CN107190297A - A kind of auto parts anodic oxidation electrolyte - Google Patents
A kind of auto parts anodic oxidation electrolyte Download PDFInfo
- Publication number
- CN107190297A CN107190297A CN201710610496.8A CN201710610496A CN107190297A CN 107190297 A CN107190297 A CN 107190297A CN 201710610496 A CN201710610496 A CN 201710610496A CN 107190297 A CN107190297 A CN 107190297A
- Authority
- CN
- China
- Prior art keywords
- parts
- anodic oxidation
- auto
- oxidation electrolyte
- aluminum phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of auto parts anodic oxidation electrolyte, is made up of the raw material components of following number:60~80 parts of tall oil diglycollic amide, 20~40 parts of cocoanut fatty acid diethanolamide, 6~10 parts of ethoxylated dodecyl alcohol sodium sulphate, 24~28 parts of vancomycin, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, 2~4 parts of benzoic acid, 2~4 parts of benzimidazole allyl sulphide, 2~15 parts of tartaric acid, 5~15 parts of lithium fluoride, 15~20 parts of electrolytic solution, deionized water is some, a kind of auto parts anodic oxidation electrolyte of the present invention can improve the cooling effect of auto parts process equipment, it is convenient to use as needed, it is easy to preferably be cooled down for auto parts process equipment.
Description
Technical field
The invention belongs to auto parts coolant technical field, and in particular to a kind of auto parts anodic oxidation electrolyte.
Background technology
Metal working fluid is mainly the liquid of intermetallic composite coating, main to play lubrication and cooling effect, has antirust cleaning etc. concurrently
Effect.General metal working fluid includes cutting fluid, cutting oil, emulsion, punching oil, quenching medium, high temperature oil, extreme pressure cutting
Liquid, grinding fluid, antirust oil, cleaning agent, blackening agent for surface, drawing oil etc..Machining of metals liquid is a kind of low foam, high-lubricity
Soluble lubricating oil, can also be preferably minimized maintenance cost, basic energy even if applying under to the exigent environment of working fluid
Suitable for all types of processing of each metalloid and alloy, its general processing to most of iron metals extremely proves effective, especially
It can give play to outstanding lubrication and cooling effect simultaneously in machined mild steel, cast iron, stainless steel and other special steels.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of auto parts anodic oxidation electrolyte, preferably improve automobile
The cooling effect of part process equipment, it is convenient to use as needed, it is easy to preferably cold for the progress of auto parts process equipment
But.
To realize above-mentioned technical purpose and the technique effect, the present invention is achieved through the following technical solutions:
A kind of auto parts anodic oxidation electrolyte, is made up of the raw material components of following number:Tall oil diglycollic amide
60~80 parts, 20~40 parts of cocoanut fatty acid diethanolamide, 6~10 parts of ethoxylated dodecyl alcohol sodium sulphate, it is mould through the ages
24~28 parts of element, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, benzoic acid 2~
4 parts, 2~4 parts of benzimidazole allyl sulphide, 2~15 parts of tartaric acid, 5~15 parts of lithium fluoride, 15~20 parts of electrolytic solution, go
Ionized water is some.
It is preferred that, it can be also made up of the raw material components of following number:60 parts of tall oil diglycollic amide, coco-nut oil fatty acid
20 parts of diglycollic amide, 6 parts of ethoxylated dodecyl alcohol sodium sulphate, 24 parts of vancomycin, 24 parts of ketoconazole, 26 parts of aluminum phosphate,
Three 3 parts of sulfenyl s-triazine trisodium salts, 2 parts of benzoic acid, 2 parts of benzimidazole allyl sulphide, 2 parts of tartaric acid, 5 parts of lithium fluoride,
15 parts of electrolytic solution, deionized water are some.
It is preferred that, it can be also made up of the raw material components of following number:70 parts of tall oil diglycollic amide, coco-nut oil fatty acid
30 parts of diglycollic amide, 8 parts of ethoxylated dodecyl alcohol sodium sulphate, 26 parts of vancomycin, 26 parts of ketoconazole, 28 parts of aluminum phosphate,
Three 4 parts of sulfenyl s-triazine trisodium salts, 3 parts of benzoic acid, 3 parts of benzimidazole allyl sulphide, 8 parts of tartaric acid, 10 parts of lithium fluoride,
18 parts of electrolytic solution, deionized water are some.
