CN107446359A - A kind of sulphurated siliastic and preparation method thereof - Google Patents
A kind of sulphurated siliastic and preparation method thereof Download PDFInfo
- Publication number
- CN107446359A CN107446359A CN201710810104.2A CN201710810104A CN107446359A CN 107446359 A CN107446359 A CN 107446359A CN 201710810104 A CN201710810104 A CN 201710810104A CN 107446359 A CN107446359 A CN 107446359A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- white carbon
- silicones
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sulphurated siliastic and preparation method thereof.It is made up of the raw material of following parts by weight:100 parts of Methyl-ethylenvinyl gum, 37 ~ 53 parts of white carbon, 2 ~ 8 parts of hydroxy silicon oil, 0.17 ~ 0.2 part of zinc stearate, 3 ~ 7 parts of silicones, 1 ~ 2 part of 2,5-dimethyl-2,5-bishexane.After above-mentioned formula and preparation method, it is reasonable due to being formulated, particularly using white carbon and silicones as supporting material, white carbon can increase the intensity of sulphurated siliastic as supporting material, silicones is made up of silica structure construction unit, three-dimensional cross-linked network structure can be formed after solidification, there is prominent weatherability and resistance to yellowing, the performance of silicon rubber can also be strengthened while can not only increasing other element impurities as reinforcing agent, in addition, rational technique is combined with so that while resilience reaches product demand, make its hardness, tearing strength and elongation at break change are less.
Description
Technical field
The present invention relates to a kind of technology of preparing of high-temperature silicon disulfide rubber, specifically a kind of sulphurated siliastic and its system
Preparation Method.
Background technology
High-temperature silicon disulfide rubber is the machine that has concurrently and the macromolecular material of inorganic in nature, has flexible network, silicon rubber
Because resilience is good, compression is relatively low, can be used as kitchen article, axle envelope circle, packing ring, nipple, sundries joint and office equipment
Deng application prospect is extensive;With the development of science and technology, higher requirement it is also proposed to the rebound performance of silicon rubber, but
Existing high resilience high-temperature silicon disulfide rubber, because the limitation of its formula and technique make it that rebound degree is still relatively low, and its
Hardness, tearing strength and elongation at break properties are poor, it is impossible to meet the specific demand of some products of in the market, thus, how
Existing technology is broken through, improves the rebound performance of high-temperature silicon disulfide rubber, the application for widening silicon rubber is a technology difficulty
Topic.
The content of the invention
The technical problem to be solved in the present invention is to provide one kind to make its hard while resilience reaches product demand
Degree, tearing strength and elongation at break change less sulphurated siliastic and preparation method thereof.
In order to solve the above-mentioned technical problem, sulphurated siliastic of the invention, it is made up of the raw material of following parts by weight:
100 parts of Methyl-ethylenvinyl gum
37 ~ 53 parts of white carbon
2 ~ 8 parts of hydroxy silicon oil
0.17 ~ 0.2 part of zinc stearate
3 ~ 7 parts of silicones
1 ~ 2 part of 2,5-dimethyl-2,5-bishexane.
A kind of preparation method of above-mentioned sulphurated siliastic, above-mentioned raw materials are prepared according to following step:
A, by 100 parts of Methyl-ethylenvinyl gum and 0.17 ~ 0.2 part of zinc stearate in Z-shaped kneader cold refining 2-5 minutes;
B, 37 ~ 53 parts of white carbon, 3 ~ 7 parts of silicones and 2 ~ 8 parts of hydroxy silicon oil are added several times, after adding every time fully
Stirring, makes white carbon be well mixed with rubber;
C, 150-170 DEG C is warming up to after sizing material is kneaded and formed, heat refining 80-100 minutes, vacuumizes plastic emitting after 25-35 minutes;
D, sizing material is carried out on double roller cylinder opening rubber mixing machine thin logical, is then filtered on rubber strainer, obtain clean free from admixture
Silicon rubber;
E, by silicon rubber and the 2 of 1 ~ 2 part, 5-dimethyl-2,5-bishexane is well mixed on rubber mixing machine, in compression molding
Vulcanization is molded on machine.
In the step E, curing temperature for 170-180 DEG C, cure time for 10-20min.
It is reasonable due to being formulated after above-mentioned formula and preparation method, particularly using white carbon and silicones as benefit
Strong material, white carbon can increase the intensity of sulphurated siliastic as supporting material, and silicones is by silica structure structure list
What member was formed, three-dimensional cross-linked network structure can be formed after solidification, has prominent weatherability and resistance to yellowing, as reinforcing agent not only
The performance of silicon rubber can also be strengthened while other element impurities can not be increased, returning in addition, being combined with rational technique
While elasticity reaches product demand, make its hardness, tearing strength and elongation at break change less.
Embodiment
With reference to embodiment, sulphurated siliastic of the present invention and preparation method thereof is made further specifically
It is bright.
Embodiment one:
The preparation method of the silicon sulfide rubber of the present embodiment, raw material is prepared according to following step:
A, by 100 parts of Methyl-ethylenvinyl gum and 0.17 part of zinc stearate in Z-shaped kneader it is cold refining 2 minutes;
B, 37 parts of white carbon, 3 parts of silicones and 4 parts of hydroxy silicon oil are added several times, is sufficiently stirred, makes after adding every time
White carbon is well mixed with rubber;
C, 150 DEG C are warming up to after sizing material is kneaded and formed, heat refining 80 minutes, vacuumizes plastic emitting after 25 minutes;
D, sizing material is carried out on double roller cylinder opening rubber mixing machine thin logical, is then filtered on rubber strainer, obtain clean free from admixture
Silicon rubber;
E, silicon rubber is mixed with 1 part of 2,5-dimethyl-2,5-bis(t-butylperoxy) hexane on opening rubber mixing machine
Uniformly, in being molded vulcanization on vulcanizing press, curing temperature for 170 DEG C, cure time for 10min.
