CN107462450A - A kind of production method of standard specimen textile - Google Patents
A kind of production method of standard specimen textile Download PDFInfo
- Publication number
- CN107462450A CN107462450A CN201710724126.7A CN201710724126A CN107462450A CN 107462450 A CN107462450 A CN 107462450A CN 201710724126 A CN201710724126 A CN 201710724126A CN 107462450 A CN107462450 A CN 107462450A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- production method
- textile
- standard specimen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of production method of standard specimen textile, including step in detail below：(1), material to be detected is dissolved in N, and in N dimethyl formamide solutions, standard liquid is made；(2), standard liquid made from step (1) is added in adhesive, mixes and adds defoamer, defoaming is stood, rubber cement is made；(3) rubber cement made from step (2), is uniformly coated on fabric face, dried, finished product.
Description
Technical field
The invention belongs to textile manufacturing field, a kind of production method of standard specimen textile of specific design.
Background technology
Quality control samples (QCM--Quality Control Material) are quality-control sample, are by proficiency testing
The sample of participant's mutual authentication, there is the designated value and its uncertainty of one or more special parameters uniform enough, it is every kind of
Sample has a certificate, and quality-control sample is effective extension of proficiency testing sample, and quality-control sample is that laboratory judges that itself is examined
Survey ability provides important technology foundation.
With the continuous development of textile and garment enterprise, textile inspection especially clothes are examined outside traditional attention
Appearance quality, which is examined, to be intended to focus on inherent quality inspection, and especially chemical property is examined, and the harmful substance such as heavy metal, azo is all
There is strict limitation, and then ensure the safety and interests of consumer, this is just to examining laboratory to propose higher requirement, for first
Create laboratory, especially examine project be in carry out initial stage, many test results by environment, personnel, equipment, standard etc. because
The influence of element, detection data have differences with other laboratories, therefore, reasonably participate in proficiency testing, Comparability test for first
Wound laboratory is that a kind of effective external quality assurance is movable, and the important supplement of laboratory internal Quality Control Technology, from
And science, preciseness, objectivity, the fairness of checkout procedure are advantageously ensured that, domestic laboratory internal quality control system
Construction is also weaker, and quality control method is relatively simple, it is necessary to establish and implement reliable internal quality control plan, it is ensured that
Detection process is controlled, ensures the accuracy and reliability of testing result.
The content of the invention
The purpose of the present invention is the shortcomings that overcoming prior art, there is provided the standard specimen weaving that a kind of stability is good, uniformity is good
The production method of product.
The present invention adopts the following technical scheme that：
A kind of production method of standard specimen textile, including step in detail below：
(1), material to be detected is dissolved in DMF solution, and standard liquid is made；
(2), standard liquid made from step (1) is added in adhesive, mixes and adds defoamer, defoaming is stood, is made
Rubber cement；
(3) rubber cement made from step (2), is uniformly coated on fabric face, dried, finished product.
Further, the material to be detected includes decomposable asymmetric choice net aromatic amine dyestuff, the 0.1-0.2 of 0.1-0.2 parts by weight
The phthalic acid ester of parts by weight, the heavy metal of 0.025-0.1 parts by weight, the alkyl phenol of 0.025-0.1 parts by weight gather
The organotin of oxygen vinethene or 0.025-0.1 parts by weight, for dissolving the DMF solution of material to be detected
For 0.1 parts by weight, the adhesive of addition is 99.8-99.9 parts by weight.
Further, the decomposable asymmetric choice net aromatic amine dyestuff be 4- aminobphenyls, benzidine, 4- chloro-o-toluidines, 2- naphthylamines,
Parachloroanilinum, 2,4- diamino anisoles, 4,4 '-MDA, 3,3 '-dichloro-benzidine, 3,3 '-dimethyl -4,
4 '-MDA, 2- methoxyl group -5- methylanilines, 4,4 '-methylene-two-(2- chloroanilines), 4,4 '-diaminourea two
Phenylate, 4,4 '-diaminodiphenyl sulfide, ortho-aminotoluene, 2,4 di amino toluene, 2,4,5- trimethylanilines, o-amino benzoyl
Ether, 2,4- dimethylanilines, 2,6- dimethylanilines, 3,3 '-dimethoxy benzidine, 3,3 '-dimethylbenzidine, 4- amino
One or more in azobenzene.
