CN107504861A - A kind of automobile-used tungsten filament heating temperature control and the bulletproof glass of signal shielding - Google Patents
A kind of automobile-used tungsten filament heating temperature control and the bulletproof glass of signal shielding Download PDFInfo
- Publication number
- CN107504861A CN107504861A CN201710880669.8A CN201710880669A CN107504861A CN 107504861 A CN107504861 A CN 107504861A CN 201710880669 A CN201710880669 A CN 201710880669A CN 107504861 A CN107504861 A CN 107504861A
- Authority
- CN
- China
- Prior art keywords
- film
- glassy layer
- temperature control
- shellproof
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile-used tungsten filament heating temperature control and the bulletproof glass of signal shielding, include glassy layer, shellproof film and heating cortina, wherein：Also include electromagnetic shielding film, the glassy layer and shellproof film are respectively equipped with four layers, the bulletproof glass is made up of the first glassy layer, heating cortina, the second glassy layer, the first shellproof film, the 3rd glassy layer, the second shellproof film, electromagnetic shielding film, the 3rd shellproof film, the 4th glassy layer, the 4th shellproof film, PC layers successively, and gross thickness is 22 53mm.The present invention has temperature control, shellproof, signal shielding function, suitable for national defence, the police vehicle glass of army, meets national strategy needs, national defence relevant unit to the defrosting-defogging and signal shielding function and safe class of strategy automobile on duty.
Description
Technical field
The present invention relates to the police vehicle glass of army, the shellproof glass of particularly a kind of automobile-used tungsten filament heating temperature control and signal shielding
Glass.
Background technology
As the progress of science and technology and national strategy need, national defence relevant unit is to the function of strategy automobile on duty and safety etc.
The requirement more and more higher of level.Bulletproof glass on the market is difficult to meet the automobile for using the training on duty of army and police relevant unit strategy
The specific requirement of glass, common bulletproof glass do not have temperature control system to ensure the defrosting-defogging requirement under the conditions of extremely trembling with fear,
The influence that wartime hostile forces are disturbed in-car or indoor electronic equipment using electronics tactics, and shellproof glass can not be ensured
Glass grade is difficult to reach 53 general 100 meters of requirement of shelter.
The content of the invention
In order to overcome the disadvantages mentioned above of prior art, it is an object of the invention to provide with function of temperature control, signal shielding work(
Can be with a kind of automobile-used tungsten filament heating temperature control of bulletproof function and the bulletproof glass of signal shielding.
The technical solution adopted for the present invention to solve the technical problems is：A kind of automobile-used tungsten filament heating temperature control and signal shielding
Bulletproof glass, include glassy layer, shellproof film and heating cortina, wherein：Also include electromagnetic shielding film, the glassy layer and
Shellproof film is respectively equipped with four layers, and the bulletproof glass is successively by the first glassy layer, heating cortina, the second glassy layer, first shellproof
Film, the 3rd glassy layer, the second shellproof film, electromagnetic shielding film, the 3rd shellproof film, the 4th glassy layer, the 4th shellproof film, PC layer groups
Into gross thickness 22-53mm.
As a further improvement on the present invention：First glassy layer, the second glassy layer, the 3rd glassy layer and the 4th glass
The thickness of layer is respectively 4mm, 4mm, 10mm and 10mm, and the first shellproof film, the second shellproof film, the 3rd shellproof film and the 4th are anti-
The thickness for playing film is respectively 0.76mm, 0.76mm, 0.76mm and 1.25mm.
As a further improvement on the present invention：The PC layers are thickness 3mm polycarbonate plate.
As a further improvement on the present invention：It is uniformly distributed in the heating cortina provided with some tungsten filaments, the tungsten filament is equal
Temperature control circuit is connected, one jiao of the bulletproof glass is additionally provided with temperature control detection probe, the temperature control detection probe and temperature control circuit
Connection.
As a further improvement on the present invention：The electromagnetic shielding film is successively by transparent protective film, insulating barrier, metal foil
Film layer, Anisotropically conductive glue-line and transparent mould release membrance composition, the shield effectiveness of the electromagnetic shielding film are more than 60db.
