CN107487094A - A kind of IML textures face-piece and its manufacture craft with sense of touch and stereoeffect - Google Patents
A kind of IML textures face-piece and its manufacture craft with sense of touch and stereoeffect Download PDFInfo
- Publication number
- CN107487094A CN107487094A CN201710923189.5A CN201710923189A CN107487094A CN 107487094 A CN107487094 A CN 107487094A CN 201710923189 A CN201710923189 A CN 201710923189A CN 107487094 A CN107487094 A CN 107487094A
- Authority
- CN
- China
- Prior art keywords
- texture
- layer
- film
- mentioned
- iml
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of IML texture face-pieces with sense of touch and stereoeffect, including film substrate and plastic basis material, the film substrate links together with plastic basis material injection, from top to bottom screen printing is brushed with either shallow texture layer, depth texture layer, primary colours layer and adhesive layer successively on the anti-surface of film substrate, from bottom to top screen printing is brushed with frosted dumb light layer and three-dimensional UV texture layers, textured pattern dislocation, the misaligned setting of the textured pattern of three-dimensional UV texture layers, the textured pattern of either shallow texture layer and depth texture layer to the front surface of film substrate successively.Compared with prior art, the IML texture face-pieces of the present invention, the sense of touch obtained by way of surface screen-printed and three-dimensional IML texture face-pieces, processing technology is simple, and need to only change the texture half tone of different texture with regard to can obtain different senses of touch, texture face-piece, conversion process is simple, quick, variation, adapts to the demand that market is changeable and quickly produces.The invention also discloses a kind of manufacture craft of the IML texture face-pieces with sense of touch and stereoeffect.
Description
Technical field
The present invention relates to the face-piece of the equipment such as communications electronics and household electrical appliance, has sense of touch and solid more particularly to one kind
The IML textures face-piece and its manufacture craft of effect.
Background technology
Existing communications electronics and home electronic panel, such as cell phone rear cover, computer rear cover, air-conditioning panel, Washing Machine Panel
It is injection-molded finished Deng, most of its, it be to use UV nothing but that this its injection-molded finished surface, which need to have the implementation of the effect of sense of touch,
Transfer printing process loses line processing on injection mould of products.Wherein, UV transfer modes need out UV to transfer texture mould, have
The defects of open time is long, costly, cause product development cycle longer；And although it is convenient to lose line processing mode, in product
Injection mold surface can make texture single if directly losing line processing, unchanged property, cause finished product single, meanwhile, table need to be changed
Face scheme works must just re-mold tool, and this undoubtedly adds product development cost；Thus, above two mode can not fit
The requirement answered market changeable and quickly produced.
In view of this, the present inventor furthers investigate to above mentioned problem, is produced then by this case.
The content of the invention
In view of this, it is an object of the invention to provide a kind of processing cost is low, finished product variation, processing technology is simple,
Process velocity is fast, adapts to that market is changeable and the IML texture face-pieces with sense of touch and stereoeffect of quick production requirement.
Low another object of the present invention is to provide a kind of processing cost, finished product variation, processing technology is simple, adds
Work speed is fast, adapts to that market is changeable and the making of the IML texture face-pieces with sense of touch and stereoeffect of quick production requirement
Technique.
In order to reach above-mentioned purpose, solution of the invention is：A kind of IML textures face with sense of touch and stereoeffect
Shell, including film substrate and plastic basis material, the film substrate links together with plastic basis material injection, with film substrate and plastics
The one side that base material is combined is anti-surface, and corresponding another side is front surface；The anti-surface of above-mentioned film substrate is from top to bottom
Screen printing is brushed with either shallow texture layer, depth texture layer, primary colours layer and adhesive layer successively, the front surface of above-mentioned film substrate by lower and
On successively screen printing be brushed with frosted dumb light layer and three-dimensional UV texture layers, it is and the textured pattern of above-mentioned three-dimensional UV texture layers, above-mentioned shallow
Spend textured pattern dislocation, the misaligned setting of the textured pattern and above-mentioned depth texture layer of texture layer.
