CN107445486A - The processing technology of the glass of pattern is embedded with a kind of wall - Google Patents
The processing technology of the glass of pattern is embedded with a kind of wall Download PDFInfo
- Publication number
- CN107445486A CN107445486A CN201710662194.5A CN201710662194A CN107445486A CN 107445486 A CN107445486 A CN 107445486A CN 201710662194 A CN201710662194 A CN 201710662194A CN 107445486 A CN107445486 A CN 107445486A
- Authority
- CN
- China
- Prior art keywords
- cup
- wall
- layer wall
- internal layer
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technology for the glass that pattern is embedded with wall; it is imprinted on using by pattern on the outer wall of internal layer wall of cup; inner layer outer wall and outer layer outer wall are merged composition individual layer wall of cup again; pattern is set to be in the inwall of wall of cup; avoid pattern to be worn, while also increase the thickness of wall of cup, make cup firmer; last layer protective film is covered in the outside of internal layer wall of cup after pattern is printed, the pattern when internal layer wall of cup is merged with outer layer wall of cup can be avoided to be scratched.
Description
Technical field
The present invention relates to a kind of processing technology for the glass that pattern is embedded with wall, belong to glass working arts field.
Background technology
Glass is free of organic chemical substance, when people are drunk water with glass or when other drinks, it is not necessary to worry
Harmful chemical substance can be drunk enter in belly, and glass surface is smooth, easily cleaning, so people are drunk water with glass is
It is most healthy, safest, but the decorative pattern of current glass is all printing or baked on the surface of glass, after the time has been grown
Easily it is worn away, and the wall of cup of single-glass cup is all relatively thin, is easily damaged.Therefore, it is proposed that it is embedded with figure in a kind of wall
The processing technology of the glass of case.
The content of the invention
It is a primary object of the present invention to provide a kind of processing technology for the glass that pattern is embedded with wall, pattern is set
Put in the inside of wall of cup, pattern can be avoided to be worn, and one layer of wall of cup is synthesized using two layers of wall of cup, add the thickness of wall of cup
Degree, makes cup firmer, effectively can solve the problems, such as in background technology.
To achieve the above object, the technical scheme taken of the present invention is:
The processing technology of the glass of pattern is embedded with a kind of wall, is comprised the following steps:
1) the different glass tube of two sizes is taken respectively as internal layer wall of cup and outer layer wall of cup;
2) by the pattern needed on screen printer print on the outer wall of internal layer wall of cup, then internal layer wall of cup is placed in low
Dried in warm drying baker;
3) in the internal layer wall of cup overcoat last layer protective film by step 2) processing;
4) the internal layer wall of cup by step 3) processing is placed in low-temperature heat case and heated, make film and internal layer wall of cup
It is completely combined, combines together;
5) inwall of the internal layer wall of cup by step 4) processing is heated using high-temperature heating equipment, makes its softening,
Unnecessary film is cut off using cutter again;
6) the internal layer wall of cup by step 5) processing is placed in outer layer wall of cup, the bottom of internal layer wall of cup and outer layer wall of cup is adopted
Sealed with film, blown at the top of internal layer wall of cup using blow molding device, internal layer wall of cup is gradually expanded outwardly, it is interior
Layer wall of cup is combined closely with outer layer wall of cup, and bubble-free produces, and obtains required cup cylinder;
7) in the cup cylinder bottom obtained by step 6), traceless linker has cup by the way of the docking of rolling vacuum, fuse process
Bottom, the top of cup cylinder make the fusion completely of internal layer wall of cup and outer layer wall of cup obtain required glass by the way of high-temperature heating merges
The crude product of cup;
8) crude product obtained by step 7) annealed, tempering, obtain required glass finished product after polishing.
Further, the drying temperature of the low temp drying oven is 40~60 DEG C, and drying time is 40~70min.
Further, the temperature of the low-temperature heat case is 80~100 DEG C, and the heat time is 5~10min.
Further, the temperature of the high-temperature heating equipment is 700~900 DEG C.
The present invention is used and is imprinted on pattern on the outer wall of internal layer wall of cup, then inner layer outer wall and outer layer outer wall are merged
Individual layer wall of cup is formed, pattern is in the inwall of wall of cup, avoids pattern and be worn, while also increases the thickness of wall of cup, is made
Cup is firmer, covers last layer protective film in the outside of internal layer wall of cup after pattern is printed, can avoid by internal layer wall of cup
Pattern is scratched when being merged with outer layer wall of cup.
