CN107523396A - The oily preparation technology of health, the wheel hub forging and stamping of environmental protection - Google Patents

The oily preparation technology of health, the wheel hub forging and stamping of environmental protection Download PDF

Info

Publication number
CN107523396A
CN107523396A CN201710870483.4A CN201710870483A CN107523396A CN 107523396 A CN107523396 A CN 107523396A CN 201710870483 A CN201710870483 A CN 201710870483A CN 107523396 A CN107523396 A CN 107523396A
Authority
CN
China
Prior art keywords
parts
oil
health
environmental protection
wheel hub
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710870483.4A
Other languages
Chinese (zh)
Inventor
昝建玖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Forster Aluminium Products Ltd By Share Ltd
Original Assignee
Anhui Forster Aluminium Products Ltd By Share Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Forster Aluminium Products Ltd By Share Ltd filed Critical Anhui Forster Aluminium Products Ltd By Share Ltd
Priority to CN201710870483.4A priority Critical patent/CN107523396A/en
Publication of CN107523396A publication Critical patent/CN107523396A/en
Pending legal-status Critical Current

Abstract

The invention discloses health, the preparation technology of the wheel hub forging and stamping oil of environmental protection, including：After each component is matched by corresponding parts by weight, under 60 ~ 75 DEG C of temperature conditionss, oil refining device is used to prepare required forging and stamping oil.The preparation technology of wheel hub forging and stamping of the present invention oil, can overcome and be unfavorable for health in the prior art, be not easy the defects of storage and feature of environmental protection difference, with realize be advantageous to health, convenient storage and the feature of environmental protection are good the advantages of.

Description

The oily preparation technology of health, the wheel hub forging and stamping of environmental protection
Technical field
The invention mainly relates to the technical field of automotive hub, and in particular to the oily system of health, the wheel hub forging and stamping of environmental protection Standby technique.
Background technology
Wheel hub, the interior cylindrical piece of metal for being used to support tire centered on axle of automobile tire, is exactly car generally The position of axletree is installed at wheel center, is connection brake drum（Brake disc）, wheel disc and semiaxis important spare part.
During wheel hub forges and presses, forging and stamping oil plays the effect such as lubrication, cooling, cooling, also has sealing function in addition： It is required that anti-leak, dust-proof, anti-collaborating；Anticorrosive antirust, it is desirable to protect friction surface not by deterioration of oil or external erosion；It is peace and quiet Rinse, it is desirable to rubbing surface incrustation is cleaned and excluded；The scattered buffering of stress, scatteredload and mitigation impact and damping；Kinetic energy transmission, Hydraulic system and telemotor and Friction Stepless etc..
Existing forging and stamping oil is more to be prepared using organic solvent, such as traditional is adjusted using dichloromethane as solvent System, this solvent is volatile, and smell is larger, there is larger toxicity to human body, and the influence to environment also should not be underestimated.Therefore need to develop Go out a kind of performance requirement that can both meet forging and stamping, the environment-protecting and non-poisonous cold forging force feed formula of and can.
The content of the invention
The invention provides a kind of health, the preparation technology of the wheel hub forging and stamping oil of environmental protection, to solve above-mentioned background skill The technical problem proposed in art.
The present invention solve the technical scheme that uses of above-mentioned technical problem for：The oily preparation of health, the wheel hub forging and stamping of environmental protection Technique, including：
(1) by following parts by weight proportioning each component：
Paraffin base lubricating oil：4 parts；
Butylated hydroxy anisole：3 parts；
Metal dithiophosphate：5 parts；
Olefine sulfide：8 parts；
Mineral oil：30 parts；
Sulfide aliphatic acid ester：25 parts；
Olefine sulfide 11：Part；
Polymeric aliphatic ester：13 parts；
Vulcanize animal oleyl amine：24 parts；
Maleic acid copolymerized ester：3.5 part；
Hydroxypropyl cellulose：4.6 part；
Corn oil：18 parts；
Volatility mineral oil：35 parts；
Sulfide aliphatic acid：3 parts；
Olefine sulfide：1 part；
Polymeric aliphatic ester：1 part；
Vulcanize grease：1 part；
(2) after each component is matched by corresponding parts by weight, under 60 ~ 75 DEG C of temperature conditionss, use oil refining device to prepare required forge Force feed.
Preferably, the boiling range of the volatility mineral oil is 60~90 degrees Celsius.
Preferably, kinematic viscosity during 40 degrees Celsius of the sulfide aliphatic acid ester is 240~280mm/s.
Preferably, the kinematic viscosity of the olefine sulfide is 35~55mm/s.
Preferably, kinematic viscosity during 40 degrees Celsius of the polymeric aliphatic ester is 2800~2900mm/s.
Preferably, the density of the refined plant oil is 0.910~0.915g/cm3 。
Preferably, kinematic viscosity during 40 degrees Celsius of the grease of vulcanization is 240~280mm/s.
Preferably, the sulfur content in the vulcanization grease is 15.5~26.0 weight %.
Compared with prior art, beneficial effects of the present invention are：
After 1. in the present invention, each component is matched by corresponding parts by weight, under 60 ~ 75 DEG C of temperature conditionss, oil refining is used Machine forges and presses oil needed for preparing；So as to overcome be unfavorable in the prior art health, be not easy storage and the feature of environmental protection difference lack Fall into, the advantages of being advantageous to health with realization, facilitate storage and the feature of environmental protection good；
2. further, the forging and stamping oil formula avoids making using oil based on biological preparation method worth mineral oil and vegetable oil With volatile, poisonous and hazardous organic solvent, so as to reach lubrication, the main body effect of cooling, the operating efficiency of forging and stamping is improved, More safety and environmental protection.
Detailed explanation is carried out to the present invention below with reference to specific embodiment.
Embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment, the oily preparation technology of health, the wheel hub forging and stamping of environmental protection, including：
(1) by following parts by weight proportioning each component：
Paraffin base lubricating oil：4 parts；
Butylated hydroxy anisole：3 parts；
Metal dithiophosphate：5 parts；
Olefine sulfide：8 parts；
Mineral oil：30 parts；
Sulfide aliphatic acid ester：25 parts；
Olefine sulfide 11：Part；
Polymeric aliphatic ester：13 parts；
Vulcanize animal oleyl amine：24 parts；
Maleic acid copolymerized ester：3.5 part；
Hydroxypropyl cellulose：4.6 part；
Corn oil：18 parts；
Volatility mineral oil：35 parts；
Sulfide aliphatic acid：3 parts；
Olefine sulfide：1 part；
Polymeric aliphatic ester：1 part；
Vulcanize grease：1 part；
(2) after each component is matched by corresponding parts by weight, under 60 ~ 75 DEG C of temperature conditionss, use oil refining device to prepare required forge Force feed.
2. the boiling range of the volatility mineral oil is 60~90 degrees Celsius, 40 degrees Celsius of the sulfide aliphatic acid ester When kinematic viscosity be 240~280mm/s, the kinematic viscosity of the olefine sulfide is 35~55mm/s, the polymerization fat Kinematic viscosity during 40 degrees Celsius of fat acid esters is 2800~2900mm/s, and the density of the refined plant oil is 0.910 ~0.915g/cm3, kinematic viscosity during 40 degrees Celsius of the grease of vulcanization is 240~280mm/s, the vulcanization Sulfur content in grease is 15.5~26.0 weight %.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention God any modification, equivalent substitution and improvements made etc., should be included in the scope of the protection with principle.

