CN107470986A - A kind of coloured glaze crude green body grinding technics - Google Patents
A kind of coloured glaze crude green body grinding technics Download PDFInfo
- Publication number
- CN107470986A CN107470986A CN201710609118.8A CN201710609118A CN107470986A CN 107470986 A CN107470986 A CN 107470986A CN 201710609118 A CN201710609118 A CN 201710609118A CN 107470986 A CN107470986 A CN 107470986A
- Authority
- CN
- China
- Prior art keywords
- coloured glaze
- polishing
- green body
- sandblasting
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of coloured glaze crude green body grinding technics, comprise the following steps：（1）, corase grind,（2）, carefully repair, using size, the shape that pen should be according to coloured glaze defect is carefully repaiied, modified to change nib；（3）, sandblasting,（4）, cleaning, after sandblastings, first the grains of sand on coloured glaze surface are removed with hydraulic giant, then coloured glaze is put into 70 80 DEG C of warm water and soaked, coloured glaze is taken out from warm water, cleaned with cleaning solution, then be rinsed with hydraulic giant；（5）, fine grinding,（6）, polishing, using sander coloured glaze surface is polished 24 times, after polishing is completed every time, the powder on coloured glaze is answered into wiped clean；（7）, polishing, the water that polishing powder is converted to upper 8 10 times, recycle polishing machine and polish powder solvent and be processed by shot blasting that coloured glaze works, which just make, after polishing is over to coloured glaze.The invention provides a kind of technique is simple, process velocity block, grinding effect is good, more securely and reliably, the higher coloured glaze crude green body grinding technics of product quality.
Description
Technical field
The present invention relates to colored glaze product, more particularly to a kind of coloured glaze crude green body grinding technics.
Background technology
Coloured glaze works or thick and heavy history culture is carried, contained the philosophic theory of religion, poured into creator to life
Have deep love for, it is exquisite to conceive, beautiful artistic conception, intension of extensive knowledge and profound scholarship, makes appreciator or ponders or come to realize or exclaim.Ancient times
Said in Confucian classics：" when being willing to that I obtains bodhi in next life, body such as coloured glaze is inside and outside bright and limpid, net flawless dirty ".It can be seen that in the sense, coloured glaze
Glass is a kind of personality, a kind of symbol of spiritual, a kind of boundary.
The raw material of manufacture coloured glaze is called crystal material, and crystal material is the British coloured glaze containing lead oxide in invention in 1676,
It is beautiful such as crystal for transparent white, therefore named crystal material.The proportioning of metal oxide is different, and the effect presented is also different.
Cobalt oxide is such as added, to manufacture blueness；Manganese dioxide, make coloured glaze that purple be presented；Potassium bichromate is added, coloured glaze can present green
Color；Add titanium oxide, yellow etc. is presented in cerium oxide.Whatsoever color is invariably coloured and dazzling for crystal material.The advantages of crystal material, is very
It is more, as refractive index is high, it is easy to burn casting, hardness is softer, is especially suitable for processing, and is more conducive to the cold techniques such as follow-up cutting, grinding, polishing
Make.We should select, match the crystal material of respective color according to the color requirements of design.Usual crystal material makes after should breaking into pieces
With.After having matched crystal material, we clean using clear water to crystal material.The impurity on crystal material surface is washed, favorably
In the cleanliness factor for improving coloured glaze.
The techniques such as the thick embryo needs of coloured glaze are roughly ground, carefully repaiied, sandblasting, cleaning, polishing, polishing are repaired to coloured glaze, with
Upper process relation is slightly neglected to the quality of coloured glaze finished product and just occurs that flaw is even not worth a farthing, influence the quality of product, give
Enterprise brings larger loss.
The content of the invention
In order to solve the problems of the prior art, the invention provides a kind of technique is simple, process velocity block, grinding effect
It is good, more securely and reliably, the higher coloured glaze crude green body grinding technics of product quality.