It is preferred that, it can be also made up of the raw material components of following number:80 parts of tall oil diglycollic amide, coco-nut oil fatty acid
40 parts of diglycollic amide, 10 parts of ethoxylated dodecyl alcohol sodium sulphate, 28 parts of vancomycin, 28 parts of ketoconazole, 30 parts of aluminum phosphate,
Three 5 parts of sulfenyl s-triazine trisodium salts, 4 parts of benzoic acid, 4 parts of benzimidazole allyl sulphide, 15 parts of tartaric acid, lithium fluoride 15
Part, 20 parts of electrolytic solution, deionized water are some.
It is preferred that, the pH value of the electrolytic solution is 8.5~9.5.
A kind of auto parts anodic oxidation electrolyte, the preparation method of the auto parts anodic oxidation electrolyte is as follows:
(1) deionized water of above-mentioned mass fraction is heated to 70~85 DEG C, then by the laruyl alcohol of above-mentioned mass fraction
APEO aluminum phosphate, vancomycin, aluminum phosphate, benzimidazole allyl sulphide are sequentially added, and are well mixed, and obtain A molten
Liquid;
(2) above-mentioned solution A is warming up to after 90~95 DEG C, sequentially adds the benzoic acid and winestone of above-mentioned mass fraction
Acid, after being well mixed, is cooled to room temperature, that is, obtains this product.
The beneficial effects of the present invention are:The auto parts anodic oxidation electrolyte of the present invention can improve auto parts and add
The cooling effect of construction equipment, it is convenient to use as needed, it is easy to preferably be cooled down for auto parts process equipment.
Embodiment
Embodiment:A kind of auto parts anodic oxidation electrolyte, is made up of the raw material components of following number:Tall oil diethyl
60~80 parts of alkylolamides, 20~40 parts of cocoanut fatty acid diethanolamide, 6~10 parts of ethoxylated dodecyl alcohol sodium sulphate,
24~28 parts of vancomycin, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, rest in peace
Fragrant 2~4 parts of acid, 2~4 parts of benzimidazole allyl sulphide, 2~15 parts of tartaric acid, 5~15 parts of lithium fluoride, electrolytic solution 15~
20 parts, deionized water it is some.
Further, it can be also made up of the raw material components of following number:60 parts of tall oil diglycollic amide, coconut oil fat
Sour 20 parts of diglycollic amide, 6 parts of ethoxylated dodecyl alcohol sodium sulphate, 24 parts of vancomycin, 24 parts of ketoconazole, aluminum phosphate 26
Part, three 3 parts of sulfenyl s-triazine trisodium salts, 2 parts of benzoic acid, 2 parts of benzimidazole allyl sulphide, 2 parts of tartaric acid, lithium fluoride 5
Part, 15 parts of electrolytic solution, deionized water are some.
Further, it can be also made up of the raw material components of following number:70 parts of tall oil diglycollic amide, coconut oil fat
Sour 30 parts of diglycollic amide, 8 parts of ethoxylated dodecyl alcohol sodium sulphate, 26 parts of vancomycin, 26 parts of ketoconazole, aluminum phosphate 28
Part, three 4 parts of sulfenyl s-triazine trisodium salts, 3 parts of benzoic acid, 3 parts of benzimidazole allyl sulphide, 8 parts of tartaric acid, lithium fluoride 10
Part, 18 parts of electrolytic solution, deionized water are some.
Further, it can be also made up of the raw material components of following number:80 parts of tall oil diglycollic amide, coconut oil fat
Sour 40 parts of diglycollic amide, 10 parts of ethoxylated dodecyl alcohol sodium sulphate, 28 parts of vancomycin, 28 parts of ketoconazole, aluminum phosphate 30
Part, three 5 parts of sulfenyl s-triazine trisodium salts, 4 parts of benzoic acid, 4 parts of benzimidazole allyl sulphide, 15 parts of tartaric acid, lithium fluoride
15 parts, 20 parts of electrolytic solution, deionized water it is some.
Further, the pH value of the electrolytic solution is 8.5~9.5.