Above-mentioned either shallow texture layer, depth texture layer, frosted dumb light layer and three-dimensional UV texture layers use silk-screen screen painting
Form, and the mesh 120T of model 300 of the silk-screen half tone of above-mentioned either shallow texture layer, the silk-screen half tone of above-mentioned depth texture layer
The mesh 140T of model 350, the mesh 100T of model 250 of the silk-screen half tone of above-mentioned frosted dumb light layer, above-mentioned three-dimensional UV texture layers
Silk-screen half tone is 100 mesh 40T.
Above-mentioned film substrate is the clear PET film that its thickness is 0.075-0.188mm or PC films.
Above-mentioned either shallow texture layer is UV thick film inks layers, and above-mentioned depth texture layer is conventional oil layer of ink, above-mentioned frosted dumb light
Layer is dumb light UV fine grinding sand oil layer of ink, and above-mentioned three-dimensional UV texture layers are that UV roughly grinds sand oil layer of ink.
A kind of manufacture craft of the IML texture face-pieces with sense of touch and stereoeffect, is achieved by the steps of：
First, film preparation
(1), pre-treatment, prepare the film substrate of entire volume, dedusting and heating preshrunk are carried out to the film substrate of entire volume afterwards
Processing, obtain shrinking stable, the film handling member with front surface and anti-surface；
(2) color positioning colour code is chased after, by the film handling member of step (1) on screen process press, passes through screen process press
Process black chases after color positioning colour code respectively on the front surface of film handling member and anti-surface；
(3) film is counter is surface-treated, and the film after color positions colour code processing is chased after in step (2) black by screen process press
Either shallow texture layer is first printed on the anti-surface of handling member, the silk-screen half tone that this either shallow texture layer passes through its model 300 mesh 120T
Printing, and printing-ink is transparent UV thick film inks, and solidification drying, UV UV energies are carried out by UV ultraviolet lights after printing
In 400-500MJ/CM2, the operating rate of UV machines is 6-8m/min；Depth texture layer is printed on either shallow texture layer afterwards, and
The misaligned setting of texture dislocation of the texture of depth texture layer and either shallow texture layer, this depth texture layer pass through its model 350
Mesh 140T silk-screen half tone and printing-ink is that the printing of common slow curing ink forms, and is wound at a slow speed by coiled strip preshrinking machine after printing
Dry, the operating temperature of the coiled strip preshrinking machine is 90-110 DEG C；Dry and complete printing base of followed by being had one's face covered with depth texture layer
Chromatograph, this primary colours layer are printed for common ink, and drying is wound at a slow speed by coiled strip preshrinking machine again after printing, the coiled strip preshrinking machine
Operating temperature is 90-110 DEG C；Finally have one's face covered with primary colours layer printing adhesion layer, dried after having printed directly on coiled strip preshrinking machine,
The operating temperature of this coiled strip preshrinking machine is 90-110 DEG C, and drying time is 40-60 minutes, finally in bonding aspect after the completion of drying
Pasting protective film protects, and obtains film processing semi-finished product；
(4) film front surface is handled, and is handled by screen process press in the film of step (3) on the front surface of semi-finished product first
Frosted dumb light layer is printed, the silk-screen half tone and printing-ink that this frosted dumb light layer passes through its model 250 mesh 100T are dumb light UV
Fine grinding sand oil ink print forms, and carries out solidification drying by UV ultraviolet lights after printing, UV UV energies are in 400-500MJ/
CM2, the operating rate of UV machines is 6-8m/min；Solidification dry after on frosted dumb light layer printed three-dimensional UV texture layers, it is above-mentioned
The misaligned setting of texture dislocation of the texture of UV texture layers, the texture of depth texture layer and either shallow texture layer, this three-dimensional UV texture
Layer is roughly ground sand oil ink print for UV by its model 100 mesh 40T silk-screen half tone and ink and formed, purple by UV after printing
Outer light carries out solidification drying, and UV UV energies are in 400-500MJ/CM2, the operating rate of UV machines is 3-5m/min, is obtained thin
Film process finished product；
2nd, injection molding, the film processing finished product of step (4) is thermally formed with product by mould high temperature
The sheet material of outer shape, the diaphragm on sheet material then removes to be put into injection mold again be molded by by film matrix and plastics
The integrally formed IML face-pieces of matrix, and plastic substrate is combined with the anti-surface of film matrix.