Embodiment two:
The preparation method of the silicon sulfide rubber of the present embodiment, raw material is prepared according to following step:
A, by 100 parts of Methyl-ethylenvinyl gum and 0.19 part of zinc stearate in Z-shaped kneader it is cold refining 3 minutes;
B, 45 parts of white carbon, 5 parts of silicones and 5 parts of hydroxy silicon oil are added several times, is sufficiently stirred, makes after adding every time
White carbon is well mixed with rubber;
C, 160 DEG C are warming up to after sizing material is kneaded and formed, heat refining 90 minutes, vacuumizes plastic emitting after 30 minutes
D, sizing material is carried out on double roller cylinder opening rubber mixing machine thin logical, is then filtered on rubber strainer, obtain clean free from admixture
Silicon rubber;
E, silicon rubber and 1 part of 2,5-dimethyl-2,5-bis(t-butylperoxy) hexane are mixed on opening rubber mixing machine
Close uniform, be molded vulcanization on vulcanizing press, curing temperature for 175 DEG C, cure time for 15min.
Embodiment three:
The preparation method of the silicon sulfide rubber of the present embodiment, raw material is prepared according to following step:
A, by 100 parts of Methyl-ethylenvinyl gum and 0.2 part of zinc stearate in Z-shaped kneader it is cold refining 3 minutes;
B, 53 parts of white carbon, 7 parts of silicones and 8 parts of hydroxy silicon oil are added several times, is sufficiently stirred, makes after adding every time
White carbon is well mixed with rubber;
C, 170 DEG C are warming up to after sizing material is kneaded and formed, heat refining 100 minutes, vacuumizes plastic emitting after 35 minutes;
D, sizing material is carried out on double roller cylinder opening rubber mixing machine thin logical, is then filtered on rubber strainer, obtain clean free from admixture
Silicon rubber;
E, silicon rubber and 2 parts of 2,5-dimethyl-2,5-bis(t-butylperoxy) hexane are mixed on opening rubber mixing machine
Close it is uniform, in being molded vulcanization on vulcanizing press, curing temperature for 180 DEG C, cure time for 20min.
By it was verified that supporting material is white carbon and silicones, white carbon can make silicon sulfide as supporting material
Rubber intensity increase, but due to white carbon reinforcing effect clearly, for make the network hole of silicon rubber become greatly with increase
Add its rebound performance, part supporting material is replaced by the slightly worse silicones of reinforcing effect, and silicones is by silica structure structure list
What member was formed, three-dimensional cross-linked network structure can be formed after solidification, has prominent weatherability and resistance to yellowing, as reinforcing agent not only
The performance of silicon rubber can also be strengthened while other element impurities can not be increased, in addition, hydroxy silicon oil is constitution controller, it is stearic
Sour zinc is releasing agent, and what peroxide vulcanizing agent was selected is the nontoxic high temperature vulcanized effect good 2 that has no irritating odor, 5-
Dimethyl-2,5-bis(t-butylperoxy) hexane, its specific properties of product are as follows:
The present invention is tested according to national standard, it is as a result as follows:
Test event | Unit | Test result | Testing standard |
Shore hardness | HA | 49 | GB 531-83 |
Tensile strength | MPa | 9.6 | GB 528-92 |
Tension fracture elongation rate | % | 520 | GB 528-92 |
Compression deformation rate | % | 27 | HG/T 2876-1997 |
Rebound degree | % | 80 | GB/T 1681-2009 |
Test result confirms that the present invention solves key issue, and rebound degree reaches expected effects.
Claims (3)
1. a kind of sulphurated siliastic, it is characterised in that be made up of the raw material of following parts by weight:
100 parts of Methyl-ethylenvinyl gum
37 ~ 53 parts of white carbon
2 ~ 8 parts of hydroxy silicon oil
0.17 ~ 0.2 part of zinc stearate
3 ~ 7 parts of silicones
1 ~ 2 part of 2,5-dimethyl-2,5-bishexane.
A kind of 2. preparation method of sulphurated siliastic as claimed in claim 1, it is characterised in that:By above-mentioned raw materials according to following
The step of prepared:
A, by 100 parts of Methyl-ethylenvinyl gum and 0.17 ~ 0.2 part of zinc stearate in Z-shaped kneader cold refining 2-5 minutes;
B, 37 ~ 53 parts of white carbon, 3 ~ 7 parts of silicones and 2 ~ 8 parts of hydroxy silicon oil are added several times, after adding every time fully
Stirring, makes white carbon be well mixed with rubber;
C, 150-170 DEG C is warming up to after sizing material is kneaded and formed, heat refining 80-100 minutes, vacuumizes plastic emitting after 25-35 minutes;
D, sizing material is carried out on double roller cylinder opening rubber mixing machine thin logical, is then filtered on rubber strainer, obtain clean free from admixture
Silicon rubber;
E, by silicon rubber and the 2 of 1 ~ 2 part, 5-dimethyl-2,5-bishexane is well mixed on rubber mixing machine, in compression molding
Vulcanization is molded on machine.
3. according to the preparation method of the sulphurated siliastic described in claim 2, it is characterised in that:In the step E, curing temperature
For 170-180 DEG C, cure time for 10-20min.