CN107443529A - A kind of bamboo mat preparation method for cable outer packing - Google Patents
A kind of bamboo mat preparation method for cable outer packing Download PDFInfo
- Publication number
- CN107443529A CN107443529A CN201710595727.2A CN201710595727A CN107443529A CN 107443529 A CN107443529 A CN 107443529A CN 201710595727 A CN201710595727 A CN 201710595727A CN 107443529 A CN107443529 A CN 107443529A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- materials
- parts
- outer packing
- cable outer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of bamboo mat preparation method for cable outer packing, comprises the following steps：Bamboo wood is removed into delimbing, leaf, splits to obtain bamboo chip, is dried to obtain pretreatment bamboo wood；Bamboo wood will be pre-processed, adds in hydrochloric acid solution and stands, will be filtered, natural air drying, standing in sodium hydroxide solution is added and obtains A materials；A materials are subjected to carbonization treatment, flattening on hot press is then sent to and obtains B materials；B materials are sent into ethanol solution, add Cocoamidopropyl betaine, butyl titanate stirring, hydrochloric acid, urea, citric acid complex silver nitrate, microcrystalline wax is added, heating stirring, filters, wash, dry, dry, braiding obtains the bamboo mat for cable outer packing.The present invention can thoroughly kill bacterium and the worm's ovum inside bamboo wood, and shaping bamboo mat stability in use can be ensure that, while effectively improve bamboo fibre bactericidal and bacteriostatic effect to the effective softening of bamboo fiber bundle, the moisture and gas in bamboo fibre absorption air are prevented, plays anti-corrosion, distortion-free effect.
Description
Technical field
The present invention relates to bamboo mat technical field, more particularly to a kind of bamboo mat preparation method for cable outer packing.
Background technology
Bamboo mat is widely used in cable outer packing because there is natural texture and natural breath to be liked by numerous people for it,
But the defects of bamboo mat can not make up there is its own, for example, it is perishable, harmful substance, easily quilt are easily grown in a humid environment
Worm-eaten.The effective fungus-proof antisepsis processing of bamboo mat at present is still Chemical treatment, and most of use organic solvent types is anti-
Mould preservative, but when being used for cable outer packing, corrosion easily is produced to the cable being wrapped by, it would be highly desirable to solve.
The content of the invention
Based on technical problem existing for background technology, the present invention proposes a kind of bamboo mat preparation side for cable outer packing
Method, bacterium and worm's ovum inside bamboo wood can be thoroughly killed, and can ensure that shaping bamboo mat makes to the effective softening of bamboo fiber bundle
Stability in, while bamboo fibre bactericidal and bacteriostatic effect is effectively improved, moisture and gas in bamboo fibre absorption air are prevented,
Play anti-corrosion, distortion-free effect.
A kind of bamboo mat preparation method for cable outer packing proposed by the present invention, comprises the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain bamboo chip, be dried to obtain pretreatment bamboo wood；Bamboo wood will be pre-processed, will be added
Stand, filter, natural air drying in hydrochloric acid solution, add standing in sodium hydroxide solution and obtain A materials；
S2, A materials are subjected to carbonization treatment, are then sent on hot press flattening and obtain B materials；
S3, will B materials be sent into ethanol solution in, add Cocoamidopropyl betaine, butyl titanate stirring, add salt
Acid, urea, citric acid complex silver nitrate, microcrystalline wax, heating stirring, are filtered, and are washed, and are dried, and are dried, and braiding obtains being used for electricity
The bamboo mat of cable outer packing.
Preferably, in S1, the concentration of hydrochloric acid solution is 0.2-0.6mol/L, and the concentration of sodium hydroxide solution is 0.4-
0.9mol/L。
Preferably, in S1, pretreatment bamboo wood, hydrochloric acid solution, the weight ratio of sodium hydroxide solution are 10-20：60-100：
60-80。
Preferably, in S1, bamboo wood is removed into delimbing, leaf, splits to obtain a width of 4-10cm bamboo chip, 70-80 DEG C of dry 2-4h,
Obtain pre-processing bamboo wood；10-20 parts are pre-processed into bamboo wood by weight, add the salt that 60-100 parts concentration is 0.2-0.6mol/L
20-40min is stood in acid solution, is filtered, natural air drying, it is molten to add the sodium hydroxide that 60-80 parts concentration is 0.4-0.9mol/L
1-2h is stood in liquid, obtains A materials.
Preferably, in S2, A materials are subjected to carbonization treatment 2-4h, carburizing temperature is 200-220 DEG C, carbonization pressure 4-
6Mpa, it is then sent to flattening on hot press and obtains B materials.
