CN107554110A - Positive and negative overprinting process using composite membrane as base material - Google Patents
Positive and negative overprinting process using composite membrane as base material Download PDFInfo
- Publication number
- CN107554110A CN107554110A CN201710827585.8A CN201710827585A CN107554110A CN 107554110 A CN107554110 A CN 107554110A CN 201710827585 A CN201710827585 A CN 201710827585A CN 107554110 A CN107554110 A CN 107554110A
- Authority
- CN
- China
- Prior art keywords
- printing paper
- transfer membrane
- printing
- multiple spot
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the positive and negative overprinting process using composite membrane as base material, the mother matrix of making multiple spot security pattern;With coating apparatus on PET basement membranes uniformly, be densely coated with coating of wax emulsion, then uniform one coating of coating in wax emulsion, then Tumblies Dry, resolidification 10 13 hours after drying;Transfer membrane is attached in printing paper, with glue spreader in the face gluing of printing paper one, the printing paper after gluing be combined with each other with transfer membrane by hot-pressing roller;By aluminium coated of the transfer membrane surface through 200 500 angstroms of thickness of vacuum aluminum-plating machine vacuum evaporation;Printing paper after stripping is sent into printing machine, pattern is accurately covered and is imprinted on the multiple spot security pattern being transferred in printing paper.
Description
Technical field
The present invention relates to chromatography field, and in particular to the positive and negative overprinting process using composite membrane as base material.
Background technology
Molding laser printing is a high-tech typography, integrates false proof and aesthetic feeling because laser graphic has
Advantage and be widely used in advertisement, illustration and packaging field.The method of prior art laser molding is first to be molded lithographic plate
Version volume is attached in cylindrical mold pressing roll, so as to be inevitably present the seam of molding version;Utilize such molding version and mould
The laser molding product that pressure device is produced, such as oriented polypropylene (OPP) (OPP) film, polyethylene terephthalate
(PET) film and polyvinyl chloride (PVC) film and paper etc., the laser graphic being stamped in above them are connect due to molding version
Stitch and version seam be present so that picture and text are discontinuous, the presence of version seam has a strong impact on laser molding product answering in web feed printing equipment
With.When printing figure message, which is printed on version, to be sewed on, spoilage will be produced;At present, some printing factories are using expensive jump seam
The molding version that device is skipped in printing on laser molding product is stitched to avoid the generation of spoilage, but it is very high to jump seam device
Close cooperation is given by molding producer expensive and that needs are special, is difficult in printing industry by the way of seam device is jumped therefore
Promote.
In the prior art, the usage amount of basement membrane is larger, and waste is more serious, while the usage amount of roller also can be more.This
The reduction and the raising of product quality that printing cost will be unfavorable for.And shift the common release agent material that film uses, spray
Aluminium lamination only contacts with mould release, can be effectively peeled off sprayed-on Al layer, but for there is one layer of relatively thick ink layer between the two, then
Being effectively peeled off for printing-ink can not be met;The common aqueous transfer glue water that uses of transfer film, can be by sprayed-on Al layer from release
Peeled away on agent material, but because there is thicker ink layer on sprayed-on Al layer, side can not meet printing ink layer and sprayed-on Al layer simultaneously
From effective transfer on peel ply.Also, plastic flexible package composite membrane picture and text print when be printing in film reverse side, then will printing
Ink surface is compound with hot sealing layer dry type and is made, it is necessary to can only be after dry type is compound again using the pattern of alumite thermoprinting foil thermoprint
Thermoprint causes that alignment can not be positioned with the printed patterns of film reverse side, picture and text are exposed to film after thermoprint on the surface of composite membrane
Surface easily abrades.
The content of the invention
The technical problems to be solved by the invention are that the cost of existing overprinting process is high, and finished product of poor quality, mesh
Be the positive and negative overprinting process using composite membrane as base material is provided, solve the problems, such as the overprinting process using composite membrane as base material.