A kind of temperature control of automobile-used tungsten filament heating and the bulletproof glass preparation method of signal shielding, it is characterized in that：The making
Method comprises the following steps：
1）Prepare four groups of glassy layers, and glassy layer is pre-processed；
2）The glassy layer completed, shellproof film, heating cortina, electromagnetic shielding film, PC layers will be pre-processed and carry out organic doubling accordingly
Close piece；
3）By press from both sides composition after the completion of glue pellet temperature be 100 to 120 DEG C and vacuum be -0.08 to -0.1MPa it is true
Precompressed is vacuumized in empty stove；
4）Composition after the completion of precompressed is put into autoclave, is heated, pressurizeed to overall by autoclave, extrude gap it
Between gas, while organic is together between making glassy layer, shellproof film, heating cortina, electromagnetic shielding film, PC layers adjacent；
5）One jiao of perforate in the glassy layer bonded with heating cortina, bore dia 10-20mm, and temperature control inspection is put into hole
Probing head, it is ensured that the contact surface of temperature control detection probe is bonded completely with the bottom hole face of glassy layer, is fixed using glass cement；
6）Every comprehensive function test is carried out respectively.
As a further improvement on the present invention：The step 1）In pretreatment comprise the following steps：
（1）Institute is accurately cut on automatic gas cutting machine by size shape to 4mm, 4mm, 10mm, 10mm sheet glass respectively
The glassy layers of 4mm first, the glassy layers of 4mm second, the glassy layers of 10mm the 3rd, the glassy layers of 10mm the 4th needed；
（2）The divided glass layer completed to cutting edging on irregular edge grinder；
（3）Silk-screen printing, the black surround or flower point on printed glass layer periphery are carried out to the divided glass layer that edging is completed；
As a further improvement on the present invention：The step 2）In organic folder glue pellet comprise the following steps：
（1）By the clear powder of four groups of glassy layers, cleaning, cleaning；
（2）Glassy layer and the cortina that generates heat, shellproof are carried out in temperature is 18 DEG C -25 DEG C, relative humidity is 18-35% dust-free workshop
Organic folder glue pellet of film.
As a further improvement on the present invention：In organic folder glue pellet（2）Include in step：Pass through production line
First glassy layer is put into and closes piece station, spreads heating cortina, heating cortina, which extends, electric power connection line, for connecting temperature control
Circuit, obtain the composition of the first glassy layer and the cortina that generates heat；Similarly, continue lay the second glassy layer, and in kind according to
The first shellproof film of secondary laying, the 3rd glassy layer, the second shellproof film, electromagnetic shielding film, the 3rd shellproof film, the 4th glassy layer, the 4th
Shellproof film and PC layer.
A kind of temperature control of automobile-used tungsten filament heating and the bulletproof glass of signal shielding, wherein：The bulletproof glass is police in army
Application on vehicle glass.The bulletproof glass is particularly applicable in army and police relevant unit, strategy training on duty uses, and ensures in pole
In-car or indoor defrosting-defogging under the conditions of cold, avoid wartime hostile forces using electronics tactics to in-car or indoor electronic equipment
Disturbed.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention has temperature control, shellproof, signal shielding function, suitable for the police vehicle glass of army, meets national strategy needs, state
Function and safe class of the anti-relevant unit to strategy automobile on duty.
The present invention realizes the thermostatic control to bulletproof glass using in Miniature temperature control detection probe implantation bulletproof glass,
Extremely cold environment is issued to the functional requirement of defrosting-defogging, while avoids wartime hostile forces from being set using electronics tactics to in-car electronics
Standby to be disturbed, bulletproof glass reaches the requirement of shelter of 53 common 100 meters of bullets.
Brief description of the drawings
Fig. 1 is the structural representation of the present invention.
Fig. 2 is the structural representation of the present invention.
Embodiment
In conjunction with brief description of the drawings, the present invention is further described with embodiment：
With reference to figure 1 and Fig. 2, the bulletproof glass of a kind of automobile-used tungsten filament heating temperature control and signal shielding, include glassy layer, shellproof film
With heating cortina 1, wherein：Also include electromagnetic shielding film 2, the glassy layer 3 and shellproof film 4 are respectively equipped with four layers, described anti-
Play glass successively by the first glassy layer, heating cortina, the second glassy layer, the first shellproof film, the 3rd glassy layer, the second shellproof film,
Electromagnetic shielding film, the 3rd shellproof film, the 4th glassy layer, the 4th shellproof film, PC layers composition 5.
First glassy layer, the second glassy layer, the thickness of the 3rd glassy layer and the 4th glassy layer be respectively 4mm, 4mm,
10mm and 10mm, the first shellproof film, the second shellproof film, the thickness of the 3rd shellproof film and the 4th shellproof film are respectively
0.76mm, 0.76mm, 0.76mm and 1.25mm.
The PC layers are thickness 3mm polycarbonate plate.
