CN107418683A - Screw lubricating wax and preparation method thereof, application - Google Patents

Screw lubricating wax and preparation method thereof, application Download PDF

Info

Publication number
CN107418683A
CN107418683A CN201710674095.9A CN201710674095A CN107418683A CN 107418683 A CN107418683 A CN 107418683A CN 201710674095 A CN201710674095 A CN 201710674095A CN 107418683 A CN107418683 A CN 107418683A
Authority
CN
China
Prior art keywords
lubricating wax
screw lubricating
wax
screw
liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710674095.9A
Other languages
Chinese (zh)
Inventor
刘汉锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Sailing Industry Co Ltd
Original Assignee
Guangdong Sailing Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Sailing Industry Co Ltd filed Critical Guangdong Sailing Industry Co Ltd
Priority to CN201710674095.9A priority Critical patent/CN107418683A/en
Publication of CN107418683A publication Critical patent/CN107418683A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of screw lubricating wax, it is characterised in that：It is made up of following components：18% 21% stearic acid, 23% 27% vaseline, 30% 35% aluminum oxide, surplus are auxiliary material.The present invention for solves the problems, such as stainless steel support stress automation, efficiency assembling epoch often because speed, friction produce instantaneous high-temperature cause metal alloying produce be stained with it is glutinous, locked, in fastener（Stainless steel bolt or CARBURIZING FURNACE FOR STAINLESS FASTENER）Surface adds pre-lubrication process, screw lubricating wax produced by the present invention is stamped in stainless steel bolt or CARBURIZING FURNACE FOR STAINLESS FASTENER surface, oil site when making the CARBURIZING FURNACE FOR STAINLESS FASTENER twist into screwed hole, CARBURIZING FURNACE FOR STAINLESS FASTENER has lubrication just can more twist into, prevent that the CARBURIZING FURNACE FOR STAINLESS FASTENER that is locked into is locked, screw lubricating wax is tack-free, it is attractive in appearance, be not necessary to the characteristics such as reserved tolerance, stabilization, it is locked to be effectively improved stainless steel support.