In order to solve the above problems, the technical solution used in the present invention is：
A kind of coloured glaze crude green body grinding technics, it is characterised in that：Comprise the following steps：
(1), roughly grind, roughly ground using grinder, prepare the thick diamond dust mud of 20 purposes, diamond dust mud is put into grinder
Hourglass on, pour little water in the above, open water-dropper, it is persistently kept the state of moistening, sand water passes to mill
On, open grinder and coloured glaze roughly grind, corase grind can only be ground to cut surface, roughly grind 5-10 minutes；
(2), carefully repair, using size, the shape that pen should be according to coloured glaze defect is carefully repaiied, modified to change nib；
(3), sandblasting, it is thin repair after progress sandblasting, during sandblasting, staff should be with safeguards such as good mouth masks, by coloured glaze
Glass, which is put into sand-blasting machine, carries out sandblasting polishing coloured glaze surface, and sandblasting carries out 15-20 minutes；
(4), after cleaning, sandblasting, first the grains of sand on coloured glaze surface is removed with hydraulic giant, coloured glaze is then put into 70-80 DEG C
Soaked in warm water, after soaking 30-40 minutes, coloured glaze is taken out from warm water, cleaned with cleaning solution, then carried out with hydraulic giant
Rinse；
(5), fine grinding, prepare the thick diamond dust mud of 100 purposes, carry out fine grinding using grinder, the fine grinding time in 5-20 minutes,
Coloured glaze should be cleaned up after fine grinding；
(6), polish, coloured glaze surface is polished 2-4 times using sander, after polishing is completed every time, by the powder on coloured glaze
Answer wiped clean in end；
(7), polishing, polishing powder is converted to upper 8-10 times of water, recycle polishing machine and polish powder solvent and coloured glaze is thrown
Light processing, coloured glaze works, which just make, after polishing is over.
A kind of foregoing coloured glaze crude green body grinding technics, it is characterised in that：The step (1), opening grinder enter to coloured glaze
Row is roughly ground, and corase grind can only be ground to cut surface, is roughly ground 8 minutes.
A kind of foregoing coloured glaze crude green body grinding technics, it is characterised in that：The step (3), coloured glaze is put into sand-blasting machine
Sandblasting polishing coloured glaze surface is carried out, sandblasting is carried out 18 minutes；
A kind of foregoing coloured glaze crude green body grinding technics, it is characterised in that：The step (4), the temperature that coloured glaze is put into 75 DEG C
Soaked in water, after soaking 35 minutes, coloured glaze is taken out from warm water, cleaned with cleaning solution, then be rinsed with hydraulic giant；
A kind of foregoing coloured glaze crude green body grinding technics, it is characterised in that：The step (5), using grinder carry out fine grinding,
The fine grinding time at 13 minutes,
A kind of foregoing coloured glaze crude green body grinding technics, it is characterised in that：The step (7), polishing powder converted upper 9 times
Water, polishing machine and polishing powder solvent is recycled to be processed by shot blasting that coloured glaze works, which just make, after polishing is over to coloured glaze.
The beneficial effect that the present invention is reached：Coloured glaze crude green body grinding technics of the present invention, process is simple, using tens of Ji Dao sections
Technique is learned, Operation Sequencing is reasonable, and each step contact is close, and step is implemented to be particular about, and process velocity is fast, substantially increases technique effect
Rate, firing effect is good, and coloured glaze product is after finishing processing, and quality is increased dramatically, and value greatly increases.
Embodiment
The following examples are only intended to illustrate the technical solution of the present invention more clearly, and can not limit the present invention with this
Protection domain.
A kind of coloured glaze crude green body grinding technics, it is characterised in that：Comprise the following steps：
(1), roughly grind, roughly ground using grinder, prepare the thick diamond dust mud of 20 purposes, diamond dust mud is put into grinder
Hourglass on, pour little water in the above, open water-dropper, it is persistently kept the state of moistening, sand water passes to mill
On, open grinder and coloured glaze roughly grind, corase grind can only be ground to cut surface, be roughly ground 8 minutes；
(2), carefully repair, using size, the shape that pen should be according to coloured glaze defect is carefully repaiied, modified to change nib；
(3), sandblasting, it is thin repair after progress sandblasting, during sandblasting, staff should be with safeguards such as good mouth masks, by coloured glaze
Glass, which is put into sand-blasting machine, carries out sandblasting polishing coloured glaze surface, and sandblasting is carried out 18 minutes；
(4), after cleaning, sandblasting, first the grains of sand on coloured glaze surface is removed with hydraulic giant, then coloured glaze is put into 75 DEG C of warm water
In soaked, immersion 35 minutes after, by coloured glaze from warm water take out, cleaned with cleaning solution, then be rinsed with hydraulic giant；
(5), fine grinding, prepare the thick diamond dust mud of 100 purposes, using grinder carry out fine grinding, the fine grinding time at 12 minutes, carefully
Coloured glaze should be cleaned up after mill；
(6), polish, coloured glaze surface is polished 3 times using sander, after polishing is completed every time, by the powder on coloured glaze
Answer wiped clean；
(7), polishing, polishing powder is converted to upper 9 times of water, recycle polishing machine and polishing powder solvent to be polished place to coloured glaze
Reason, coloured glaze works, which just make, after polishing is over.
