CN107511307A - Novel aqueous system coating and its construction technology on a kind of steel plate - Google Patents
Novel aqueous system coating and its construction technology on a kind of steel plate Download PDFInfo
- Publication number
- CN107511307A CN107511307A CN201710839365.7A CN201710839365A CN107511307A CN 107511307 A CN107511307 A CN 107511307A CN 201710839365 A CN201710839365 A CN 201710839365A CN 107511307 A CN107511307 A CN 107511307A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- adhesive layer
- layer
- interface adhesive
- laying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the novel aqueous system coating on a kind of steel plate and its construction technology, it includes steel plate, the surface of the steel plate scribbles interface adhesive layer, the surface of the interface adhesive layer scribbles glued resistance to compression layer, the surface of the glued resistance to compression layer scribbles antislip colour surface layer, antislip colour surface layer can reach specious simple and elegant, mark substantially, in addition to construction technology：Steel plate processing, the laying of interface adhesive layer, skid resistant surface laying, the laying of chromogen bonded polymer finishing coat, antiultraviolet topping laying；By above-mentioned technical scheme, the present invention has wear-resisting, pressure-resistant, impact resistance, service life length；With anti-skidding, steady, shockproof effect, make bicycle running comfortable, so as to reduce vehicle traveling noise, improve driving condition；Dabbled with reduction and water smoke, increase rainy day travel safety；It is good with resistance to low temperature, UV resistant irradiation, and resistant to thermal aging, round-the-clock use.
Description
Technical field
Mat formation coating structure the present invention relates to one kind, and in particular to a kind of novel aqueous system coating on steel plate and its apply
Work technique.
Background technology
With the construction of urban road, urban road also individually builds elevated self track at present, mainly passes through steel box-girder
Build, coating is then carried out on the steel plate of steel case top surface, the coating is without wear-resisting, pressure-resistant, impact resistance, non-skid property
Difference, potential safety hazard be present to automatic vehicle traveling.
The content of the invention
In order to solve the weak point present in background technology, it is an object of the invention to provide a kind of anti-corrosion, wear-resisting, resistance to
Thick novel aqueous system coating.
The present invention is achieved through the following technical solutions：A kind of novel aqueous system coating on steel plate, including steel plate, it is described
The surface of steel plate scribbles interface adhesive layer, and the surface of the interface adhesive layer scribbles glued resistance to compression layer, the glued resistance to compression layer
Surface scribbles skid resistant surface, and the surface of the skid resistant surface scribbles antiultraviolet surface layer.
Further, skid resistant surface of the present invention uses colour-wash coating.
The construction technology of novel aqueous system coating on a kind of steel plate of the present invention, comprises the following steps：
（1）Steel plate processing：First steel plate is rinsed well with giant, surface of steel plate rusty scale, all polishing cleans up；
（2）Interface adhesive layer laying：From U.S. line paper by step（1）The surrounding at steel plate edge covers, solvent-free gluing primary coat
AB agent is with 5：1 ratio stirs material, and a people intersects uniform roller coating with trowel on steel plate anyhow, another people's drift bolt footwear
The 20 uniform spreadings of mesh quartz sand are pasted into layer surface in interface, interface adhesive layer firm time is 6-8 hours, hardening temperature 15
More than DEG C；After unnecessary quartz sand being cleaned after the hardening of interface adhesive layer, then by solvent-free gluing primary coat AB agent with 5:1 ratio
Material is continued after stirring, intersects uniform roller coating anyhow with roller on priming coat, the interface adhesive layer post-curing time
For 6-8 hours, hardening temperature is more than 15 DEG C；Remarks：Atmospheric humidity is more than 70%, below 5 DEG C of temperature, avoids constructing.
(3) glued resistance to compression layer laying：By brilliant steel resin mortar true qualities dry powder and emulsion with 5:1 ratio stirs, will
The raw material being stirred uniformly is laid on priming coat with 5.5mm aluminium alloys guiding ruler, and its firm time is 8 hours, and hardening temperature is
More than 15 DEG C；
(4) skid resistant surface is laid：By colored brilliant steel resin material with 4:1 ratio is stirred to bucket bottom deposit-free, a people and will stirred
The material mixed uniformly is paved uniformly with 5mm trowels；Another people's drift bolt footwear are by the uniform spreading of the special mesh of quartz sand 40 in brilliant steel tree
On fat wearing layer, next stage construction can be carried out after unnecessary quartz sand is cleaned up after to be hardened, its firm time is 8 small
When, hardening temperature is more than 15 DEG C；
(5) chromogen bonded polymer finishing coat is laid：Chromogen bonded polymer covering material roller is intersected into uniform roller coating in brilliant steel anyhow
On resin wear-resisting antiskid face；
(6) antiultraviolet topping laying：The material of clear, colorless is mixed evenly, using intersecting uniform rolling anyhow with roller
It is applied on chromogen bonded polymer overlay coating.