The present invention is achieved through the following technical solutions:
Positive and negative overprinting process using composite membrane as base material, comprises the following steps:
S1:Anti-fake scheme is determined, multiple spot security pattern is formulated according to end user's Demand Design;
S2:Make multiple spot security pattern mother matrix, using light-resist plate as carrier, with laser head on light-resist plate the scorification depth
The pixel to differ, so as to be engraved as the pattern of plane or solid, then the light-resist plate after engraving is put into electroplating bath, passed through
Electroplating technology makes light-resist plate surface form nickel matter picture and text layer, nickel matter picture and text layer is separated with light-resist plate nickel matter picture and text mother matrix is made;
S3:Make transfer membrane, with coating apparatus on PET basement membranes uniformly, densely be coated with coating of wax emulsion, then in wax
Uniformly one coating of coating, then Tumble Dry, resolidification 10-13 hours after drying in emulsion;
S4:Multiple spot security pattern in die work version is embossed on transfer membrane, die work version is surrounded into roller
On, roller is arranged in moulding press, the transfer membrane being cured is subjected to two pairs of rollers molding with the roller in moulding press and pressure roller, will
Multiple spot security pattern in die work version is transferred on transfer membrane;
S5:Transfer membrane is attached in printing paper, with glue spreader in the face gluing of printing paper one, by the printing after gluing
Manufactured transfer membrane is combined with each other by hot-pressing roller during paper walks with S5;
S6:By the transfer membrane surface being combined with each other in S5 with hot-pressing roller through 200-500 angstroms of vacuum aluminum-plating machine vacuum evaporation
The aluminium coated of thickness;
S7:Transfer membrane after composite membrane cuts separation with printing paper, now the multiple spot security pattern on transfer membrane by
The surface of printing paper is transferred to, while the multiple spot security pattern on transfer membrane is still present, and it is above-mentioned compound with peeling off work
Skill can be repeated several times;
S8:Installation chromatography, the printing paper after S7 steps are stripped are sent into printing machine, make the upper figure of printing plate cylinder of printing machine
Case, which accurately covers, to be imprinted on the multiple spot security pattern being transferred in printing paper;
S9:Die cutting qualified ratio, S8 is walked into the slitting paper after printing into finished product.
Positive and negative overprinting process using composite membrane as base material, in the S3 drying dried using five warm areas, five warm areas drying temperature
Degree is respectively 80 DEG C, 120 DEG C, 145 DEG C, 135 DEG C, 115 DEG C.
Coating includes the component of following parts by weight in the S3:Waterborne polyurethane resin 24~29%, water soluble acrylic acid
Resin 10~16%, distilled water 35%~45%, defoamer 0.4~1.5%.Coating includes following parts by weight in the S3
Component:Waterborne polyurethane resin 26%, water-based acrylic resin 13%, distilled water 41%, defoamer 0.8%.
Positive and negative overprinting process using composite membrane as base material, the thickness of mother matrix is 0.1 μm~0.3 μm in the S2.
Further, the print product security pattern that the present invention produces is distributed in whole printed matter into multiple spot, passes through control
Deformation rate of the system transfer film in pattern transfer processes, and control galley and the set of multipoint positioning pattern in printing paper
Precision is printed, antifalse effect is good so as to reaching, the effect of clear patterns.And general printing enterprise is to be extremely difficult to such false proof effect
Fruit.And the product can be transferred to transfer coated in printing paper by transfer membrane, transfer film can be used repeatedly.Cause
This can reduce transfer film pollution on the environment, while can also reduce printing cost.
Further, and hot stamping pattern and the accurate chromatography of ink printing figure message can be realized, after product is compound printing layer and
For thermoprint layer in printing film inner surface, reflecting feel is strong, will not be influenceed and abraded by external force.
