CN107419362A - A kind of ageing-resistant fishing net - Google Patents
A kind of ageing-resistant fishing net Download PDFInfo
- Publication number
- CN107419362A CN107419362A CN201710334603.9A CN201710334603A CN107419362A CN 107419362 A CN107419362 A CN 107419362A CN 201710334603 A CN201710334603 A CN 201710334603A CN 107419362 A CN107419362 A CN 107419362A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- ageing
- composite
- resistant
- montmorillonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ageing-resistant fishing net, including:Dispensing, melting extrusion, cooling preliminary draft, drafting forming, wind, line processed, knitmesh;The ageing-resistant fishing net that the present invention makes has preferable ageing-resistant performance, the composite of polyamide fibre 6 is made by the modification to chinlon 6 section, the stability and resistance to ag(e)ing of fishing net made of can improving, by using treated montmorillonite, nano titanium oxide, epoxidized soybean oil carries out mixing with chinlon 6 section and composite is made, the molecule of polyamide fibre 6 is enabled to contain flexible group, manufactured composite has reactivity height, the features such as adhesive force is strong, to heat, photochemistry, oxidation Decomposition has good tolerance, so as to greatly improve the ageing-resistant performance of manufactured fishing net.
Description
Technical field
The invention belongs to fishing net preparing technical field, and in particular to a kind of ageing-resistant fishing net.
Background technology
Fishing net is the net of fishing, and men of old uses coarse cloth to be used as raw material plus fiber crops, and fishnet is made by the method for tying volume.
Although this fishing net is perishable, toughness is poor, and it is fished efficiency and greatly improved.With the development of fishery, fishing and hunting
Object is more than fish, and the instrument of fishing also grows with each passing hour.Men of old uses coarse cloth to be used as raw material plus fiber crops, the method by tying volume
Fishnet is made.Although this fishing net is perishable, toughness is poor, and it is fished efficiency and greatly improved.With the hair of fishery
Exhibition, the object of fishing and hunting are more than fish, and the instrument of fishing also grows with each passing hour.Modern fishing net mainly uses the raw material such as polyethylene, nylon
It is processed, has longer service life, and higher catching rate, but existing fishing net makes to being chronically exposed in air
With the requirement of its resistance to ag(e)ing gradually needs to improve, due to the comprehensive function of the factors such as light, oxygen, heat, water so that fishing net pole
Easily there is aging, reduce fishing net service life.
The content of the invention
The purpose of the present invention is to be directed to the problem of existing, there is provided a kind of ageing-resistant fishing net.
The present invention is achieved by the following technical solutions:
A kind of ageing-resistant fishing net, comprises the following steps:
(1)Dispensing:
By weight by terylene 2.0-2.5, glass fibre 1.4-1.8, dimethicone 0.3-0.7, the fourth of phthalic acid two
Ester 0.2-0.5, sodium alginate 0.3-0.6, the composite 70-80 of modified nylon 6 are mixed, and obtain compound;The modification
The composite material and preparation method thereof of polyamide fibre 6 is:Hexadecyltrimethylammonium chloride and water are pressed 1:After 83 mass ratio uniformly mixes,
Hexadecyltrimethylammonium chloride solution is obtained, montmorillonite of the particle diameter at 20-25 μm is then used into mass fraction as 2.5%
Hydrochloric acid solution soaks 30min at 45 DEG C, then filters, deionized water washing, drying, then with hexadecyltrimethylammonium chloride
Solution presses 1:80 mass ratios mix, and are heated to 55 DEG C, stir 40min with 250r/min rotating speeds, then filter, deionization washing
Wash, dry, treated montmorillonite is obtained, by treated montmorillonite, epoxidized soybean oil, nano titanium oxide, polyamide fibre 6
Section presses 2:1:0.12:100 mass ratios uniformly after mixing, carry out being kneaded in banbury and fusion intercalation are compound, be kneaded temperature
Spend for 168 DEG C, mixing time 12min, obtain the composite of modified nylon 6;
(2)Melting extrusion:
The compound prepared stirs by plastic extruder melting extrusion;
(3)Cool down preliminary draft:The fiber of melting extrusion is put into 18 DEG C of tanks of temperature and cooled down, 3.5 times of pre-draft multiple, after cooling
Monfil carry out drawing-off, drawing temperature be 82 DEG C, 10 times of drafting multiple;
(4)Drafting forming:
The monofilament being drawn through is shaped, and setting temperature is 94 DEG C, relaxation shrinkage 2.4%;
(5)Winding:
The monfil shaped is batched on winder with winding tension 250cN, coiling speed 120m/min;
(6)Line processed:
By monofilament be made 80-100 twists/m of the twist, a diameter of 0.3-0.8mm netting twine;
(7)Knitmesh:
The a length of 10-100mm of mesh fishing net is spun into the netting twine.
