CN107459678A - A kind of anti-aging Tensile cable sheath material and preparation method thereof - Google Patents
A kind of anti-aging Tensile cable sheath material and preparation method thereof Download PDFInfo
- Publication number
- CN107459678A CN107459678A CN201710707893.7A CN201710707893A CN107459678A CN 107459678 A CN107459678 A CN 107459678A CN 201710707893 A CN201710707893 A CN 201710707893A CN 107459678 A CN107459678 A CN 107459678A
- Authority
- CN
- China
- Prior art keywords
- antioxidant
- rubber
- aging tensile
- cable sheath
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-aging Tensile cable sheath material and preparation method thereof, its raw material includes by weight:Natural rubber, polyurethane rubber, EP rubbers, isoprene rubber, ethylene-vinyl acetate copolymer, Kynoar, carbon black, naphthenic oil, fatty acid zinc, vinyl bis-stearamides, silane coupler KH560, zinc methacrylate, age resistor 445, antioxidant 2246, antioxidant 264, antioxidant MB, vulcanizing agent.The present invention is cooperated as major ingredient with properly mixed natural rubber, polyurethane rubber, EP rubbers and isoprene rubber, it is auxiliary material to be aided with ethylene-vinyl acetate copolymer and Kynoar again, make the hardness of base-material suitable, stability, ageing resistance, stretch-resistance are notable, further coordinate other each raw materials, complemented each other between raw material, make finished product that there is stronger anti-aging tensile resistance, greatly prolong the service life of cable.
Description
Technical field
The present invention relates to electrical equipment technical field, more particularly to a kind of anti-aging Tensile cable sheath material and its preparation
Method.
Background technology
With developing rapidly for economy, electric wire is widely used in industry-by-industry, field.
Cable, typically by several or similar rope that several groups of wires (every group at least two) are twisted cable, often
Mutually insulated between group wire, and be often twisted into around a center, whole outside is surrounded by the cable cover(ing) of high-insulation.Cable
With interior energization, the feature of external insulation.
The anti-aging tensile resistance of existing cable protective cover material is poor, causes its life-span to receive influence.
The content of the invention
It is an object of the invention to overcome the above-mentioned problems in the prior art, there is provided a kind of anti-aging stretch-proof cable
Protective cover material and preparation method thereof.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of anti-aging Tensile cable sheath material, its raw material include by weight:
Preferably, its raw material includes by weight:
Wherein, the vulcanizing agent is BAA.
A kind of preparation method of anti-aging Tensile cable sheath material, comprises the following steps:
Step1, each raw material is weighed by predetermined weight part;
Step2, by natural rubber, polyurethane rubber, EP rubbers, isoprene rubber, ethylene-vinyl acetate copolymer, poly-
Vinylidene, fatty acid zinc, vinyl bis-stearamides, silane coupler KH560, zinc methacrylate add stirred autoclave
In, with 180-200 DEG C of temperature, 700-850r/min speed stirring 20-35min;
Step3,70-80 DEG C is cooled the temperature to, then add carbon black, naphthenic oil, age resistor 445, antioxidant 2246, anti-old
Agent 264, antioxidant MB, 10-15min is stirred with 500-600r/min speed;
Step4, vulcanizing agent is added, is vulcanized on vulcanizing press, gets product cable jacket material.
Beneficial effects of the present invention:The present invention is with properly mixed natural rubber, polyurethane rubber, EP rubbers and isoamyl
It is major ingredient that rubber, which cooperates, then it is auxiliary material to be aided with ethylene-vinyl acetate copolymer and Kynoar, fits the hardness of base-material
Preferably, stability, ageing resistance, stretch-resistance are notable, further coordinate other each raw materials, are complemented each other between raw material, make finished product
With stronger anti-aging tensile resistance, greatly prolong the service life of cable.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
(1) each raw material is weighed by following parts by weight:
(2) by natural rubber, polyurethane rubber, EP rubbers, isoprene rubber, ethylene-vinyl acetate copolymer, poly- inclined fluorine
Ethene, fatty acid zinc, vinyl bis-stearamides, silane coupler KH560, zinc methacrylate are added in stirred autoclave,
With 180-200 DEG C of temperature, 700-850r/min speed stirring 20-35min;
(3) 70-80 DEG C is cooled the temperature to, then adds carbon black, naphthenic oil, age resistor 445, antioxidant 2246, age resistor
264th, antioxidant MB, 10-15min is stirred with 500-600r/min speed;
(4) vulcanizing agent is added, is vulcanized on vulcanizing press, gets product cable jacket material.