Above-mentioned film substrate is the clear PET film that its thickness is 0.075-0.188mm or PC films.
The thickness of above-mentioned three-dimensional UV texture layers is 50-100um.
After adopting the above technical scheme, a kind of IML texture face-pieces with sense of touch and stereoeffect of the present invention, pass through
The printing on the positive and negative surface of film substrate can substantially increase the thickness sense of global pattern, and utilize the texture of three-dimensional UV texture layers
The misaligned setting of textured pattern dislocation of pattern, the textured pattern of either shallow texture layer and depth texture layer has global pattern texture
There are abundant level effect and stronger stereoscopic visual effect, then coordinate three-dimensional UV texture layers hand to touch can substantially feel concavo-convex
Texture, make IML texture face-pieces that there is preferable sense of touch and stereoeffect.Compared with prior art, IML textures face of the invention
Shell, its surface, which has preferable sense of touch and stereoeffect, to be obtained by way of surface screen-printed, and processing technology is simple,
And without carrying out larger transformation to existing IML printing production lines and increasing equipment, without to existing product injection mold
Changed, need to only change the texture half tone of different texture with regard to the IML texture face-pieces of different senses of touch, different texture can be obtained, become
It is simple, quick to change technique, IML texture face-piece finished products can be made flexibly to change, variation, it is practical, adapt to market it is changeable and
Quick production requirement has sense of touch and stereoeffect.
Brief description of the drawings
Fig. 1 is the structural representation of the present invention.
Embodiment
A kind of IML texture face-pieces with sense of touch and stereoeffect of the present invention, as shown in figure 1, including the He of film substrate 1
Plastic basis material 2, this film substrate 1 are the PET film or PC films for the all-transparent that its thickness is 0.075-0.188mm, the film
The injection of base material 1 and plastic basis material 2 links together, and the one side being combined using film substrate 1 with plastic basis material 2 is anti-surface, phase
Corresponding another side is front surface；From top to bottom screen printing is brushed with either shallow texture layer 3, depth successively on the anti-surface of the film substrate 1
Degree texture layer 4, primary colours layer 5 and adhesive layer 6, i.e. either shallow texture layer 3, depth texture layer 4, primary colours layer 5 and adhesive layer 6 use
Screen printer print forms, and the misaligned setting of texture sequence of the texture of either shallow texture layer 3 and depth texture layer 4, shallow
Spend the mesh 120T of model 300 of silk-screen half tone used by texture layer 3, the model of silk-screen half tone used by depth texture layer 4
For 350 mesh 140T, printing-ink is UV thick film inks used by either shallow texture layer 3, is printed used by depth texture layer 4
Ink is common ink, and this common ink is slow curing type.
From bottom to top screen printing is brushed with frosted dumb light layer 7 and three-dimensional UV texture layers 8 to the front surface of the film substrate 1 successively,
The mesh 100T of model 250 of silk-screen half tone wherein used by frosted dumb light layer 7, printing-ink used by frosted dumb light layer 7
For the thin frosted inks of dumb light UV, the mesh 40T of model 100 of silk-screen half tone, three-dimensional UV texture layers used by three-dimensional UV texture layers 8
Printing-ink is the thick frosted inks of UV used by 8, and the texture and depth of the texture of three-dimensional UV texture layers and either shallow texture layer
The texture of texture layer misplaces misaligned setting, i.e. the texture of three misplaces misaligned setting.
A kind of IML texture face-pieces with sense of touch and stereoeffect of the present invention, pass through the positive and negative surface of film substrate
Printing can substantially increase the thickness sense of global pattern, and utilize textured pattern, the line of either shallow texture layer 3 of three-dimensional UV texture layers 8
The misaligned setting of the textured pattern of reason pattern and depth texture layer 4 dislocation makes global pattern texture have abundant level effect
Stronger stereoscopic visual effect, then coordinate three-dimensional UV texture layers 8 substantially to feel concavo-convex texture with hand touch, make IML textures
Face-piece has preferable sense of touch and stereoeffect.Compared with prior art, IML texture face-pieces of the invention, its surface have compared with
Good sense of touch and stereoeffect is obtained by way of surface screen-printed, and processing technology is relatively simple, and without to existing
Some IML printing production lines carry out larger transformation and increase equipment, are changed without to existing product injection mold, only
The texture half tone of different texture, which need to be changed, just can obtain the IML texture face-pieces of different senses of touch, different texture, conversion process is simple,
Quickly, IML texture face-piece finished products can be made flexibly to change, variation, it is practical, adapt to that market is changeable and quick production requirement
There is sense of touch and stereoeffect.