In summary：Coloured glaze crude green body grinding technics of the present invention, process is simple, using tens of a few road scientific technologies, process row
Sequence is reasonable, and each step contact is close, and step is implemented to be particular about, and process velocity is fast, substantially increases process efficiency, and firing effect is good,
Coloured glaze product is after finishing processing, and quality is increased dramatically, and value greatly increases.
General principle, the main features and advantages of the present invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, the original for simply illustrating the present invention described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
It all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claims and its equivalent circle
It is fixed.
Claims (6)
- A kind of 1. coloured glaze crude green body grinding technics, it is characterised in that：Comprise the following steps：（1）, corase grind, roughly ground using grinder, prepare the thick diamond dust mud of 20 purposes, diamond dust mud be put into the sand of grinder In leakage, little water is poured in the above, opens water-dropper, it is persistently kept the state of moistening, and sand water is passed on mill, beaten Drive grinder coloured glaze roughly grind, corase grind can only be ground cut surface, roughly grind 5-10 minutes；（2）, carefully repair, using size, the shape that pen should be according to coloured glaze defect is carefully repaiied, modified to change nib；（3）, sandblasting, it is thin repair after progress sandblasting, during sandblasting, staff should put coloured glaze with safeguards such as good mouth masks Enter to carry out sandblasting polishing coloured glaze surface in sand-blasting machine, sandblasting carries out 15-20 minutes；（4）, cleaning, after sandblastings, first the grains of sand on coloured glaze surface are removed with hydraulic giant, then coloured glaze is put into 70-80 DEG C of warm water In soaked, soak 30-40 minutes after, by coloured glaze from warm water take out, cleaned with cleaning solution, then rushed with hydraulic giant Wash；（5）, fine grinding, prepare the thick diamond dust mud of 100 purposes, using grinder carry out fine grinding, the fine grinding time is in 5-20 minutes, fine grinding After coloured glaze should be cleaned up；（6）, polishing, using sander to coloured glaze surface polish 2-4 times, every time polishing complete after, by the powder on coloured glaze should Wiped clean；（7）, polishing, the water that polishing powder is converted to upper 8-10 times, recycle polishing machine and polish powder solvent place is polished to coloured glaze Reason, coloured glaze works, which just make, after polishing is over.
- A kind of 2. coloured glaze crude green body grinding technics according to claim 1, it is characterised in that：The step（1）, open grinding Machine to coloured glaze roughly grind, and corase grind can only be ground to cut surface, is roughly ground 8 minutes.
- A kind of 3. coloured glaze crude green body grinding technics according to claim 2, it is characterised in that：The step（3）, coloured glaze put Enter to carry out sandblasting polishing coloured glaze surface in sand-blasting machine, sandblasting is carried out 18 minutes.
- A kind of 4. coloured glaze crude green body grinding technics according to claim 3, it is characterised in that：The step（4）, coloured glaze put Enter and soaked in 75 DEG C of warm water, after soaking 35 minutes, coloured glaze is taken out from warm water, cleaned with cleaning solution, then use water Rifle is rinsed.
- A kind of 5. coloured glaze crude green body grinding technics according to claim 4, it is characterised in that：The step（5）, use grinding Machine carries out fine grinding, and the fine grinding time was at 13 minutes.
- A kind of 6. coloured glaze crude green body grinding technics according to claim 5, it is characterised in that：The step（7）, by polishing powder 9 times of water is converted, recycles polishing machine and polishing powder solvent to be processed by shot blasting that coloured glaze works have just made after polishing to coloured glaze .