CN107501964A - It is a kind of to determine thickness meltable composition - Google Patents
It is a kind of to determine thickness meltable composition Download PDFInfo
- Publication number
- CN107501964A CN107501964A CN201710799535.3A CN201710799535A CN107501964A CN 107501964 A CN107501964 A CN 107501964A CN 201710799535 A CN201710799535 A CN 201710799535A CN 107501964 A CN107501964 A CN 107501964A
- Authority
- CN
- China
- Prior art keywords
- resin
- wax
- parts
- fixed thickness
- meltable composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fixed thickness meltable composition, including thermoplastic elastomer (TPE), wax and resin, the fixed thickness is with the content of each component of meltable composition：In terms of mass parts, 0.1 20 parts of thermoplastic elastomer (TPE), 20 85 parts of wax, 1 50 parts of resin, wherein the fusing point of the wax is 45 110 DEG C.Through the above way, the fixed thickness meltable composition of the present invention, with low melting point, runny advantage, it can be applied during the priming by vacuum multiple glazing steel with high-barrier characteristic is produced, hollow layer thickness can be controlled, realizes the production of double glazing steel construction thickness control and multilayer hollow structure.
Description
Technical field
The present invention relates to a kind of composition, determines thickness meltable composition more particularly to a kind of.
Background technology
Oil tank is the container for storing crude oil or other oil products, can be used in oil plant, gas station, oil field, oil depot with
And in other industry.The existing most of oil tank for being embedded in underground and transport oil tank are common steel oil tank, and it lacks anti-let out
Leakage technology, leakage easily occurs and causes great potential safety hazard.The original buried tank of national industry requirement and related fortune at present
The mandatory transformation of oil transportation tank, it is necessary to can effectively solve the problems, such as anti-leak, strict implement SH/3177-2015 and SH/3178-2015
Standard.
There is the demand changed or transformed in domestic substantial amounts of oil tank, then the transformation of multilayer liner tank on the basis of original
As must solve the problems, such as at present.Because construction environment is impacted, moulding process and the sandwich construction with high-barrier characteristic,
And sandwich construction low intensity is the difficult point part in industry, it is therefore desirable to priming by vacuum multilayer of the production with high-barrier characteristic
Double glazing steel.
The content of the invention
The present invention solves the technical problem of a kind of fixed thickness meltable composition is provided, there is low melting point, mobility
Excellent characteristic.
In order to solve the above technical problems, one aspect of the present invention is：A kind of fixed thick fusible combination is provided
Thing, including thermoplastic elastomer (TPE), wax and resin, the fixed thickness are with the content of each component of meltable composition：In terms of mass parts,
Thermoplastic elastomer (TPE) 0.1-20 parts, wax 20-85 parts, resin 1-50 parts, wherein the fusing point of the wax is 45-110 DEG C.
In a preferred embodiment of the present invention, the dosage of the thermoplastic elastomer (TPE) is 3-15 parts；The dosage of the wax
For 30-70 parts；The dosage of the resin is 10-45 parts.
In a preferred embodiment of the present invention, the thermoplastic elastomer (TPE) be ethylene-vinyl acetate copolymer, ethene-
Ethyl acrylate copolymer, ethylene-octene copolymer, amorphous propylene copolymer, amorphous state alpha olefin copolymer, ethylene, propylene
One or more blends in acid copolymer.
In a preferred embodiment of the present invention, the thermoplastic elastomer (TPE) is ethylene-vinyl acetate copolymer EVA or non-
Crystalline state propylene copolymer.
In a preferred embodiment of the present invention, the wax be vegetable wax, it is hydrogenated vegetable fat, hydrogenated animal grease, dynamic
Thing wax, mineral wax, pertroleum wax, synthetic wax, take one or more in dewaxing, paraffin, microwax.
In a preferred embodiment of the present invention, the wax be vegetable wax, it is hydrogenated vegetable fat, hydrogenated animal grease, dynamic
One or more in thing wax, the dropping point scope of the wax is 45-99 DEG C.
In a preferred embodiment of the present invention, the wax be pertroleum wax, synthetic wax, take dewax in one or more,
The dropping point scope of the wax is 45-110 DEG C.
In a preferred embodiment of the present invention, the resin is thermoplastic resin.
In a preferred embodiment of the present invention, the thermoplastic resin is Petropols, modified petroleum resin, polymerization pine
Perfume, modified rosin resin, C 5 petroleum resin, C 9 petroleum resin, the resin of hydrogenated carbon five, the resin of hydrogenated carbon nine, light dydrocarbon carbon nine
Copolymer resins, phenylethene modified light dydrocarbon resin, the resin of styrene modified C nine, phenolic resin, rosin modified phenolic resin, terpenes
One kind in resin, terpene phenolic resin, Terpene styron, rosin resin, modified resin, 138 resins, ester gum
It is or a variety of；Wherein described terpene resin is No. 0 color terpene resin, France and imported from America terpene resin.
In a preferred embodiment of the present invention, the fixed thickness meltable composition produces in priming by vacuum double glazing steel
Purposes in technical process.
The beneficial effects of the invention are as follows：The fixed thickness meltable composition of the present invention, there is low melting point, runny advantage,
It can be applied during the priming by vacuum multiple glazing steel with high-barrier characteristic is produced, hollow layer can be controlled
Thickness, realize the production of double glazing steel construction thickness control and multilayer hollow structure.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only the part of the embodiment of the present invention, rather than whole embodiments.It is common based on the embodiment in the present invention, this area
All other embodiment that technical staff is obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
Embodiment one：
For a kind of fixed thick meltable composition, including thermoplastic elastomer (TPE), wax and resin.It is described to determine each of thickness meltable composition
The content of component is：In terms of mass parts, 15 parts of paraffin 52#, 20 parts of 46# soft waxs, 20 parts of beeswax, 3 parts of EVA210, light dydrocarbon tree
Fat（100 DEG C of softening point）42 parts, fixed thick excellent effect.
