CN107522929A - A kind of anlistatig high polymer material - Google Patents
A kind of anlistatig high polymer material Download PDFInfo
- Publication number
- CN107522929A CN107522929A CN201710745618.4A CN201710745618A CN107522929A CN 107522929 A CN107522929 A CN 107522929A CN 201710745618 A CN201710745618 A CN 201710745618A CN 107522929 A CN107522929 A CN 107522929A
- Authority
- CN
- China
- Prior art keywords
- parts
- molecular weight
- polymer material
- high polymer
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anlistatig high polymer material, it is characterised in that：It is made up of the component of following mass parts：Ultra-high molecular weight polyethylene 80 90 part, poly- fragrant alkali 35 part, plasticizer 36 part, concentrated hydrochloric acid 13 part, propylene glycol ester terephthalate valeric acid butanediol 10 12 part, stalk ashes 25 part, poly- nonyl dianhydride 13 part, hydrogenated rosin 24 part, antioxidant RD 14 part, crosslinked starch 24 part, carbon black 13 part, sodium citrate 25 part and glass fibre 35 part of the molecular weight for 500 600 ten thousand.The high polymer material of the present invention is using ultra-high molecular weight polyethylene as base-material, the high polymer material produced has resistant to elevated temperatures performance, simultaneously, glass fibre is with the addition of in the present invention, it is big using the insulating properties possessed in itself and tensile strength of glass fibre, improve the antistatic and mechanical performance of high polymer material.
Description
Technical field
The invention belongs to technical field of macromolecules, and in particular to a kind of anlistatig high polymer material.
Background technology
At present, the rapid development of modern industrial society, the utilization of high polymer material is more and more extensive, major colleges and universities, research
Mechanism is both provided with high polymer material research center, and high polymer material is the material being made up of the higher compound of relative molecular mass
Material, including rubber, plastics, fiber, coating, adhesive and polymer-based composite, macromolecule are forms existing for life.Institute
Some life entities can be regarded as high molecular set.At present, good mechanical property, high temperature resistant and anlistatig macromolecule material are gone back
Material.
The content of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of good mechanical property, resistant to elevated temperatures
Anlistatig high polymer material, to solve the problems, such as proposed in background technology.
To achieve the above object, the technical solution adopted by the present invention is：A kind of anlistatig high polymer material, its innovative point
It is：It is made up of the component of following mass parts：Molecular weight be 500-600 ten thousand ultra-high molecular weight polyethylene 80-90 parts, gather fragrant alkali
3-5 parts, plasticizer 3-6 parts, concentrated hydrochloric acid 1-3 parts, propylene glycol ester terephthalate-valeric acid butanediol 10-12 parts, stalk ashes 2-
5 parts, poly- nonyl dianhydride 1-3 parts, hydrogenated rosin 2-4 parts, antioxidant RD1-4 parts, crosslinked starch 2-4 parts, carbon black 1-3 parts, citron
Sour sodium 2-5 parts and glass fibre 3-5 parts.
Further, a kind of anlistatig high polymer material, is made up of the component of following mass parts：Molecular weight is 500-
6000000 ultra-high molecular weight polyethylene 82-88 parts, gather fragrant alkali 3-4 parts, plasticizer 4-5 parts, concentrated hydrochloric acid 1-2 parts, terephthaldehyde
Acid propylene glycol ester-valeric acid butanediol 10-11 parts, stalk ashes 3-4 parts, poly- nonyl dianhydride 1-3 parts, hydrogenated rosin 2-3 parts, antioxygen
Agent RD2-3 parts, crosslinked starch 2-3 parts, carbon black 2-3 parts, sodium citrate 3-4 parts and glass fibre 3-4 parts.
Further, a kind of anlistatig high polymer material, is made up of the component of following mass parts：Molecular weight is 500-
6000000 85 parts of ultra-high molecular weight polyethylene, gather fragrant 3 parts of alkali, 4 parts of plasticizer, 2 parts of concentrated hydrochloric acid, propylene glycol ester terephthalate-
11 parts of valeric acid butanediol, 4 parts of stalk ashes, 3 parts of poly- nonyl dianhydride, 3 parts of hydrogenated rosin, antioxidant RD3 parts, crosslinked starch 2
Part, 2 parts of carbon black, 4 parts of sodium citrate and 4 parts of glass fibre.
The present invention has the beneficial effect that：The high polymer material of the present invention, as base-material, is given birth to using ultra-high molecular weight polyethylene
The high polymer material of output has resistant to elevated temperatures performance, meanwhile, glass fibre is with the addition of in the present invention, utilizes the sheet of glass fibre
The insulating properties and tensile strength that body possesses are big, improve the antistatic and mechanical performance of high polymer material.
