CN107459763A - A kind of novel noise reduction phenolic aldehyde foam thermal insulation material - Google Patents
A kind of novel noise reduction phenolic aldehyde foam thermal insulation material Download PDFInfo
- Publication number
- CN107459763A CN107459763A CN201710566953.8A CN201710566953A CN107459763A CN 107459763 A CN107459763 A CN 107459763A CN 201710566953 A CN201710566953 A CN 201710566953A CN 107459763 A CN107459763 A CN 107459763A
- Authority
- CN
- China
- Prior art keywords
- parts
- noise reduction
- thermal insulation
- insulation material
- phenolic aldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of novel noise reduction phenolic aldehyde foam thermal insulation material, it is composed of the following raw materials by weight:50 70 parts of phenolic resin;46 parts of curing agent;7 10 parts of foaming agent;35 parts of surfactant;48 parts of zeolite;15 parts of CNT, viscosity modifier;Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid;Viscosity modifier is dioctyl phthalate;Foam modifier is aliphatic alcohol polyethenoxy.There is the present invention high insulating effect, resistance to compression, noise reduction to have significantly advantage.
Description
Technical field
The present invention relates to a kind of novel noise reduction phenolic aldehyde foam thermal insulation material.
Background technology
Traditional heat-insulating heat-preserving material such as polyurethane foam, polystyrene foam etc. meet fire easily burning, and are produced during burning
Raw dense smoke and poisonous, pernicious gas cause serious harm to the mankind.In recent years, fire incident happened occasionally, and caused people
Member's injures and deaths and property massive losses.Therefore many departments not only consider its heat-proof quality, while also examine when using heat-barrier material
Consider its combination property used.Phenolic foam is a kind of novel heat insulation material, have lightweight, low toxicity, fire retardant, low cigarette, every
The advantages that heat, high-low temperature resistant, it is applied to every field more and more widely.Phenol formaldehyde foam is in the case of high temperature or chance fire, table
Face occurs charing and internal layer is played a protective role, therefore can keep good heat-proof quality, is heat preservation fireproofing material of new generation.Phenol
Aldehyde foam is also more and more extensive as energy-saving material utilization under construction.Although the hole of phenol formaldehyde foam itself can noise reduction, then
Noise reduction coefficient is not also very high, and the soundproof effect of phenolic foam board stills need to strengthen.In order to improve noise reduction, typically make
Used time, acoustical cotton is pasted on phenol formaldehyde foam surface, technics comparing is cumbersome.Or phenol formaldehyde foam is placed in mould during foaming
In tool, by mold structure, phenol formaldehyde foam is set to be internally formed high-efficiency sound-absorbing hole, but the intensity of phenolic foam board can be influenceed.
The content of the invention
Goal of the invention:The invention aims to solve deficiency of the prior art, there is provided a kind of high insulating effect, resist
Pressure, noise reduction have a kind of novel noise reduction phenolic aldehyde foam thermal insulation material significantly lifted.
Technical scheme:A kind of novel noise reduction phenolic aldehyde foam thermal insulation material of the present invention, is composed of the following raw materials by weight:
Phenolic resin 50-70 parts;Curing agent 4-6 parts;Foaming agent 7-10 parts;Surfactant 3-5 parts;Zeolite 4-8 parts;Carbon is received
Mitron 1-5 parts, viscosity modifier 2-4 parts;
Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid.
Further improvement of the present invention is that viscosity modifier is dioctyl phthalate.
Further improvement of the present invention is that foam modifier is aliphatic alcohol polyethenoxy.
Beneficial effect:
Zeolite has microcellular structure, adds in phenol formaldehyde foam, while phenol formaldehyde foam bulk strength is improved, also improves entirety
Noise reduction;CNT has the characteristic of the Hao ﹑ ﹑ of the Nai Mo Hua of the Nai Lao ﹑ weatherabilities of Qiang Du Gao ﹑ Ren, improves phenol formaldehyde foam
The compression strength and resistance to ag(e)ing of plate.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
Embodiment 1,
Raw material:A kind of novel noise reduction phenolic aldehyde foam thermal insulation material, is composed of the following raw materials by weight:
50 parts of phenolic resin;4 parts of curing agent;7 parts of foaming agent;3 parts of surfactant;4 parts of zeolite;1 part of CNT, viscosity
2 parts of conditioning agent;
Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid;Viscosity modifier is dioctyl phthalate;Foam modifier is fat
Fat alcohol polyoxyethylene.