Further, the phthalic acid ester is diisononyl phthalate, phthalic acid two (2- ethyl hexyls)
Ester, di-n-octyl phthalate, diisooctyl phthalate, BBP(Butyl Benzyl Phthalate, dibutyl phthalate, neighbour
Phthalic acid diisobutyl ester, diamyl phthalate, the C of phthalic acid two6-8Branched alkyl ester, phthalic acid dimethoxy
One or more in base ethyl ester.
Further, the heavy metal is the one or more in arsenic, cadmium, cobalt, chromium, copper, nickel, lead, antimony.
Further, the APES is in OPEO, NPE
It is one or more.
Further, the organotin is Monobutyltin, dibutyl tin, the one or more of tributyl tin.
Further, described adhesive is oiliness PU or water-based PU, during mixing, is selected according to the property of test substance water-based
PU or oiliness PU are mixed.
Further, the step (2) includes, by standard liquid made from step (1), being selected according to the property of standard liquid
Select and add under conditions of oiliness or water-based PU, low whipping speed 1000r/min, add 0.5% defoamer, stand, pass through vacuum
Defoaming device is defoamed, and rubber cement is made.
Further, the step (3) includes rubber cement made from step (2) being uniformly coated in by printing equipment and knitted
Thing surface, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
From the above-mentioned description of this invention, compared with prior art, the beneficial effects of the invention are as follows：Using above-mentioned side
Test textile is according to CNAS-GL03 made of method：2006《Proficiency testing sample homogeneity and estimation of stability guide》Rule
It is fixed, uniformity testing is carried out using statistical method, sample inhomogeneities standard deviation is satisfied by requiring, so its test weaving
The uniformity of product is good；Using textile is tested made of the above method, within the time that Check-Out Time span is 30 days, it is stable
Property meets CNAS-GL03：2006《Proficiency testing sample homogeneity and estimation of stability guide》Regulation, it can be seen that it is stable
Property is good；Material to be detected is dissolved using DMF solution, is added water-based PU or oiliness PU, is then added
0.5% defoamer, manufactured rubber cement, coated in fabric face, its stability of textile to be measured and uniformity, which is made, can accord with
Close CNAS-GL03：2006《Proficiency testing sample homogeneity and estimation of stability guide》Regulation.
Embodiment
Below by way of embodiment, the invention will be further described.
A kind of production method of standard specimen textile, including step in detail below：
(1), material to be detected is dissolved in DMF solution, and standard liquid is made；
(2), by standard liquid made from step (1), selected to add oiliness or water-based PU according to the property of standard liquid,
Under conditions of mixing speed 1000r/min, 0.5% defoamer is added, is stood, is defoamed, be made by vacuum defoaming device
Rubber cement, specifically, 0.5% weight for referring to addition defoamer accounts for standard liquid, adhesive and defoamer gross weight 0.5%；
(3) rubber cement made from step (2) uniformly, is coated in fabric face by printing equipment, through 100 DEG C of drying
1min, 120 DEG C of baking 30s, finished product.