Embodiment two：
A kind of fixed thickness meltable composition, including thermoplastic elastomer (TPE), wax and resin are provided.The fixed thickness meltable composition
The content of each component is：In terms of mass parts, 10 parts of 80# microwaxes, 10 parts of Tissuemat E, 40 parts of beeswax, 13 parts of EVA410, carbon
Nine resins（110 DEG C of softening point）27 parts, fixed thick effect is very good.
Embodiment three：
A kind of fixed thickness meltable composition, including thermoplastic elastomer (TPE), wax and resin are provided.The fixed thickness meltable composition
The content of each component is：In terms of mass parts, 5 parts of 80# microwaxes, 30 parts of 46# soft waxs, Fischer-Tropsch wax（94 DEG C of dropping point）5 parts, honeybee
20 parts of wax, 1 part of EVA210,2 parts of EVA410, light dydrocarbon resin（100 DEG C of softening point）28 parts, the resin of carbon nine（110 DEG C of softening point）
10 parts, fixed thick excellent effect.
Example IV：
A kind of fixed thickness meltable composition, including thermoplastic elastomer (TPE), wax and resin are provided.The fixed thickness meltable composition
The content of each component is：In terms of mass parts, 5 parts of 80# microwaxes, 15 parts of paraffin 52#, 1 part of 48# paraffin, Fischer-Tropsch wax（Dropping point 94
℃）9 parts, 10 parts of beeswax, 10 parts of EVA210, light dydrocarbon resin（100 DEG C of softening point）45 parts, the resin of carbon nine（110 DEG C of softening point）
5 parts, fixed thick excellent effect.
Embodiment five：
A kind of fixed thickness meltable composition, including thermoplastic elastomer (TPE), wax and resin are provided.The fixed thickness meltable composition
The content of each component is：In terms of mass parts, 5 parts of 80# microwaxes, 35 parts of 48# paraffin, 5 parts of EVA210, light dydrocarbon resin（Softening
100 DEG C of point）20 parts, the resin of carbon nine（110 DEG C of softening point）10 parts, fixed thick effect is very good.
Embodiment six：
A kind of fixed thickness meltable composition, including thermoplastic elastomer (TPE), wax and resin are provided.The fixed thickness meltable composition
The content of each component is：In terms of mass parts, 20 parts of paraffin 52#, Fischer-Tropsch wax（94 DEG C of dropping point）20 parts, 15 parts of beeswax, light dydrocarbon tree
Fat（100 DEG C of softening point）35 parts, the resin of carbon nine（11 DEG C of softening point）10 parts, fixed thick excellent effect.
The preferred embodiments of the present invention have shown and described in described above, and content and technical characterstic have revealed that as above, upper
Antioxidant, pigment and plasticizer etc. can be added in the scope of this patent on the basis of component by stating.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (10)
1. a kind of fixed thickness meltable composition, it is characterised in that including thermoplastic elastomer (TPE), wax and resin, fixed thick use can
The content of each component of molten composition is：In terms of mass parts, thermoplastic elastomer (TPE) 0.1-20 parts, wax 20-85 parts, resin 1-50
Part, wherein the fusing point of the wax is 45-110 DEG C.
2. fixed thickness meltable composition according to claim 1, it is characterised in that the dosage of the thermoplastic elastomer (TPE) is
3-15 parts；The dosage of the wax is 30-70 parts；The dosage of the resin is 10-45 parts.
3. fixed thickness meltable composition according to claim 1, it is characterised in that the thermoplastic elastomer (TPE) for ethene-
Acetate ethylene copolymer, ethylene-ethyl acrylate copolymer, ethylene-octene copolymer, amorphous propylene copolymer, amorphous state
One or more blends in alpha olefin copolymer, ethylene acrylic acid co polymer.
4. fixed thickness meltable composition according to claim 3, it is characterised in that the thermoplastic elastomer (TPE) for ethene-
Vinyl acetate copolymer eva or amorphous propylene copolymer.
5. fixed thickness meltable composition according to claim 1, it is characterised in that the wax is vegetable wax, hydrogenated vegetable
Grease, hydrogenated animal grease, animal wax, mineral wax, pertroleum wax, synthetic wax, take one kind or more in dewaxing, paraffin, microwax
Kind.
6. fixed thickness meltable composition according to claim 5, it is characterised in that the wax is vegetable wax, hydrogenated vegetable
One or more in grease, hydrogenated animal grease, animal wax, the dropping point scope of the wax is 45-99 DEG C.
7. fixed thickness meltable composition according to claim 5, it is characterised in that the wax is pertroleum wax, synthetic wax, taken
One or more in dewaxing, the dropping point scope of the wax is 45-110 DEG C.
8. fixed thickness meltable composition according to claim 1, it is characterised in that the resin is thermoplastic resin.
9. fixed thickness meltable composition according to claim 8, it is characterised in that the thermoplastic resin is oil tree
Fat, modified petroleum resin, newtrex, modified rosin resin, C 5 petroleum resin, C 9 petroleum resin, the resin of hydrogenated carbon five,
The resin of hydrogenated carbon nine, the copolymer resins of light dydrocarbon carbon nine, phenylethene modified light dydrocarbon resin, the resin of styrene modified C nine, phenolic resin,
Rosin modified phenolic resin, terpene resin, terpene phenolic resin, Terpene styron, rosin resin, modified resin, 138 trees
One or more in fat, ester gum.
10. fixed thickness meltable composition according to claim 1, it is characterised in that the fixed thickness meltable composition exists
Purposes in priming by vacuum double glazing steel production process.