A kind of auto parts anodic oxidation electrolyte, the preparation method of the auto parts anodic oxidation electrolyte is as follows:
(1) deionized water of above-mentioned mass fraction is heated to 70~85 DEG C, then by the laruyl alcohol of above-mentioned mass fraction
APEO aluminum phosphate, vancomycin, aluminum phosphate, benzimidazole allyl sulphide are sequentially added, and are well mixed, and obtain A molten
Liquid;
(2) above-mentioned solution A is warming up to after 90~95 DEG C, sequentially adds the benzoic acid and winestone of above-mentioned mass fraction
Acid, after being well mixed, is cooled to room temperature, that is, obtains this product.
Described above is only the preferred application implementation mode of the present invention, it is noted that for the common skill of the art
For art personnel, without departing from the technical principles of the invention, some improvement can also be made.
Claims (6)
1. a kind of auto parts anodic oxidation electrolyte, it is characterised in that:It is made up of the raw material components of following number:Tall oil two
60~80 parts of glycollic amide, 20~40 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate 6~10
Part, 24~28 parts of vancomycin, 24~28 parts of ketoconazole, 26~30 parts of aluminum phosphate, three 3~5 parts of sulfenyl s-triazine trisodium salts, peace
Fragrant 2~4 parts of the acid of breath, 2~4 parts of benzimidazole allyl sulphide, 2~15 parts of tartaric acid, 5~15 parts of lithium fluoride, electrolytic solution 15
~20 parts, deionized water it is some.
2. auto parts anodic oxidation electrolyte according to claim 1, it is characterised in that:By the raw material group of following number
It is grouped into:60 parts of tall oil diglycollic amide, 20 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate
6 parts, 24 parts of vancomycin, 24 parts of ketoconazole, 26 parts of aluminum phosphate, three 3 parts of sulfenyl s-triazine trisodium salts, 2 parts of benzoic acid, benzo
2 parts of imidazoles allyl sulphide, 2 parts of tartaric acid, 5 parts of lithium fluoride, 15 parts of electrolytic solution, deionized water are some.
3. auto parts anodic oxidation electrolyte according to claim 1, it is characterised in that:By the raw material group of following number
It is grouped into:70 parts of tall oil diglycollic amide, 30 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate
8 parts, 24 parts of vancomycin, 24 parts of ketoconazole, 26 parts of aluminum phosphate, three 4 parts of sulfenyl s-triazine trisodium salts, 3 parts of benzoic acid, benzo
3 parts of imidazoles allyl sulphide, 8 parts of tartaric acid, 10 parts of lithium fluoride, 18 parts of electrolytic solution, deionized water are some.
4. auto parts anodic oxidation electrolyte according to claim 1, it is characterised in that:By the raw material group of following number
It is grouped into:80 parts of tall oil diglycollic amide, 40 parts of cocoanut fatty acid diethanolamide, ethoxylated dodecyl alcohol sodium sulphate
10 parts, 28 parts of vancomycin, 28 parts of ketoconazole, 30 parts of aluminum phosphate, three 5 parts of sulfenyl s-triazine trisodium salts, 4 parts of benzoic acid, benzene
And 4 parts of imidazoles allyl sulphide, 15 parts of tartaric acid, 15 parts of lithium fluoride, 20 parts of electrolytic solution, deionized water are some.
5. the auto parts anodic oxidation electrolyte according to Claims 1-4, it is characterised in that:The electrolytic solution
PH value is 8.5~9.5.
6. the auto parts anodic oxidation electrolyte according to any one of Claims 1-4, it is characterised in that:The automobile
The preparation method of part anode oxidation electrolyte is as follows:
(1) deionized water of above-mentioned mass fraction is heated to 70~85 DEG C, then by the laruyl alcohol polyoxy of above-mentioned mass fraction
Vinethene aluminum phosphate, vancomycin, aluminum phosphate, benzimidazole allyl sulphide are sequentially added, and are well mixed, and obtain solution A;
(2) above-mentioned solution A is warming up to after 90~95 DEG C, sequentially adds the benzoic acid and tartaric acid of above-mentioned mass fraction, mixed
After closing uniformly, room temperature is cooled to, that is, obtains this product.