CN107542549A - Triangle acid-proof ceramics honeycomb substrate - Google Patents
Triangle acid-proof ceramics honeycomb substrate Download PDFInfo
- Publication number
- CN107542549A CN107542549A CN201610469693.8A CN201610469693A CN107542549A CN 107542549 A CN107542549 A CN 107542549A CN 201610469693 A CN201610469693 A CN 201610469693A CN 107542549 A CN107542549 A CN 107542549A
- Authority
- CN
- China
- Prior art keywords
- acid
- triangle
- next door
- stomata
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of triangle acid-proof ceramics honeycomb substrate.Section that it includes cylindrical body cylindrical body is triangle, including the first side（1）, the second side（2）With the 3rd side（3）, the cylindrical body is densely covered with stomata in the axial direction（4）, the stomata（4）One end be opening（9）, the other end is provided with closure face（5）, the two neighboring stomata（4）Between be provided with next door（6）, next door（6）On be provided with micropore in cellular arrangement（7）, next door（6）It is upper to be coated with catalyst coat（10）, ceramic honey comb surface is coated with acid-proof coating.A kind of triangle acid-proof ceramics honeycomb substrate of the present invention, acid resistance is good, good integrity, increases filter area to greatest extent in the confined space, and easy for installation, good purification；Micropore on next door can effectively filter the black smoke particle in waste gas, and black smoke particle can be burned off in the presence of catalyst coat, further increase tail gas clean-up effect.
Description
Technical field
The present invention relates to a kind of triangle acid-proof ceramics honeycomb substrate, for purifying vehicle exhaust.Belong to Ceramic manufacturing to set
Standby technical field.
Background technology
At present, the automobile exhaust purifier of unobstructed application both at home and abroad, its catalyst carrier are typically all carried using ceramic honeycomb
Body, this carrier are to add adhesive with synthesis of dichroite raw material, burn and lose agent, blended spice, pugging, extrusion, drying, sintering,
Then impregnated catalyst re-dry is made.In use, it is put into exhaust purifier metal shell stage casing.
Conventional ceramic honeycomb carrier is generally square cylinder, and it is net that the ceramic honeycomb carrier of such a shape is loaded into tail gas
When changing in the metal shell of device, often cause the space between ceramic honeycomb carrier and metal shell big so that tail gas clean-up
Device can not effectively utilize the space of automobile chassis, and some producers can add the pottery of small dimension to plug the gap in gap
Porcelain honeycomb substrate, this can cause the globality poor of the ceramic honeycomb carrier in metal-back, increase the resistance during vent gas treatment,
Tail gas clean-up effect is reduced, and honeycomb substrate is when mounted, complex operation, and efficiency is low；The gas of such a honeycomb substrate simultaneously
Hole is clear opening, poor to the waste gas purification effect containing black smoke particle.
Existing honeycomb substrate can not be effectively acidproof, can not meet the needs of client.
The content of the invention
It is an object of the invention to overcome above-mentioned deficiency, there is provided a kind of triangle acid-proof ceramics honeycomb substrate, this ceramics
Honeycomb substrate good integrity, good purification, easy for installation, honeycomb substrate can be effectively acidproof.
The object of the present invention is achieved like this：
A kind of triangle acid-proof ceramics honeycomb substrate, including cylindrical body, are characterized in：The section of the cylindrical body is triangle
Shape, including first while, second while and the 3rd side, described first while, second while and the connecting place on the 3rd side use round-corner transition, institute
State cylindrical body and be densely covered with stomata in the axial direction, one end of the stomata is opening, and the other end is provided with closure face, the envelope
Stifled face and open space are arranged, are provided with next door between the two neighboring stomata, are provided with next door in the micro- of cellular arrangement
Hole, catalyst coat is coated with next door, the honeycomb substrate surface is coated with acid-proof coating, and this acid-proof coating is mainly by following
Raw materials by weight portion proportioning is made：13 parts of quartz sand, 12 parts of petroleum coke, 9 parts of wood chip, 8 parts of sodium chloride, 1 part of titanium dioxide, second
13 parts of alcohol, 30 parts of water；
The preparation method of the acid-proof coating, is comprised the steps of：
（1）Quartz sand, petroleum coke and wood chip are pulverized, powder diameter is 400 mesh；
（2）By step（1）In powder and sodium chloride powder the input high temperature resistance furnace of acquisition, radiant heating, temperature is maintained at
1000 DEG C, 0.5 hour；
（3）Through step（2）Powder after pyrolytic semlting is with titania powder by weight 3:It is added to the water after 1 mixing, while stirring
Mix side and add ethanol thereto, microelectronics surface acid-proof coating can be obtained to all dissolvings.
A kind of triangle acid-proof ceramics honeycomb substrate of the present invention, the hole count of its stomata is 600 holes/square inch.
A kind of triangle acid-proof ceramics honeycomb substrate of the present invention, the thickness in its next door is 0.13 ~ 0.14mm.
Compared with prior art, the beneficial effects of the invention are as follows：
A kind of triangle acid-proof ceramics honeycomb substrate of the present invention, good integrity, the increase filtering to greatest extent in the confined space
Area, and easy for installation, good purification；Micropore on next door can effectively filter the black smoke particle in waste gas, and be catalyzed
Black smoke particle can be burned off in the presence of agent coating, further increase tail gas clean-up effect；The present invention is by the way that raw material is added
The method that work is sprayed into aqua, one kind, which is prepared, can be sprayed directly on ceramic honey comb surface, form one layer of densification, consolidation
Protective layer.
Brief description of the drawings
Fig. 1 is a kind of structural representation of triangle acid-proof ceramics honeycomb substrate of the present invention.
Fig. 2 is a kind of partial axial section figure of triangle acid-proof ceramics honeycomb substrate of the present invention.
