CN107460636B - A kind of production technology of cotton face-cloth - Google Patents
A kind of production technology of cotton face-cloth Download PDFInfo
- Publication number
- CN107460636B CN107460636B CN201611164342.2A CN201611164342A CN107460636B CN 107460636 B CN107460636 B CN 107460636B CN 201611164342 A CN201611164342 A CN 201611164342A CN 107460636 B CN107460636 B CN 107460636B
- Authority
- CN
- China
- Prior art keywords
- cotton
- compression set
- cotton layer
- face
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a kind of production technology of cotton face-cloth, using ES cotton and viscose glue cotton as the primary raw material of face-cloth, successively by mixing, dedusting, combing, paving cotton, compression, knitting, sizing and finishing process, the face-cloth produced is cotton face-cloth, with high-hygroscopicity and gas permeability, intensity is high, phozy not hair loss, good hand touch, it is nontoxic to human skin, it is water-fastness simultaneously to be unlikely to deform, it is reusable, it is suitble to be further processed into the amenities such as napkin, towel and cotton pads.
Description
Technical field
The present invention relates to cotton product manufacture fields, and in particular to be that a kind of can be used as the complete of cotton pads, towel and shawl
The production technology of cotton face-cloth.
Background technique
Non-woven fabrics is commonly used to fabricate into the amenities such as napkin, towel and cotton pads to be used in people's lives
In field, but find that the water imbibition of non-woven fabrics is not high in use, and be easy to appear soft flocks absorption showing on the skin
As causing skin pore blocking even allergy.The main component of non-woven fabrics is synthetic fibers, and raw material resources have non-renewable
Property, it can not reuse, not environmentally.In addition, the production of non-woven fabrics generallys use water jet process, the production equipment of water jet process at
This height, complex technical process.
In view of the above-mentioned problems, the applicant search out a kind of alternative non-woven fabrics material be used as production napkin, towel and
The raw material of cotton pads, and its production technology is studied, there is this case generation then.
Summary of the invention
The purpose of the present invention is to provide a kind of production technology of cotton face-cloth, the cotton face-cloth of production has high-hygroscopicity
And gas permeability, intensity are high, phozy not hair loss, good hand touch is nontoxic to human skin, at the same it is water-fastness be unlikely to deform, can
It reuses, is suitble to be further processed into the amenities such as napkin, towel and cotton pads.
In order to achieve the above objectives, solution of the invention is:
A kind of production technology of cotton face-cloth, comprising the following steps:
(1) mixing: equal by automatic plucker using the ES cotton of 10~20wt% and the viscose glue cotton of 80~90wt% as raw material
It is even to be mixed into mixing cotton；
(2) the mixing cotton in step (1) dedusting: is transported to the powder for removing in dust cleaning case and adhering on the mixing cotton
Dirt and impurity little particle, to improve the cleanliness of product；
(3) it combs: the mixing cotton feeding carding machine in step (2) Jing Guo dedusting is combed into thin netted cotton
Layer；
(4) it spreads cotton: the cotton layer in step (3) is delivered to be overlapped repeatedly on the paving cotton device of edge machine and is paved into
Cotton layer, the cotton dosage of the cotton layer are 60~500g/m2；
(5) compress: the cotton layer completed repeatedly is compressed via the compression set of edge machine, compressed every time
The overall thickness of cotton layer reduces 15-25%, until being 0.4~0.6mm by the overall thickness of the cotton layer；
(6) it is knitted: carrying out braiding reinforcing by the knitting device that compressed cotton layer enters edge machine, the braiding
Needlework density is 10~22 needles/inch；
(7) be formed: by by the cotton layer of step (6) knitting process be delivered to calender carry out thermocompression forming obtain half at
Product, the temperature of the thermocompression forming are 130~135 DEG C, and the pressure of the thermocompression forming is 1-2 kilograms；
(8) it carries out disinfection, cut to get to the cotton face-cloth after cooling down the semi-finished product obtained by step (7) at room temperature.
In step (5), the compression set of the edge machine is compressed by the first compression set, the second compression set and third to be filled
Composition is set, is connected with conveyer belt between first compression set, second compression set and the third compression set, is spread
The good cotton layer is successively carried out via first compression set, second compression set and the third compression set
Compression.
In step (6), needlework used in the braiding are pure cotton line of the needlework thickness in 75D~300D.