The present invention compared with prior art, has advantages below and beneficial effect：
1st, the present invention has wear-resisting, pressure-resistant, impact resistance, service life length.
2nd, the present invention has anti-skidding, steady, shockproof effect, makes bicycle running comfortable, so as to reduce vehicle traveling
Noise, improve driving condition.
3rd, there is the present invention reduction to dabble and water smoke, increase rainy day travel safety.
4th, the present invention has resistance to low temperature good, and UV resistant irradiates, and resistant to thermal aging, round-the-clock use.
5th, it is of the invention using colored skid resistant surface, there is simple and elegant, mark attractive in appearance substantially.
Brief description of the drawings
The detailed description made by reading with reference to the following drawings to non-limiting example, other features of the invention,
Objects and advantages will become apparent：
Fig. 1 is the structural representation of the embodiment of the present invention 1.
Embodiment
Embodiments of the invention are described below in detail, the example of the embodiment is shown in the drawings, wherein from beginning to end
Same or similar label represents same or similar element or the element with same or like function.Below with reference to attached
The embodiment of figure description is exemplary, is only used for explaining the present invention, and is not considered as limiting the invention.
In the description of the invention, it is to be understood that term " " center ", " longitudinal direction ", " transverse direction ", " on ", " under ",
The orientation or position relationship of the instruction such as "front", "rear", "left", "right", " vertical ", " level ", " top ", " bottom ", " interior ", " outer " are
Based on orientation shown in the drawings or position relationship, it is for only for ease of the description present invention and simplifies description, rather than instruction or dark
Show that the device of meaning or element there must be specific orientation, with specific azimuth configuration and operation, thus it is it is not intended that right
The limitation of the present invention.In the description of the invention, unless otherwise indicated, " multiple " are meant that two or more.
In the description of the invention, it is necessary to illustrate, unless otherwise clearly defined and limited, term " installation ", " phase
Even ", " connection " should be interpreted broadly, for example, it may be being fixedly connected or being detachably connected, or be integrally connected；Can
To be mechanical connection or electrical connection；Can also be joined directly together or be indirectly connected by intermediary, can
To be the connection of two element internals.For the ordinary skill in the art, above-mentioned term can be understood with concrete condition
Concrete meaning in the present invention.
Novel aqueous system coating on a kind of steel plate of the present embodiment, including steel plate 1, the surface of the steel plate 1 scribble
Interface adhesive layer 2, the surface of the interface adhesive layer 2 scribble glued resistance to compression layer 3, and the surface of the glued resistance to compression layer 3 scribbles anti-
Sliding surface layer 4, skid resistant surface use colour-wash coating, and the surface of the skid resistant surface scribbles antiultraviolet surface layer, has appearance
More attractive simple and elegant, mark is substantially.
A kind of construction technology of novel aqueous system coating on steel plate, comprises the following steps：
（1）Steel plate processing：First steel plate is rinsed well with giant, surface of steel plate rusty scale, all polishing cleans up；
（2）Interface adhesive layer laying：From U.S. line paper by step（1）The surrounding at steel plate edge covers, solvent-free gluing primary coat
AB agent is with 5：1 ratio stirs material, and a people intersects uniform roller coating with trowel on steel plate anyhow, another people's drift bolt footwear
The 20 uniform spreadings of mesh quartz sand are pasted into layer surface in interface, interface adhesive layer firm time is 6-8 hours, hardening temperature 15
More than DEG C；After unnecessary quartz sand being cleaned after the hardening of interface adhesive layer, then by solvent-free gluing primary coat AB agent with 5:1 ratio
Material is continued after stirring, intersects uniform roller coating anyhow with roller on priming coat, the interface adhesive layer post-curing time
For 6-8 hours, hardening temperature is more than 15 DEG C；Remarks：Atmospheric humidity is more than 70%, below 5 DEG C of temperature, avoids constructing.
