CN107471887A - The preparation method of carbon dust transfer paper - Google Patents
The preparation method of carbon dust transfer paper Download PDFInfo
- Publication number
- CN107471887A CN107471887A CN201710854911.4A CN201710854911A CN107471887A CN 107471887 A CN107471887 A CN 107471887A CN 201710854911 A CN201710854911 A CN 201710854911A CN 107471887 A CN107471887 A CN 107471887A
- Authority
- CN
- China
- Prior art keywords
- temperature
- degree
- carbon dust
- transfer paper
- film head
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The preparation method that the present invention discloses carbon dust transfer paper, including carbon dust transfer paper, Silicon coating machine, baking oven and extruder, carbon dust transfer paper are made by brown paper, silicone oil and polyethylene;Its steps taken is:The first step applies silicon, and Silicon coating machine Switching Power Supply is closed, check power supply and motor whether normal operation, and will unreel, each deflector roll checks once in winding and baking oven, determines if clean;Second step drenches PEF film, adjusts polyethylene film head, the temperature of screw rod, constant processing temperature is the necessary condition of PE stable performances, and the steady temperature scope of setting value is regulated before start;3rd step, when temperature reaches assigned temperature value, film head is adjusted in start, knifing head, is changed filter screen, the 4th step, is driven extruder, checks whether creeping artificial situation is uniformly abundant;The major function of carbon dust transfer paper of the present invention is that the pattern on carbon dust transfer paper is transferred in other media by transfer carbon dust, and such as woodwork, PU, PVC, cladding, plastics, transferring rate need to reach more than 98%.
Description
Technical field
The preparation method that the present invention discloses carbon dust transfer paper.
Background technology
Transfer paper be can will the pattern of thermoprint exported with ink-jet printer, then print on clothes, light color can be divided into and turned
Printing paper and dark transfer paper, light transfer paper are adapted to print the light clothes such as white;Dark transfer paper is adapted to print the dark clothing such as black
Clothes, transfer paper be can will the pattern of thermoprint exported with ink-jet printer, then print on clothes, can be divided into light transfer paper and
Dark transfer paper, wherein light transfer paper is adapted to print the light clothes such as white, dark transfer paper is adapted to print the dark clothes such as black.
Transfer paper can also be divided into metal transfer paper and the major class of pigment transfer paper two, in addition to thermocolor paint or pressure-sensitive coating material production
Coating paper, surface scribble moistening transfer film paper, such as letter carving transfer film carve.
The existing production method for transfer paper mainly includes silk-screen, UV and heat sublimation, wherein, the operation of silk-screen technology
More complicated, a performance only prints a kind of color, and multiple color needs to print repeatedly, and has needed quantitative;UV printing presses
Equipment is expensive, and UV ink is expensive, and machine maintenance takes height, and most of product needs specific coatings to print;Heat sublimation can only be imprinted on white
On color product, it is impossible to transferred on dark product, and need heat sublimation ink, most of transfer product needs processing spray special
Coating, ability transferability.
The content of the invention
For the present invention in order to solve problem of the prior art, the major function for disclosing carbon dust transfer paper is transfer carbon dust, is turned
Print rate needs the preparation method for reaching more than 95% carbon dust transfer paper.
The concrete technical scheme of the present invention is as follows:The preparation method of carbon dust transfer paper, including carbon dust transfer paper, Silicon coating machine,
Baking oven and extruder, the formula of the carbon dust transfer paper include brown paper, silicone oil and polyethylene;
Its preparation method is including step:
The first step, Silicon coating machine Switching Power Supply is closed, check power supply and motor whether normal operation, and will unreel, wind
And each deflector roll checks once in baking oven, determine if clean;
Second step, polyethylene film head is adjusted, the temperature of screw rod, constant processing temperature is the necessary bar of PE stable performances
Part, the steady temperature scope of setting value is regulated before start (Temperature numerical of different platform is variant);
3rd step, when temperature reaches assigned temperature value, film head is adjusted in start, knifing head, changes filter screen;
4th step, extruder is driven, check whether creeping artificial situation is uniformly abundant;
5th step, to be started shooting in the temperature setting range for reaching stable, temperature is polyethylene gel is directly quickly volatilized,
And make to be adhesive with moderately good solidification basis, so that excellent performance is being embodied on base material in polyethylene, just
Often the corona value under operating can not be more than 4.8 numerical value, and numerical value is excessive may to puncture gum cover;
6th step, board running speed to coordinate temperature height cemented loosely with modeling depending on, blindly operation improve speed meeting
Influence quality;
7th step, under normal board running speed, film loss must control, and the modeling paper that gives up is less than or equal to 0.2%, original of giving up
Paper is less than or equal to 0.2%, and the particle that gives up is less than or equal to 0.1%.
As further limitation ground of the invention, the temperature control in the baking oven is divided in eight sections, eight sections
Wei not be 70 degree, 120 degree, 130 degree, 135 degree, 125 degree, 120 degree, 50 degree.
Respectively it is divided into eight sections as further limitation ground, the polyethylene film head, screw rod of the invention, its is corresponding.