In step (6), needlework used in the braiding are the yarn that is had by the compressed cotton layer.
After the knitting process of step (6), remaining cotton-wool is recycled by exhaust column and is conveyed again the cotton layer
It is recycled to the automatic plucker.
After adopting the above technical scheme, a kind of production technology of cotton face-cloth of the present invention, using loop bonding technique, with ES cotton and
Primary raw material of the viscose glue cotton as face-cloth, the face-cloth produced are cotton face-cloth, have high-hygroscopicity and gas permeability, and intensity is high,
Phozy not hair loss, good hand touch is nontoxic to human skin, at the same it is water-fastness be unlikely to deform, it is reusable, be suitble into one
Step is processed as the amenities such as napkin, towel and cotton pads.
Further, in step (6), needlework used in the braiding are the yarn that is had by the compressed cotton layer
Line, needlework of the cotton yarn being had using cotton layer itself as braiding, avoidable there is a phenomenon where broken yarns in the weaving process.
Specific embodiment
In order to further explain the technical solution of the present invention, being explained in detail below by specific embodiment the present invention
It states.
Embodiment one
A kind of production technology of cotton face-cloth, comprising the following steps:
(1) it mixing: using the ES cotton of 10wt% and the viscose glue cotton of 90wt% as raw material, is uniformly mixed by automatic plucker
Mix cotton；
(2) the mixing cotton in step (1) dedusting: is transported to the dust and impurity for removing in dust cleaning case and adhering on mixing cotton
Little particle, to improve the cleanliness of product；
(3) it combs: the mixing cotton feeding carding machine in step (2) Jing Guo dedusting is combed into thin netted cotton layer；
(4) it spreads cotton: the cotton layer in step (3) is delivered to be overlapped repeatedly on the paving cotton device of edge machine and is paved into cotton
Layer, the cotton dosage of cotton layer are 60g/m2；
(5) compress: the cotton layer completed repeatedly is compressed via the compression set of edge machine, the compression set of edge machine
It is made of the first compression set, the second compression set and third compression set, the first compression set, the second compression set and third
Conveyer belt is connected between compression set, the cotton layer completed is successively via the first compression set, the second compression set and third
Compression set is compressed, and the overall thickness of each compressed cotton layer reduces 15-25%, until being by the overall thickness of cotton layer
0.4mm；
(6) it is knitted: entering the knitting device of edge machine by compressed cotton layer and carry out braiding reinforcing, weave used
Needlework are pure cotton line of the needlework thickness in 75D, and the needlework density of braiding is 10 needles/inch, and cotton layer is remaining after braiding
Cotton-wool recycles by exhaust column and is delivered to automatic plucker again and recycled；
(7) be formed: by by the cotton layer of step (6) knitting process be delivered to calender carry out thermocompression forming obtain half at
Product, the temperature of thermocompression forming are 130 DEG C, and the pressure of thermocompression forming is 1 kilogram；
(8) it carries out disinfection, cut after cooling down the semi-finished product obtained by step (7) at room temperature, being processed into specification is 10cm
The cotton face-cloth of × 10cm.
There is high-hygroscopicity and gas permeability by the cotton face-cloth that the present invention produces, intensity is high, phozy not hair loss, feel
It is good, it is nontoxic to human skin, while it is water-fastness be unlikely to deform, it is reusable, can be used as cotton pads use.
