CN107488014A - Rotten Marble Powder concrete permeable brick and preparation method thereof - Google Patents
Rotten Marble Powder concrete permeable brick and preparation method thereof Download PDFInfo
- Publication number
- CN107488014A CN107488014A CN201710946008.0A CN201710946008A CN107488014A CN 107488014 A CN107488014 A CN 107488014A CN 201710946008 A CN201710946008 A CN 201710946008A CN 107488014 A CN107488014 A CN 107488014A
- Authority
- CN
- China
- Prior art keywords
- permeable brick
- rotten
- marble powder
- concrete permeable
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a kind of rotten Marble Powder concrete permeable brick and preparation method thereof, it is related to building material technical field.A kind of preparation method of rotten Marble Powder concrete permeable brick, including：By vibration pressurization, shaping after rotten Marble Powder concrete stirring, rotten Marble Powder concrete permeable brick inside is provided with through hole, is conserved 2~4 days in the environment of being 70~90% in relative humidity, and the Marble Powder concrete that goes bad is 1 by mass ratio:2~3:0.1~0.5:0.1~0.5:0.5:3~4 useless powder of cement, sand, polymeric hollow microsphere, water-loss reducer, water and marble is made.This method preparation technology is simple, is adapted to large-scale production.A kind of rotten Marble Powder concrete permeable brick, is made by above-mentioned preparation method.A kind of rotten Marble Powder concrete permeable brick, the concrete permeable brick raw material are easy to get, and cost is cheap, have some strength, not easy to crack.
Description
Technical field
The present invention relates to building material technical field, and more particularly to a kind of rotten Marble Powder concrete permeable brick and its
Preparation method.
Background technology
Cement concrete since the appearance, go through by the development that experienced low-intensity, moderate strength, high intensity or even superhigh intensity
Journey, it appears that people are always happy to pursue the continuous improvement of intensity.But since nearly 40 or five ten years, concrete structure is bad because of material
Change, cause premature failure so that the accident for destroying avalanche is at home and abroad but shown in fresh repeatly, and become worse.Concrete structure
Reinforcing be all the time an awfully hot door topic, with the high speed development of national economy, living standards of the people are increasingly
Improve, people also continue to develop to the demand of building, and many existing buildings either state of appearance still uses function,
The requirement of the modern life can not be met, continue to reinforce and transform.Then reinforce and transformation process in, suitable material with
Meet use function and the safety and environmental protection requirement of construction requirement and building, be a highly important content.
The content of the invention
It is an object of the invention to provide a kind of preparation method of rotten Marble Powder concrete permeable brick, prepared by this method
Technique is simple, is adapted to large-scale production.
Another object of the present invention is to provide a kind of rotten Marble Powder concrete permeable brick, the concrete permeable brick is former
Material is easy to get, and cost is cheap, has some strength, not easy to crack.
The present invention is solved its technical problem and realized using following technical scheme.
The present invention proposes a kind of preparation method of rotten Marble Powder concrete permeable brick, including：By rotten Marble Powder
Vibration pressurization, shaping after concrete stirring, rotten Marble Powder concrete permeable brick inside are provided with through hole, are 70 in relative humidity
Conserved 2~4 days in the environment of~90%, the Marble Powder concrete that goes bad is 1 by mass ratio:2~3:0.1~0.5:0.1~
0.5:0.5:3~4 useless powder of cement, sand, polymeric hollow microsphere, water-loss reducer, water and marble is made.
The present invention proposes a kind of rotten Marble Powder concrete permeable brick, by above-mentioned rotten Marble Powder concrete permeable brick
Preparation method be made.
A kind of beneficial effect of rotten Marble Powder concrete permeable brick of the embodiment of the present invention and preparation method thereof is：
A kind of preparation method of rotten Marble Powder concrete permeable brick, it will be vibrated after rotten Marble Powder concrete stirring
Pressurization, shaping, through hole is provided with inside rotten Marble Powder concrete permeable brick, be advantageous to flowing of the water in water-permeable brick and aquatic
Animal can move about in through-holes.Because the through hole is arranged inside water-permeable brick, the structural soundness of water-permeable brick is reduced, if intensity difference
It is easily caused the fracture of water-permeable brick.Raw material system is used as using the useless powder of cement, sand, polymeric hollow microsphere, water-loss reducer, water and marble
Standby concrete, the useless powder of marble improve the mechanical strength of concrete permeable brick, reduce deformation, reduce cost, twice laid, protection
Environment.The defects of polymeric hollow microsphere can be filled up due to concrete shrinkage and produced in contraction process, water-loss reducer reduce
The contraction of concrete volume in process of setting, there is synergistic function with the marble powder that gives up, make the concrete after solidification saturating
Water brick internal structure is even closer, strengthens the intensity of concrete permeable brick, not easy to crack.This method preparation technology is simple, controllable
Property it is strong, be adapted to large-scale production.