Preferably, in S3, it is molten that 30-40 part B materials are sent into the ethanol that 80-120 parts concentration is 50-70wt% by weight
In liquid, 2-4 parts Cocoamidopropyl betaine, the stirring of 2-5 parts butyl titanate are added, it is 1-2mol/L's to add 3-6 parts concentration
Hydrochloric acid, 1-2 parts urea, 0.6-0.8 part citric acid complexs silver nitrate, 8-14 part microcrystalline waxes, heating stirring, are filtered, and are washed, and are done
It is dry, dry, braiding obtains the bamboo mat for cable outer packing.
Preferably, in S3, it is molten that 30-40 part B materials are sent into the ethanol that 80-120 parts concentration is 50-70wt% by weight
In liquid, 2-4 parts Cocoamidopropyl betaine, 2-5 parts butyl titanate stirring 20-30min are added, it is 1- to add 3-6 parts concentration
2mol/L hydrochloric acid, 1-2 parts urea, 0.6-0.8 part citric acid complexs silver nitrate, 8-14 part microcrystalline waxes, is warming up to 130-140
DEG C stirring 2-4h, filter, wash, dry, 75-85 DEG C of drying, braiding obtain the bamboo mat for cable outer packing.
Bamboo wood is removed delimbing, Ye Hou by the present invention, after drying after peracid alkali process, can by sugared part inside bamboo wood, air,
Impurity etc. is extracted out, is removed moth needed nutrient matter, is left behind wood fibre, prevent bacteriological aftergrowth, and is not easy to be damaged by worms, can
To the effective softening of bamboo fiber bundle, it is effectively formed internal stress and releases the slow line of rabbet joint, effectively remove surface stress, make forming material using process
In the release of its internal stress have the passage of science, ensure that shaping bamboo mat stability in use；In certain high pressure and mistake
Under vapours state, bamboo material surface carbonization, bacterium and the worm's ovum inside bamboo wood can be thoroughly killed；Using urea as nitrogen source, in lemon
In the presence of acid complexing silver nitrate, nitrogen is combined with silver ion codope with the bamboo fibre after carbonization, not only heat endurance pole
It is good, and it is fabulous to effectively improve bamboo fibre bactericidal and bacteriostatic effect；Simultaneously because be grafted on bamboo fibre surface, therefore in bamboo
Fiber surface forms layer protecting film layer, obstructs the contact of ambient atmos, can further prevent the water in bamboo fibre absorption air
Point and gas, play anti-corrosion, distortion-free effect.
Embodiment
Below, technical scheme is described in detail by specific embodiment.
Embodiment 1
A kind of bamboo mat preparation method for cable outer packing proposed by the present invention, comprises the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain bamboo chip, be dried to obtain pretreatment bamboo wood；Bamboo wood will be pre-processed, will be added
Stand, filter, natural air drying in hydrochloric acid solution, add standing in sodium hydroxide solution and obtain A materials；
S2, A materials are subjected to carbonization treatment, are then sent on hot press flattening and obtain B materials；
S3, will B materials be sent into ethanol solution in, add Cocoamidopropyl betaine, butyl titanate stirring, add salt
Acid, urea, citric acid complex silver nitrate, microcrystalline wax, heating stirring, are filtered, and are washed, and are dried, and are dried, and braiding obtains being used for electricity
The bamboo mat of cable outer packing.
Embodiment 2
A kind of bamboo mat preparation method for cable outer packing proposed by the present invention, comprises the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain a width of 4-10cm bamboo chip, 70 DEG C of dry 4h, obtain pre-processing bamboo
Material；Bamboo wood is pre-processed by 10 parts by weight, adds in the hydrochloric acid solution that 100 parts of concentration are 0.2mol/L and stands 40min, mistake
Filter, natural air drying, add in the sodium hydroxide solution that 60 parts of concentration are 0.9mol/L and stand 1h, obtain A materials；
S2, A materials are carried out to carbonization treatment 4h, carburizing temperature is 200 DEG C, carbonization pressure 6Mpa, is then sent to hot pressing
Flattening obtains B materials on machine；
S3,30 parts of B materials are sent into the ethanol solution that 120 parts of concentration are 50wt% by weight, add 4 parts of cocounut oil acyls
Amine CAB, 2 parts of butyl titanate stirring 30min, add hydrochloric acid, 1 part of urea, 0.8 portion of lemon that 3 parts of concentration are 2mol/L
Acid complexing silver nitrate, 8 parts of microcrystalline waxes, 140 DEG C of stirring 2h are warming up to, filters, washs, dry, 85 DEG C of dryings, braiding is used
In the bamboo mat of cable outer packing.