It is uniformly distributed in the heating cortina 1 provided with some tungsten filaments 11, the copper contact pin of the tungsten filament and heating wire film edge
12 connections, the copper contact pin 12, which is extended, electric power connection line 13, and the electric power connection line is connected with temperature control circuit, described shellproof
One jiao of glass is additionally provided with temperature control detection probe 14, and the temperature control detection probe is connected with temperature control circuit.The temperature control detection is visited
Head is used for the real time temperature for obtaining bulletproof glass, controls temperature by temperature control circuit, the temperature control circuit is visited according to temperature detection
The real time temperature that head obtains, the tungsten filament heating of driving heating cortina, makes bulletproof glass temperature maintain 25 DEG C, reaches bulletproof glass
The effect of defrosting-defogging, can under subzero -45 DEG C of extremely cold environment bulletproof glass normal operating conditions.
The electromagnetic shielding film is successively by transparent protective film, insulating barrier, metal film layer, Anisotropically conductive glue-line and transparent
Mould release membrance forms, and the shield effectiveness of the electromagnetic shielding film is more than 60db.The electromagnetic shielding film can effectively block radio wave,
The radiation of the various Eavesdropping conventional frequencies such as infrared, ultraviolet, so as to prevent the influence of tapped signal and electromagnetic interference, simultaneously
The leakage of electromagnetic signal can be prevented or reduce, suitable for the form of army's police vehicle.
A kind of temperature control of automobile-used tungsten filament heating and the bulletproof glass preparation method of signal shielding, it is characterized in that：The making
Method comprises the following steps：
1）Prepare four groups of glassy layers, and glassy layer is pre-processed；
1.1）Institute is accurately cut on automatic gas cutting machine by size shape to 4mm, 4mm, 10mm, 10mm sheet glass respectively
The glassy layers of 4mm first, the glassy layers of 4mm second, the glassy layers of 10mm the 3rd, the glassy layers of 10mm the 4th needed；
1.2）The divided glass layer completed to cutting edging on irregular edge grinder, grinds off sharp seamed edge, can eliminate work
The edge micro-crack that side leaves is broken in sequence cutting, while avoids sharp corners from hurting operative employee；
1.3）Silk-screen printing, black surround or the flower point or related special on printed glass layer periphery are carried out to the divided glass layer that edging is completed
Property；
2）The glassy layer completed, shellproof film, heating cortina, electromagnetic shielding film, PC layers will be pre-processed and carry out organic doubling accordingly
Close piece；
2.1）By the clear powder of four groups of glassy layers, cleaning, cleaning；
2.2）Glassy layer and the cortina that generates heat, shellproof are carried out in temperature is 18 DEG C -25 DEG C, relative humidity is 18-35% dust-free workshop
Organic folder glue pellet of film；
The first glassy layer is put into by production line and closes piece station, spreads heating cortina, heating wire film edge press-in copper contact pin, institute
Stating copper contact pin and extending has electric power connection line, for connecting temperature control circuit, obtains the composition of the first glassy layer and the cortina that generates heat；
Similarly, continue to lay the second glassy layer, and in kind the first shellproof film of laying, the 3rd glassy layer, second prevent successively
Play film, electromagnetic shielding film, the 3rd shellproof film, the 4th glassy layer, the 4th shellproof film and PC layer；
3）By press from both sides composition after the completion of glue pellet temperature be 100 to 120 DEG C and vacuum be -0.08 to -0.1MPa it is true
Precompressed is vacuumized in empty stove, most of air between each layer is squeezed out by negative pressure；
4）Composition after the completion of precompressed is put into autoclave, is heated, pressurizeed to overall by autoclave, extrude gap it
Between gas, while organic is together between making glassy layer, shellproof film, heating cortina, electromagnetic shielding film, PC layers adjacent；
5）One jiao of perforate in the glassy layer bonded with heating cortina, bore dia 10-20mm, and temperature control inspection is put into hole
Probing head, it is ensured that the contact surface of temperature control detection probe is bonded completely with the bottom hole face of glassy layer, is fixed using glass cement；Temperature control is examined
Probing head obtains the real time temperature of bulletproof glass, and heating cortina is heated by temperature control circuit, ensures that bulletproof glass makes
Temperature constant state is maintained during.
6）Every comprehensive function test is carried out respectively.
In summary, after one of ordinary skill in the art reads file of the present invention, technique according to the invention scheme and
Technical concept makes other various corresponding conversion schemes without creative mental labour, belongs to the model that the present invention is protected
Enclose.
Claims (9)
1. a kind of automobile-used tungsten filament heating temperature control and the bulletproof glass of signal shielding, include glassy layer, shellproof film and heating cortina,
It is characterized in that：Also include electromagnetic shielding film, the glassy layer and shellproof film are respectively equipped with four layers, the bulletproof glass successively by
First glassy layer, heating cortina, the second glassy layer, the first shellproof film, the 3rd glassy layer, the second shellproof film, electromagnetic shielding film, the
Three shellproof films, the 4th glassy layer, the 4th shellproof film, PC layers composition, gross thickness 22-53mm.