Embodiment
, below will be in the embodiment of the present invention to make the purpose, technical scheme and advantage of the embodiment of the present invention clearer
Technical scheme be clearly and completely described.Unreceipted actual conditions person, builds according to normal condition or manufacturer in embodiment
The condition of view is carried out.Agents useful for same or the unreceipted production firm person of instrument, it is the conventional production that can be obtained by commercially available purchase
Product.
A kind of rotten Marble Powder concrete permeable brick of the embodiment of the present invention and preparation method thereof is carried out below specific
Explanation.
A kind of preparation method of rotten Marble Powder concrete permeable brick provided in an embodiment of the present invention, including：
By vibration pressurization, shaping after rotten Marble Powder concrete stirring.The present invention is using rotten Marble Powder concrete
As material is prepared, rotten Marble Powder concrete gives up including cement, sand, polymeric hollow microsphere, water-loss reducer, water and marble
Powder.
A large amount of obsolete materials can be produced in building course, as marble gives up powder, this kind of obsolete material accumulates year by year, accumulates
Take and waste soil, potential threat to environment be present, constrain the development of building trade significantly.In the present invention, using marble
Useless powder improves the mechanical strength of concrete permeable brick, reduces deformation, reduce cost, twice laid, protection ring as primary raw material
Border.
Further, in preferred embodiments of the present invention, the useless powder of marble includes rotten Marble Powder, artificial marble
At least one of dead meal and limestone rubble powder.Rotten marble is high compared to strength of artificial marble, but artificial marble
Price is low, in light weight, easy to clean.Preferably, it is 1~5 that the useless powder of marble, which includes mass ratio,:1~2:3 rotten Marble Powder,
Artificial marble dead meal and limestone rubble powder, the ratio form cause marble give up powder cost it is relatively low, while have compared with
Good intensity.
Polymeric hollow microsphere is a kind of material with specific form structure function, and its hollow parts can be gas,
Some small-molecule substances can also be encapsulated.When concrete permeable brick solidifies, certain contraction is had, polymeric hollow microsphere can
The defects of being produced to be filled up in contraction process due to contraction, strengthen reinforcement contractility.Water-loss reducer can reduce concrete
The contraction of volume in process of setting, there is synergistic function with polymeric hollow microsphere, the useless powder of marble, after making solidification
Concrete permeable brick internal structure is even closer, strengthens intensity, the impact resistance of concrete permeable brick.Preferably, in the present invention
In, polymeric hollow microsphere is hollow poly (methyl methacrylate) micro-sphere, and it is fine that water-loss reducer includes Sodium Polyacrylate, hydroxypropyl methyl
Dimension element and lignin.
Further, in preferred embodiments of the present invention, the particle diameter of polymeric hollow microsphere is 1~10 μm, is ensured micro-
Ball is evenly distributed in concrete permeable brick, can fill up small spaces, realizes enhancing intensity, impact resistance effect.
Preferably, the mass ratio of the useless powder of cement, sand, polymeric hollow microsphere, water-loss reducer, water and marble is in concrete
1:2~3:0.1~0.5:0.1~0.5:0.5:3~4.Under the ratio, the intensity and water penetration of concrete are preferable.
Rotten Marble Powder concrete permeable brick in the present invention can be layed in underwater, and the rotten Marble Powder of shaping mixes
Coagulate native water-permeable brick surface and be provided with some blind holes, lived away from home for the raw green plant growth of silted sandy soil water supply and aquatic animal.Preferably, it is blind
The aperture in hole is 5~10cm.In order to preferably adapt to underwater environment, be advantageous to the existence and growth of planktonic organism, Dali of going bad
Through hole is provided with inside rock dust concrete permeable brick.Aquatic animal can move about in through-holes, be advantageous to flowing of the water in water-permeable brick,
Strengthen water penetration.Preferably, on the premise of water-permeable brick intensity and integrality is not influenceed, the aperture of through hole is 1~3cm.Through hole
Can be linear can also bend, the present invention without limit.
