CN107459801A - A kind of LED materials for filtering gold-tinted - Google Patents
A kind of LED materials for filtering gold-tinted Download PDFInfo
- Publication number
- CN107459801A CN107459801A CN201710715441.3A CN201710715441A CN107459801A CN 107459801 A CN107459801 A CN 107459801A CN 201710715441 A CN201710715441 A CN 201710715441A CN 107459801 A CN107459801 A CN 107459801A
- Authority
- CN
- China
- Prior art keywords
- tinted
- parts
- gold
- led
- filtering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to technical field of polymer materials, and in particular to a kind of LED materials for filtering gold-tinted.A kind of LED materials of filtering gold-tinted of the present invention, it includes the raw material of following mass parts:60 100 parts of base material, 1 13 parts of phytosterol, 0.1 1.0 parts of ultra-violet absorber, 0.1 0.8 parts of stannous octoate, 0.2 0.4 parts of dispersant DP310,2 26 parts of deionized water, wherein, the phytosterol is one or more kinds of mixtures in expoxy propane, neodymia, polyvinyl alcohol and glass fibre.The excellent in optical properties such as the filtering gold-tinted of LED materials of the filtering gold-tinted that the present invention is produced, light transmittance, mist degree, can effectively filter and eliminate gold-tinted caused by LED, mitigate relieving eye strain, eyes is exempted from gold-tinted injury.
Description
Technical field
The present invention relates to technical field of polymer materials, and in particular to a kind of LED materials for filtering gold-tinted and its preparation side
Method.
Background technology
The worsening reality of prior art energy crisis, greenhouse effects and ecological environment, promotes people to find energy-conservation
Illuminate substitute.Light emitting diode (LightEmittingDiode, LED), because its small volume, long lifespan, colour developing are abundant and prominent
Many advantages, such as energy-conserving and environment-protective characteristic gone out, obtains increasingly extensive application in fields such as display, traffic, electrical equipment and illuminations, is me
One of key technology of state's energy-saving and emission-reduction, clean manufacturing and sustainable development.China's LED industry has begun to take shape and with good
Growth momentum.But general LED is because light source is white light, and gold-tinted is also easy to produce, causes eye fatigue, it is therefore desirable to disappear
Remove.In presently relevant document and patent and the report about filtering gold-tinted in LED is had not seen, and in traditional glass production technology
Reach similar effect using neodymia rare earth, but because LED material category is more, there are the materials such as PC, PMMA, PCTG,
The refractive index of material is different, causes modified material transmissivity and mist degree gap larger, therefore the extinction filler for finding matching shows
Obtain particularly important.
The content of the invention
In order to overcome shortcoming and defect present in prior art, it is an object of the invention to provide a kind of filtering gold-tinted
The excellent in optical properties such as LED materials, the filtering gold-tinted of LED materials of the filtering gold-tinted that the present invention is produced, light transmittance, mist degree,
It can effectively filter and eliminate gold-tinted caused by LED, mitigate relieving eye strain, protect eyes, eyes is exempted from gold-tinted injury.
Another object of the present invention is to provide a kind of preparation method for the LED materials for filtering gold-tinted, material preparation method technique letter
Single, convenient operation and control, steady quality, high yield rate, production efficiency is high, and production cost is low, can large-scale industrial production.
The purpose of the present invention is achieved through the following technical solutions:
A kind of LED materials for filtering gold-tinted, it includes the raw material of following mass parts:
Base material 60-100 parts,
Phytosterol 1-13 parts,
Ultra-violet absorber 0.1-1.0 parts,
Stannous octoate 0.1-0.8 parts,
Dispersant DP310 0.2-0.4 parts,
Deionized water 2-26 parts,
Wherein, the phytosterol is one or more kinds of in expoxy propane, neodymia, polyvinyl alcohol and glass fibre
Mixture.
Preferably, the LED materials of described a kind of filtering gold-tinted, it includes the raw material of following mass parts:
Base material 70-90 parts,
Phytosterol 5-10 parts,
Ultra-violet absorber 0.2-0.8 parts,
Stannous octoate 0.3-0.6 parts,
Dispersant DP310 0.2-0.4 parts,
Deionized water 10-20 parts,
Wherein, the phytosterol is one or more kinds of in expoxy propane, neodymia, polyvinyl alcohol and glass fibre
Mixture.