Further, the montmorillonite cation exchange capacity (CEC) is 82-88mol/100g.
Further, the nano titanium oxide granularity is 30-32nm.
The present invention has advantages below compared with prior art:The ageing-resistant fishing net that the present invention makes has preferably ageing-resistant
Performance, the composite of polyamide fibre 6 is made by the modification to chinlon 6 section, can improve made of fishing net stability and
Resistance to ag(e)ing, it is kneaded by using treated montmorillonite, nano titanium oxide, epoxidized soybean oil and chinlon 6 section
Composite is made, the molecular chain structure of polyamide fibre 6 can be changed so that the molecule of polyamide fibre 6 contains flexible group, manufactured composite wood
Material has the characteristics that reactivity is high, adhesive force is strong, has good tolerance to heat, photochemistry, oxidation Decomposition, so as to greatly
Improve made of fishing net ageing-resistant performance.
Embodiment
Embodiment 1
A kind of ageing-resistant fishing net, comprises the following steps:
(1)Dispensing:
By weight by terylene 2.0, glass fibre 1.4, dimethicone 0.3, dibutyl phthalate 0.2, alginic acid
Sodium 0.3, the composite 70 of modified nylon 6 are mixed, and obtain compound;The composite material and preparation method thereof of modified nylon 6 is:
Hexadecyltrimethylammonium chloride and water are pressed 1:83 mass ratio uniformly after mixing, obtains hexadecyltrimethylammonium chloride
Solution, then mass fraction is used to soak 30min at 45 DEG C for 2.5% hydrochloric acid solution montmorillonite of the particle diameter at 20 μm, so
After filter, deionized water washing, drying, then with hexadecyltrimethylammonium chloride solution press 1:80 mass ratios mix, heating
To 55 DEG C, 40min is stirred with 250r/min rotating speeds, then filtered, deionized water washing, drying, obtained treated cover and take off
Soil, treated montmorillonite, epoxidized soybean oil, nano titanium oxide, chinlon 6 section are pressed 2:1:0.12:100 mass ratios
Uniformly after mixing, carrying out being kneaded in banbury and fusion intercalation is compound, melting temperature is 168 DEG C, mixing time 12min,
Obtain the composite of modified nylon 6;
(2)Melting extrusion:
The compound prepared stirs by plastic extruder melting extrusion;
(3)Cool down preliminary draft:The fiber of melting extrusion is put into 18 DEG C of tanks of temperature and cooled down, 3.5 times of pre-draft multiple, after cooling
Monfil carry out drawing-off, drawing temperature be 82 DEG C, 10 times of drafting multiple;
(4)Drafting forming:
The monofilament being drawn through is shaped, and setting temperature is 94 DEG C, relaxation shrinkage 2.4%;
(5)Winding:
The monfil shaped is batched on winder with winding tension 250cN, coiling speed 120m/min;
(6)Line processed:
By monofilament be made 80 twists/m of the twist, a diameter of 0.3mm netting twine;
(7)Knitmesh:
The a length of 10mm of mesh fishing net is spun into the netting twine.
The montmorillonite cation exchange capacity (CEC) is 82mol/100g.
The nano titanium oxide granularity is 30nm.