Embodiment 2
(1) each raw material is weighed by following parts by weight:
(2) by natural rubber, polyurethane rubber, EP rubbers, isoprene rubber, ethylene-vinyl acetate copolymer, poly- inclined fluorine
Ethene, fatty acid zinc, vinyl bis-stearamides, silane coupler KH560, zinc methacrylate are added in stirred autoclave,
With 180-200 DEG C of temperature, 700-850r/min speed stirring 20-35min;
(3) 70-80 DEG C is cooled the temperature to, then adds carbon black, naphthenic oil, age resistor 445, antioxidant 2246, age resistor
264th, antioxidant MB, 10-15min is stirred with 500-600r/min speed;
(4) vulcanizing agent is added, is vulcanized on vulcanizing press, gets product cable jacket material.
Embodiment 3
(1) each raw material is weighed by following parts by weight:
(2) by natural rubber, polyurethane rubber, EP rubbers, isoprene rubber, ethylene-vinyl acetate copolymer, poly- inclined fluorine
Ethene, fatty acid zinc, vinyl bis-stearamides, silane coupler KH560, zinc methacrylate are added in stirred autoclave,
With 180-200 DEG C of temperature, 700-850r/min speed stirring 20-35min;
(3) 70-80 DEG C is cooled the temperature to, then adds carbon black, naphthenic oil, age resistor 445, antioxidant 2246, age resistor
264th, antioxidant MB, 10-15min is stirred with 500-600r/min speed;
(4) vulcanizing agent is added, is vulcanized on vulcanizing press, gets product cable jacket material.
Embodiment 4
(1) each raw material is weighed by following parts by weight:
(2) by natural rubber, polyurethane rubber, EP rubbers, isoprene rubber, ethylene-vinyl acetate copolymer, poly- inclined fluorine
Ethene, fatty acid zinc, vinyl bis-stearamides, silane coupler KH560, zinc methacrylate are added in stirred autoclave,
With 180-200 DEG C of temperature, 700-850r/min speed stirring 20-35min;
(3) 70-80 DEG C is cooled the temperature to, then adds carbon black, naphthenic oil, age resistor 445, antioxidant 2246, age resistor
264th, antioxidant MB, 10-15min is stirred with 500-600r/min speed;
(4) vulcanizing agent is added, is vulcanized on vulcanizing press, gets product cable jacket material.
Cable jacket material and common protective cover material to the embodiment of the present invention carry out performance test, and test result is:
The present invention is based on the mutual cooperation of properly mixed natural rubber, polyurethane rubber, EP rubbers and isoprene rubber
Material, then it is auxiliary material to be aided with ethylene-vinyl acetate copolymer and Kynoar, makes the hardness of base-material suitable, stability, anti-aging
Property, stretch-resistance it is notable, further coordinate other each raw materials, complemented each other between raw material, there is finished product stronger anti-aging
Tensile resistance, greatly prolong the service life of cable.
The general principle and principal character of the present invention has been shown and described above.It should be understood by those skilled in the art that
The present invention is not limited to the above embodiments, merely illustrating the principles of the invention described in above-described embodiment and specification,
Without departing from the spirit and scope, various changes and modifications of the present invention are possible, and these changes and improvements all fall
Enter in scope of the claimed invention.The scope of the present invention is defined by the appended claims and its equivalents.
Claims (4)
1. a kind of anti-aging Tensile cable sheath material, it is characterised in that its raw material includes by weight:
A kind of 2. anti-aging Tensile cable sheath material according to claim 1, it is characterised in that:Its raw material is by weight
Including:
A kind of 3. anti-aging Tensile cable sheath material according to claim 1 or 2, it is characterised in that:The vulcanizing agent
For BAA.
4. a kind of preparation method of anti-aging Tensile cable sheath material, it is characterised in that comprise the following steps:
Step1, each raw material is weighed by predetermined weight part;
Step2, by natural rubber, polyurethane rubber, EP rubbers, isoprene rubber, ethylene-vinyl acetate copolymer, poly- inclined fluorine
Ethene, fatty acid zinc, vinyl bis-stearamides, silane coupler KH560, zinc methacrylate are added in stirred autoclave,
With 180-200 DEG C of temperature, 700-850r/min speed stirring 20-35min;
Step3,70-80 DEG C is cooled the temperature to, then add carbon black, naphthenic oil, age resistor 445, antioxidant 2246, age resistor
264th, antioxidant MB, 10-15min is stirred with 500-600r/min speed;
Step4, vulcanizing agent is added, is vulcanized on vulcanizing press, gets product cable jacket material.