The present invention uses DP310 effectively to reduce nethike embrane blocking as dispersant, lower the back-pressure in extruder and reach
To processing more efficiently;Screw speed can be increased in processing, while can also reach more preferable dispersive property;Can be effective
Pigment agglomerates are broken up, reduce spot, increase material glossiness;It can bring product more stable quality, reduce tie rod fracture
Occur, so as to reduce percent defective, improve the quality of material, reduce production cost.
Preferably, the base material is one kind in PC, PMMA, COP, PETG, PCTG, ABS, PS and AS.
Preferably, the ultra-violet absorber is organosilicon ultra-violet absorber or acrylate ultra-violet absorber.Have
Machine silicon ultra-violet absorber or acrylate ultra-violet absorber, the relatively general ultra-violet absorber of organosilicon ultra-violet absorber
With efficiency high, heat resistance especially protrusion, the control of chromaticness stabilization, non yellowing, particle microscopic pattern is finer, particle diameter distribution is narrow
Significant advantage, material mechanical performance and interior impact property are excellent.
Preferably, the stannous octoate is 1076 and 168 mixture.1076 oxidants and the collaboration of 168 oxidants use,
Volatility is low, and hydrolytic resistance is outstanding, can effectively prevent the change of molecular weight caused by oxidative degradation in mixing and granulation process(Such as
Chain rupture and crosslinking), prevent color change.
A kind of preparation method for the LED materials for filtering gold-tinted, comprises the following steps:
Step A, the deionized water and phytosterol for taking prescription quality part are dispersed in large beaker, are heated to 80-90 while stirring
DEG C, reach target temperature after, static isothermal holding 1.5-2.5h, then air cooling dry, until supernatant surplus is 8-12ml
When, directly supernatant is outwelled, the residue in large beaker is transferred to place in baking oven in iron ware and toasted, toasts drying
After the completion of, the powder of gained is taken out, is cooled to room temperature, it is standby;
Step B, the standby powder in the ultra-violet absorber, stannous octoate, DP310 and step A of prescription quality part is taken to add respectively
Enter in homogenizer and mixed, to after being thoroughly mixed, stop stirring, take mixed powder standby;
Step C, by mixed powder obtained by step B and the resin of prescription quality part is taken to add high speed machine, after being uniformly mixed,
Extruding pelletization in extruder.
Preferably, the drying process mode in the step A is:The residue first is placed in into 110-130 DEG C of baking oven to dry
Roasting 11-13h, then go to 290-310 DEG C of baking oven baking 22-26h.
Because after supernatant is outwelled, residual moisture is still relatively more, may be acutely now if too high-temperature toasts
Boiling, iron ware is gone out, 110-130 DEG C is mainly removed free water;290-310 DEG C is in order to which further remove may be with
The deionized water of Hydrogenbond, two steps are different because extrusion or injection ceiling temperature at 300 DEG C, if water at a temperature of this
Can't get out just does not influence on system, so only needing to remove less than 310 DEG C of moisture.
Preferably, the agitating mode in the step B stops 30s often to stir 3min, and it is extremely complete so to repeat stirring 4-6 time
After full mixing, stop stirring.By batch type, material mixing is more abundant, and mixing is more uniformly distributed.Stirred using intermittence
The advantages of be:Because continuously stirring, quickly, interior heat can cause material to have certain degraded to heat, and this material belongs to optical material,
Slight change can all produce certain influence to follow-up spectrogram, and the degraded of material is avoided using batch type.
Preferably, a kind of preparation method for the LED materials for filtering gold-tinted, five sections of extrusion temperatures difference of the extruder
It is:One area's temperature is 200-230 DEG C, and two area's temperature are 210-230 DEG C, and three area's temperature are 210-230 DEG C, and four area's temperature are 210-
265 DEG C, five area's temperature are 210-260 DEG C, and the rotating speed of the extruder is 360-440r/min.
The beneficial effects of the present invention are:Filtering gold-tinted, the printing opacity of the LED materials for the filtering gold-tinted that the present invention is produced
The excellent in optical properties such as rate, mist degree, it can effectively filter and eliminate gold-tinted caused by LED, mitigate relieving eye strain, protect eye
Eyeball, eyes are made to exempt from gold-tinted injury.The centre wavelength of gold-tinted is 570nm, by the present invention in that being used as plant by the use of the compound of neodymium
Sterol, gold-tinted of the wavelength in 560-590nm can must be effectively filtered away, filtering gold-tinted is thorough, limited can prevent that eyes are yellow
Light injures;Using organosilicon ultra-violet absorber or acrylate ultra-violet absorber, efficiency high, heat resistance are especially prominent, color
Matter stabilization, non yellowing, the significant advantage that the control of particle microscopic pattern is finer, particle diameter distribution is narrow, material mechanical performance and interior punching
Hit excellent performance.
