CN107457346A - A kind of sodium silicate sand with high wet-compressive strength - Google Patents
A kind of sodium silicate sand with high wet-compressive strength Download PDFInfo
- Publication number
- CN107457346A CN107457346A CN201710898130.5A CN201710898130A CN107457346A CN 107457346 A CN107457346 A CN 107457346A CN 201710898130 A CN201710898130 A CN 201710898130A CN 107457346 A CN107457346 A CN 107457346A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- powder
- sodium silicate
- compressive strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sodium silicate sand with high wet-compressive strength, is made up of the raw material of following parts by weight:55 75 parts of silica sand, 30 40 parts of diamond dust, 10 15 parts of lime stone, 58 parts of bentonite, 47 parts of modified water glass, 23 parts of gum arabic powder, 12 parts of dioctyl phthalate, 34 parts of graphite powder, 23 parts of talcum powder, 1.5 2.5 parts of gypsum, 12 parts of triisopropanolamine, 0.5 1 parts of stearic acid, 35 parts of water.The advantage of the invention is that:Water-glass sand green compression strength of the present invention is high, easy molding and repairing type, fully meets the technological requirement of first molding after-hardening, and good fluidity, gas forming amount is low, and good permeability, collapsibility are good, can significantly improve casting quality, reduces casting wasted product rate.
Description
Technical field
The present invention relates to glass sand technical field, more particularly to a kind of sodium silicate sand with high wet-compressive strength.
Background technology
Big-and-middle-sized casting is produced in the past and all uses clay-beaded sand, and drying oven drying is sent to after having made type, the production cycle is grown,
Casting accuracy is poor, and working condition is poor, far can not meet the needs of production development.Water-glass sand is because mobility is high, compact rate of molding
Height, hardening is fast, and casting accuracy is high, and source is wider, cheap, it is green the features such as, it has also become develop in recent decades most
One of fast molding sand species.Current most of steel-castings and large-sized iron casting are produced using water virus, although waterglass
Sand advantage is a lot, but there is green compression strength it is low the shortcomings that, certain difficulty is brought to molding and repairing type, can not be met
The technological requirement of first molding after-hardening.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of sodium silicate sand with high wet-compressive strength for being capable of easy molding.
In order to solve the above technical problems, the technical scheme is that:A kind of sodium silicate sand with high wet-compressive strength, its innovative point
It is:It is made up of the raw material of following parts by weight:Silica sand 55-75 parts, diamond dust 30-40 parts, lime stone 10-15 parts, bentonite 5-8
Part, modified water glass 4-7 parts, gum arabic powder 2-3 parts, dioctyl phthalate 1-2 parts, graphite powder 3-4 parts, talcum powder
2-3 parts, gypsum 1.5-2.5 parts, triisopropanolamine 1-2 parts, stearic acid 0.5-1 parts, water 3-5 parts.
Further, 65 parts of silica sand, 35 parts of diamond dust, 12 parts of lime stone, 6 parts of bentonite, 5 parts of modified water glass, I
Primary 2.5 parts of gum powder, 1.5 parts of dioctyl phthalate, 3.5 parts of graphite powder, 2.5 parts of talcum powder, 2 parts of gypsum, three isopropanols
1.5 parts of amine, 0.7 part of stearic acid, 4 parts of water.
The advantage of the invention is that:Water-glass sand green compression strength of the present invention is high, easy molding and repairing type, fully meets and first rises
The technological requirement of mould after-hardening, and good fluidity, gas forming amount is low, and good permeability, collapsibility are good, can significantly improve casting matter
Amount, reduce casting wasted product rate.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Embodiment 1
A kind of sodium silicate sand with high wet-compressive strength, it is made up of the raw material of following parts by weight:55 parts of silica sand, 30 parts of diamond dust, lime stone
10 parts, it is 5 parts of bentonite, 4 parts of modified water glass, 2 parts of gum arabic powder, 1 part of dioctyl phthalate, 3 parts of graphite powder, sliding
2 parts of stone flour, 1.5 parts of gypsum, 1 part of triisopropanolamine, 0.5 part of stearic acid, 3 parts of water.
Embodiment 2
A kind of sodium silicate sand with high wet-compressive strength, it is made up of the raw material of following parts by weight:75 parts of silica sand, 40 parts of diamond dust, lime stone
15 parts, it is 8 parts of bentonite, 7 parts of modified water glass, 3 parts of gum arabic powder, 2 parts of dioctyl phthalate, 4 parts of graphite powder, sliding
3 parts of stone flour, 2.5 parts of gypsum, 2 parts of triisopropanolamine, 1 part of stearic acid, 5 parts of water.
Embodiment 3
A kind of sodium silicate sand with high wet-compressive strength, it is made up of the raw material of following parts by weight:65 parts of silica sand, 35 parts of diamond dust, lime stone
12 parts, 6 parts of bentonite, 5 parts of modified water glass, 2.5 parts of gum arabic powder, 1.5 parts of dioctyl phthalate, graphite powder
3.5 parts, 2.5 parts of talcum powder, 2 parts of gypsum, 1.5 parts of triisopropanolamine, 0.7 part of stearic acid, 4 parts of water.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The skill of the industry
For art personnel it should be appreciated that the present invention is not limited to the above embodiments, described in above-described embodiment and specification is explanation
The principle of the present invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these
Changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and
Its equivalent thereof.
Claims (2)
- A kind of 1. sodium silicate sand with high wet-compressive strength, it is characterised in that:It is made up of the raw material of following parts by weight:Silica sand 55-75 parts, gold Emery 30-40 parts, lime stone 10-15 parts, bentonite 5-8 parts, modified water glass 4-7 parts, gum arabic powder 2-3 parts, adjacent benzene Diformazan dioctyl phthalate 1-2 parts, graphite powder 3-4 parts, talcum powder 2-3 parts, gypsum 1.5-2.5 parts, triisopropanolamine 1-2 parts, tristearin Sour 0.5-1 parts, water 3-5 parts.
- A kind of 2. sodium silicate sand with high wet-compressive strength according to claim 1, it is characterised in that:65 parts of silica sand, diamond dust 35 Part, 12 parts of lime stone, 6 parts of bentonite, 5 parts of modified water glass, 2.5 parts of gum arabic powder, dioctyl phthalate 1.5 Part, 3.5 parts of graphite powder, 2.5 parts of talcum powder, 2 parts of gypsum, 1.5 parts of triisopropanolamine, 0.7 part of stearic acid, 4 parts of water.