A kind of manufacture craft of IML texture face-pieces with sense of touch and stereoeffect of the present invention, it is real as follows
It is existing：
First, film preparation
(1), pre-treatment, the film substrate of entire volume is prepared, this film substrate is that its thickness is the saturating of 0.075-0.188mm
Bright PET film or PC films, dedusting and heating preshrunk processing are carried out to the film substrate of entire volume afterwards, obtain shrinking stable, tool
There is the film handling member on front surface and anti-surface；
(2) color positioning colour code is chased after, by the film handling member of step (1) on screen process press, passes through screen process press
Process black chases after color positioning colour code respectively on the front surface of film handling member and anti-surface；
(3) film is counter is surface-treated, and the film after color positions colour code processing is chased after in step (2) black by screen process press
Either shallow texture layer is first printed on the anti-surface of handling member, the silk-screen half tone that this either shallow texture layer passes through its model 300 mesh 120T
Printing, and printing-ink is transparent UV thick film inks, it is preferred that the transparent UV thick film inks are by mass percent
The model IPL-1112A of 99.5% beautiful magnificent company's production transparent UV thick film inks and 0.5% black UV light solid four
Color ink mixing preparation forms；Solidification drying is carried out by UV ultraviolet lights after printing, UV UV energies are in 400-500MJ/
CM2, the operating rate 6-8m/min of UV machines；Depth texture layer, and the line of depth texture layer are printed on either shallow texture layer afterwards
Reason and the misaligned setting of texture dislocation of either shallow texture layer, the silk printing screen that this depth texture layer passes through its model 350 mesh 140T
Version and printing-ink are that the printing of common slow curing ink forms, and wind drying at a slow speed by coiled strip preshrinking machine after printing, the coiled strip is pre-
The operating temperature of contracting machine is 90-110 DEG C；Dry and complete printing primary colours layer of followed by being had one's face covered with depth texture layer, this primary colours layer
Printed for common ink, serve and set off texture, drying is wound at a slow speed by coiled strip preshrinking machine after printing, the coiled strip preshrinking machine
Operating temperature is 90-110 DEG C；Finally had one's face covered with primary colours layer printing adhesion layer, printed and dried directly on coiled strip preshrinking machine, should
The operating temperature of coiled strip preshrinking machine is 90-110 DEG C, and drying time is 40-60 minutes, finally in bonding aspect after the completion of drying
Pasting protective film protects, and obtains film processing semi-finished product；It is used to depth texture layer, primary colours layer and adhesive layer in the step (3) dry
Coiled strip preshrinking machine used, also can be in different coiled strip preshrunk hands- operations also in same coiled strip preshrunk hands- operation；
(4) film front surface is handled, and is handled by screen process press in the film of step (3) on the front surface of semi-finished product first
Frosted dumb light layer is printed, the silk-screen half tone and printing-ink that this frosted dumb light layer passes through its model 250 mesh 100T are dumb light UV
Thin frosted ink, its model GS-UV- that the thin frosted inks of this dumb light UV are preferably given birth to using Xiamen Jin Shang companies
U3KS-2INK delustring polishes, solidification drying is carried out by UV ultraviolet lights after printing, UV UV energies are in 400-500MJ/
CM2, the operating rate of UV machines is 6-8m/min；Solidification dry after on frosted dumb light layer printed three-dimensional UV texture layers, above-mentioned UV
The misaligned setting of texture dislocation of the texture of texture layer, the texture of depth texture layer and either shallow texture layer, this three-dimensional UV texture layer
Sand oil ink print is roughly ground by its model 100 mesh 40T silk-screen half tone and ink for UV to form, the thick frosted inks of this UV are preferred
Be produced by the Hua Yan companies of Fuji that mass percent is 97%, model UPET-20B UV light-curable inks and 3%
The beautiful production of magnificent company, model TPF-D19S dumb light powder ink mixing preparation form, the thickness of the thick frosted inks of this UV
Spend for 50-100um, solidification drying is carried out by UV ultraviolet lights after printing, UV UV energies are in 400-500MJ/CM2, UV machines
Operating rate be 3-5m/min, obtain film processing finished product；
2nd, injection molding, the film of step (4) processing finished product is molded and face-piece by the high-temperature heating of mould
The sheet material that outer shape matches, diaphragm then removes to be put into again in injection mold be molded by by film matrix and plastics base
The IML face-pieces of body by integral forming, and plastic substrate is combined with the anti-surface of film matrix.
