CN107446676A - A kind of wear-resisting high tack food machinery lubricant and preparation method thereof - Google Patents
A kind of wear-resisting high tack food machinery lubricant and preparation method thereof Download PDFInfo
- Publication number
- CN107446676A CN107446676A CN201710690961.3A CN201710690961A CN107446676A CN 107446676 A CN107446676 A CN 107446676A CN 201710690961 A CN201710690961 A CN 201710690961A CN 107446676 A CN107446676 A CN 107446676A
- Authority
- CN
- China
- Prior art keywords
- parts
- food
- wear
- lubricant
- grade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of wear-resisting high tack food machinery lubricant, it is made up of the raw material of following parts by weight:100 parts of food-level white oil, 1 ~ 5 part of extreme-pressure wear-resistant auxiliary agent, 4 ~ 8 parts of cellulose ethers additive, 1 ~ 3 part of stearic acid, 2 ~ 6 parts of polyvinylpyrrolidone, 2 ~ 4 parts of sucrose ester, 2 ~ 4 parts of polyoxyethylene carboxylate, thio-2 acid double 0.3 ~ 0.8 part of lauryl, 3 ~ 8 parts of Tween 80,1 ~ 5 part of food-grade aerosil, 0.2 ~ 0.6 part of medical grade propene carbonate, 0.2 ~ 1 part of phytic acid.When the lubricant of the present invention is used for food machinery, not only possess excellent wearability and lubricity, and tack is excellent, can keep the lubrication of lubricant housings in a long time, and technique is simple, is easy to large-scale industrial production and use.Meanwhile lubricant of the invention disclosure satisfy that the lubrication needs of the plant equipment in food service industry process, meet the safety and health request of food-grade-lubricant.
Description
Technical field
The present invention relates to lubricant grease technical field, and in particular to a kind of wear-resisting high tack food machinery lubricant and its
Preparation method.
Background technology
Food processing equipment is widely used as necessity and infrastructure of food production, currently, food processing process
In widely used various mechanical device equipment, the inside and outside mechanical device and running part of these equipment in operating and
In the course of work, to prevent the abrasion of mechanical part, corrosion or reducing heat caused by friction, it will use and arrive lubricant grease.
Lubricant grease is of crucial importance for food processing equipment normal operation, is essential in some food processing enterprises, but
It is that can cause cross pollution if improper use, produces food-safety problem.
Current food-processing industry is faced with stern challenge.One side food demand amount increases, it is necessary to increase continuous
Yield;On the other hand, also urgently further improved based on current food security situation, food quality.The food enterprises must
Product safety, protection brand reputation must be ensured under the background of economic retrechment, improves company's production capacity and space of raising profits.In view of
Food processing and it is packaged in whole industrial chain and is in extremely important status, if improves quality and the production of food simultaneously
Amount, accomplish green, safe and environment-friendly, energy-conservation, just food production processing and packaging scheme must thoroughly be changed from technical system
Enter.Lubricating oils is exactly a wherein potential key factor.The food enterprises are wide in protection using Food-grade lubricant agent
While big consumer's life and health, and the interests of protection the food enterprises itself.Enterprise uses Food-grade lubricant
Agent not only extends the drain period, reduces equipment loss, meets enterprise and pursues cost control and the requirement of benefit;
And improve the brand image and the market competitiveness of enterprise itself.Therefore, food production is looked forward to using Food-grade lubricant agent
It is for industry and its important.
Existing food machinery with lubricator in use, because the contact operating of machinery constantly produces heat, is led
Cause constantly to be raised with the spot temperature of lubricating oils anti-attrition, lubricating oils causes lubricating oils stream due to heated easily increase mobility
Dynamic or drippage adds worker's workload and easily because omission causes mechanical abrasion, dropped, it is necessary to often add lubricating oils
Low operating efficiency, influence food machinery and normally operate.
The content of the invention
In view of the shortcomings of the prior art, with lubricator and its made the invention provides a kind of food machinery of wear-resisting high tack
Preparation Method.
The present invention solve the technical scheme that uses of above-mentioned technical problem for:A kind of wear-resisting high tack food machinery lubrication
Agent, it is made up of the raw material of following parts by weight:100 parts of food-level white oil, 1 ~ 5 part of extreme-pressure wear-resistant auxiliary agent, cellulose ethers addition
4 ~ 8 parts of agent, 1 ~ 3 part of stearic acid, 2 ~ 6 parts of polyvinylpyrrolidone, 2 ~ 4 parts of sucrose ester, 2 ~ 4 parts of polyoxyethylene carboxylate, sulphur
For dipropionic acid double 0.3 ~ 0.8 part of lauryl, 3 ~ 8 parts of Tween 80,1 ~ 5 part of food-grade aerosil, medical grade propylene carbonates
0.2 ~ 0.6 part of ester, 0.2 ~ 1 part of phytic acid.