Material to be detected includes decomposable asymmetric choice net aromatic amine dyestuff, the adjacent benzene of 0.1-0.2 parts by weight of 0.1-0.2 parts by weight
Dicarboxylic acid esters, the heavy metal of 0.025-0.1 parts by weight, 0.025-0.1 parts by weight APES or
The organotin of 0.025-0.1 parts by weight, the DMF solution for dissolving material to be detected are 0.1 weight
Part, the adhesive of addition is 99.8-99.9 parts by weight；
Specifically, decomposable asymmetric choice net aromatic amine dyestuff be 4- aminobphenyls, benzidine, 4- chloro-o-toluidines, 2- naphthylamines, to chlorobenzene
Amine, 2,4- diamino anisoles, 4,4 '-MDA, 3,3 '-dichloro-benzidine, 3,3 '-dimethyl -4,4 '-diamino
Base diphenyl-methane, 2- methoxyl group -5- methylanilines, 4,4 '-methylene-two-(2- chloroanilines), 4,4 '-diaminodiphenyl ether, 4,
4 '-diaminodiphenyl sulfide, ortho-aminotoluene, 2,4 di amino toluene, 2,4,5- trimethylanilines, o-aminoanisole, 2,4-
Dimethylaniline, 2,6- dimethylanilines, 3,3 '-dimethoxy benzidine, 3,3 '-dimethylbenzidine, 4- aminoazabenzols
In one or more；
Phthalic acid ester is diisononyl phthalate (DINP), phthalic acid two (2- ethyl hexyls) ester
(DEHP), di-n-octyl phthalate (DNOP), diisooctyl phthalate (DIDP), BBP(Butyl Benzyl Phthalate
(BBP), dibutyl phthalate (DBP), diisobutyl phthalate (DIBP), diamyl phthalate (DPP), neighbour
The C of phthalic acid two6-8One or more in branched alkyl ester (DIHP), DMEP (DMEP)；
APES is one in OPEO (OPEO), NPE (NPEO)
Kind is a variety of；
Heavy metal is the one or more in arsenic, cadmium, cobalt, chromium, copper, nickel, lead, antimony；
Organotin is Monobutyltin, dibutyl tin, the one or more of tributyl tin；
Adhesive is oiliness PU or water-based PU, and during mixing, water-based PU or oiliness PU is selected according to the property of test substance
Mixed；Defoamer is organic silicon solution or mineral oil.
Embodiment 1
A kind of production method of standard specimen textile, including step in detail below：
(1), by the 3,3- dimethoxy benzidines of 0.045 parts by weight, the 4- aminoazabenzols of 0.02 parts by weight, 0.035
The benzidine of parts by weight is dissolved in the DMF solution of 0.1 parts by weight, and standard liquid is made；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.8 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 2
A kind of production method of standard specimen textile, including step in detail below：
(1), by the o-aminoanisole of 0.05 parts by weight, 0.05 parts by weight 4,4 '-methylene-two-(2- chloroanilines),
The benzidine of 0.05 parts by weight is dissolved in the DMF solution of 0.1 parts by weight, and standard liquid is made；
(2), by standard liquid made from step (1), add in the water-based PU of 99.85 parts by weight, low whipping speed
Under conditions of 1000r/min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, glue is made
Slurry；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 3
A kind of production method of standard specimen textile, including step in detail below：
(1), by the 2,4- diamino anisoles of 0.075 parts by weight, 3,3 '-dimethyl -4,4 '-two of 0.039 parts by weight
Diaminodiphenylmethane, the 2,4 di amino toluene of 0.086 parts by weight are dissolved in the N,N-dimethylformamide solution of 0.1 parts by weight
In, standard liquid is made；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.9 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 4
A kind of production method of standard specimen textile, including step in detail below：
(1), the DNOP of 0.08 parts by weight, 0.02 parts by weight BBP are dissolved in the N of 0.1 parts by weight, N- dimethyl formyls
In amine aqueous solution, standard liquid is made；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.8 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 5
A kind of production method of standard specimen textile, including step in detail below：
(1), the DEHP of 0.13 parts by weight, 0.07 parts by weight DIDP are dissolved in the N of 0.1 parts by weight, N- dimethyl methyls
In amide solution, standard liquid is made；
(2), by standard liquid made from step (1), add in the water-based PU of 99.9 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 6
A kind of production method of standard specimen textile, including step in detail below：
(1), the DPP of 0.075 parts by weight, 0.075 parts by weight DIDP are dissolved in the N of 0.1 parts by weight, N- dimethyl methyls
In amide solution, standard liquid is made；
(2), by standard liquid made from step (1), add in the water-based PU of 99.85 parts by weight, low whipping speed
Under conditions of 1000r/min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, glue is made
Slurry；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 7
A kind of production method of standard specimen textile, including step in detail below：
