CN107540331A - A kind of good vitrified small ball wall insulation material of fire protecting performance - Google Patents
A kind of good vitrified small ball wall insulation material of fire protecting performance Download PDFInfo
- Publication number
- CN107540331A CN107540331A CN201710802504.9A CN201710802504A CN107540331A CN 107540331 A CN107540331 A CN 107540331A CN 201710802504 A CN201710802504 A CN 201710802504A CN 107540331 A CN107540331 A CN 107540331A
- Authority
- CN
- China
- Prior art keywords
- insulation material
- small ball
- protecting performance
- fire protecting
- wall insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of good vitrified small ball wall insulation material of fire protecting performance of building material field, the good vitrified small ball wall insulation material of the fire protecting performance includes following components：100 ~ 150 parts of glass bead, 30 ~ 50 parts of talcum powder, 30 ~ 60 parts of cement, 30 ~ 60 parts of waterglass, 1 ~ 10 part of curing agent, 1 ~ 10 part of hydrophober, 1 ~ 10 part of bleeding agent.The good vitrified small ball wall insulation material of the fire protecting performance has the advantages that density is big, compression strength is big, thermal conductivity factor is low, high insulating effect, and fire-protection rating is A levels, is a kind of fire-retardant heat-insulation material of high comprehensive performance.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of good vitrified small ball wall insulation material of fire protecting performance.
Background technology
Century energy crisis comes and has promoted the quick hair of building thermal insulation material with enforcing for Building Energy Conservation Policy
Exhibition.
Present insulation material is more to make dry-mixed thermal insulation mortar aglite with common talcum powder and granular polystyrene, but talcum
Powder has the easy efflorescence of water imbibition great ﹑, and cubical contraction is big in slurry stirring, easily causes that product later strength is low and hollowing cracking
Phenomena such as, and there is granular polystyrene organic material Yi Ran ﹑ fire protecting performance Cha ﹑ high temperature to produce pernicious gas and ageing-resistant weatherability
The defects of least big in Di ﹑ constructions, the combination property and workability of thermal insulation mortar need further to improve.
Because glass bead has certain granule strength, physicochemical property is sufficiently stable, and ageing-resistant weatherability is strong, has excellent
Different Jue Re ﹑ Fang Huo ﹑ sound absorption qualities, it is adapted to make light filling aggregate and Jue Re ﹑ Fang Huo ﹑ Xi Yin ﹑ insulation materials in numerous areas.
In building material industry, by the use of glass bead as aglite, can improve mortar and easy mobility and from anti-intensity,
Material shrinkage factor is reduced, improves product combination property, reduces comprehensive production cost.
The content of the invention
It is an object of the invention to provide a kind of good vitrified small ball wall insulation material of fire protecting performance, to make up prior art
Deficiency.
A kind of good vitrified small ball wall insulation material of fire protecting performance, the good vitrified small ball wall insulation of the fire protecting performance
Material includes following components：100~150 parts of glass bead, 30~50 parts of talcum powder, 30~60 parts of cement, waterglass 30~60
Part, 1~10 part of curing agent, 1~10 part of hydrophober, 1~10 part of bleeding agent.
Further, the good vitrified small ball wall insulation material of the fire protecting performance includes following components：Glass bead 100
~120 parts, 30~50 parts of talcum powder, 30~50 parts of cement, 30~50 parts of waterglass, 1~5 part of curing agent, 1~5 part of hydrophober,
1~5 part of bleeding agent.
The production technology of the good vitrified small ball wall insulation material of the fire protecting performance comprises the steps：
（1）Weigh glass bead, talcum powder, cement, waterglass, curing agent, hydrophober, bleeding agent according to the proportioning and be put into and stir
Mix and be mixed and stirred in machine uniformly；
（2）Distilled water is added into said mixture, continues 30~60min of stirring with mixer；
（3）Above-mentioned slurry, which is poured into mould, uses press-forming machine compressing, natural curing 48h, produces the fire line
The good vitrified small ball wall insulation material of energy.
Further, step（2）The addition distilled water, wherein ratio of water to material are 0.40~0.55:1.
Further, step（3）The compressing pressure is set as 0.80~0.85MPa.
Further, step（3）The compressing press time is set as 20~60min.
Further, step（3）The size of the mould is 1200mm × 600mm × 50mm.
In the application of wall heat insulation material, made with glass bead replacement traditional common talcum powder and granular polystyrene dry-mixed
Thermal insulation mortar aglite, the easy efflorescence of talcum powder water imbibition great ﹑ is overcome, cubical contraction is big in slurry stirring, easily causes
Product later strength is low and phenomena such as hollowing cracking, while it is high to compensate for granular polystyrene organic material Yi Ran ﹑ fire protecting performance Cha ﹑ again
Temperature produces the defects of least big in pernicious gas and ageing-resistant weatherability Di ﹑ constructions, improves the perfect synthesis of thermal insulation mortar
Performance and workability.
The good vitrified small ball wall insulation material of the fire protecting performance have density is big, compression strength is big, thermal conductivity factor is low,
The advantages that high insulating effect, and fire-protection rating is A levels, is a kind of fire-retardant heat-insulation material of high comprehensive performance.