As further limitation ground of the invention, eight sections are respectively 295 degree of polyethylene film head temperature, extruder temperature
190 degree;300 degree of polyethylene film head temperature, 320 degree of extruder temperature;332 degree of polyethylene film head temperature, 328 degree of extruder temperature;It is poly-
324 degree of vinyl film head temperature, 328 degree of extruder temperature;320 degree of polyethylene film head temperature, 333 degree of extruder temperature;Polyethylene film head
333 degree of temperature, 333 degree of extruder temperature;333 degree of polyethylene film head temperature, 333 degree of extruder temperature;Polyethylene film head temperature 330
Degree, 295 degree of extruder temperature.
The technique effect of the present invention:The major function of carbon dust transfer paper of the present invention is transfer carbon dust, and transferring rate needs to reach
More than 95%, carbon dust transfer paper technology is that the abundant colour of disposable transfer can be realized by color laser printer on works,
And it need not rise quantitative;The product of carbon dust transfer technique need not carry out special processing can transfer mostly, and use is original-pack
Powder need not use special powder, and cost is than cheap, and carbon dust transfer technique can be transferred on dark product, original-pack ink powder, no
Special ink powder is needed, most of product does not need specific coatings.
Brief description of the drawings
Fig. 1 is baking oven temperature control value reference view of the present invention.
Fig. 2 is polyethylene film head of the present invention, the temperature control value reference view of screw rod.
Embodiment
Below, the substantive distinguishing features and advantage of the present invention are further described with reference to example, but not office of the invention
It is limited to listed embodiment.
As shown in Figure 1 to Figure 2, the preparation method of the carbon dust transfer paper of the present embodiment, including carbon dust transfer paper, Silicon coating machine,
Baking oven and extruder, the formula of the carbon dust transfer paper include brown paper, silicone oil and polyethylene;
Its preparation method comprises the following steps:
The first step, Silicon coating machine Switching Power Supply is closed, check power supply and motor whether normal operation, and will unreel, wind
And each deflector roll checks once in baking oven, determine if clean;
Second step, polyethylene film head is adjusted, the temperature of screw rod, constant processing temperature is the necessary bar of PE stable performances
Part, the steady temperature scope of setting value is regulated before start (Temperature numerical of different platform is variant);
3rd step, when temperature reaches assigned temperature value, film head is adjusted in start, knifing head, changes filter screen;
4th step, extruder is driven, check whether creeping artificial situation is uniformly abundant;
5th step, to be started shooting in the temperature setting range for reaching stable, temperature is polyethylene gel is directly quickly volatilized,
Corona value under normal operation can not be more than 4.8 numerical value;
6th step, board running speed to coordinate temperature height cemented loosely with modeling depending on;
7th step, under normal board running speed, film loss must control, and the modeling paper that gives up is less than or equal to 0.2%, original of giving up
Paper is less than or equal to 0.2%, and the particle that gives up is less than or equal to 0.1%.
As further limitation ground of the invention, the temperature control in the baking oven is divided in eight sections, eight sections
Wei not be 70 degree, 120 degree, 130 degree, 135 degree, 125 degree, 120 degree, 50 degree.
The polyethylene film head, screw rod are respectively divided into eight sections, and its is corresponding.
Eight sections are respectively 295 degree of polyethylene film head temperature, 190 degree of extruder temperature;Polyethylene film head temperature 300
Degree, 320 degree of extruder temperature;332 degree of polyethylene film head temperature, 328 degree of extruder temperature;324 degree of polyethylene film head temperature, screw rod temperature
328 degree of degree;320 degree of polyethylene film head temperature, 333 degree of extruder temperature;333 degree of polyethylene film head temperature, 333 degree of extruder temperature;
333 degree of polyethylene film head temperature, 333 degree of extruder temperature;330 degree of polyethylene film head temperature, 295 degree of extruder temperature.
By such scheme, specifically, can be used more using the laser carbon dust printer of carbon dust transfer technique
On kind product, including leather and fur products, such as leather suitcase, leather certificate cover, leather cell-phone cover, leather notepad, leather key
Button;Plastic products, such as plastic bead pen, plastic handset button, plastic cup;Woodwork, such as wooden wine box, wooden ball pen, wood
Tank, wooden key chain;Ceramic, such as ceramic white cup, ceramic frosted cup, the color cup of ceramics.
Its transfer machine accordingly used includes, Pyrograph machine, prints a machine, bakes cup machine, and transfer temperature is controlled at 120 degree extremely
180 degree, time 5-65S.
Embodiment 1
Leather transfers:
1st, using carbon dust transfer paper laser carbon dust printer;
2nd, the pattern printed and the leather that will be transferred are got out;
3rd, pattern and leather are fixed with High temperature-resistanadhesive adhesive tape and clung;
4th, using Pyrograph machine and to set temperature be 180 degree, time 40S, hot pressure;
5th, after the completion of hot pressure, transfer is completed.