(1), the OPEO of 0.025 parts by weight is dissolved in the DMF solution of 0.1 parts by weight, mark is made
Quasi- solution；
(2), by standard liquid made from step (1), add in the water-based PU of 99.8 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 8
A kind of production method of standard specimen textile, including step in detail below：
(1), the NPEO of 0.1 parts by weight is dissolved in the DMF solution of 0.1 parts by weight, standard is made
Solution；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.9 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 9
A kind of production method of standard specimen textile, including step in detail below：
(1), the OPEO of 0.04 parts by weight, 0.04 parts by weight NPEO are dissolved in the N of 0.1 parts by weight, N- dimethyl methyls
In amide solution, standard liquid is made；
(2), by standard liquid made from step (1), add in the water-based PU of 99.85 parts by weight, low whipping speed
Under conditions of 1000r/min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, glue is made
Slurry；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 10
A kind of production method of standard specimen textile, including step in detail below：
(1), by the cadmium of 0.04 parts by weight, 0.04 parts by weight copper dissolution 0.1 parts by weight N,N-dimethylformamide
In solution, standard liquid is made；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.85 parts by weight, low whipping speed
Under conditions of 1000r/min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, glue is made
Slurry；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 11
A kind of production method of standard specimen textile, including step in detail below：
(1), the nickel of the cobalt of 0.016 parts by weight, 0.009 parts by weight is dissolved in the N of 0.1 parts by weight, N- dimethyl formyls
In amine aqueous solution, standard liquid is made；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.8 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 12
A kind of production method of standard specimen textile, including step in detail below：
(1), the lead of the arsenic of 0.035 parts by weight, 0.065 parts by weight is dissolved in the N of 0.1 parts by weight, N- dimethyl formyls
In amine aqueous solution, standard liquid is made；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.9 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 13
A kind of production method of standard specimen textile, including step in detail below：
(1), the tributyl tin of 0.025 parts by weight is dissolved in the DMF solution of 0.1 parts by weight, made
Into standard liquid；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.8 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 14
A kind of production method of standard specimen textile, including step in detail below：
(1), the dibutyl tin of 0.09 parts by weight is dissolved in the DMF solution of 0.1 parts by weight, made
Into standard liquid；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.88 parts by weight, low whipping speed
Under conditions of 1000r/min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, glue is made
Slurry；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Embodiment 15
A kind of production method of standard specimen textile, including step in detail below：
(1), the Monobutyltin of 0.1 parts by weight is dissolved in the DMF solution of 0.1 parts by weight, is made
Standard liquid；
(2), by standard liquid made from step (1), add in the oiliness PU of 99.9 parts by weight, low whipping speed 1000r/
Under conditions of min, 0.5% organic silicon solution is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made；
(3) rubber cement made from step (2) uniformly, is coated in fabric table by high-precision ceramic roller printing equipment
Face, through 100 DEG C of drying 1min, 120 DEG C bakee 30s, finished product.
Using test textile made of the above method according to CNAS-GL03：2006《Proficiency testing sample homogeneity and steady
Qualitative evaluation guide》Regulation, using statistical method carry out uniformity testing, sample inhomogeneities standard deviation be satisfied by will
Ask, so the uniformity of its test textile is good；It is 30 in Check-Out Time span using textile is tested made of the above method
In it time, its stability meets CNAS-GL03：2006《Proficiency testing sample homogeneity and estimation of stability guide》Rule
It is fixed, it can be seen that its stability is good；Material to be detected is dissolved using DMF solution, adds water-based PU
Or oiliness PU, then add 0.5% organic silicon solution, manufactured rubber cement, coated in fabric face, be made textile to be measured its
Stability and uniformity can meet CNAS-GL03：2006《Proficiency testing sample homogeneity and estimation of stability guide》Rule
It is fixed.