Embodiment 2,
Raw material:A kind of novel noise reduction phenolic aldehyde foam thermal insulation material, is composed of the following raw materials by weight:
50 parts of phenolic resin;5 parts of curing agent;8 parts of foaming agent;4 parts of surfactant;5 parts of zeolite;3 parts of CNT, viscosity
3 parts of conditioning agent;
Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid;Viscosity modifier is dioctyl phthalate;Foam modifier is fat
Fat alcohol polyoxyethylene.
Embodiment 3,
Raw material:A kind of novel noise reduction phenolic aldehyde foam thermal insulation material, is composed of the following raw materials by weight:
60 parts of phenolic resin;4 parts of curing agent;7 parts of foaming agent;3 parts of surfactant;4 parts of zeolite;1 part of CNT, glue
Spend 2 parts of conditioning agent;
Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid;Viscosity modifier is dioctyl phthalate;Foam modifier is fat
Fat alcohol polyoxyethylene.
Embodiment 4,
Raw material:A kind of novel noise reduction phenolic aldehyde foam thermal insulation material, is composed of the following raw materials by weight:
55 parts of phenolic resin;5 parts of curing agent;7 parts of foaming agent;5 parts of surfactant;5 parts of zeolite;3 parts of CNT, glue
Spend 3 parts of conditioning agent;
Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid;Viscosity modifier is dioctyl phthalate;Foam modifier is fat
Fat alcohol polyoxyethylene.
Embodiment 5,
Raw material:A kind of novel noise reduction phenolic aldehyde foam thermal insulation material, is composed of the following raw materials by weight:
70 parts of phenolic resin;5 parts of curing agent;10 parts of foaming agent;4 parts of surfactant;5 parts of zeolite;3 parts of CNT, glue
Spend 3 parts of conditioning agent;
Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid;Viscosity modifier is dioctyl phthalate;Foam modifier is fat
Fat alcohol polyoxyethylene.
Embodiment 6,
Raw material:A kind of novel noise reduction phenolic aldehyde foam thermal insulation material, is composed of the following raw materials by weight:
70 parts of phenolic resin;4 parts of curing agent;7 parts of foaming agent;3 parts of surfactant;4 parts of zeolite;1 part of CNT, viscosity
2 parts of conditioning agent;
Foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
Curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid;Viscosity modifier is dioctyl phthalate;Foam modifier is fat
Fat alcohol polyoxyethylene.
Experimental method, phenolic foam board made of embodiment 1-6 is surrounded into square, wherein five faces are fixed, in addition
It is simultaneously active face, extraneous decibel is arranged to 100, and decibel test, the square that embodiment 1-6 is surrounded are carried out to square inside
Internal decibel is respectively 43,45,48,46,46,42, and the square that common phenolic foam board surrounds, same environment,
The decibel of the inside measured is 55.By experimental data, noise reduction of the invention is more preferable.Embodiment 1-6 density is equal
Between 30-40kg/m3.Strong and pressure test, specific numerical value are compressed to embodiment 1-6 and is shown in Table 1.
Table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 | |
Compressive strength | 0.453MPa | 0.467MPa | 0.459MPa | 0.456MPa | 0.421MPa | 0.454MPa |
Tensile strength | 0.12MPa | 0.12MPa | 0.13MPa | 0.11MPa | 0.11MPa | 0.12MPa |
From table 1, phenolic foam board provided by the invention, the colleague of the ability of noise reduction is improved in phenol formaldehyde foam, not
Having reduces its mechanical property.
Above-mentioned embodiment, technical concept and architectural feature only to illustrate the invention, it is therefore intended that allow and be familiar with this
The stakeholder of item technology can implement according to this, but above content is not intended to limit protection scope of the present invention, every according to this hair
Any equivalent change or modification that bright Spirit Essence is made, all should fall under the scope of the present invention.
Claims (3)
1. a kind of novel noise reduction phenolic aldehyde foam thermal insulation material, it is characterised in that be composed of the following raw materials by weight:
Phenolic resin 50-70 parts;Curing agent 4-6 parts;Foaming agent 7-10 parts;Surfactant 3-5 parts;Zeolite 4-8 parts;Carbon is received
Mitron 1-5 parts, viscosity modifier 2-4 parts;
The foaming agent is the one or more in pentane, pentamethylene, dichloromethane, chloroform;
The curing agent is the mixed acid of phosphoric acid and benzene sulfonic acid.
A kind of 2. novel noise reduction phenolic aldehyde foam thermal insulation material according to claim 1, it is characterised in that the viscosity regulation
Agent is dioctyl phthalate.
A kind of 3. novel noise reduction phenolic aldehyde foam thermal insulation material according to claim 1, it is characterised in that the foam regulation
Agent is aliphatic alcohol polyethenoxy.