Preferably, a kind of described wear-resisting high tack food machinery lubricant, by the raw material group of following parts by weight
Into:100 parts of food-level white oil, 3 parts of extreme-pressure wear-resistant auxiliary agent, 6 parts of cellulose ethers additive, 2 parts of stearic acid, polyvinylpyrrolidine
4 parts of ketone, 3 parts of sucrose ester, 3 parts of polyoxyethylene carboxylate, thio-2 acid double 0.5 part of lauryl, 5 parts of Tween 80, food-grades
3 parts of aerosil, 0.4 part of medical grade propene carbonate, 0.6 part of phytic acid.
Further, the extreme-pressure wear-resistant auxiliary agent is organoboron compound SW-2.
Further, described cellulose ethers additive is hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxy propyl cellulose
One or more mixing in element, hydroxypropyl methyl cellulose, hydroxyethylmethylcellulose.
A kind of preparation method of described wear-resisting high tack food machinery lubricant, comprises the following steps:
(1)Food-level white oil is placed in mixing kettle, is heated to 60 ~ 70 DEG C, sequentially added under stirring at low speed state stearic acid,
Tween 80, polyoxyethylene carboxylate and medical grade propene carbonate, then 15 ~ 30min of high-speed stirred obtain emulsion one;
(2)By step(1)The emulsion one of gained is heated to 100 ~ 120 DEG C, added under stirring at low speed cellulose ethers additive,
Polyvinylpyrrolidone and sucrose ester, middling speed 20 ~ 40min of insulated and stirred is then modulated, obtains emulsion two;
(3)By step(2)The emulsion two of gained is cooled to 70 ~ 80 DEG C, and extreme-pressure wear-resistant auxiliary agent, sulphur are sequentially added under stirring at low speed
For dipropionic acid double lauryl, food-grade aerosil and phytic acid, insulation continues 3 ~ 5h of stirring, then grinds three times and produces this
The lubricant of invention.
Compared with prior art, the advantages of present invention possesses be:When the lubricant of the present invention is used for food machinery, not only have
Standby excellent wearability and lubricity, and tack is excellent, can keep the lubrication of lubricant housings, Er Qiegong in a long time
Skill is simple, is easy to large-scale industrial production and use.Meanwhile lubricant of the invention disclosure satisfy that food service industry process
In plant equipment lubrication needs, meet the safety and health request of food-grade-lubricant.
Embodiment
With reference to specific embodiment, the present invention is described further, but following embodiments is not formed to this hair
The limitation of bright right.
Embodiment 1:A kind of wear-resisting high tack food machinery lubricant, is made up of the raw material of following parts by weight:Food
100 parts of grade white oil, 3 parts of extreme-pressure wear-resistant auxiliary agent, 6 parts of cellulose ethers additive, 2 parts of stearic acid, 4 parts of polyvinylpyrrolidone,
3 parts of sucrose ester, 3 parts of polyoxyethylene carboxylate, thio-2 acid double 0.5 part of lauryl, 6 parts of Tween 80, food-grade gas phases two
3 parts of silica, 0.4 part of medical grade propene carbonate, 0.6 part of phytic acid.
Further, the extreme-pressure wear-resistant auxiliary agent is organoboron compound SW-2;Described cellulose ethers additive is
The mixing of hydroxymethyl cellulose and hydroxyethylmethylcellulose.
A kind of preparation method of described wear-resisting high tack food machinery lubricant, comprises the following steps:
(1)Food-level white oil is placed in mixing kettle, is heated to 65 DEG C, stearic acid is sequentially added under stirring at low speed state, is told
Temperature 80, polyoxyethylene carboxylate and medical grade propene carbonate, then high-speed stirred 20min obtain emulsion one;
(2)By step(1)The emulsion one of gained is heated to 100 ~ 120 DEG C, added under stirring at low speed cellulose ethers additive,
Polyvinylpyrrolidone and sucrose ester, middling speed insulated and stirred 30min is then modulated, obtains emulsion two;
(3)By step(2)The emulsion two of gained is cooled to 75 DEG C, and extreme-pressure wear-resistant auxiliary agent, thio is sequentially added under stirring at low speed
Dipropionic acid double lauryl, food-grade aerosil and phytic acid, insulation continue to stir 4h, then grind three times and produce the present invention
Lubricant.
