CN1074193A - Continuous production technology for edible phosphoric acid

Info

Publication number: CN1074193A
Application number: CN 92110527
Authority: CN
Inventors: 项耀明; 张照; 朱英杰; 李仁琇; 于立新; 毛朗
Original assignee: PHOSPHORUS INDUSTRY Co YUNNAN PROV
Current assignee: PHOSPHORUS INDUSTRY Co YUNNAN PROV
Priority date: 1992-09-08
Filing date: 1992-09-08
Publication date: 1993-07-14
Anticipated expiration: 2007-09-08
Also published as: CN1032581C

Abstract

The present invention is a raw material with hot method industrial phosphoric acid (86%), adds P ₂S ₅A certain amount of dearsenic agent of solid and NaOH solution preparation, under the situation of continuous dosing, through stirs, leave standstill, vacuum filtration, packing tower blowing H ₂S and commute oxide process obtain food grade phosphoric acid, and the thickness of laying super-cell during filtration is not less than 4 millimeters.

Description

Continuous production technology for edible phosphoric acid

The present invention relates to hot method industrial phosphoric acid is raw material, removes the production technique that harmful toxic substances such as arsenic, lead are produced food grade phosphoric acid.

Food grade phosphoric acid and food-grade phosphate have been produced multi-series, many kinds, it is a kind of acidic flavoring agent of cheapness, and the production that is used for milk preparation, meat product, fishery products and various beverages in a large number has and adjusts structure and the color, smell and taste sensory trait that improves food as foodstuff additive.Food grade phosphoric acid is in China and all be in great demand in the world.China has made the standard GB 3149-82 " foodstuff additive-phosphoric acid " of food grade phosphoric acid.Food grade phosphoric acid is produced after can adopting hot method industrial phosphoric acid or wet method industrial phosphoric acid to purify, and hot method industrial phosphoric acid hazardous and noxious substances content is low, and treatment process is fairly simple, but consumption of calorie is higher; Adopt though low with wet method industrial phosphoric acid energy consumption, the purification reparation technology is comparatively complicated, be difficult to general manufacturer.

The method that adopts hot method industrial phosphoric acid to produce food grade phosphoric acid mainly contains chemical purification (also claiming specific composition to remove method), electrolytic process and crystallization process.

The chemical purification of knowing so far, all the industrial phosphoric acid with 75% concentration purifies and produces, and needs earlier the product with 85% be diluted to 75%, remove impurity after, also to heat and just can dispatch from the factory after being concentrated to 85% national standard, dilute, concentrate two treating processess.Scavenging process can not carry out continuously in addition, feeds intake and produces next still but produce a still (groove), thereby yield poorly, and floor space is big, the energy consumption height.

The objective of the invention is to avoid above-mentioned weak point of the prior art and a kind of continuous production technology for edible phosphoric acid is provided, its energy continuous production improve output, and vitriol produces still less in oxidising process, and product colourity improves.

Purpose of the present invention can reach by following measure: add with solid P in the dearsenification still ₂S ₅A certain amount of dearsenic agent with the 0.5%NaOH preparation, in still, feed intake continuously, stirred 0.5-1 hour down at 80-85 ℃, by the potential difference overflow, flow into one and leave standstill the cohesion still, time of repose 2.5-3 hour, flow into the filter vat vacuum filtration through pipeline again, be covered with super-cell in the filter vat, flow in the packing tower after filtering and remove H ₂S, the pressurized air that is blown in acid enters through a plate-type heat exchanger, and the acid temperature keeps 60-80 ℃, stirs and blows down to H ₂S concentration enters stills for air blowing again and does the readily oxidizable substance processing less than 0.0075%, and its condition is 80-90 ℃ and is incubated 2 hours, H down ₂O ₂Add-on be theoretical 200-300%.

The dearsenification still, leave standstill still, filter plant, all link to each other between each equipment such as packing tower and stills for air blowing with pipeline.

The present invention is described in further detail below in conjunction with drawings and Examples:

Fig. 1 is the continuous food grade phosphoric acid technological process of production that proposes according to the present invention.

As shown in the figure, its working condition is:

(1) raw material

1,86% industrial phosphoric acid, its index is as follows:

Composition

H ₃PO ₄

Colourity

Muriate (Cl)

Vitriol (SO ₄)

Iron

Arsenic (AS)

Heavy metal is in Pb

Content

85.67%

10

0.0002％

0.0005％

0.0002％

0.005％

0.0008％

2, thiophosphoric anhydride

P ₂O ₅Content: 92%

3, hydrogen peroxide

H ₂O ₂：30%

4, Yunnan Province's Tengchong Mh type algae soil

Index is as follows:

Composition	SiO ₂	Fe ₂o ₃	Al ₂O ₃	Cao	Mgo	PH	The salt acid-soluble substance	The water solubles	Weight loss on drying
										Content	91.22	0.51	2.72	0.51	0.30	7.5	1.27	0.31	0.06

5, sodium hydroxide chemical pure

NaOH 96%

(2) reaction mechanism

Arsenic is many with arsenus acid (H in industrial phosphoric acid ₃AsO ₃) form exist, and lead is to exist with phosphatic form, they all with the thiophosphoric anhydride hydrolysis after the H that produces ₂S generates precipitation.Its chemical equation is:

In cold phosphoric acid solution, this reaction is carried out very slow, is heated to 80-90 ℃ and then can reacts rapidly.This characteristic reactions is the technology basis of phosphoric acid purification dearsenification.

