CN107418702A - A kind of auto parts electrophoretic process coolant - Google Patents
A kind of auto parts electrophoretic process coolant Download PDFInfo
- Publication number
- CN107418702A CN107418702A CN201710610459.7A CN201710610459A CN107418702A CN 107418702 A CN107418702 A CN 107418702A CN 201710610459 A CN201710610459 A CN 201710610459A CN 107418702 A CN107418702 A CN 107418702A
- Authority
- CN
- China
- Prior art keywords
- parts
- auto
- aluminum phosphate
- electrophoretic process
- vancomycin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of auto parts electrophoretic process coolant, is made up of the raw material components of following number:60~80 parts of tall oil diglycollic amide, 20~40 parts of cocoanut fatty acid diethanolamide, 6~10 parts of ethoxylated dodecyl alcohol sodium sulphate, 24~28 parts of vancomycin, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, 2~4 parts of benzoic acid, 2~4 parts of benzimidazole allyl sulphide, 2~4 parts of paranitrobenzoic acid, 1~2 part of sodium tetraborate, 2~3 parts of dimethyl maleic anhydride, deionized water is some, a kind of auto parts electrophoretic process coolant of the present invention can improve the cooling effect of auto parts process equipment, it is convenient to use as needed, it is easy to preferably be cooled down for auto parts process equipment.
Description
Technical field
The invention belongs to auto parts coolant technical field, and in particular to a kind of auto parts electrophoretic process coolant.
Background technology
Metal working fluid is mainly the liquid of intermetallic composite coating, main to play lubrication and cooling effect, has antirust cleaning etc. concurrently
Effect.In general metal working fluid includes cutting fluid, cutting oil, emulsion, punching oil, quenching medium, high temperature oil, extreme pressure cutting
Liquid, grinding fluid, antirust oil, cleaning agent, blackening agent for surface, drawing oil etc..Machining of metals liquid is a kind of low foam, high-lubricity
Soluble lubricating oil, it can also be preferably minimized maintenance cost under to the exigent environment of working fluid even if applying, basic energy
Suitable for all types of processing of each metalloid and alloy, its general processing to most of iron metals extremely proves effective, especially
It can give play to outstanding lubrication and cooling effect simultaneously in machined mild steel, cast iron, stainless steel and other special steels.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of auto parts electrophoretic process coolant, preferably improve automobile
The cooling effect of part process equipment, it is convenient to use as needed, it is easy to preferably cold for the progress of auto parts process equipment
But.
To realize above-mentioned technical purpose and the technique effect, the present invention is achieved through the following technical solutions:
A kind of auto parts electrophoretic process coolant, is made up of the raw material components of following number:Tall oil diglycollic amide
60~80 parts, 20~40 parts of cocoanut fatty acid diethanolamide, 6~10 parts of ethoxylated dodecyl alcohol sodium sulphate, it is mould through the ages
24~28 parts of element, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, benzoic acid 2~
4 parts, 2~4 parts of benzimidazole allyl sulphide, 2~4 parts of paranitrobenzoic acid, 1~2 part of sodium tetraborate, dimethyl maleic anhydride
2~3 parts, deionized water it is some.
Preferably, can be also made up of the raw material components of following number:60 parts of tall oil diglycollic amide, coco-nut oil fatty acid
20 parts of diglycollic amide, 6 parts of ethoxylated dodecyl alcohol sodium sulphate, 24 parts of vancomycin, 24 parts of ketoconazole, 26 parts of aluminum phosphate,
Three 3 parts of sulfenyl s-triazine trisodium salts, 2 parts of benzoic acid, benzo
2 parts of imidazoles allyl sulphide, 2 parts of paranitrobenzoic acid, 1 part of sodium tetraborate, 2 parts of dimethyl maleic anhydride, go from
Sub- water is some.
Preferably, can be also made up of the raw material components of following number:70 parts of tall oil diglycollic amide, coco-nut oil fatty acid
30 parts of diglycollic amide, 8 parts of ethoxylated dodecyl alcohol sodium sulphate, 26 parts of vancomycin, 26 parts of ketoconazole, 28 parts of aluminum phosphate,
Three 4 parts of sulfenyl s-triazine trisodium salts, 3 parts of benzoic acid, 3 parts of benzimidazole allyl sulphide, 3 parts of paranitrobenzoic acid, four boron
Sour 1 part of sodium, 2 parts of dimethyl maleic anhydride, deionized water are some.