Embodiment 2
A kind of ageing-resistant fishing net, comprises the following steps:
(1)Dispensing:
By weight by terylene 2.5, glass fibre 1.8, dimethicone 0.7, dibutyl phthalate 0.5, alginic acid
Sodium 0.6, the composite 80 of modified nylon 6 are mixed, and obtain compound;The composite material and preparation method thereof of modified nylon 6 is:
Hexadecyltrimethylammonium chloride and water are pressed 1:83 mass ratio uniformly after mixing, obtains hexadecyltrimethylammonium chloride
Solution, then mass fraction is used to soak 30min at 45 DEG C for 2.5% hydrochloric acid solution montmorillonite of the particle diameter at 25 μm, so
After filter, deionized water washing, drying, then with hexadecyltrimethylammonium chloride solution press 1:80 mass ratios mix, heating
To 55 DEG C, 40min is stirred with 250r/min rotating speeds, then filtered, deionized water washing, drying, obtained treated cover and take off
Soil, treated montmorillonite, epoxidized soybean oil, nano titanium oxide, chinlon 6 section are pressed 2:1:0.12:100 mass ratios
Uniformly after mixing, carrying out being kneaded in banbury and fusion intercalation is compound, melting temperature is 168 DEG C, mixing time 12min,
Obtain the composite of modified nylon 6;
(2)Melting extrusion:
The compound prepared stirs by plastic extruder melting extrusion;
(3)Cool down preliminary draft:The fiber of melting extrusion is put into 18 DEG C of tanks of temperature and cooled down, 3.5 times of pre-draft multiple, after cooling
Monfil carry out drawing-off, drawing temperature be 82 DEG C, 10 times of drafting multiple;
(4)Drafting forming:
The monofilament being drawn through is shaped, and setting temperature is 94 DEG C, relaxation shrinkage 2.4%;
(5)Winding:
The monfil shaped is batched on winder with winding tension 250cN, coiling speed 120m/min;
(6)Line processed:
By monofilament be made 100 twists/m of the twist, a diameter of 0.8mm netting twine;
(7)Knitmesh:
The a length of 100mm of mesh fishing net is spun into the netting twine.
The montmorillonite cation exchange capacity (CEC) is 88mol/100g.
The nano titanium oxide granularity is 32nm.
Embodiment 3
A kind of ageing-resistant fishing net, comprises the following steps:
(1)Dispensing:
By weight by terylene 2.2, glass fibre 1.6, dimethicone 0.5, dibutyl phthalate 0.3, alginic acid
Sodium 0.4, the composite 75 of modified nylon 6 are mixed, and obtain compound;The composite material and preparation method thereof of modified nylon 6 is:
Hexadecyltrimethylammonium chloride and water are pressed 1:83 mass ratio uniformly after mixing, obtains hexadecyltrimethylammonium chloride
Solution, then mass fraction is used to soak 30min at 45 DEG C for 2.5% hydrochloric acid solution montmorillonite of the particle diameter at 22 μm, so
After filter, deionized water washing, drying, then with hexadecyltrimethylammonium chloride solution press 1:80 mass ratios mix, heating
To 55 DEG C, 40min is stirred with 250r/min rotating speeds, then filtered, deionized water washing, drying, obtained treated cover and take off
Soil, treated montmorillonite, epoxidized soybean oil, nano titanium oxide, chinlon 6 section are pressed 2:1:0.12:100 mass ratios
Uniformly after mixing, carrying out being kneaded in banbury and fusion intercalation is compound, melting temperature is 168 DEG C, mixing time 12min,
Obtain the composite of modified nylon 6;
(2)Melting extrusion:
The compound prepared stirs by plastic extruder melting extrusion;
(3)Cool down preliminary draft:The fiber of melting extrusion is put into 18 DEG C of tanks of temperature and cooled down, 3.5 times of pre-draft multiple, after cooling
Monfil carry out drawing-off, drawing temperature be 82 DEG C, 10 times of drafting multiple;
(4)Drafting forming:
The monofilament being drawn through is shaped, and setting temperature is 94 DEG C, relaxation shrinkage 2.4%;
(5)Winding:
The monfil shaped is batched on winder with winding tension 250cN, coiling speed 120m/min;
(6)Line processed:
By monofilament be made 90 twists/m of the twist, a diameter of 0.5mm netting twine;
(7)Knitmesh:
The a length of 600mm of mesh fishing net is spun into the netting twine.
The montmorillonite cation exchange capacity (CEC) is 85mol/100g.
The nano titanium oxide granularity is 31nm.
Comparative example 1:Step is differed only in embodiment 1(1)The middle brocade that the composite of polyamide fibre 6 is replaced with to common equivalent
Synthetic fibre 6 is cut into slices.
Comparative example 2:Step is differed only in embodiment 1(1)The middle composite of polyamide fibre 6 is not added in preparing by processing
Montmorillonite.
Comparative example 3:Step is differed only in embodiment 1(1)The middle composite of polyamide fibre 6 does not add nano-silica in preparing
Change titanium.