(3) continuous processing flow process:

1, preparation contains P in 50 grams per liter NaOH solution ₂S ₅The dearsenic agent solution of 30 grams per liters.Select for use 0.5%NaOH solution to make dissolving P ₂S ₅Solvent, though bring sodium ion into, a small amount of sodium ion does not influence the quality of phosphoric acid for food, and it is fast to have a dissolving, does not have H substantially ₂S evaporable advantage.Dearsenic agent solution is placed on high-order bottle, and usefulness+word folder dominant discharge adds the dearsenification still, and consumption is a theoretical amount 150%, is placed on the elevated industrial phosphoric acid simultaneously and adds the dearsenification still, and charging capacity is 2.7 liters/hour.In the still chuck, feed steam and heat, treat that the phosphoric acid temperature is raised to 80 ℃ in the still, open agitator, 13 meters/minute of stirring intensities, about 30 minutes of reaction times.

2, the overflow of phosphoric acid potential difference enters and leaves standstill the cohesion still in the still, reaches after certain treatment capacity 80-85 ℃ of insulation, leaves standstill 2.30 hours.

Through leaving standstill for some time, help H ₂Reaction such as S and arsenic, heavy metal lead generates red arsenic and metallic sulfide precipitation, and reaction time is long, and coacervation of colloid helps to filter better.

3, leave standstill in the still phosphoric acid and send into vacuum filter through pipeline and filter, to remove arsenic, the heavy metal sulfide precipitation that forms in the disacidify.Filtration condition: the suction filtration vacuum is the 60-100mmHg post, and filtering layer adopts one deck terylen 208 filter clothes at least, lays the diatomite of treated mistake on the filter cloth, and its thickness is not less than 4mm.Through test, guarantee that the colloid thing do not wear filter, and intensity filter reduces few.Diatomite should be selected SO for use ₄Content is low.

4, take off H ₂S.In the work in-process acid after the filtration, also be dissolved with a spot of H ₂S removes H ₂S carries out in the packing tower that is evenly equipped with wadding (as polypropylene), and chuck feeds steam heating phosphoric acid in tower, feeds filtrated air in acid, and filtered air just feeds after one group of plate-type heat exchanger preheating in the tower in the acid, and sour temperature remains on 60-80 ℃ and blows and catch up with H ₂S blows down to H ₂S concentration is less than 0.0075%.Blowing is complete as far as possible, otherwise when hydrogen peroxide was handled, product colourity may be defective.Hydrogen sulfide is through aiutage emptying.

5, take off H ₂Phosphoric acid behind the S carries out oxide process in pipeline is sent into stills for air blowing, be incubated 2 hours down at 80-90 ℃, and the add-on of hydrogen peroxide is the 200-300% of theoretical amount.

Full scale production process successive reaction is after 7 hours, and sampling analysis was taken a sample once every 2 hours, and detecting whole indexs qualified is phosphoric acid for food, can the finished product packing warehouse-in.

In Production Flow Chart provided by the invention, dearsenic agent, hydrogen peroxide etc. all may be brought less water into, thereby phosphoric acid quality is wanted strict control, preferably concentration is greater than 86%, in addition, because hydrogen peroxide is all easily brought trace sulfate in diatomite, dearsenic agent solution and the process, therefore, raw material acid preferably selects for use sulphate content low.Equipment used and pipeline should select the few corrosion resistant material of impurity to manufacture in the production.

Continuity method production technology provided by the invention is compared batch process production and is had following advantage: continuous dosing, thereby output improves greatly, reaction is the solution shape with Hydrodearsenic Catalyst, and is easy to control even; Adopt packed tower to blow down H₂S is more thorough, and effect is better, and sulfate produces and lacks in oxidizing process, thereby product colourity improves; Whole flow process does not produce the phosphorus loss basically, and the material balance power consumption is low. Save 30% with the investment of comparing of the batch process phosphoric acid for food production technology of identical scale, operating personnel reduce 20%, can introduce microcomputer and carry out the computer control operation.

Claims

1, continuous production technology for edible phosphoric acid feeds H in industrial phosphoric acid ₂S, under the certain temperature condition, H ₂S and arsenic, reaction such as heavy metal lead generate red arsenic and the metallic sulfide shallow lake is heavy, sends into filter vat and filter, and disgorging feeds pressurized air in the acid after the filtration, remove H ₂S, it is characterized in that: in the dearsenification still, feed intake continuously, under 80-85 ℃ of temperature, in still, add dearsenic agent consumption 150-300%, stirred 0.5-1 hour, stirring intensity is 13 meters/minute, relies on the potential difference overflow to send into the cohesion still and leaves standstill 2.5-3 hour, send into the filter vat of laying the diatomite filtration layer through pipeline again, the acid after the filtration flows into packing tower and removes H ₂S, the acid temperature remains on 60-80 ℃ during blowing, removes H ₂Phosphoric acid is sent into stills for air blowing behind the S, adds H ₂O ₂Be the 200-300% of theoretical amount, be incubated 2 hours down at 80-90 ℃.

2, production technology according to claim 1 is characterized in that dearsenic agent is 0.5%NaOH and solid P ₂S ₅Formulated.

3, production technology according to claim 1 is characterized in that the diatomite bed thickness of laying in the filter vat is not less than 4mm on filter cloth, the suction filtration vacuum is the 60-100mmHg post.

4, production technology according to claim 1 is characterized in that removing H ₂S carries out in being evenly equipped with the packing tower of wadding, and the pressurized air of feeding preheats to 60 ℃ through one group of plate-type heat exchanger.