sintered body progress ball milling, crushing, washing, drying can obtain the light conversion agent；
2）Prepared by masterbatch, the light conversion agent, modified additive and film resin are added in mixer and are stirred, to be mixed uniform
Afterwards, by the extruder extruding pelletization that extrusion temperature is 130~200 DEG C, screw speed is 100~500r/min, it is made described
Light conversion master batch；
3）Then the light conversion master batch is diluted with film resin and uniformly mixed, be blow molded by blow moulding machine described in being made and turn light
Film.