Claims (8)

1. the oily preparation technology of health, the wheel hub forging and stamping of environmental protection, it is characterised in that including：
(1) by following parts by weight proportioning each component：
Paraffin base lubricating oil：4 parts；
Butylated hydroxy anisole：3 parts；
Metal dithiophosphate：5 parts；
Olefine sulfide：8 parts；
Mineral oil：30 parts；
Sulfide aliphatic acid ester：25 parts；
Olefine sulfide 11：Part；
Polymeric aliphatic ester：13 parts；
Vulcanize animal oleyl amine：24 parts；
Maleic acid copolymerized ester：3.5 part；
Hydroxypropyl cellulose：4.6 part；
Corn oil：18 parts；
Volatility mineral oil：35 parts；
Sulfide aliphatic acid：3 parts；
Olefine sulfide：1 part；
Polymeric aliphatic ester：1 part；
Vulcanize grease：1 part；
(2) after each component is matched by corresponding parts by weight, under 60 ~ 75 DEG C of temperature conditionss, use oil refining device to prepare required forge Force feed.
2. the oily preparation technology of health according to claim 1, the wheel hub forging and stamping of environmental protection, it is characterised in that described to wave The boiling range of hair property mineral oil is 60~90 degrees Celsius.
3. the preparation technology of the wheel hub forging and stamping oil of health, environmental protection according to claim 1, it is characterised in that described Kinematic viscosity during 40 degrees Celsius of sulfide aliphatic acid ester is 240~280mm/s.
4. the preparation technology of the wheel hub forging and stamping oil of health, environmental protection according to claim 1, it is characterised in that described The kinematic viscosity of olefine sulfide is 35~55mm/s.
5. the preparation technology of the wheel hub forging and stamping oil of health, environmental protection according to claim 1, it is characterised in that described Kinematic viscosity during 40 degrees Celsius of polymeric aliphatic ester is 2800~2900mm/s.
6. the preparation technology of the wheel hub forging and stamping oil of health, environmental protection according to claim 1, it is characterised in that described The density of refined plant oil is 0.910~0.915g/cm3 。
7. the preparation technology of the wheel hub forging and stamping oil of health, environmental protection according to claim 1, it is characterised in that described Kinematic viscosity when vulcanizing 40 degrees Celsius of grease is 240~280mm/s.
8. the preparation technology of the wheel hub forging and stamping oil of health, environmental protection according to claim 7, it is characterised in that described The sulfur content vulcanized in grease is 15.5~26.0 weight %.
CN201710870483.4A 2017-09-23 2017-09-23 The oily preparation technology of health, the wheel hub forging and stamping of environmental protection Pending CN107523396A (en)