Embodiment two
A kind of production technology of cotton face-cloth, comprising the following steps:
(1) it mixing: using the ES cotton of 15wt% and the viscose glue cotton of 85wt% as raw material, is uniformly mixed by automatic plucker
Mix cotton；
(2) the mixing cotton in step (1) dedusting: is transported to the dust and impurity for removing in dust cleaning case and adhering on mixing cotton
Little particle, to improve the cleanliness of product；
(3) it combs: the mixing cotton feeding carding machine in step (2) Jing Guo dedusting is combed into thin netted cotton layer；
(4) it spreads cotton: the cotton layer in step (3) is delivered to be overlapped repeatedly on the paving cotton device of edge machine and is paved into cotton
Layer, the cotton dosage of cotton layer are 280g/m2；
(5) compress: the cotton layer completed repeatedly is compressed via the compression set of edge machine, the compression set of edge machine
It is made of the first compression set, the second compression set and third compression set, the first compression set, the second compression set and third
Conveyer belt is connected between compression set, the cotton layer completed is successively via the first compression set, the second compression set and third
Compression set is compressed, and the overall thickness of each compressed cotton layer reduces 15-25%, until being by the overall thickness of cotton layer
0.5mm；
(6) it is knitted: entering the knitting device of edge machine by compressed cotton layer and carry out braiding reinforcing, weave used
Needlework are pure cotton line of the needlework thickness in 200D, and the needlework density of braiding is 16 needles/inch, and cotton layer is after braiding, residual
Cotton-wool pass through exhaust column and recycle and be delivered to automatic plucker again and recycled；
(7) be formed: by by the cotton layer of step (6) knitting process be delivered to calender carry out thermocompression forming obtain half at
Product, the temperature of thermocompression forming are 130 DEG C, and the pressure of thermocompression forming is 2 kilograms；
(8) it carries out disinfection, cut after cooling down the semi-finished product obtained by step (7) at room temperature, being processed into specification is 20cm
The cotton face-cloth of × 20cm.
There is high-hygroscopicity and gas permeability by the cotton face-cloth that the present invention produces, intensity is high, phozy not hair loss, feel
It is good, it is nontoxic to human skin, while it is water-fastness be unlikely to deform, it is reusable, can be used as napkin use.
Embodiment three
A kind of production technology of cotton face-cloth, comprising the following steps:
(1) it mixing: using the ES cotton of 20wt% and the viscose glue cotton of 80wt% as raw material, is uniformly mixed by automatic plucker
Mix cotton；
(2) the mixing cotton in step (1) dedusting: is transported to the dust and impurity for removing in dust cleaning case and adhering on mixing cotton
Little particle, to improve the cleanliness of product；
(3) it combs: the mixing cotton feeding carding machine in step (2) Jing Guo dedusting is combed into thin netted cotton layer；
(4) it spreads cotton: the cotton layer in step (3) is delivered to be overlapped repeatedly on the paving cotton device of edge machine and is paved into cotton
Layer, the cotton dosage of cotton layer are 500g/m2；
(5) compress: the cotton layer completed repeatedly is compressed via the compression set of edge machine, the compression set of edge machine
It is made of the first compression set, the second compression set and third compression set, the first compression set, the second compression set and third
Conveyer belt is connected between compression set, the cotton layer completed is successively via the first compression set, the second compression set and third
Compression set is compressed, and the overall thickness of each compressed cotton layer reduces 15-25%, until being by the overall thickness of cotton layer
0.6mm；
(6) it is knitted: entering the knitting device of edge machine by compressed cotton layer and carry out braiding reinforcing, weave used
Needlework are pure cotton line of the needlework thickness in 300D, and the needlework density of braiding is 22 needles/inch, and cotton layer is after braiding, residual
Cotton-wool pass through exhaust column and recycle and be delivered to automatic plucker again and recycled；
(7) be formed: by by the cotton layer of step (6) knitting process be delivered to calender carry out thermocompression forming obtain half at
Product, the temperature of thermocompression forming are 135 DEG C, and the pressure of thermocompression forming is 2 kilograms；
(8) it carries out disinfection, cut after cooling down the semi-finished product obtained by step (7) at room temperature, being processed into specification is 50cm
The cotton face-cloth of × 50cm.
There is high-hygroscopicity and gas permeability by the cotton face-cloth that the present invention produces, intensity is high, phozy not hair loss, feel
It is good, it is nontoxic to human skin, while it is water-fastness be unlikely to deform, it is reusable, can be used as towel use.