Embodiment
To be easy to understand the technical means, the inventive features, the objects and the advantages of the present invention, with reference to
Embodiment, the present invention is expanded on further.
Embodiment 1
The processing technology of the glass of pattern is embedded with a kind of wall, is comprised the following steps:
1) the different glass tube of two sizes is taken respectively as internal layer wall of cup and outer layer wall of cup;
2) by the pattern needed on screen printer print on the outer wall of internal layer wall of cup, then internal layer wall of cup is placed in low
Dried in warm drying baker;
3) in the internal layer wall of cup overcoat last layer protective film by step 2) processing;
4) the internal layer wall of cup by step 3) processing is placed in low-temperature heat case and heated, make film and internal layer wall of cup
It is completely combined, combines together;
5) inwall of the internal layer wall of cup by step 4) processing is heated using high-temperature heating equipment, makes its softening,
Unnecessary film is cut off using cutter again;
6) the internal layer wall of cup by step 5) processing is placed in outer layer wall of cup, the bottom of internal layer wall of cup and outer layer wall of cup is adopted
Sealed with film, blown at the top of internal layer wall of cup using blow molding device, internal layer wall of cup is gradually expanded outwardly, it is interior
Layer wall of cup is combined closely with outer layer wall of cup, and bubble-free produces, and obtains required cup cylinder;
7) in the cup cylinder bottom obtained by step 6), traceless linker has cup by the way of the docking of rolling vacuum, fuse process
Bottom, the top of cup cylinder make the fusion completely of internal layer wall of cup and outer layer wall of cup obtain required glass by the way of high-temperature heating merges
The crude product of cup;
8) crude product obtained by step 7) annealed, tempering, obtain required glass finished product after polishing.
It is imprinted on using by pattern on the outer wall of internal layer wall of cup, then inner layer outer wall and outer layer outer wall is merged composition list
Layer wall of cup, makes pattern be in the inwall of wall of cup, avoids pattern and be worn, while also increases the thickness of wall of cup, makes cup more
Add firm, cover last layer protective film in the outside of internal layer wall of cup after pattern is printed, can avoid by internal layer wall of cup and outer layer
Pattern is scratched when wall of cup merges.
Further, the drying temperature of the low temp drying oven is 40 DEG C, drying time 70min, using low temperature drying,
Prevent from temperature too high being imprinted on the Pattern damage of internal layer wall of cup outer wall.
Further, the temperature of the low-temperature heat case is 80 DEG C, heat time 10min, makes protective film softening patch
Close in internal layer wall of cup outer surface.
Further, the temperature of the high-temperature heating equipment is 700 DEG C, high-temperature heating, softens internal layer wall of cup, Ke Yiyu
Outer layer wall of cup is bonded completely, forms individual layer wall of cup.
Embodiment 2
The processing technology of the glass of pattern is embedded with a kind of wall, is comprised the following steps:
1) the different glass tube of two sizes is taken respectively as internal layer wall of cup and outer layer wall of cup;
2) by the pattern needed on screen printer print on the outer wall of internal layer wall of cup, then internal layer wall of cup is placed in low
Dried in warm drying baker;
3) in the internal layer wall of cup overcoat last layer protective film by step 2) processing;
4) the internal layer wall of cup by step 3) processing is placed in low-temperature heat case and heated, make film and internal layer wall of cup
It is completely combined, combines together;
5) inwall of the internal layer wall of cup by step 4) processing is heated using high-temperature heating equipment, makes its softening,
Unnecessary film is cut off using cutter again;
6) the internal layer wall of cup by step 5) processing is placed in outer layer wall of cup, the bottom of internal layer wall of cup and outer layer wall of cup is adopted
Sealed with film, blown at the top of internal layer wall of cup using blow molding device, internal layer wall of cup is gradually expanded outwardly, it is interior
Layer wall of cup is combined closely with outer layer wall of cup, and bubble-free produces, and obtains required cup cylinder;
7) in the cup cylinder bottom obtained by step 6), traceless linker has cup by the way of the docking of rolling vacuum, fuse process
Bottom, the top of cup cylinder make the fusion completely of internal layer wall of cup and outer layer wall of cup obtain required glass by the way of high-temperature heating merges
The crude product of cup;
8) crude product obtained by step 7) annealed, tempering, obtain required glass finished product after polishing.
Further, the drying temperature of the low temp drying oven is 60 DEG C, drying time 40min.