Artificial accelerated aging test:
Instrument uses the Japanese weather-proof instrument of WEL-SUN-DC sunlight types, and condition is Continuous irradiation:43 ± 2 DEG C of test flume temperature, blackboard
58 ± 1 DEG C of generation trough temperature, humidity generation trough relative humidity 65-70%, rainfall cycle 12 divide/hour, will be single made of polyamide fibre 6
Silk, fishing lines made of embodiment, fishing lines made of comparative example are rotating around being 0.1cm aluminium sheets in long 30cm, wide 8cm, thickness
On, around when adjacent filaments and line it is not overlapping, then model is fixed on ageing oven specimen holder and operated, carry out Continuous irradiation, periodically
Sampling, sample sampling Hou Zai laboratories keep after being balanced 24 hours under standard atmosphere condition, tested, tester uses state
Y361-30, Y361-3 strength tester are produced, condition is:20 ± 2 DEG C of room temperature, relative humidity are 65 ± 5%, and decrease speed is
300mm/min, upper and lower clamp distance 200mm, by a single line knot is made a call among every sample, write down in testing when breaking nodule
Peak load, every sample test 8-10 times, takes arithmetic average,(Embodiment uses 1mm with comparative example fishing line fineness)It is right
Than:
Table 1
As can be seen from Table 1, fishing net ageing-resistant performance made of adding the composite of polyamide fibre 6 of the inventive method preparation obtains pole
Big raising, the composite of polyamide fibre 6 do not add fishing net resistance to ag(e)ing made of nano titanium oxide in preparing and slightly reduced, polyamide fibre
6 composites do not add fishing net resistance to ag(e)ing made of treated montmorillonite in preparing and declined to a certain extent.
Claims (3)
1. a kind of ageing-resistant fishing net, it is characterised in that comprise the following steps:
(1)Dispensing:
By weight by terylene 2.0-2.5, glass fibre 1.4-1.8, dimethicone 0.3-0.7, the fourth of phthalic acid two
Ester 0.2-0.5, sodium alginate 0.3-0.6, the composite 70-80 of modified nylon 6 are mixed, and obtain compound;The modification
The composite material and preparation method thereof of polyamide fibre 6 is:Hexadecyltrimethylammonium chloride and water are pressed 1:After 83 mass ratio uniformly mixes,
Hexadecyltrimethylammonium chloride solution is obtained, montmorillonite of the particle diameter at 20-25 μm is then used into mass fraction as 2.5%
Hydrochloric acid solution soaks 30min at 45 DEG C, then filters, deionized water washing, drying, then with hexadecyltrimethylammonium chloride
Solution presses 1:80 mass ratios mix, and are heated to 55 DEG C, stir 40min with 250r/min rotating speeds, then filter, deionization washing
Wash, dry, treated montmorillonite is obtained, by treated montmorillonite, epoxidized soybean oil, nano titanium oxide, polyamide fibre 6
Section presses 2:1:0.12:100 mass ratios uniformly after mixing, carry out being kneaded in banbury and fusion intercalation are compound, be kneaded temperature
Spend for 168 DEG C, mixing time 12min, obtain the composite of modified nylon 6;
(2)Melting extrusion:
The compound prepared stirs by plastic extruder melting extrusion;
(3)Cool down preliminary draft:The fiber of melting extrusion is put into 18 DEG C of tanks of temperature and cooled down, 3.5 times of pre-draft multiple, after cooling
Monfil carry out drawing-off, drawing temperature be 82 DEG C, 10 times of drafting multiple;
(4)Drafting forming:
The monofilament being drawn through is shaped, and setting temperature is 94 DEG C, relaxation shrinkage 2.4%;
(5)Winding:
The monfil shaped is batched on winder with winding tension 250cN, coiling speed 120m/min;
(6)Line processed:
By monofilament be made 80-100 twists/m of the twist, a diameter of 0.3-0.8mm netting twine;
(7)Knitmesh:
The a length of 10-100mm of mesh fishing net is spun into the netting twine.
2. a kind of ageing-resistant fishing net as claimed in claim 1, it is characterised in that the montmorillonite cation exchange capacity (CEC) is 82-
88mol/100g。
3. a kind of ageing-resistant fishing net as claimed in claim 1, it is characterised in that the nano titanium oxide granularity is 30-
32nm。