Preferably, can be also made up of the raw material components of following number:80 parts of tall oil diglycollic amide, coco-nut oil fatty acid
40 parts of diglycollic amide, 10 parts of ethoxylated dodecyl alcohol sodium sulphate, 28 parts of vancomycin, 28 parts of ketoconazole, 30 parts of aluminum phosphate,
Three 5 parts of sulfenyl s-triazine trisodium salts, 4 parts of benzoic acid, 4 parts of benzimidazole allyl sulphide, 4 parts of paranitrobenzoic acid, four boron
Sour 2 parts of sodium, 3 parts of dimethyl maleic anhydride, deionized water are some.
A kind of auto parts electrophoretic process coolant, the preparation method of the auto parts electrophoretic process coolant are as follows:
(1) deionized water of above-mentioned mass fraction is heated to 70~85 DEG C, then by the laruyl alcohol of above-mentioned mass fraction
APEO aluminum phosphate, vancomycin, aluminum phosphate, benzimidazole allyl sulphide sequentially add, and are well mixed, and it is molten to obtain A
Liquid;
(2) after above-mentioned solution A being warming up into 90~95 DEG C, the benzoic acid and tetraboric acid of above-mentioned mass fraction are sequentially added
Sodium, after being well mixed, room temperature is cooled to, that is, obtains this product.
The beneficial effects of the present invention are:The auto parts electrophoretic process coolant of the present invention can improve auto parts and add
The cooling effect of construction equipment, it is convenient to use as needed, it is easy to preferably be cooled down for auto parts process equipment.
Embodiment
Embodiment:A kind of auto parts electrophoretic process coolant, is made up of the raw material components of following number:Tall oil diethyl
60~80 parts of alkylolamides, 20~40 parts of cocoanut fatty acid diethanolamide, 6~10 parts of ethoxylated dodecyl alcohol sodium sulphate,
24~28 parts of vancomycin, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, rest in peace
Fragrant 2~4 parts of acid, 2~4 parts of benzimidazole allyl sulphide, 2~4 parts of paranitrobenzoic acid, 1~2 part of sodium tetraborate, dimethyl
2~3 parts of maleic anhydride, deionized water are some.
Preferably, can be also made up of the raw material components of following number:60 parts of tall oil diglycollic amide, coco-nut oil fatty acid
20 parts of diglycollic amide, 6 parts of ethoxylated dodecyl alcohol sodium sulphate, 24 parts of vancomycin, 24 parts of ketoconazole, 26 parts of aluminum phosphate,
Three 3 parts of sulfenyl s-triazine trisodium salts, 2 parts of benzoic acid, 2 parts of benzimidazole allyl sulphide, 2 parts of paranitrobenzoic acid, four boron
Sour 1 part of sodium, 2 parts of dimethyl maleic anhydride, deionized water are some.
Preferably, can be also made up of the raw material components of following number:70 parts of tall oil diglycollic amide, coco-nut oil fatty acid
30 parts of diglycollic amide, 8 parts of ethoxylated dodecyl alcohol sodium sulphate, 26 parts of vancomycin, 26 parts of ketoconazole, 28 parts of aluminum phosphate,
Three 4 parts of sulfenyl s-triazine trisodium salts, 3 parts of benzoic acid, 3 parts of benzimidazole allyl sulphide, 3 parts of paranitrobenzoic acid, four boron
Sour 1 part of sodium, 2 parts of dimethyl maleic anhydride, deionized water are some.
Preferably, can be also made up of the raw material components of following number:80 parts of tall oil diglycollic amide, coco-nut oil fatty acid
40 parts of diglycollic amide, 10 parts of ethoxylated dodecyl alcohol sodium sulphate, 28 parts of vancomycin, 28 parts of ketoconazole, 30 parts of aluminum phosphate,
Three 5 parts of sulfenyl s-triazine trisodium salts, 4 parts of benzoic acid, 4 parts of benzimidazole allyl sulphide, 4 parts of paranitrobenzoic acid, four boron
Sour 2 parts of sodium, 3 parts of dimethyl maleic anhydride, deionized water are some.