Further, the temperature of the low-temperature heat case is 100 DEG C, heat time 5min.
Further, the temperature of the high-temperature heating equipment is 900 DEG C.
Embodiment 3
The processing technology of the glass of pattern is embedded with a kind of wall, is comprised the following steps:
1) the different glass tube of two sizes is taken respectively as internal layer wall of cup and outer layer wall of cup;
2) by the pattern needed on screen printer print on the outer wall of internal layer wall of cup, then internal layer wall of cup is placed in low
Dried in warm drying baker;
3) in the internal layer wall of cup overcoat last layer protective film by step 2) processing;
4) the internal layer wall of cup by step 3) processing is placed in low-temperature heat case and heated, make film and internal layer wall of cup
It is completely combined, combines together;
5) inwall of the internal layer wall of cup by step 4) processing is heated using high-temperature heating equipment, makes its softening,
Unnecessary film is cut off using cutter again;
6) the internal layer wall of cup by step 5) processing is placed in outer layer wall of cup, the bottom of internal layer wall of cup and outer layer wall of cup is adopted
Sealed with film, blown at the top of internal layer wall of cup using blow molding device, internal layer wall of cup is gradually expanded outwardly, it is interior
Layer wall of cup is combined closely with outer layer wall of cup, and bubble-free produces, and obtains required cup cylinder;
7) in the cup cylinder bottom obtained by step 6), traceless linker has cup by the way of the docking of rolling vacuum, fuse process
Bottom, the top of cup cylinder make the fusion completely of internal layer wall of cup and outer layer wall of cup obtain required glass by the way of high-temperature heating merges
The crude product of cup;
8) crude product obtained by step 7) annealed, tempering, obtain required glass finished product after polishing.
Further, the drying temperature of the low temp drying oven is 50 DEG C, drying time 58min.
Further, the temperature of the low-temperature heat case is 90 DEG C, heat time 7min.
Further, the temperature of the high-temperature heating equipment is 800 DEG C.
Some one exemplary embodiments of the present invention are only described by way of explanation above, undoubtedly, for ability
The those of ordinary skill in domain, without departing from the spirit and scope of the present invention, can be with a variety of modes to institute
The embodiment of description is modified.Therefore, foregoing description is inherently illustrative, and should not be construed as will to right of the present invention
Ask the limitation of protection domain.
Claims (4)
1. the processing technology of the glass of pattern is embedded with a kind of wall, it is characterised in that comprise the following steps:
1) the different glass tube of two sizes is taken respectively as internal layer wall of cup and outer layer wall of cup;
2) by pattern required on screen printer print on the outer wall of internal layer wall of cup, then internal layer wall of cup is placed in low temperature and dried
Dried in dry case;
3) in the internal layer wall of cup overcoat last layer protective film by step 2) processing;
4) the internal layer wall of cup by step 3) processing is placed in low-temperature heat case and heated, make film and internal layer wall of cup complete
With reference to combining together;
5) inwall of the internal layer wall of cup by step 4) processing is heated using high-temperature heating equipment, makes its softening, then adopt
Unnecessary film is cut off with cutter;
6) the internal layer wall of cup by step 5) processing is placed in outer layer wall of cup, the bottom of internal layer wall of cup and outer layer wall of cup is using thin
Film is sealed, and is blown at the top of internal layer wall of cup using blow molding device, internal layer wall of cup is gradually expanded outwardly, inner-layer cup
Wall is combined closely with outer layer wall of cup, and bubble-free produces, and obtains required cup cylinder;
7) in the cup cylinder bottom obtained by step 6), traceless linker has bottom of a cup, cup by the way of the docking of rolling vacuum, fuse process
The top of cylinder makes the fusion completely of internal layer wall of cup and outer layer wall of cup obtain required glass by the way of high-temperature heating merges
Crude product;
8) crude product obtained by step 7) annealed, tempering, obtain required glass finished product after polishing.
2. the processing technology of the glass of pattern is embedded with a kind of wall according to claim 1, it is characterised in that:It is described
The drying temperature of low temp drying oven is 40~60 DEG C, and drying time is 40~70min.
3. the processing technology of the glass of pattern is embedded with a kind of wall according to claim 1, it is characterised in that:It is described
The temperature of low-temperature heat case is 80~100 DEG C, and the heat time is 5~10min.
4. the processing technology of the glass of pattern is embedded with a kind of wall according to claim 1, it is characterised in that:It is described
The temperature of high-temperature heating equipment is 700~900 DEG C.