Fig. 3 is the structural representation in the next door of the present invention.
In figure：
First side 1,
Second side 2,
3rd side 3,
Stomata 4,
Closure face 5,
Next door 6,
Micropore 7,
Tail gas 8,
Opening 9,
Catalyst coat 10.
Embodiment
Referring to Fig. 1-3, the present invention relates to a kind of triangle acid-proof ceramics honeycomb substrate, and it includes cylindrical body, the post
The section of shape body is triangle, including first at 1, second 2 and the 3rd side 3, and described first at 1, second 2 and the 3rd side
3 connecting place uses round-corner transition, and the cylindrical body is densely covered with stomata 4 in the axial direction, and one end of the stomata 4 is opening
9, the other end is provided with closure face 5, the closure face 5 and the arranged for interval of opening 9, is provided between the two neighboring stomata 4
Next door 6, the micropore 7 in cellular arrangement is provided with next door 6, catalyst coat 10 is coated with next door 6.
Wherein, the hole count of stomata 4 is 600 holes/square inch, and the thickness in next door 6 is 0.13 ~ 0.14mm.
The ceramic honey comb surface is coated with acid-proof coating, and this acid-proof coating is mainly matched by following raw materials by weight portion
It is made：13 parts of quartz sand, 12 parts of petroleum coke, 9 parts of wood chip, 8 parts of sodium chloride, 1 part of titanium dioxide, 13 parts of ethanol, 30 parts of water.
The preparation method of the acid-proof coating, is comprised the steps of：
（1）Quartz sand, petroleum coke and wood chip are pulverized, powder diameter is 400 mesh；
（2）By step（1）In powder and sodium chloride powder the input high temperature resistance furnace of acquisition, radiant heating, temperature is maintained at
1000 DEG C, 0.5 hour；
（3）Through step（2）Powder after pyrolytic semlting is with titania powder by weight 3:It is added to the water after 1 mixing, while stirring
Mix side and add ethanol thereto, microelectronics surface acid-proof coating can be obtained to all dissolvings.
Operation principle：The present invention is fabricated to honeycomb ceramic carrier using cordierite, and is built in diesel engine vent gas purification
In device, the waste gas with black smoke particle of diesel engine discharge enters from the opening 9 of stomata 4, because stomata 4 is opened at one end
Mouthfuls 9, and be then closure face 5 in the other end, therefore waste gas can be by the next door 6 with micropore 7, then opening from adjacent air holes 4
Mouth 9 is discharged, and because the diameter of black smoke particle is big compared with micropore 7, therefore the black smoke particle in waste gas will catch next door 6 by filtering
On, air-flow then passes through from micropore 7.
Active rare earth of the catalyst coat 10 containing noble metal, Main Ingredients and Appearance have Pt, Pd, Rh, Al2O3、Ce、La、
Zr, Cu, Mn, the waste gas of diesel combustion（The predominantly pernicious gas such as CO, HC, NOx）During through micropore 7, coat on next door 6
Catalyst coat 10 will strengthen CO, HC, NOxThe activity of three kinds of gas, it is promoted to carry out certain oxidationreduction chemistry anti-
Should, wherein CO is oxidized to colourless nontoxic carbon dioxide at high temperature, and HC compounds resolve into water at high temperature（H2O）With
Carbon dioxide, NOxIt is reduced into nitrogen and oxygen.
When diesel exhaust gas temperature reaches 375 degrees Celsius, in the presence of catalyst coat 10, the black smoke on next door 6
Particle can progressively burn and aoxidize, and the purifying rate of black smoke particle about reaches more than 85%, when reaction temperature reaches 500 degrees Celsius
When catalyst and black smoke particle reaction fall so as to completely burned（Catalysis burning）, now the purifying rate of black smoke particle up to 90% with
On.
Claims (3)
1. a kind of triangle acid-proof ceramics honeycomb substrate, including cylindrical body, it is characterised in that：The section of the cylindrical body is
Triangle, including the first side（1）, the second side（2）With the 3rd side（3）, first side（1）, the second side（2）With the 3rd side（3）
Connecting place use round-corner transition, the cylindrical body is densely covered with stomata in the axial direction（4）, the stomata（4）One end be
Opening（9）, the other end is provided with closure face（5）, the closure face（5）And opening（9）Arranged for interval, the two neighboring stomata
（4）Between be provided with next door（6）, next door（6）On be provided with micropore in cellular arrangement（7）, next door（6）It is upper to be coated with catalyst
Coating（10）, the ceramic honey comb surface is coated with acid-proof coating, and this acid-proof coating is mainly matched somebody with somebody by following raw materials by weight portion
Than being made：13 parts of quartz sand, 12 parts of petroleum coke, 9 parts of wood chip, 8 parts of sodium chloride, 1 part of titanium dioxide, 13 parts of ethanol, 30 parts of water；
The preparation method of the acid-proof coating, is comprised the steps of：
（1）Quartz sand, petroleum coke and wood chip are pulverized, powder diameter is 400 mesh；
（2）By step（1）In powder and sodium chloride powder the input high temperature resistance furnace of acquisition, radiant heating, temperature is maintained at
1000 DEG C, 0.5 hour；
（3）Through step（2）Powder after pyrolytic semlting is with titania powder by weight 3:It is added to the water after 1 mixing, while stirring
Mix side and add ethanol thereto, microelectronics surface acid-proof coating can be obtained to all dissolvings.
A kind of 2. triangle acid-proof ceramics honeycomb substrate according to claim 1, it is characterised in that：The stomata（4）'s
Hole count is 600 holes/square inch.
A kind of 3. triangle acid-proof ceramics honeycomb substrate according to claim 1 or 2, it is characterised in that：The next door（6）
Thickness be 0.13 ~ 0.14mm.