Embodiment
Present embodiment use technical scheme be：
Embodiment 1
A kind of anlistatig high polymer material, is made up of the component of following mass parts：Molecular weight is the super of 500-600 ten thousand
80 parts of High molecular weight polyethylene, gather fragrant 3 parts of alkali, 3 parts of plasticizer, 1 part of concentrated hydrochloric acid, propylene glycol ester terephthalate-valeric acid fourth two
10 parts of alcohol, 2 parts of stalk ashes, 1 part of poly- nonyl dianhydride, 2 parts of hydrogenated rosin, antioxidant RD1 parts, 2 parts of crosslinked starch, 1 part of carbon black,
3 parts of 2 parts of sodium citrate and glass fibre.
Embodiment 2
A kind of anlistatig high polymer material, is made up of the component of following mass parts：Molecular weight is the super of 500-600 ten thousand
90 parts of High molecular weight polyethylene, gather fragrant 5 parts of alkali, 6 parts of plasticizer, 3 parts of concentrated hydrochloric acid, propylene glycol ester terephthalate-valeric acid fourth two
12 parts of alcohol, 5 parts of stalk ashes, 3 parts of poly- nonyl dianhydride, 4 parts of hydrogenated rosin, antioxidant RD4 parts, 4 parts of crosslinked starch, 3 parts of carbon black,
5 parts of 5 parts of sodium citrate and glass fibre.
Embodiment 3
A kind of anlistatig high polymer material, is made up of the component of following mass parts：Molecular weight is the super of 500-600 ten thousand
85 parts of High molecular weight polyethylene, gather fragrant 3 parts of alkali, 4 parts of plasticizer, 2 parts of concentrated hydrochloric acid, propylene glycol ester terephthalate-valeric acid fourth two
11 parts of alcohol, 4 parts of stalk ashes, 3 parts of poly- nonyl dianhydride, 3 parts of hydrogenated rosin, antioxidant RD3 parts, 2 parts of crosslinked starch, 2 parts of carbon black,
4 parts of 4 parts of sodium citrate and glass fibre.
Using ultra-high molecular weight polyethylene as base-material, the high polymer material produced has the high polymer material of the present invention
Have resistant to elevated temperatures performance, meanwhile, the present invention in the addition of glass fibre, using glass fibre the insulating properties possessed in itself and
Tensile strength is big, improves the antistatic and mechanical performance of high polymer material.
It is described above, it is merely illustrative of the technical solution of the present invention and unrestricted, those of ordinary skill in the art are to this hair
The other modifications or equivalent substitution that bright technical scheme is made, without departing from the spirit and scope of technical solution of the present invention,
It all should cover among scope of the presently claimed invention.
Claims (3)
- A kind of 1. anlistatig high polymer material, it is characterised in that：It is made up of the component of following mass parts：Molecular weight is 500- 6000000 ultra-high molecular weight polyethylene 80-90 parts, gather fragrant alkali 3-5 parts, plasticizer 3-6 parts, concentrated hydrochloric acid 1-3 parts, terephthalic acid (TPA) Propylene glycol ester-valeric acid butanediol 10-12 parts, stalk ashes 2-5 parts, poly- nonyl dianhydride 1-3 parts, hydrogenated rosin 2-4 parts, antioxidant RD 1-4 parts, crosslinked starch 2-4 parts, carbon black 1-3 parts, sodium citrate 2-5 parts and glass fibre 3-5 parts.
- A kind of 2. anlistatig high polymer material according to claim 1, it is characterised in that：By the component of following mass parts Composition：Molecular weight is 500-600 ten thousand ultra-high molecular weight polyethylene 82-88 parts, poly- fragrant alkali 3-4 parts, plasticizer 4-5 parts, dense salt Sour 1-2 parts, propylene glycol ester terephthalate-valeric acid butanediol 10-11 parts, stalk ashes 3-4 parts, poly- nonyl dianhydride 1-3 parts, hydrogenation Rosin 2-3 parts, antioxidant RD 2-3 parts, crosslinked starch 2-3 parts, carbon black 2-3 parts, sodium citrate 3-4 parts and glass fibre 3-4 Part.
- A kind of 3. anlistatig high polymer material according to claim 1, it is characterised in that：By the component of following mass parts Composition：85 parts of ultra-high molecular weight polyethylene that molecular weight is 500-600 ten thousand, gather fragrant 3 parts of alkali, be 4 parts of plasticizer, 2 parts of concentrated hydrochloric acid, right Benzene dicarboxylic acid trimethylene glycol ester -11 parts of valeric acid butanediol, 4 parts of stalk ashes, 3 parts of poly- nonyl dianhydride, 3 parts of hydrogenated rosin, antioxidant 4 parts of 3 parts of RD, 2 parts of crosslinked starch, 2 parts of carbon black, 4 parts of sodium citrate and glass fibre.