Example IV
A kind of production technology of cotton face-cloth, comprising the following steps:
(1) it mixing: using the ES cotton of 20wt% and the viscose glue cotton of 80wt% as raw material, is uniformly mixed by automatic plucker
Mix cotton；
(2) the mixing cotton in step (1) dedusting: is transported to the dust and impurity for removing in dust cleaning case and adhering on mixing cotton
Little particle, to improve the cleanliness of product；
(3) it combs: the mixing cotton feeding carding machine in step (2) Jing Guo dedusting is combed into thin netted cotton layer；
(4) it spreads cotton: the cotton layer in step (3) is delivered to be overlapped repeatedly on the paving cotton device of edge machine and is paved into cotton
Layer, the cotton dosage of cotton layer are 500g/m2；
(5) compress: the cotton layer completed repeatedly is compressed via the compression set of edge machine, the compression set of edge machine
It is made of the first compression set, the second compression set and third compression set, the first compression set, the second compression set and third
Conveyer belt is connected between compression set, the cotton layer completed is successively via the first compression set, the second compression set and third
Compression set is compressed, and the overall thickness of each compressed cotton layer reduces 15-25%, until being by the overall thickness of cotton layer
0.6mm；
(6) it is knitted: entering the knitting device of edge machine by compressed cotton layer and carry out braiding reinforcing, weave used
The yarn that needlework are had by cotton layer itself, the needlework density of braiding are 22 needles/inch, and cotton layer is after braiding, residual
Cotton-wool pass through exhaust column and recycle and be delivered to automatic plucker again and recycled；
(7) be formed: by by the cotton layer of step (6) knitting process be delivered to calender carry out thermocompression forming obtain half at
Product, the temperature of thermocompression forming are 135 DEG C, and the pressure of thermocompression forming is 2 kilograms；
(8) it carries out disinfection, cut after cooling down the semi-finished product obtained by step (7) at room temperature, being processed into specification is 50cm
The cotton face-cloth of × 50cm.
There is high-hygroscopicity and gas permeability by the cotton face-cloth that the present invention produces, intensity is high, phozy not hair loss, feel
It is good, it is nontoxic to human skin, while it is water-fastness be unlikely to deform, it is reusable, can be used as towel use.
Automatic plucker, dust cleaning case, carding machine, edge machine and calender in the present invention are that the known of this field sets
It is standby.
Above-described embodiment and non-limiting product form and style of the invention, the ordinary skill people of any technical field
The appropriate changes or modifications that member does it, all should be regarded as not departing from patent category of the invention.
Claims (5)
1. a kind of production technology of cotton face-cloth, it is characterised in that: the following steps are included:
(1) it mixing: using the ES cotton of 10~20wt% and the viscose glue cotton of 80~90wt% as raw material, is uniformly mixed by automatic plucker
It is combined into mixing cotton；
(2) dedusting: the mixing cotton in step (1) is transported to remove in dust cleaning case the dust adhered on the mixing cotton and
Impurity little particle；
(3) it combs: the mixing cotton feeding carding machine in step (2) Jing Guo dedusting is combed into thin netted cotton layer；
(4) it spreads cotton: the cotton layer in step (3) is delivered to be overlapped repeatedly on the paving cotton device of edge machine and is paved into cotton
Layer, the cotton dosage of the cotton layer are 60~500g/m2；
(5) compress: the cotton layer completed repeatedly is compressed via the compression set of edge machine, each compressed cotton
The overall thickness of layer reduces 15-25%, until being 0.4~0.6mm by the overall thickness of the cotton layer；
(6) it is knitted: carrying out braiding reinforcing, the needlework of the braiding by the knitting device that compressed cotton layer enters edge machine
Density is 10~22 needles/inch；
(7) it is formed: calender progress thermocompression forming will be delivered to by the cotton layer of step (6) knitting process and obtain semi-finished product,
The temperature of the thermocompression forming is 130~135 DEG C, and the pressure of the thermocompression forming is 1-2 kilograms；
(8) it carries out disinfection, cut to get to the cotton face-cloth after cooling down the semi-finished product obtained by step (7) at room temperature.
2. a kind of production technology of cotton face-cloth according to claim 1, it is characterised in that: in step (5), the tape edge
The compression set of machine is made of the first compression set, the second compression set and third compression set, first compression set, institute
It states and is connected with conveyer belt between the second compression set and the third compression set, the cotton layer completed is successively via described
First compression set, second compression set and the third compression set are compressed.
3. a kind of production technology of cotton face-cloth according to claim 1, it is characterised in that: in step (6), the braiding
Needlework used are pure cotton line of the needlework thickness in 75D~300D.
4. a kind of production technology of cotton face-cloth according to claim 1, it is characterised in that: in step (6), the braiding
The yarn that needlework used are had for the compressed cotton layer of process.
5. a kind of production technology of cotton face-cloth according to claim 1, it is characterised in that: the cotton layer passes through step
(6) after knitting process, remaining cotton-wool recycles by exhaust column and is delivered to the automatic plucker again and recycled.