The present invention compared with prior art, has the following advantages and advantages:
1st, positive and negative overprinting process of the present invention using composite membrane as base material, the cost that prepared product is consumed is relatively low, and
And the final product quality prepared is preferable, is more convenient for using;
2nd, positive and negative overprinting process of the present invention using composite membrane as base material, preparation technology of the invention is simple, easy to operation.
Embodiment
For the object, technical solutions and advantages of the present invention are more clearly understood, with reference to embodiment, the present invention is made
Further to describe in detail, exemplary embodiment of the invention and its explanation are only used for explaining the present invention, are not intended as to this
The restriction of invention.
Embodiment 1
Positive and negative overprinting process of the present invention using composite membrane as base material, comprises the following steps:
S1:Anti-fake scheme is determined, multiple spot security pattern is formulated according to end user's Demand Design;
S2:Make multiple spot security pattern mother matrix, using light-resist plate as carrier, with laser head on light-resist plate the scorification depth
The pixel to differ, so as to be engraved as the pattern of plane or solid, then the light-resist plate after engraving is put into electroplating bath, passed through
Electroplating technology makes light-resist plate surface form nickel matter picture and text layer, nickel matter picture and text layer is separated with light-resist plate nickel matter picture and text mother matrix is made;
S3:Make transfer membrane, with coating apparatus on PET basement membranes uniformly, densely be coated with coating of wax emulsion, then in wax
Uniformly one coating of coating, then Tumble Dry, resolidification 10-13 hours after drying in emulsion;
S4:Multiple spot security pattern in die work version is embossed on transfer membrane, die work version is surrounded into roller
On, roller is arranged in moulding press, the transfer membrane being cured is subjected to two pairs of rollers molding with the roller in moulding press and pressure roller, will
Multiple spot security pattern in die work version is transferred on transfer membrane;
S5:Transfer membrane is attached in printing paper, with glue spreader in the face gluing of printing paper one, by the printing after gluing
Manufactured transfer membrane is combined with each other by hot-pressing roller during paper walks with S5;
S6:By the transfer membrane surface being combined with each other in S5 with hot-pressing roller through 200-500 angstroms of vacuum aluminum-plating machine vacuum evaporation
The aluminium coated of thickness;
S7:Transfer membrane after composite membrane cuts separation with printing paper, now the multiple spot security pattern on transfer membrane by
The surface of printing paper is transferred to, while the multiple spot security pattern on transfer membrane is still present, and it is above-mentioned compound with peeling off work
Skill can be repeated several times;
S8:Installation chromatography, the printing paper after S7 steps are stripped are sent into printing machine, make the upper figure of printing plate cylinder of printing machine
Case, which accurately covers, to be imprinted on the multiple spot security pattern being transferred in printing paper;
S9:Die cutting qualified ratio, S8 is walked into the slitting paper after printing into finished product.
The described positive and negative overprinting process using composite membrane as base material, in the S3 drying dried using five warm areas, five warm areas
Drying temperature is respectively 80 DEG C, 120 DEG C, 145 DEG C, 135 DEG C, 115 DEG C.
The described positive and negative overprinting process using composite membrane as base material, coating includes the group of following parts by weight in the S3
Point:Waterborne polyurethane resin 24~29%, water-based acrylic resin 10~16%, distilled water 35%~45%, defoamer 0.4~
1.5%.Coating includes the component of following parts by weight in the S3:Waterborne polyurethane resin 26%, water-based acrylic resin
13%th, distilled water 41%, defoamer 0.8%.
The described positive and negative overprinting process using composite membrane as base material, the thickness of mother matrix is 0.1 μm~0.3 μm in the S2.
Embodiment 2
On the basis of the chromatography of the present invention, using existing false proof process, chromatography is carried out, existing block letter is obtained, makes
Compared with the obtained block letter of the present invention, obtain, the wear resistance of block letter of the invention is better than existing 36.8%, no
Easily rub, and for cost, cost of the invention is than existing low 28.4%;It is existing for service life
Service life there was only 2~3 months, and the present invention service life it is longer, indifference when starting at 4~5 months and most.