Rotten Marble Powder concrete permeable brick after shaping conserves 2~4 in the environment of being 70~90% in relative humidity
My god.Due to containing water-loss reducer in concrete, curing time is reduced, shortens the production cycle.
The present invention provides a kind of rotten Marble Powder concrete permeable brick, by above-mentioned rotten Marble Powder concrete permeable brick
Preparation method be prepared.
The feature and performance of the present invention are described in further detail with reference to embodiments.
Embodiment 1
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:2:0.1:0.1:0.5:3 blended cements, sand, polymeric hollow microsphere, water-loss reducer, water and Dali
Stone gives up powder.Wherein, the mass ratio of the useless powder mesometamorphism Marble Powder of marble, artificial marble dead meal and limestone rubble powder is
1:1:3.The average grain diameter of polymeric hollow microsphere is 5 μm.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 5cm, inside is provided with the through hole that aperture is 1cm.
Conserved 4 days in the environment of being 70% in relative humidity.
Embodiment 2
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:3:0.5:0.5:0.5:4 blended cements, sand, polymeric hollow microsphere, water-loss reducer, water and Dali
Stone gives up powder.Wherein, the mass ratio of the useless powder mesometamorphism Marble Powder of marble, artificial marble dead meal and limestone rubble powder is
5:2:3.The particle diameter of polymeric hollow microsphere is 1~10 μm.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 10cm, inside is provided with the through hole that aperture is 3cm.
Conserved 2 days in the environment of being 90% in relative humidity.
Embodiment 3
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:3:0.3:0.3:0.5:3 blended cements, sand, polymeric hollow microsphere, water-loss reducer, water and Dali
Stone gives up powder.Wherein, the mass ratio of the useless powder mesometamorphism Marble Powder of marble, artificial marble dead meal and limestone rubble powder is
3:2:3.The average grain diameter of polymeric hollow microsphere is 2 μm.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 10cm, inside is provided with the through hole that aperture is 3cm.
Conserved 4 days in the environment of being 90% in relative humidity.
Embodiment 4
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:2.5:0.3:0.3:0.5:3.5 blended cements, sand, polymeric hollow microsphere, water-loss reducer, water and
Marble gives up powder.Wherein, the quality of the useless powder mesometamorphism Marble Powder of marble, artificial marble dead meal and limestone rubble powder
Than for 3:1.5:3.The average grain diameter of polymeric hollow microsphere is 8 μm.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 6cm, inside is provided with the through hole that aperture is 2cm.
Conserved 3 days in the environment of being 80% in relative humidity.
Embodiment 5
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:2.5:0.3:0.3:0.5:4 blended cements, sand, polymeric hollow microsphere, water-loss reducer, water and big
Reason stone is given up powder.Wherein, the mass ratio of the useless powder mesometamorphism Marble Powder of marble, artificial marble dead meal and limestone rubble powder
For 4:2:3.The average grain diameter of polymeric hollow microsphere is 6 μm.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 10cm, inside is provided with the through hole that aperture is 3cm.
Conserved 2 days in the environment of being 90% in relative humidity.
Comparative example 1
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:2:0.5:3 blended cements, sand, water and sand.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 5cm, inside is provided with the through hole that aperture is 1cm.
Comparative example 2
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:3:0.5:The useless powder of 3 blended cements, sand, water and marble.Wherein, the useless powder mesometamorphism of marble is big
The mass ratio for managing rock dust, artificial marble dead meal and limestone rubble powder is 2:2:3.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 10cm, inside is provided with the through hole that aperture is 1cm.
Comparative example 3
A kind of rotten Marble Powder concrete permeable brick is present embodiments provided, is mainly prepared by following methods：
It is 1 in mass ratio:3:.5:0.5:0.5:4 blended cements, sand, polymeric hollow microsphere, water-loss reducer, water and sand.In
The average grain diameter of empty polymer microballoon is 10 μm.
By vibration pressurization, shaping after mixture stirring.So that the rotten Marble Powder concrete permeable brick surface of shaping is set
There is the blind hole that some apertures are 5cm, inside is provided with the through hole that aperture is 3cm.
Conserved 3 days in the environment of being 80% in relative humidity.
Comparative example 4
This comparative example provides a kind of normal concrete water-permeable brick on the market.
Test example
Choose embodiment 1~5, the concrete permeable brick that comparative example 1~4 provides, built according to JB/T945-2005 water-permeable bricks
Material professional standard test performance, as a result such as table 1.