A kind of auto parts electrophoretic process coolant, the preparation method of the auto parts electrophoretic process coolant are as follows:
(1) deionized water of above-mentioned mass fraction is heated to 70~85 DEG C, then by the laruyl alcohol of above-mentioned mass fraction
APEO aluminum phosphate, vancomycin, aluminum phosphate, benzimidazole allyl sulphide sequentially add, and are well mixed, and it is molten to obtain A
Liquid;
(2) after above-mentioned solution A being warming up into 90~95 DEG C, the benzoic acid and tetraboric acid of above-mentioned mass fraction are sequentially added
Sodium, after being well mixed, room temperature is cooled to, that is, obtains this product.
Described above is only the preferred application implementation mode of the present invention, it is noted that for the common skill of the art
For art personnel, without departing from the technical principles of the invention, some improvement can also be made.
Claims (5)
- A kind of 1. auto parts electrophoretic process coolant, it is characterised in that:It is made up of the raw material components of following number:Tall oil two 60~80 parts of glycollic amide, 20~40 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate 6~10 Part, 24~28 parts of vancomycin, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, peace Fragrant 2~4 parts of the acid of breath, 2~4 parts of benzimidazole allyl sulphide, 2~4 parts of paranitrobenzoic acid, 1~2 part of sodium tetraborate, diformazan 2~3 parts of base maleic anhydride, deionized water are some.
- 2. auto parts electrophoretic process coolant according to claim 1, it is characterised in that:By the raw material group of following number It is grouped into:60 parts of tall oil diglycollic amide, 20 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate 6 parts, 24 parts of vancomycin, 24 parts of ketoconazole, 26 parts of aluminum phosphate, three 3 parts of sulfenyl s-triazine trisodium salts, 2 parts of benzoic acid, benzo 2 parts of imidazoles allyl sulphide, 2 parts of paranitrobenzoic acid, 1 part of sodium tetraborate, 2 parts of dimethyl maleic anhydride, deionized water are some.
- 3. auto parts electrophoretic process coolant according to claim 1, it is characterised in that:By the raw material group of following number It is grouped into:70 parts of tall oil diglycollic amide, 30 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate 8 parts, 24 parts of vancomycin, 24 parts of ketoconazole, 26 parts of aluminum phosphate, three 4 parts of sulfenyl s-triazine trisodium salts, 3 parts of benzoic acid, benzo 3 parts of imidazoles allyl sulphide, 3 parts of paranitrobenzoic acid, 1 part of sodium tetraborate, 2 parts of dimethyl maleic anhydride, deionized water are some.
- 4. auto parts electrophoretic process coolant according to claim 1, it is characterised in that:By the raw material group of following number It is grouped into:80 parts of tall oil diglycollic amide, 40 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate 10 parts, 28 parts of vancomycin, 28 parts of ketoconazole, 30 parts of aluminum phosphate, three 5 parts of sulfenyl s-triazine trisodium salts, 4 parts of benzoic acid, benzene And if 4 parts of imidazoles allyl sulphide, 4 parts of paranitrobenzoic acid, 2 parts of sodium tetraborate, 3 parts of dimethyl maleic anhydride, deionized water It is dry.
- 5. the auto parts electrophoretic process coolant according to any one of Claims 1-4, it is characterised in that:The automobile The preparation method of part electrophoretic process coolant is as follows:(1) deionized water of above-mentioned mass fraction is heated to 70~85 DEG C, then by the laruyl alcohol polyoxy of above-mentioned mass fraction Vinethene aluminum phosphate, vancomycin, aluminum phosphate, benzimidazole allyl sulphide sequentially add, and are well mixed, and obtain solution A;(2) after above-mentioned solution A being warming up into 90~95 DEG C, the benzoic acid and sodium tetraborate of above-mentioned mass fraction are sequentially added, After well mixed, room temperature is cooled to, that is, obtains this product.