CN107447508A - Conductive wool fabric is prepared with mercaptoacetic acid solution - Google Patents
Conductive wool fabric is prepared with mercaptoacetic acid solution Download PDFInfo
- Publication number
- CN107447508A CN107447508A CN201710787499.9A CN201710787499A CN107447508A CN 107447508 A CN107447508 A CN 107447508A CN 201710787499 A CN201710787499 A CN 201710787499A CN 107447508 A CN107447508 A CN 107447508A
- Authority
- CN
- China
- Prior art keywords
- wool fabric
- lysate
- wool
- nano
- decatize
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a kind of method that conductive wool fabric is prepared using mercaptoacetic acid solution, this method comprises the following steps:(1)The preparation of lysate:TGA, lithium chloride and lauryl sodium sulfate are added to the water, mixed dissolution liquid is formed, sodium hydroxide regulation pH value is 9 10, and sodium hydroxide regulation pH value is 9 10, then nano conducting powderses are added in lysate, obtain being dispersed with the lysate of nano conducting powderses under sonic oscillation;(2)By wool fabric in step(1)Repeatedly padded in the lysate of gained;(3)Wool fabric after padding carries out decatize;(4)Wool fabric after decatize is impregnated in polyvinyl alcohol water solution and solidified, then washes, dry.This technology of preparing is simple and easy, and cost is cheap, small to the strength damage of wool fabric, does not change wool surface performance, and nano conducting powderses have good fastness on wool fabric;Any adhesive is not used in this preparation process, it is nontoxic.
Description
Technical field
The present invention relates to a kind of preparation method of function fabric, especially one kind to prepare conductive sheep using mercaptoacetic acid solution
The method of wool fabric.
Background technology
Nano-particle is introduced into textile fabric, functional fiber material can be prepared.Nano-particle is drawn at present
It is many to enter the preparation method of wool fiber, such as:Absorption method, sol-gal process, layer assembly method, coating etc..However, absorption method
By mainly making nano-particle be adsorbed onto wool surface by intermolecular Van der Waals force and ionic forces, washing fastness compared with
It is low;The technical process of sol-gal process and layer assembly method is longer, and more difficult control;Coating is to utilize adhesive by nanoparticle
Son is adhered to wool surface, reduces skin-friendly of the wool fiber to human body.
TGA(TGA)Both had the response feature of hydroxy acid, and had the response feature of sulfydryl again, most important of which reaction is
Reaction between disulphide.Reacted particularly under alkalescence condition with the cystine in wool fibre, cut off cystine(-S-
S-)Key, generation are easy to the cysteine of curling.
The content of the invention
The technical problems to be solved by the invention are the shortcomings that presence for above prior art, propose that one kind uses mercapto
The method that guanidine-acetic acid solution prepares conductive wool fabric.The technology of preparing is simple and easy, and cost is cheap, to the strength of wool fabric
Damage small, do not change wool surface performance, nano conducting powderses have good fastness on wool fabric;This was prepared
Any adhesive is not used in journey, it is nontoxic.
To achieve these goals, the solution taken of the present invention is:One kind is prepared conductive using mercaptoacetic acid solution
The method of wool fabric, it is characterised in that comprise the following steps:
(1)The preparation of lysate:TGA, lithium chloride and lauryl sodium sulfate are added to the water, form mixed dissolution
Liquid, sodium hydroxide regulation pH value are 9-10, and sodium hydroxide regulation pH value is 9-10, and conductive nano grain is then added in lysate
Son, obtain being dispersed with the lysate of nano conducting powderses under sonic oscillation;
(2)By wool fabric in step(1)Repeatedly padded in the lysate of gained;
(3)By the wool fabric after padding at 100-120 DEG C decatize 5-30min;
(4)Wool fabric after decatize is impregnated in polyvinyl alcohol water solution and solidified, then washes, dry.