The performance test results of table 1
As seen from the above table, the rotten Marble Powder concrete permeable brick provided compared to comparative example 1~4, embodiment 1~5
The rotten Marble Powder concrete permeable brick mechanical property provided is more preferably.Because the rotten Marble Powder that embodiment 1~5 provides mixes
Coagulate and added polymeric hollow microsphere, water-loss reducer more in the raw material of native water-permeable brick, at the same using marble give up powder replace sand etc. its
His aggregate, therefore obtained rotten Marble Powder concrete permeable brick is than rotten Marble Powder concrete that comparative example 1~4 provides
Water-permeable brick intensity is higher, and fracture resistance is strong, and corresponding water penetration is slightly worse.Wherein, the rotten Marble Powder coagulation that embodiment 5 provides
The performance of native water-permeable brick is optimal, illustrates that raw material proportioning and preparation method are more scientific and reasonable.
In summary, a kind of preparation method of rotten Marble Powder concrete permeable brick, using cement, sand, hollow polymeric
The useless powder of thing microballoon, resin, curing agent, water and marble prepares concrete as raw material, and the useless powder of marble improves concrete permeable
The mechanical strength of brick, deformation is reduced, reduces cost, twice laid, environmental protection.Polymeric hollow microsphere can be in contraction process
In the defects of filling up due to concrete shrinkage and producing, water-loss reducer reduces the contraction of concrete volume in process of setting, and big
The useless powder of reason stone has synergistic function, makes the concrete permeable brick internal structure after solidification even closer, enhancing concrete is saturating
The intensity of water brick, it is not easy to crack.This method preparation technology is simple, and controllability is strong, is adapted to large-scale production.
Embodiments described above is part of the embodiment of the present invention, rather than whole embodiments.The reality of the present invention
The detailed description for applying example is not intended to limit the scope of claimed invention, but is merely representative of the selected implementation of the present invention
Example.Based on the embodiment in the present invention, what those of ordinary skill in the art were obtained under the premise of creative work is not made
Every other embodiment, belongs to the scope of protection of the invention.
Claims (10)
- A kind of 1. preparation method of rotten Marble Powder concrete permeable brick, it is characterised in that including：Rotten Marble Powder is mixed Vibration is pressurizeed, is molded after coagulating native stirring, is provided with through hole inside the rotten Marble Powder concrete permeable brick, is in relative humidity Conserved 2~4 days in the environment of 70~90%, the rotten Marble Powder concrete is 1 by mass ratio:2~3:0.1~0.5: 0.1~0.5:0.5:3~4 useless powder of cement, sand, polymeric hollow microsphere, water-loss reducer, water and marble is made.
- 2. the preparation method of rotten Marble Powder concrete permeable brick according to claim 1, it is characterised in that in described Empty polymer microballoon is hollow poly (methyl methacrylate) micro-sphere.
- 3. the preparation method of rotten Marble Powder concrete permeable brick according to claim 2, it is characterised in that in described The particle diameter of empty polymer microballoon is 1~10 μm.
- 4. the preparation method of rotten Marble Powder concrete permeable brick according to claim 1, it is characterised in that described big The useless powder of reason stone includes at least one of rotten Marble Powder, artificial marble dead meal and limestone rubble powder.
- 5. the preparation method of rotten Marble Powder concrete permeable brick according to claim 4, it is characterised in that described big It is 1~5 that the useless powder of reason stone, which includes mass ratio,:1~2:3 rotten Marble Powder, artificial marble dead meal and limestone rubble powder.
- 6. the preparation method of rotten Marble Powder concrete permeable brick according to claim 1, it is characterised in that the guarantor Aqua includes at least one of Sodium Polyacrylate, hydroxypropyl methyl cellulose and lignin.
- 7. the preparation method of rotten Marble Powder concrete permeable brick according to claim 1, it is characterised in that the change Matter Marble Powder concrete permeable brick surface is provided with some blind holes.
- 8. the preparation method of rotten Marble Powder concrete permeable brick according to claim 7, it is characterised in that described blind The aperture in hole is 5~10cm.
- 9. the preparation method of rotten Marble Powder concrete permeable brick according to claim 1, it is characterised in that described logical The aperture in hole is 1~3cm.
- 10. a kind of rotten Marble Powder concrete permeable brick, it is characterised in that as the change as described in any one of claim 1~9 The preparation method of matter Marble Powder concrete permeable brick is made.