A kind of preparation method of the LED materials of filtering gold-tinted of the present invention, the material preparation method technique is simple, operation control
System is convenient, steady quality, high yield rate, and production efficiency is high, and production cost is low, can large-scale industrial production.The present invention uses
DP310 can effectively reduce all plugs of nethike embrane, lower the back-pressure in extruder and reach processing more efficiently as dispersant;
Screw speed can be increased in processing, while can also reach more preferable dispersive property;Pigment agglomerates can be effectively broken up, are subtracted
Few spot, increases material glossiness;It can bring product more stable quality, the generation of tie rod fracture be reduced, so as to reduce waste product
Rate, the quality of material is improved, reduce production cost.
Embodiment
In order that technical problems, technical solutions and advantageous effects to be solved by the present invention are more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only explaining
The present invention, it is not intended to limit the present invention.
A kind of LED materials for filtering gold-tinted provided by the invention, can effectively filter gold-tinted caused by eliminating LED, subtract
Light relieving eye strain, protect eyes, eyes are made to exempt from gold-tinted injury.It is yellow another object of the present invention is to provide a kind of filtering
The preparation method of the LED materials of light, the material preparation method technique is simple, convenient operation and control, steady quality, high yield rate,
Production efficiency is high, and production cost is low, can large-scale industrial production.
The present invention is achieved through the following technical solutions:
A kind of LED materials for filtering gold-tinted, it includes the raw material of following mass parts:
Base material 60-100 parts,
Phytosterol 1-13 parts,
Ultra-violet absorber 0.1-1.0 parts,
Stannous octoate 0.1-0.8 parts,
Dispersant DP310 0.2-0.4 parts,
Deionized water 2-26 parts,
Wherein, phytosterol is one or more kinds of mixing in expoxy propane, neodymia, polyvinyl alcohol and glass fibre
Thing.
In other embodiments, the LED materials of gold-tinted are filtered, the raw material of following mass parts can also be included:
Base material 70-90 parts,
Phytosterol 5-10 parts,
Ultra-violet absorber 0.2-0.8 parts,
Stannous octoate 0.3-0.6 parts,
Dispersant DP3100.2-0.4 parts,
Deionized water 10-20 parts,
Wherein, phytosterol is one or more kinds of mixing in expoxy propane, neodymia, polyvinyl alcohol and glass fibre
Thing.
The present invention uses DP310 effectively to reduce nethike embrane blocking as dispersant, lower the back-pressure in extruder and reach
To processing more efficiently;Screw speed can be increased in processing, while can also reach more preferable dispersive property;Can be effective
Pigment agglomerates are broken up, reduce spot, increase material glossiness;It can bring product more stable quality, reduce tie rod fracture
Occur, so as to reduce percent defective, improve the quality of material, reduce production cost.
Base material is one kind in PC, PMMA, COP, PETG, PCTG, ABS, PS and AS.
Ultra-violet absorber is organosilicon ultra-violet absorber or acrylate ultra-violet absorber.
Organosilicon ultra-violet absorber or acrylate ultra-violet absorber, organosilicon ultra-violet absorber are relatively general purple
There is ultraviolet absorbers efficiency high, heat resistance especially protrusion, chromaticness stabilization, non yellowing, particle microscopic pattern to control finer, grain
The significant advantage of footpath narrowly distributing, material mechanical performance and interior impact property are excellent.
Stannous octoate is 1076 and 168 mixture.1076 oxidants and the collaboration of 168 oxidants use, and volatility is low, resistance to
It is water-disintegrable outstanding, it can effectively prevent the change of molecular weight caused by oxidative degradation in mixing and granulation process(Such as chain rupture and friendship
Connection), prevent color change.