Compared with prior art, manufacture craft of the invention, its integrated artistic are had by the way of silk-screen printing
There are the IML texture face-pieces of sense of touch and stereoeffect, integrated artistic is simple, and needs to mold different texture or sense of touch in whole technique
IML texture face-pieces when without carrying out larger transformation to existing IML printing production lines and increasing equipment, without to existing
Injection mould of products is changed, and need to only change the texture half tone of different texture, makes the texture transformation work of IML texture face-pieces
Skill is simple, quick, IML texture face-piece finished products can be made flexibly to change, variation, practical, and it is changeable and quick to adapt to market
Production requirement has sense of touch and stereoeffect；In addition, it is exactly the either shallow line developed using applicant in the manufacture craft of the present invention
Manage used by layer ink used by ink and three-dimensional UV texture layers, and with depth texture layer used by ink and frosted it is mute
The combination of ink can make the stereoeffect of whole IML textures face-piece and sense of touch effect very good used by photosphere.
Above-described embodiment and accompanying drawing and non-limiting product form of the invention and style, any art it is common
The appropriate change or modification that technical staff is done to it, it all should be regarded as not departing from the patent category of the present invention.
Claims (9)
1. a kind of IML texture face-pieces with sense of touch and stereoeffect, including film substrate and plastic basis material, the film substrate with
Plastic basis material injection links together, and for the one side being combined using film substrate with plastic basis material as anti-surface, corresponding is another
Face is front surface；It is characterized in that：From top to bottom screen printing is brushed with either shallow texture layer, depth successively on the anti-surface of above-mentioned film substrate
Texture layer, primary colours layer and adhesive layer are spent, from bottom to top screen printing is brushed with frosted dumb light layer to the front surface of above-mentioned film substrate successively
With three-dimensional UV texture layers, and the textured pattern of above-mentioned three-dimensional UV texture layers, the textured pattern of above-mentioned either shallow texture layer and above-mentioned depth
Spend textured pattern dislocation, the misaligned setting of texture layer.
A kind of 2. IML texture face-pieces with sense of touch and stereoeffect according to claim 1, it is characterised in that：It is above-mentioned
Either shallow texture layer, depth texture layer, frosted dumb light layer and three-dimensional UV texture layers are formed using silk-screen screen painting, and above-mentioned shallow
Spend the mesh 120T of model 300 of the silk-screen half tone of texture layer, the mesh of model 350 of the silk-screen half tone of above-mentioned depth texture layer
140T, the mesh 100T of model 250 of the silk-screen half tone of above-mentioned frosted dumb light layer, the silk-screen half tone of above-mentioned three-dimensional UV texture layers are
100 mesh 40T.
A kind of 3. IML texture face-pieces with sense of touch and stereoeffect according to claim 1, it is characterised in that：It is above-mentioned
Film substrate is the clear PET film that its thickness is 0.075-0.188mm or PC films.
A kind of 4. IML texture face-pieces with sense of touch and stereoeffect according to claim 2, it is characterised in that：It is above-mentioned
Either shallow texture layer is UV thick film inks layers, and above-mentioned depth texture layer is conventional oil layer of ink, and above-mentioned frosted dumb light layer is that dumb light UV is thin
Frosted ink layer, above-mentioned three-dimensional UV texture layers are that UV roughly grinds sand oil layer of ink.