Embodiment 3
A kind of bamboo mat preparation method for cable outer packing proposed by the present invention, comprises the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain a width of 4-10cm bamboo chip, 80 DEG C of dry 2h, obtain pre-processing bamboo
Material；Bamboo wood is pre-processed by 20 parts by weight, adds in the hydrochloric acid solution that 60 parts of concentration are 0.6mol/L and stands 20min, filter,
Natural air drying, add in the sodium hydroxide solution that 80 parts of concentration are 0.4mol/L and stand 2h, obtain A materials；
S2, A materials are carried out to carbonization treatment 2h, carburizing temperature is 220 DEG C, carbonization pressure 4Mpa, is then sent to hot pressing
Flattening obtains B materials on machine；
S3,40 parts of B materials are sent into the ethanol solution that 80 parts of concentration are 70wt% by weight, add 2 parts of cocounut oil acyls
Amine CAB, 5 parts of butyl titanate stirring 20min, add hydrochloric acid, 2 parts of urea, 0.6 portion of lemon that 6 parts of concentration are 1mol/L
Acid complexing silver nitrate, 14 parts of microcrystalline waxes, 130 DEG C of stirring 4h are warming up to, filters, washs, dry, 75 DEG C of dryings, braiding obtains
Bamboo mat for cable outer packing.
Embodiment 4
A kind of bamboo mat preparation method for cable outer packing proposed by the present invention, comprises the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain a width of 4-10cm bamboo chip, 72 DEG C of dry 3.5h, obtain pre-processing bamboo
Material；Bamboo wood is pre-processed by 12 parts by weight, adds in the hydrochloric acid solution that 90 parts of concentration are 0.3mol/L and stands 35min, filter,
Natural air drying, add in the sodium hydroxide solution that 65 parts of concentration are 0.7mol/L and stand 1.2h, obtain A materials；
S2, A materials are carried out to carbonization treatment 3.5h, carburizing temperature is 205 DEG C, carbonization pressure 5.5Mpa, is then sent to
Flattening obtains B materials on hot press；
S3,32 parts of B materials are sent into the ethanol solution that 110 parts of concentration are 55wt% by weight, add 3.5 portions of cocounut oil
Amido propyl betaine, 3 parts of butyl titanates stirring 28min, add hydrochloric acid, 1.4 parts of urea that 4 parts of concentration are 1.6mol/L,
0.75 part of citric acid complex silver nitrate, 10 parts of microcrystalline waxes, 138 DEG C of stirring 2.5h are warming up to, filters, washs, dry, 82 DEG C dry
Dry, braiding obtains the bamboo mat for cable outer packing.
Embodiment 5
A kind of bamboo mat preparation method for cable outer packing proposed by the present invention, comprises the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain a width of 4-10cm bamboo chip, 78 DEG C of dry 2.5h, obtain pre-processing bamboo
Material；Bamboo wood is pre-processed by 18 parts by weight, adds in the hydrochloric acid solution that 70 parts of concentration are 0.5mol/L and stands 25min, filter,
Natural air drying, add in the sodium hydroxide solution that 75 parts of concentration are 0.5mol/L and stand 1.8h, obtain A materials；
S2, A materials are carried out to carbonization treatment 2.5h, carburizing temperature is 215 DEG C, carbonization pressure 4.5Mpa, is then sent to
Flattening obtains B materials on hot press；
S3,38 parts of B materials are sent into the ethanol solution that 90 parts of concentration are 65wt% by weight, add 2.5 portions of cocounut oil
Amido propyl betaine, 4 parts of butyl titanates stirring 22min, add hydrochloric acid, 1.8 parts of urea that 5 parts of concentration are 1.2mol/L,
0.65 part of citric acid complex silver nitrate, 12 parts of microcrystalline waxes, 132 DEG C of stirring 3.5h are warming up to, filters, washs, dry, 78 DEG C dry
Dry, braiding obtains the bamboo mat for cable outer packing.