In summary, the present invention and hot stamping pattern and the accurate chromatography of ink printing figure message can be realized, the compound printing afterwards of product
Layer and thermoprint layer are in printing film inner surface, and reflecting feel is strong, will not be influenceed and abraded by external force, and not only service life is longer,
Quality is more preferable, and cost is relatively low.
Above-described embodiment, the purpose of the present invention, technical scheme and beneficial effect are carried out further
Describe in detail, should be understood that the embodiment that the foregoing is only the present invention, be not intended to limit the present invention
Protection domain, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc., all should include
Within protection scope of the present invention.
Claims (5)
1. using composite membrane as the positive and negative overprinting process of base material, it is characterised in that comprise the following steps:
S1:Anti-fake scheme is determined, multiple spot security pattern is formulated according to end user's Demand Design;
S2:The mother matrix of multiple spot security pattern is made, using light-resist plate as carrier, scorification is deep mixed on light-resist plate with laser head
Pixel, so as to be engraved as plane or solid pattern, then the light-resist plate after engraving is put into electroplating bath, passes through plating
Technique makes light-resist plate surface form nickel matter picture and text layer, nickel matter picture and text layer is separated with light-resist plate nickel matter picture and text mother matrix is made;
S3:Make transfer membrane, with coating apparatus on PET basement membranes uniformly, densely be coated with coating of wax emulsion, then in wax emulsion
One coating of upper uniform coating, then Tumble Dry, resolidification 10-13 hours after drying;
S4:Multiple spot security pattern in die work version is embossed on transfer membrane, die work version is surrounded in roller, will
Roller is arranged in moulding press, and the transfer membrane being cured is carried out into two pairs of rollers molding with the roller in moulding press and pressure roller, will be molded
Multiple spot security pattern on working version is transferred on transfer membrane;
S5:Transfer membrane is attached in printing paper, with glue spreader in the face gluing of printing paper one, by the printing paper after gluing
Manufactured transfer membrane is combined with each other by hot-pressing roller in being walked with S5;
S6:By the transfer membrane surface being combined with each other in S5 with hot-pressing roller through 200-500 angstroms of thickness of vacuum aluminum-plating machine vacuum evaporation
Aluminium coated;
S7:Transfer membrane after composite membrane is cut separation with printing paper, and now the multiple spot security pattern on transfer membrane has been transferred
To the surface of printing paper, while the multiple spot security pattern on transfer membrane is still present, and above-mentioned compound and stripping technology can
It is repeated several times;
S8:Installation chromatography, the printing paper after S7 steps are stripped are sent into printing machine, make pattern essence on the printing plate cylinder of printing machine
Cover and be imprinted on the multiple spot security pattern being transferred in printing paper accurately;
S9:Die cutting qualified ratio, S8 is walked into the slitting paper after printing into finished product.
2. the positive and negative overprinting process according to claim 1 using composite membrane as base material, it is characterised in that dried in the S3
Dried using five warm areas, five warm area drying temperatures are respectively 80 DEG C, 120 DEG C, 145 DEG C, 135 DEG C, 115 DEG C.
3. the positive and negative overprinting process according to claim 1 using composite membrane as base material, it is characterised in that coating in the S3
Include the component of following parts by weight:Waterborne polyurethane resin 24~29%, water-based acrylic resin 10~16%, distilled water
35%~45%, defoamer 0.4~1.5%.
4. the positive and negative overprinting process according to claim 3 using composite membrane as base material, it is characterised in that coating in the S3
Include the component of following parts by weight:Waterborne polyurethane resin 26%, water-based acrylic resin 13%, distilled water 41%, defoaming
Agent 0.8%.
5. the positive and negative overprinting process according to claim 1 using composite membrane as base material, it is characterised in that mother matrix in the S2
Thickness be 0.1 μm~0.3 μm.