Embodiment
Embodiment 1
A kind of good vitrified small ball wall insulation material of fire protecting performance, the good vitrified small ball wall insulation material of the fire protecting performance
Including following components：100 parts of glass bead, 50 parts of talcum powder, 50 parts of cement, 30 parts of waterglass, 3 parts of curing agent, hydrophober 5
Part, 3 parts of bleeding agent.
The production technology of the good vitrified small ball wall insulation material of the fire protecting performance comprises the steps：
（1）Weigh glass bead, talcum powder, cement, waterglass, curing agent, hydrophober, bleeding agent according to the proportioning and be put into and stir
Mix and be mixed and stirred in machine uniformly；
（2）Distilled water is added into said mixture, is continued to stir 30min with mixer；
（3）Above-mentioned slurry, which is poured into mould, uses press-forming machine compressing, wherein compressing pressure is set as
0.80MPa, press time are set as 30min, last natural curing 48h, produce the good vitrified small ball wall of the fire protecting performance
Insulation material.
Embodiment 2
A kind of good vitrified small ball wall insulation material of fire protecting performance, the good vitrified small ball wall insulation material of the fire protecting performance
Including following components：120 parts of glass bead, 50 parts of talcum powder, 30 parts of cement, 50 parts of waterglass, 3 parts of curing agent, hydrophober 3
Part, 3 parts of bleeding agent.
The production technology of the good vitrified small ball wall insulation material of the fire protecting performance comprises the steps：
（1）Weigh glass bead, talcum powder, cement, waterglass, curing agent, hydrophober, bleeding agent according to the proportioning and be put into and stir
Mix and be mixed and stirred in machine uniformly；
（2）Distilled water is added into said mixture, is continued to stir 40min with mixer；
（3）Above-mentioned slurry, which is poured into mould, uses press-forming machine compressing, wherein compressing pressure is set as
0.80MPa, press time are set as 40min, last natural curing 48h, produce the good vitrified small ball wall of the fire protecting performance
Insulation material.
Embodiment 3
A kind of good vitrified small ball wall insulation material of fire protecting performance, the good vitrified small ball wall insulation material of the fire protecting performance
Including following components：110 parts of glass bead, 50 parts of talcum powder, 40 parts of cement, 20 parts of waterglass, 5 parts of curing agent, hydrophober 5
Part, 3 parts of bleeding agent.
The production technology of the good vitrified small ball wall insulation material of the fire protecting performance comprises the steps：
（1）Weigh glass bead, talcum powder, cement, waterglass, curing agent, hydrophober, bleeding agent according to the proportioning and be put into and stir
Mix and be mixed and stirred in machine uniformly；
（2）Distilled water is added into said mixture, is continued to stir 40min with mixer；
（3）Above-mentioned slurry, which is poured into mould, uses press-forming machine compressing, wherein compressing pressure is set as
0.80MPa, press time are set as 40min, last natural curing 48h, produce the good vitrified small ball wall of the fire protecting performance
Insulation material.
Claims (7)
1. the good vitrified small ball wall insulation material of a kind of fire protecting performance, it is characterised in that the good vitreous of the fire protecting performance is micro-
Pearl wall heat insulation material includes following components：100~150 parts of glass bead, 30~50 parts of talcum powder, 30~60 parts of cement, water
30~60 parts of glass, 1~10 part of curing agent, 1~10 part of hydrophober, 1~10 part of bleeding agent.
2. the good vitrified small ball wall insulation material of a kind of fire protecting performance according to claim 1, it is characterised in that described
The good vitrified small ball wall insulation material of fire protecting performance includes following components：100~120 parts of glass bead, talcum powder 30~50
Part, 30~50 parts of cement, 30~50 parts of waterglass, 1~5 part of curing agent, 1~5 part of hydrophober, 1~5 part of bleeding agent.
3. the good vitrified small ball wall insulation material of a kind of fire protecting performance according to claim 1, it is characterised in that described
The production technology of the good vitrified small ball wall insulation material of fire protecting performance comprises the steps：
（1）Weigh glass bead, talcum powder, cement, waterglass, curing agent, hydrophober, bleeding agent according to the proportioning and be put into and stir
Mix and be mixed and stirred in machine uniformly；
（2）Distilled water is added into said mixture, continues 30~60min of stirring with mixer；
（3）Above-mentioned slurry, which is poured into mould, uses press-forming machine compressing, natural curing 48h, produces the fire line
The good vitrified small ball wall insulation material of energy.
A kind of 4. good vitrified small ball wall insulation material of fire protecting performance according to claim 3, it is characterised in that
Step（2）The addition distilled water, wherein ratio of water to material are 0.40~0.55:1.
A kind of 5. good vitrified small ball wall insulation material of fire protecting performance according to claim 3, it is characterised in that step
（3）The compressing pressure is set as 0.80~0.85MPa.
A kind of 6. good vitrified small ball wall insulation material of fire protecting performance according to claim 3, it is characterised in that step
（3）The compressing press time is set as 20~60min.
A kind of 7. good vitrified small ball wall insulation material of fire protecting performance according to claim 3, it is characterised in that step
（3）The size of the mould is 1200mm × 600mm × 50mm.