5. a kind of manufacture craft of the IML texture face-pieces with sense of touch and stereoeffect, it is characterised in that real as follows
It is existing：
First, film preparation
(1), pre-treatment, prepare the film substrate of entire volume, dedusting and heating preshrunk processing carried out to the film substrate of entire volume afterwards,
Obtain shrinking stable, the film handling member with front surface and anti-surface；
(2) color positioning colour code is chased after, by the film handling member of step (1) on screen process press, by screen process press thin
Process black chases after color positioning colour code respectively on the front surface of film process part and anti-surface；
(3) film is counter is surface-treated, and chasing after color in step (2) black by screen process press positions the film processing after colour code processing
First print either shallow texture layer on the anti-surface of part, this either shallow texture layer by its model 300 mesh 120T silk-screen screen painting,
And printing-ink is transparent UV thick film inks, carries out solidification drying by UV ultraviolet lights after printing, UV UV energies are in 400-
500MJ/CM2, the operating rate of UV machines is 6-8m/min；Depth texture layer, and depth line are printed on either shallow texture layer afterwards
The texture of layer and the misaligned setting of texture dislocation of either shallow texture layer are managed, this depth texture layer passes through its model 350 mesh 140T
Silk-screen half tone and printing-ink be common slow curing ink printing form, drying is wound at a slow speed by coiled strip preshrinking machine after printing,
The operating temperature of the coiled strip preshrinking machine is 90-110 DEG C；Dry and complete printing primary colours layer of followed by being had one's face covered with depth texture layer,
This primary colours layer prints for common ink, winds drying at a slow speed by coiled strip preshrinking machine again after printing, the work of the coiled strip preshrinking machine
Temperature is 90-110 DEG C；Finally have one's face covered with primary colours layer printing adhesion layer, dried after having printed directly on coiled strip preshrinking machine, this volume
The operating temperature for expecting preshrinking machine is 90-110 DEG C, and drying time is 40-60 minutes, is finally protected after the completion of drying in bonding aspect patch
Cuticula protects, and obtains film processing semi-finished product；
(4) film front surface is handled, and is handled in the film of step (3) by screen process press and is first printed on the front surface of semi-finished product
Frosted dumb light layer, the silk-screen half tone and printing-ink that this frosted dumb light layer passes through its model 250 mesh 100T are dumb light UV fine grindings
Sand oil ink print forms, and carries out solidification drying by UV ultraviolet lights after printing, UV UV energies are in 400-500MJ/CM2,UV
The operating rate of machine is 6-8m/min；Solidification dry after on frosted dumb light layer printed three-dimensional UV texture layers, above-mentioned UV texture layers
Texture, the texture of texture and either shallow texture layer of depth texture layer misplace misaligned setting, this three-dimensional UV texture layer passes through it
The mesh 40T of model 100 silk-screen half tone and ink is that UV corase grind sand oil ink prints form, and is consolidated after printing by UV ultraviolet lights
Change drying, UV UV energies are in 400-500MJ/CM2, the operating rate of UV machines is 3-5m/min, obtains film processing finished product；
2nd, injection molding, the film processing finished product of step (4) is molded by mould and matched with face-piece outer shape
Sheet material, then the diaphragm on sheet material is removed be put into again in injection mold be molded by by film matrix and plastic substrate one
The IML face-pieces of shaping, and plastic substrate is combined with the anti-surface of film matrix.
6. a kind of manufacture craft of IML texture face-pieces with sense of touch and stereoeffect as claimed in claim 5, its feature exist
In：Above-mentioned film substrate is the clear PET film that its thickness is 0.075-0.188mm or PC films.
7. a kind of manufacture craft of IML texture face-pieces with sense of touch and stereoeffect as claimed in claim 5, its feature exist
In：The thickness of above-mentioned three-dimensional UV texture layers is 50-100um.
8. a kind of manufacture craft of IML texture face-pieces with sense of touch and stereoeffect as claimed in claim 5, its feature exist
In：UV that the above-mentioned thick frosted inks of UV are produced by the Hua Yan companies of Fuji that mass percent is 97%, model UPET-20B
Light-curable ink and 3% beautiful magnificent company's production, model TPF-D19S dumb light powder ink mixing preparation form.
9. a kind of manufacture craft of IML texture face-pieces with sense of touch and stereoeffect as claimed in claim 8, its feature exist
In：The model IPL-1112A for beautiful magnificent company's production that above-mentioned transparent UV thick film inks are 99.5% by mass percent
Transparent UV thick film inks and the solid four color ink mixing preparations of 0.5% black UV light form.