Embodiment 2
Fibertip pen transfers
1st, using carbon dust transfer paper laser carbon dust printer;
2nd, the pattern printed and the fibertip pen that will be transferred are got out;
3rd, pattern and fibertip pen are fixed with High temperature-resistanadhesive adhesive tape and clung;
4th, using Pyrograph machine and to set temperature be 100-130 degree, time 20-40S, hot pressure;
5th, after the completion of hot pressure, paper is torn, transfer is completed.
Embodiment 3
Wooden transfer
1st, using carbon dust transfer paper laser carbon dust printer;
6th, the pattern printed and the wooden unit that will be transferred are got out;
7th, pattern and wooden unit are fixed with High temperature-resistanadhesive adhesive tape and clung;
8th, the use of Pyrograph machine and setting temperature is 130 degree, time 65S, hot pressure;
9th, hot pressure tears paper, and transfer is completed.
The present invention has advantages below:
First, carbon dust transfer technique contrast silk-screen technology, carbon dust transfer paper technology is can be real by color laser printer
Now the abundant colour of disposable transfer is on works, and need not rise and quantify, and the operation of silk-screen technology is more complicated, a performance
A kind of color is only printed, multiple color needs to print repeatedly, and has needed quantitative;
Second, carbon dust transfer technique contrast UV printing techniques, it is special that the product of carbon dust transfer technique need not be carried out mostly
Can transfer to be processed, special powder need not be used using original-pack powder, cost is cheaper than UV, and UV printing machinery and equipments are expensive,
UV ink is expensive, and machine maintenance takes height, and most of product needs specific coatings to print;
3rd, carbon dust transfer technique contrast heat sublimation technology, carbon dust transfer technique can be transferred on dark product, original-pack ink
Powder, it is not necessary to which special ink powder, most of product do not need specific coatings, and heat sublimation can only be imprinted in white products, it is impossible in depth
Transferred on color product, and need heat sublimation ink, most of transfer product needs to process spray specific coatings, ability transferability.
The major function of carbon dust transfer paper of the present invention is transfer carbon dust, and transferring rate needs to reach more than 95%;Carbon dust transfers
Paper technology is that the abundant colour of disposable transfer can be realized by color laser printer on works, and need not be risen quantitative;
The product of carbon dust transfer technique need not carry out special processing can transfer mostly, and it is special to be used using original-pack powder
Powder, cost is than cheap;Carbon dust transfer technique can be transferred on dark product, original-pack ink powder, it is not necessary to special ink powder, it is most of
Product does not need specific coatings.
It is pointed out that the technical concepts and features of above-mentioned preferred embodiment only to illustrate the invention, its object is to
Allow person skilled in the art to understand present disclosure and implement according to this, the protection of the present invention can not be limited with this
Scope.Any equivalent change or modification in accordance with the spirit of the invention, it should all be included within the scope of the present invention.
Claims (4)
1. the preparation method of carbon dust transfer paper, including carbon dust transfer paper, Silicon coating machine, baking oven and extruder, it is characterised in that described
Carbon dust transfer paper is made by brown paper, silicone oil and polyethylene;
Its preparation method is including step:
The first step, Silicon coating machine Switching Power Supply is closed, check power supply and motor whether normal operation, and will unreel, and wind and dry
Each deflector roll checks once in case, determines if clean;
Second step, polyethylene film head is adjusted, the temperature of screw rod, constant processing temperature is the necessary condition of PE stable performances, is opened
The steady temperature scope of setting value is regulated before machine (Temperature numerical of different platform is variant);
3rd step, when temperature reaches assigned temperature value, film head is adjusted in start, knifing head, changes filter screen;
4th step, extruder is driven, check whether creeping artificial situation is uniformly abundant;
5th step, started shooting in the temperature setting range for reaching stable, temperature is polyethylene gel is directly quickly volatilized, just
Often the corona value under operating can not be more than 4.8 numerical value;
6th step, board running speed to coordinate temperature height cemented loosely with modeling depending on;
7th step, under normal board running speed, film loss must control, and the modeling paper that gives up is less than or equal to 0.2%, and the body paper that gives up is small
It is less than or equal to 0.1% in the particle that equal to 0.2%, gives up.
2. the preparation method of carbon dust transfer paper as claimed in claim 1, it is characterised in that the temperature control in the baking oven
In eight sections, eight sections are respectively 70 degree, 120 degree, 130 degree, 135 degree, 125 degree, 120 degree, 50 degree.
3. the preparation method of tool carbon dust transfer paper as claimed in claim 1, it is characterised in that the polyethylene film head, screw rod
Respectively it is divided into eight sections, its is corresponding.
4. the preparation method of carbon dust transfer paper as claimed in claim 3, it is characterised in that eight sections are respectively poly- second
295 degree of alkene film head temperature, 190 degree of extruder temperature;300 degree of polyethylene film head temperature, 320 degree of extruder temperature;Polyethylene film head temperature
332 degree of degree, 328 degree of extruder temperature;324 degree of polyethylene film head temperature, 328 degree of extruder temperature;320 degree of polyethylene film head temperature,
333 degree of extruder temperature;333 degree of polyethylene film head temperature, 333 degree of extruder temperature;Polyethylene film head temperature 333, extruder temperature 333
Degree;330 degree of polyethylene film head temperature, 295 degree of extruder temperature.