The foregoing is only a preferred embodiment of the present invention, therefore the scope that the present invention is implemented can not be limited with this, i.e.,
The equivalent changes and modifications made according to scope of the present invention patent and description, it all should still belong to what patent of the present invention covered
In the range of.
Claims (10)
- A kind of 1. production method of standard specimen textile, it is characterised in that：Including step in detail below：(1), material to be detected is dissolved in DMF solution, and standard liquid is made；(2), standard liquid made from step (1) is added in adhesive, mixes and adds defoamer, defoaming is stood, rubber cement is made；(3) rubber cement made from step (2), is uniformly coated on fabric face, dried, finished product.
- A kind of 2. production method of standard specimen textile according to claim 1, it is characterised in that：The material bag to be detected Include decomposable asymmetric choice net aromatic amine dyestuff, the phthalic acid ester of 0.1-0.2 parts by weight, the 0.025-0.1 weight of 0.1-0.2 parts by weight Measure the organic of the heavy metal of number, the APES of 0.025-0.1 parts by weight or 0.025-0.1 parts by weight Tin, the DMF solution for dissolving material to be detected are 0.1 parts by weight, and the adhesive of addition is 99.8- 99.9 parts by weight.
- A kind of 3. production method of standard specimen textile according to claim 2, it is characterised in that：The decomposable asymmetric choice net aromatic amine Dyestuff is 4- aminobphenyls, benzidine, 4- chloro-o-toluidines, 2- naphthylamines, parachloroanilinum, 2,4- diamino anisoles, 4,4 '-two Diaminodiphenylmethane, 3,3 '-dichloro-benzidine, 3,3 '-dimethyl -4,4 '-MDA, 2- methoxyl group -5- methyl Aniline, 4,4 '-methylene-two-(2- chloroanilines), 4,4 '-diaminodiphenyl ether, 4,4 '-diaminodiphenyl sulfide, adjacent toluene Amine, 2,4 di amino toluene, 2,4,5- trimethylanilines, o-aminoanisole, 2,4- dimethylanilines, 2,6- dimethyl benzenes One or more in amine, 3,3 '-dimethoxy benzidine, 3,3 '-dimethylbenzidine, 4- aminoazabenzols.
- A kind of 4. production method of standard specimen textile according to claim 2, it is characterised in that：The phthalic acid ester For diisononyl phthalate, phthalic acid two (2- ethyl hexyls) ester, di-n-octyl phthalate, phthalic acid two Isodecyl ester, BBP(Butyl Benzyl Phthalate, dibutyl phthalate, diisobutyl phthalate, diamyl phthalate, The C of phthalic acid two6-8One or more in branched alkyl ester, DMEP.
- A kind of 5. production method of standard specimen textile according to claim 2, it is characterised in that：The heavy metal be arsenic, One or more in cadmium, cobalt, chromium, copper, nickel, lead, antimony.
- A kind of 6. production method of standard specimen textile according to claim 2, it is characterised in that：The alkyl phenol polyoxy second Alkene ether is the one or more in OPEO, NPE.
- A kind of 7. production method of standard specimen textile according to claim 2, it is characterised in that：The organotin is only son Ji Xi, dibutyl tin, the one or more of tributyl tin.
- 8. a kind of production method of test textile with Quality Control Function according to claim 1, its feature exist In：Described adhesive is oiliness PU or water-based PU, during mixing, selects water-based PU or oiliness PU to enter according to the property of test substance Row mixing.
- A kind of 9. production method of standard specimen textile according to claim 1, it is characterised in that：The step (2) includes By standard liquid made from step (1), selected to add oiliness or water-based PU, low whipping speed according to the property of standard liquid Under conditions of 1000r/min, 0.5% defoamer is added, is stood, is defoamed by vacuum defoaming device, rubber cement is made.
- A kind of 10. production method of standard specimen textile according to claim 1, it is characterised in that：The step (3) includes Rubber cement made from step (2) is uniformly coated in fabric face by printing equipment, through 100 DEG C of drying 1min, 120 DEG C of bakings 30s, finished product.