Embodiment 2:A kind of wear-resisting high tack food machinery lubricant, is made up of the raw material of following parts by weight:Food
100 parts of grade white oil, 1 part of extreme-pressure wear-resistant auxiliary agent, 4 parts of cellulose ethers additive, 1 part of stearic acid, 2 parts of polyvinylpyrrolidone,
2 parts of sucrose ester, 2 parts of polyoxyethylene carboxylate, thio-2 acid double 0.3 part of lauryl, 3 parts of Tween 80, food-grade gas phases two
1 part of silica, 0.2 part of medical grade propene carbonate, 0.2 part of phytic acid.
Further, the extreme-pressure wear-resistant auxiliary agent is organoboron compound SW-2;Described cellulose ethers additive is
Hydroxyethyl cellulose.
A kind of preparation method of described wear-resisting high tack food machinery lubricant, comprises the following steps:
(1)Food-level white oil is placed in mixing kettle, is heated to 60 DEG C, stearic acid is sequentially added under stirring at low speed state, is told
Temperature 80, polyoxyethylene carboxylate and medical grade propene carbonate, then high-speed stirred 30min obtain emulsion one;
(2)By step(1)The emulsion one of gained is heated to 100 DEG C, and cellulose ethers additive, poly- second are added under stirring at low speed
Alkene pyrrolidone and sucrose ester, middling speed insulated and stirred 40min is then modulated, obtains emulsion two;
(3)By step(2)The emulsion two of gained is cooled to 70 DEG C, and extreme-pressure wear-resistant auxiliary agent, thio is sequentially added under stirring at low speed
Dipropionic acid double lauryl, food-grade aerosil and phytic acid, insulation continue to stir 5h, then grind three times and produce the present invention
Lubricant.
Embodiment 3:A kind of wear-resisting high tack food machinery lubricant, is made up of the raw material of following parts by weight:Food
100 parts of grade white oil, 5 parts of extreme-pressure wear-resistant auxiliary agent, 8 parts of cellulose ethers additive, 3 parts of stearic acid, 6 parts of polyvinylpyrrolidone,
4 parts of sucrose ester, 4 parts of polyoxyethylene carboxylate, thio-2 acid double 0.8 part of lauryl, 8 parts of Tween 80, food-grade gas phases two
5 parts of silica, 0.6 part of medical grade propene carbonate, 1 part of phytic acid.
Further, the extreme-pressure wear-resistant auxiliary agent is organoboron compound SW-2;Described cellulose ethers additive is
Hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxypropyl methyl cellulose and hydroxyethylmethylcellulose it is mixed
Close.
A kind of preparation method of described wear-resisting high tack food machinery lubricant, comprises the following steps:
(1)Food-level white oil is placed in mixing kettle, is heated to 70 DEG C, stearic acid is sequentially added under stirring at low speed state, is told
Temperature 80, polyoxyethylene carboxylate and medical grade propene carbonate, then high-speed stirred 15min obtain emulsion one;
(2)By step(1)The emulsion one of gained is heated to 120 DEG C, and cellulose ethers additive, poly- second are added under stirring at low speed
Alkene pyrrolidone and sucrose ester, middling speed insulated and stirred 20min is then modulated, obtains emulsion two;
(3)By step(2)The emulsion two of gained is cooled to 80 DEG C, and extreme-pressure wear-resistant auxiliary agent, thio is sequentially added under stirring at low speed
Dipropionic acid double lauryl, food-grade aerosil and phytic acid, insulation continue to stir 3h, then grind three times and produce the present invention
Lubricant.
Embodiment 4:A kind of wear-resisting high tack food machinery lubricant, is made up of the raw material of following parts by weight:Food
100 parts of grade white oil, 1 part of extreme-pressure wear-resistant auxiliary agent, 8 parts of cellulose ethers additive, 1 part of stearic acid, 6 parts of polyvinylpyrrolidone,
2 parts of sucrose ester, 4 parts of polyoxyethylene carboxylate, thio-2 acid double 0.3 part of lauryl, 8 parts of Tween 80, food-grade gas phases two
1 part of silica, 0.6 part of medical grade propene carbonate, 0.2 part of phytic acid.
Further, the extreme-pressure wear-resistant auxiliary agent is organoboron compound SW-2;Described cellulose ethers additive is
Hydroxymethyl cellulose and hydroxyethyl cellulose.
A kind of preparation method of described wear-resisting high tack food machinery lubricant, its specific steps is the same as embodiment 1.
Embodiment 5:A kind of wear-resisting high tack food machinery lubricant, is made up of the raw material of following parts by weight:Food
100 parts of grade white oil, 2 parts of extreme-pressure wear-resistant auxiliary agent, 5 parts of cellulose ethers additive, 2 parts of stearic acid, 5 parts of polyvinylpyrrolidone,
3 parts of sucrose ester, 4 parts of polyoxyethylene carboxylate, thio-2 acid double 0.6 part of lauryl, 7 parts of Tween 80, food-grade gas phases two
4 parts of silica, 0.3 part of medical grade propene carbonate, 0.8 part of phytic acid.