(3) glued resistance to compression layer laying：By brilliant steel resin mortar true qualities dry powder and emulsion with 5:1 ratio stirs, will
The raw material being stirred uniformly is laid on priming coat with 5.5mm aluminium alloys guiding ruler, and its firm time is 8 hours, and hardening temperature is
More than 15 DEG C；
(4) skid resistant surface is laid：By colored brilliant steel resin material with 4:1 ratio is stirred to bucket bottom deposit-free, a people and will stirred
The material mixed uniformly is paved uniformly with 5mm trowels；Another people's drift bolt footwear are by the uniform spreading of the special mesh of quartz sand 40 in brilliant steel tree
On fat wearing layer, next stage construction can be carried out after unnecessary quartz sand is cleaned up after to be hardened, its firm time is 8 small
When, hardening temperature is more than 15 DEG C；
(5) chromogen bonded polymer finishing coat is laid：Chromogen bonded polymer covering material roller is intersected into uniform roller coating in brilliant steel anyhow
On resin wear-resisting antiskid face；
(6) antiultraviolet topping laying：The material of clear, colorless is mixed evenly, using intersecting uniform rolling anyhow with roller
It is applied on chromogen bonded polymer overlay coating.
Although an embodiment of the present invention has been shown and described, it will be understood by those skilled in the art that：Not
A variety of change, modification, replacement and modification can be carried out to these embodiments by departing under the principle and objective of the present invention, of the invention
Scope is limited by claim and its equivalent.
Claims (4)
1. the novel aqueous system coating on a kind of steel plate, including steel plate, it is characterised in that：The surface of the steel plate scribbles interface
Adhesive layer, the surface of the interface adhesive layer scribble glued resistance to compression layer, and the surface of the glued resistance to compression layer scribbles skid resistant surface, institute
The surface for stating skid resistant surface scribbles antiultraviolet surface layer.
2. the novel aqueous system coating on a kind of steel plate according to claim 1, it is characterised in that：The skid resistant surface
Using colour-wash coating.
3. the construction technology of the novel aqueous system coating on a kind of steel plate according to claim 1, comprises the following steps：
（1）Steel plate processing：First steel plate is rinsed well with giant, surface of steel plate rusty scale, all polishing cleans up；
（2）Interface adhesive layer laying：From U.S. line paper by step（1）The surrounding at steel plate edge covers, solvent-free gluing primary coat
AB agent is with 5：1 ratio stirs material, and a people intersects uniform roller coating with trowel on steel plate anyhow, another people's drift bolt footwear
The 20 uniform spreadings of mesh quartz sand are pasted into layer surface in interface, interface adhesive layer firm time is 6-8 hours, hardening temperature 15
More than DEG C；After unnecessary quartz sand being cleaned after the hardening of interface adhesive layer, then by solvent-free gluing primary coat AB agent with 5:1 ratio
Material is continued after stirring, intersects uniform roller coating anyhow with roller on priming coat, the interface adhesive layer post-curing time
For 6-8 hours, hardening temperature is more than 15 DEG C；Remarks：Atmospheric humidity is more than 70%, below 5 DEG C of temperature, avoids constructing.
4. (3) glued resistance to compression layer laying：By brilliant steel resin mortar true qualities dry powder and emulsion with 5:1 ratio stirs, and will stir
The raw material mixed uniformly is laid on priming coat with 5.5mm aluminium alloys guiding ruler, and its firm time is 8 hours, hardening temperature 15
More than DEG C；
(4) skid resistant surface is laid：By colored brilliant steel resin material with 4:1 ratio is stirred to bucket bottom deposit-free, a people and will stirred
The material mixed uniformly is paved uniformly with 5mm trowels；Another people's drift bolt footwear are by the uniform spreading of the special mesh of quartz sand 40 in brilliant steel tree
On fat wearing layer, next stage construction can be carried out after unnecessary quartz sand is cleaned up after to be hardened, its firm time is 8 small
When, hardening temperature is more than 15 DEG C；
(5) chromogen bonded polymer finishing coat is laid：Chromogen bonded polymer covering material roller is intersected into uniform roller coating in brilliant steel anyhow
On resin wear-resisting antiskid face；
(6) antiultraviolet topping laying：The material of clear, colorless is mixed evenly, using intersecting uniform rolling anyhow with roller
It is applied on chromogen bonded polymer overlay coating.