Embodiment 6
A kind of bamboo mat preparation method for cable outer packing proposed by the present invention, comprises the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain a width of 4-10cm bamboo chip, 75 DEG C of dry 3h, obtain pre-processing bamboo
Material；Bamboo wood is pre-processed by 15 parts by weight, adds in the hydrochloric acid solution that 80 parts of concentration are 0.4mol/L and stands 30min, filter,
Natural air drying, add in the sodium hydroxide solution that 70 parts of concentration are 0.6mol/L and stand 1.5h, obtain A materials；
S2, A materials are carried out to carbonization treatment 3h, carburizing temperature is 210 DEG C, carbonization pressure 5Mpa, is then sent to hot pressing
Flattening obtains B materials on machine；
S3,35 parts of B materials are sent into the ethanol solution that 100 parts of concentration are 60wt% by weight, add 3 parts of cocounut oil acyls
Amine CAB, 3.5 parts of butyl titanates stirring 25min, add hydrochloric acid, 1.6 parts of urea that 4.5 parts of concentration are 1.4mol/L,
0.7 part of citric acid complex silver nitrate, 11 parts of microcrystalline waxes, 135 DEG C of stirring 3h are warming up to, filters, washs, dry, 80 DEG C of dryings,
Braiding obtains the bamboo mat for cable outer packing.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (7)
1. a kind of bamboo mat preparation method for cable outer packing, it is characterised in that comprise the following steps：
S1, bamboo wood is gone to delimbing, leaf, split to obtain bamboo chip, be dried to obtain pretreatment bamboo wood；Bamboo wood will be pre-processed, adds hydrochloric acid
Stand, filter, natural air drying in solution, add standing in sodium hydroxide solution and obtain A materials；
S2, A materials are subjected to carbonization treatment, are then sent on hot press flattening and obtain B materials；
S3, will B materials be sent into ethanol solution in, add Cocoamidopropyl betaine, butyl titanate stirring, add hydrochloric acid, urine
Element, citric acid complex silver nitrate, microcrystalline wax, heating stirring, are filtered, and are washed, and are dried, and are dried, and braiding obtains being used for outside cable
The bamboo mat of packaging.
2. it is used for the bamboo mat preparation method of cable outer packing according to claim 1, it is characterised in that in S1, hydrochloric acid solution
Concentration be 0.2-0.6mol/L, the concentration of sodium hydroxide solution is 0.4-0.9mol/L.
3. the bamboo mat preparation method according to claim 1 or claim 2 for cable outer packing, it is characterised in that in S1, pretreatment
Bamboo wood, hydrochloric acid solution, the weight ratio of sodium hydroxide solution are 10-20：60-100：60-80.
4. it is used for the bamboo mat preparation method of cable outer packing according to claim any one of 1-3, it is characterised in that in S1,
Bamboo wood is removed into delimbing, leaf, splits to obtain a width of 4-10cm bamboo chip, 70-80 DEG C of dry 2-4h, obtains pre-processing bamboo wood；By weight
Measure part and 10-20 parts are pre-processed into bamboo wood, add in the hydrochloric acid solution that 60-100 parts concentration is 0.2-0.6mol/L and stand 20-
40min, filtering, natural air drying, add in the sodium hydroxide solution that 60-80 parts concentration is 0.4-0.9mol/L and stand 1-2h, obtain
To A materials.
5. it is used for the bamboo mat preparation method of cable outer packing according to claim any one of 1-4, it is characterised in that in S2,
A materials are subjected to carbonization treatment 2-4h, carburizing temperature is 200-220 DEG C, carbonization pressure 4-6Mpa, is then sent on hot press
Flattening obtains B materials.
6. it is used for the bamboo mat preparation method of cable outer packing according to claim any one of 1-5, it is characterised in that in S3,
30-40 part B materials are sent into the ethanol solution that 80-120 parts concentration is 50-70wt% by weight, add 2-4 part cocounut oil acyls
Amine CAB, the stirring of 2-5 parts butyl titanate, add hydrochloric acid, 1-2 parts urea, 0.6- that 3-6 parts concentration is 1-2mol/L
0.8 part of citric acid complex silver nitrate, 8-14 part microcrystalline waxes, heating stirring, are filtered, and are washed, and are dried, and are dried, and braiding is used
In the bamboo mat of cable outer packing.
7. it is used for the bamboo mat preparation method of cable outer packing according to claim any one of 1-6, it is characterised in that in S3,
30-40 part B materials are sent into the ethanol solution that 80-120 parts concentration is 50-70wt% by weight, add 2-4 part cocounut oil acyls
Amine CAB, 2-5 parts butyl titanate stirring 20-30min, it is 1-2mol/L hydrochloric acid, 1-2 parts urine to add 3-6 parts concentration
Element, 0.6-0.8 part citric acid complexs silver nitrate, 8-14 part microcrystalline waxes, 130-140 DEG C of stirring 2-4h is warming up to, filtering, is washed
Wash, dry, 75-85 DEG C of drying, braiding obtains the bamboo mat for cable outer packing.