Further, the extreme-pressure wear-resistant auxiliary agent is organoboron compound SW-2;Described cellulose ethers additive is
Hydroxymethyl cellulose.
A kind of preparation method of described wear-resisting high tack food machinery lubricant, its specific steps is the same as embodiment 1.
With food-level white oil and commercially available conventional food-grade-lubricant as a comparison case 1 and comparative example 2, take on same amount of
The lubricant for stating embodiment 1-5 and comparative example 1-2 does performance test under the same conditions, as a result as shown in the table:
Performance | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Comparative example 1 | Comparative example 2 |
Lubricity PB values(N) | 475.5 | 424.6 | 531.1 | 466.8 | 483.6 | 118.2 | 309.3 |
Viscosity index (VI) | 122 | 117 | 124 | 120 | 121 | 93 | 114 |
Coefficient of friction | 0.033 | 0.045 | 0.048 | 0.037 | 0.039 | 0.094 | 0.068 |
From test result as can be seen that the lubricant of the present invention is a kind of excellent product of greasy property, and using process
In adhesion property far above comparative example 1 and higher than comparative example 2, excellent lubricating function can be kept within the longer term.
Certainly, described above is not limitation of the present invention, and the present invention is also not limited to above-described embodiment, the art
Technical staff, the present invention essential scope in, made variations, modifications, additions or substitutions, should all belong to the present invention
Protection domain.
Claims (5)
1. a kind of wear-resisting high tack food machinery lubricant, it is characterised in that be made up of the raw material of following parts by weight:Food
100 parts of grade white oil, 1 ~ 5 part of extreme-pressure wear-resistant auxiliary agent, 4 ~ 8 parts of cellulose ethers additive, 1 ~ 3 part of stearic acid, polyvinylpyrrolidine
2 ~ 6 parts of ketone, 2 ~ 4 parts of sucrose ester, 2 ~ 4 parts of polyoxyethylene carboxylate, thio-2 acid double 0.3 ~ 0.8 part of lauryl, Tween 80s
3 ~ 8 parts, 1 ~ 5 part of food-grade aerosil, 0.2 ~ 0.6 part of medical grade propene carbonate, 0.2 ~ 1 part of phytic acid.
2. the wear-resisting high tack food machinery lubricant of one kind according to claim 1, it is characterised in that by following weight
The raw material composition of number:100 parts of food-level white oil, 3 parts of extreme-pressure wear-resistant auxiliary agent, 6 parts of cellulose ethers additive, 2 parts of stearic acid,
4 parts of polyvinylpyrrolidone, 3 parts of sucrose ester, 3 parts of polyoxyethylene carboxylate, thio-2 acid double 0.5 part of lauryl, tweens
80 5 parts, 3 parts of food-grade aerosil, 0.4 part of medical grade propene carbonate, 0.6 part of phytic acid.
3. the wear-resisting high tack food machinery lubricant of one kind according to claim 1 or 2, it is characterised in that the extreme pressure
Antiwear assistant is organoboron compound SW-2.
4. the wear-resisting high tack food machinery lubricant of one kind according to claim 1 or 2, it is characterised in that described fibre
Plain ether additive is tieed up as hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxypropyl methyl cellulose, hydroxyl second
One or more mixing in ylmethyl cellulose.
A kind of 5. preparation method of wear-resisting high tack food machinery lubricant described in claim 1 or 2, it is characterised in that
Comprise the following steps:
(1)Food-level white oil is placed in mixing kettle, is heated to 60 ~ 70 DEG C, sequentially added under stirring at low speed state stearic acid,
Tween 80, polyoxyethylene carboxylate and medical grade propene carbonate, then 15 ~ 30min of high-speed stirred obtain emulsion one;
(2)By step(1)The emulsion one of gained is heated to 100 ~ 120 DEG C, added under stirring at low speed cellulose ethers additive,
Polyvinylpyrrolidone and sucrose ester, middling speed 20 ~ 40min of insulated and stirred is then modulated, obtains emulsion two;
(3)By step(2)The emulsion two of gained is cooled to 70 ~ 80 DEG C, and extreme-pressure wear-resistant auxiliary agent, sulphur are sequentially added under stirring at low speed
For dipropionic acid double lauryl, food-grade aerosil and phytic acid, insulation continues 3 ~ 5h of stirring, then grinds three times and produces this
The lubricant of invention.