2. a kind of automobile-used tungsten filament heating temperature control according to claim 1 and the bulletproof glass of signal shielding, it is characterized in that：Institute
The thickness for stating the first glassy layer, the second glassy layer, the 3rd glassy layer and the 4th glassy layer is respectively 4mm, 4mm, 10mm and 10mm,
The first shellproof film, the second shellproof film, the thickness of the 3rd shellproof film and the 4th shellproof film be respectively 0.76mm, 0.76mm,
0.76mm and 1.25mm.
3. a kind of automobile-used tungsten filament heating temperature control according to claim 1 and the bulletproof glass of signal shielding, it is characterized in that：Institute
State and be uniformly distributed in heating cortina provided with some tungsten filaments, the tungsten filament is all connected with temperature control circuit, and one jiao of the bulletproof glass is also
Provided with temperature control detection probe, the temperature control detection probe is connected with temperature control circuit.
4. a kind of automobile-used tungsten filament heating temperature control according to claim 1 and the bulletproof glass of signal shielding, it is characterized in that：Institute
Electromagnetic shielding film is stated successively by transparent protective film, insulating barrier, metal film layer, Anisotropically conductive glue-line and transparent mould release membrance group
Into the shield effectiveness of the electromagnetic shielding film is more than 60db.
5. a kind of temperature control of automobile-used tungsten filament heating and the bulletproof glass preparation method of signal shielding, it is characterized in that：The making side
Method comprises the following steps：
1）Prepare four groups of glassy layers, and glassy layer is pre-processed；
2）The glassy layer completed, shellproof film, heating cortina, electromagnetic shielding film, PC layers will be pre-processed and carry out organic doubling accordingly
Close piece；
3）By press from both sides composition after the completion of glue pellet temperature be 100 to 120 DEG C and vacuum be -0.08 to -0.1MPa it is true
Precompressed is vacuumized in empty stove；
4）Composition after the completion of precompressed is put into autoclave, is heated, pressurizeed to overall by autoclave, extrude gap it
Between gas, while organic is together between making glassy layer, shellproof film, heating cortina, electromagnetic shielding film, PC layers adjacent；
5）One jiao of perforate in the glassy layer bonded with heating cortina, bore dia 10-20mm, and temperature control inspection is put into hole
Probing head, it is ensured that the contact surface of temperature control detection probe is bonded completely with the bottom hole face of glassy layer, is fixed using glass cement；
6）Every comprehensive function test is carried out respectively.
6. a kind of temperature control of automobile-used tungsten filament heating according to claim 5 and the bulletproof glass preparation method of signal shielding,
It is characterized in that：The step 1）In pretreatment comprise the following steps：
（1）Institute is accurately cut on automatic gas cutting machine by size shape to 4mm, 4mm, 10mm, 10mm sheet glass respectively
The glassy layers of 4mm first, the glassy layers of 4mm second, the glassy layers of 10mm the 3rd, the glassy layers of 10mm the 4th needed；
（2）The divided glass layer completed to cutting edging on irregular edge grinder；
（3）Silk-screen printing, the black surround or flower point on printed glass layer periphery are carried out to the divided glass layer that edging is completed.
7. a kind of temperature control of automobile-used tungsten filament heating according to claim 5 and the bulletproof glass preparation method of signal shielding,
It is characterized in that：The step 2）In organic folder glue pellet comprise the following steps：
（1）By the clear powder of four groups of glassy layers, cleaning, cleaning；
（2）Glassy layer and the cortina that generates heat, shellproof are carried out in temperature is 18 DEG C -25 DEG C, relative humidity is 18-35% dust-free workshop
Organic folder glue pellet of film.
8. a kind of temperature control of automobile-used tungsten filament heating according to claim 7 and the bulletproof glass preparation method of signal shielding,
It is characterized in that：In organic folder glue pellet（2）Include in step：The first glassy layer is put into by production line and closes piece work
Position, spreads heating cortina, and heating cortina, which extends, electric power connection line, for connecting temperature control circuit, obtain the first glassy layer with
The composition of heating cortina；Similarly, continue to lay the second glassy layer, and in kind lay the first shellproof film, the 3rd successively
Glassy layer, the second shellproof film, electromagnetic shielding film, the 3rd shellproof film, the 4th glassy layer, the 4th shellproof film and PC layer.
9. a kind of temperature control of automobile-used tungsten filament heating and the bulletproof glass of signal shielding, it is characterized in that：The bulletproof glass is in army and police
With the application on vehicle glass.