The preparation method of the LED materials of gold-tinted is filtered, is comprised the following steps:
Step A, the deionized water and phytosterol for taking prescription quality part are dispersed in large beaker, are heated to 80-90 while stirring
DEG C, reach target temperature after, static isothermal holding 1.5-2.5h, then air cooling dry, until supernatant surplus is 8-12ml
When, directly supernatant is outwelled, the residue in large beaker is transferred to place in baking oven in iron ware and toasted, toasts drying
After the completion of, the powder of gained is taken out, is cooled to room temperature, it is standby;
Step B, the standby powder in the ultra-violet absorber, stannous octoate, DP310 and step A of prescription quality part is taken to add respectively
Enter in homogenizer and mixed, to after being thoroughly mixed, stop stirring, take mixed powder standby;
Step C, by mixed powder obtained by step B and the resin of prescription quality part is taken to add high speed machine, after being uniformly mixed,
Extruding pelletization in extruder.
Drying process mode in step A is:The residue is first placed in 110-130 DEG C of baking oven baking 11-13h, so
After go to 290-310 DEG C of baking oven baking 22-26h.
Because after supernatant is outwelled, residual moisture is still relatively more, may be acutely now if too high-temperature toasts
Boiling, iron ware is gone out, 110-130 DEG C is mainly removed free water;290-310 DEG C is in order to which further remove may be with
The deionized water of Hydrogenbond, two steps are different because extrusion or injection ceiling temperature at 300 DEG C, if water at a temperature of this
Can't get out just does not influence on system, so only needing to remove less than 310 DEG C of moisture.
Agitating mode in step B stops 30s, so repeats stirring 4-6 times to after being thoroughly mixed, stop often to stir 3min
Only stir.By batch type, material mixing is more abundant, and mixing is more uniformly distributed.It is using the advantages of intermittence stirring:Cause
To continuously stir, quickly, interior heat can cause material to have certain degraded to heat, and this material belongs to optical material, slight change
Certain influence can all be produced to follow-up spectrogram, the degraded of material is avoided using batch type.
Five sections of extrusion temperatures of extruder are respectively:One area's temperature be 200-230 DEG C, two area's temperature be 210-230 DEG C, three
Area's temperature is 210-230 DEG C, and four area's temperature are 210-265 DEG C, and five area's temperature are 210-260 DEG C, and the rotating speed of the extruder is
360-440r/min。
The beneficial effects of the present invention are:Filtering gold-tinted, the printing opacity of the LED materials for the filtering gold-tinted that the present invention is produced
The excellent in optical properties such as rate, mist degree, it can effectively filter and eliminate gold-tinted caused by LED, mitigate relieving eye strain, protect eye
Eyeball, eyes are made to exempt from gold-tinted injury.The centre wavelength of gold-tinted is 570nm, by the present invention in that being used as plant by the use of the compound of neodymium
Sterol, gold-tinted of the wavelength in 560-590nm can must be effectively filtered away, filtering gold-tinted is thorough, limited can prevent that eyes are yellow
Light injures;Using organosilicon ultra-violet absorber or acrylate ultra-violet absorber, efficiency high, heat resistance are especially prominent, color
Matter stabilization, non yellowing, the significant advantage that the control of particle microscopic pattern is finer, particle diameter distribution is narrow, material mechanical performance and interior punching
Hit excellent performance.
A kind of preparation method of the LED materials of filtering gold-tinted of the present invention, the material preparation method technique is simple, operation control
System is convenient, steady quality, high yield rate, and production efficiency is high, and production cost is low, can large-scale industrial production.The present invention uses
DP310 can effectively reduce all plugs of nethike embrane, lower the back-pressure in extruder and reach processing more efficiently as dispersant;
Screw speed can be increased in processing, while can also reach more preferable dispersive property;Pigment agglomerates can be effectively broken up, are subtracted
Few spot, increases material glossiness;It can bring product more stable quality, the generation of tie rod fracture be reduced, so as to reduce waste product
Rate, the quality of material is improved, reduce production cost.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
All any modification, equivalent and improvement made within refreshing and principle etc., should be included in the scope of the protection.
Claims (1)
- A kind of 1. LED materials for filtering gold-tinted, it is characterised in that:It includes the raw material of following mass parts:Base material 60-100 parts,Phytosterol 1-13 parts,Ultra-violet absorber 0.1-1.0 parts,Stannous octoate 0.1-0.8 parts,Dispersant DP310 0.2-0.4 parts,Deionized water 2-26 parts,Wherein, the phytosterol is one or more kinds of in expoxy propane, neodymia, polyvinyl alcohol and glass fibre Mixture.