The beneficial effects of the present invention are,(1)Limited mercaptoacetic acid solution is set to be distributed mainly on wool using padding method
The surface of fiber, the decatize of short time can only be partly dissolved to wool surface, without damaging inside wool fiber,
Reduce the damage to wool fiber and fabric;(2)In the partly soluble wool protein shape of wool surface
Into protein compression solution, there is adhesive attraction to nano-particle;(3)The protein compression solution that wool surface is formed is in poly- second
Solidified again in the enol aqueous solution, play bonding to nano-particle, package action;(4)It is not used in preparation process any viscous
Mixture, it is nontoxic.
Embodiment
The present invention is described in detail below in conjunction with specific embodiment.It should be noted that the skill described in following embodiments
The combination of art feature or technical characteristic is not construed as isolated, and they can be mutually combined so as to reach more preferable
Technique effect.
Embodiment 1
(1)The preparation of lysate:30g TGAs, 2g lithium chlorides and 3g lauryl sodium sulfate are added in 100ml water,
Mixed dissolution liquid is formed, sodium hydroxide regulation pH value is 9-10,0.3g Nano graphite powders is then added in lysate, ultrasound is shaken
Obtain being dispersed with the lysate of Nano graphite powder under swinging;
(2)By wool fabric in step(1)Repeatedly padded in the lysate of gained, pick-up 70%;
(3)By the wool fabric after padding at 120 DEG C decatize 10min;
(4)Wool fabric after decatize is impregnated in polyvinyl alcohol water solution(Mass fraction is 12%)Middle solidification 10min, then
Washing, drying.
Embodiment 2
(1)The preparation of lysate:40g TGAs, 2g lithium chlorides and 3g lauryl sodium sulfate are added in 100ml water,
Mixed dissolution liquid is formed, sodium hydroxide regulation pH value is 9-10, and 0.6g nanometer carboxylic graphite alkene is then added in lysate,
Obtain being dispersed with the lysate of nanometer carboxylic graphite alkene under sonic oscillation;
(2)By wool fabric in step(1)Repeatedly padded in the lysate of gained, pick-up 100%;
(3)By the wool fabric after padding at 120 DEG C decatize 8min;
(4)Wool fabric after decatize is impregnated in polyvinyl alcohol water solution(Mass fraction is 14%)Middle solidification 10min, then
Washing, drying.
Embodiment 3
(1)The preparation of lysate:45g TGAs, 3g lithium chlorides and 4g lauryl sodium sulfate are added in 100ml water,
Mixed dissolution liquid is formed, sodium hydroxide regulation pH value is 9-10, and 0.8g CNTs, sonic oscillation are then added in lysate
Under obtain being dispersed with the lysate of CNT;
(2)By wool fabric in step(1)Repeatedly padded in the lysate of gained, pick-up 110%;
(3)By the wool fabric after padding at 110 DEG C decatize 25min;
(4)Wool fabric after decatize is impregnated in polyvinyl alcohol water solution(Mass fraction is 18%)Middle solidification 10min, then
Washing, drying.
Although having been presented for some embodiments of the present invention herein, it will be appreciated by those of skill in the art that
Without departing from the spirit of the invention, the embodiments herein can be changed.Above-described embodiment be it is exemplary, no
Restriction that should be using the embodiments herein as interest field of the present invention.
Claims (2)
- A kind of 1. method that conductive wool fabric is prepared using mercaptoacetic acid solution, it is characterised in that comprise the following steps:(1)The preparation of lysate:TGA, lithium chloride and lauryl sodium sulfate are added to the water, form mixed dissolution Liquid, sodium hydroxide regulation pH value are 9-10, and sodium hydroxide regulation pH value is 9-10, and conductive nano grain is then added in lysate Son, obtain being dispersed with the lysate of nano conducting powderses under sonic oscillation;(2)By wool fabric in step(1)Repeatedly padded in the lysate of gained;(3)By the wool fabric after padding at 100-120 DEG C decatize 5-30min;(4)Wool fabric after decatize is impregnated in polyvinyl alcohol water solution and solidified, then washes, dry.
- 2. a kind of method that conductive wool fabric is prepared using mercaptoacetic acid solution according to claim 1, its feature are existed In:Nano conducting powderses have Nano graphite powder, carboxylated graphene, CNT etc..