Description

Screw lubricating wax and preparation method thereof, application
Technical field
The present invention relates to assemble field, espespecially a kind of screw lubricating wax and its preparation side applied to stainless steel outer-hexagonal screw Method, application.
Background technology
Automation, efficiency assembling are stressed in existing assembling, and stainless steel outer-hexagonal screw is producing instantaneous high-temperature because of speed, friction Cause metal alloying and producing to be stained with glutinous, the screwed hole above product and CARBURIZING FURNACE FOR STAINLESS FASTENER the problem of locked is occurred in assembling process.
The content of the invention
To solve the above problems, the present invention provides a kind of spiral shell for avoiding stainless steel outer-hexagonal screw from installing locked problem appearance Silk lubricating wax.
To achieve the above object, it is a kind of screw lubricating wax that the present invention, which adopts the following technical scheme that, and it is by following components Form：
Stearic acid 18%-21%
Vaseline 23%-27%
Aluminum oxide 30%-35%
Surplus is auxiliary material.
Preferably, described auxiliary material and dosage are：Paraffin 4%-6%, water soluble wax 3%-4.5%, microwax 4%-6.5%, stone Black alkene powder 9%-11%.
Lubricating wax auxiliary material is prepared by the way that Graphene powder is used as, the fusing point of lubricating wax is not only increased, lubricating wax is easily stored up Deposit, and after screw has been beaten by lubricating wax, screw is tack-free.
Preferably, the differences such as bulk, column, tabular can be made by user's requirement from different moulds, screw lubricating wax The product of shape.
Preferably, described aluminum oxide is calcined alumina powder, and particle diameter is 200~210 nm.
A kind of preparation method of screw lubricating wax, comprises the following steps：
Step 1：Paraffin is taken, by heating paraffin to 56 DEG C -62 DEG C, adds water soluble wax, microwax, Graphene powder, stirring increases Temperature all dissolves to 90-110 DEG C, to it, and stir to obtain A liquid；
Step 2：Stearic acid is added into A liquid, stir to obtain B liquid；
Step 3：Vaseline is added into B liquid, stir to obtain C liquid；
Step 4：Aluminum oxide is added into C liquid, stirred, then C liquid is recorded in model, is cooled down 30 minutes at normal temperatures, Take out shaping and form screw lubricating wax.
A kind of application of screw lubricating wax, several fasteners and several screw lubricating waxes are put into roller, roller Rotating speed is 3000r/min, after rotating 20 minutes, makes fastener surface is viscous to affix a thin layer of screw lubricating wax.
Screw lubricating wax has the advantages that nonpoisonous and tasteless, stability is strong, lubricity is good, and has three kinds of spring and autumn, summer, winter specifications Product, adapt to a variety of demands of different user respectively, for different room temperatures, can suitably adjust formula, make product with more Kind different melting point, hardness, oil content and waxing rate, it is widely used in the demand of different user.The present invention uses oxygen aluminum oxide Powder particles particle diameter is 200~210nm, and ellipse and column is presented, and without obvious sharp corners, plays ablation, makes stainless steel Screw is waxed during rotating speed 3000r/min rollers roll with the friction of screw lubricating wax, more supernumerary segment when making one to screw Save the strength, and be effectively improved the locked problem of stainless steel support.
The beneficial effects of the present invention are：Stainless steel support stress automation, efficiency assembling epoch often because speed, Friction produces instantaneous high-temperature and causes metal alloying and produce and be stained with the problem of glutinous, locked, and the present invention is locked to improve stainless steel support The problem of, in fastener（Stainless steel bolt or CARBURIZING FURNACE FOR STAINLESS FASTENER）Surface adds pre-lubrication process, i.e., in stainless steel bolt or not Rust steel screw surface waxing, makes CARBURIZING FURNACE FOR STAINLESS FASTENER be lubricated when twisting into screwed hole, and CARBURIZING FURNACE FOR STAINLESS FASTENER has lubrication just can more twist into, Prevent that the CARBURIZING FURNACE FOR STAINLESS FASTENER that is locked into is locked（It is locked just to refer to that CARBURIZING FURNACE FOR STAINLESS FASTENER has twisted into, come it is difficult to back-out）, screw lubricating wax It is tack-free, be not necessary to the characteristic such as reserved tolerance (making fastener surface form film-form screw lubricating wax), stable, be effectively improved stainless Steel fastening is locked.
Embodiment
Embodiment 1：
The present invention provides a kind of screw lubricating wax, and it is made up of following components：18 parts of stearic acid, 23 parts of vaseline, 30 parts of oxidations Aluminium, 4 parts of paraffin, 3 parts of water soluble waxs, 6.5 parts of microwaxes, 11 parts of Graphene powders, described aluminum oxide are calcined alumina powder, Particle diameter is 200~210 nm.
Wherein, a kind of preparation method of screw lubricating wax：4 parts of paraffin is taken, by heating paraffin to 58 DEG C -60 DEG C, is added 3 parts of water soluble wax, 8 parts of microwax, 9 parts of Graphene powder, stirring are heated to 90-110 DEG C, are all dissolved to it, by 18 Part stearic acid, 23 parts of vaseline, 30 parts of aluminum oxide are sequentially added and stirred, then solution is recorded in block model, in normal temperature Lower cooling 30 minutes, take out shaping and obtain block screw lubricating wax.Screw lubricating wax made from this method, suitable for spring and autumn Two seasons.
Wherein, a kind of application of screw lubricating wax, several fasteners and several screw lubricating waxes are put into roller, Drum rotation speed is 3000r/min, after rotating 20 minutes, makes fastener surface is viscous to affix a thin layer of screw lubricating wax.
Embodiment 2：
The present invention provides a kind of screw lubricating wax, and it is made up of following components：21 parts of stearic acid, 27 parts of vaseline, 35 parts of oxidations Aluminium, 6 parts of paraffin, 4.5 parts of water soluble waxs, 6.5 parts of microwaxes, 11 parts of Graphene powders, described aluminum oxide are calcined oxide aluminium powder Body, particle diameter are 200~210 nm.
Wherein, a kind of preparation method of screw lubricating wax：6 parts of paraffin is taken, by heating paraffin to 60 DEG C -62 DEG C, is added 4.5 parts of water soluble wax, 6.5 parts of microwax, 11 parts of Graphene powder, stirring are heated to 90-110 DEG C, are all dissolved to it, 21 parts of stearic acid, 27 parts of vaseline, 35 parts of aluminum oxide are sequentially added and stirred, then solution is recorded in column model, Cooled down 20 minutes under normal temperature, take out shaping and obtain screw lubricating wax.The screw lubricating wax of column is made in this method, suitable for the summer Season.Auxiliary material effectively changes the fusing point of screw lubricating wax, according to the carry out ratio adjustment of season difference.
Wherein, a kind of application of screw lubricating wax, several fasteners and several screw lubricating waxes are put into roller, Drum rotation speed is 3000r/min, after rotating 20 minutes, makes fastener surface is viscous to affix a thin layer of screw lubricating wax.Screw Lubricating wax makes CARBURIZING FURNACE FOR STAINLESS FASTENER be lubricated when twisting into screwed hole, and CARBURIZING FURNACE FOR STAINLESS FASTENER has lubrication just can more twist into, and prevents what is be locked into CARBURIZING FURNACE FOR STAINLESS FASTENER is locked.
Embodiment of above is only that the preferred embodiment of the present invention is described, and not the scope of the present invention is entered Row limits, on the premise of design spirit of the present invention is not departed from, technical side of this area ordinary skill technical staff to the present invention The various modifications and improvement that case is made, it all should fall into the protection domain of claims of the present invention determination.

Claims (5)

  1. A kind of 1. screw lubricating wax, it is characterised in that：It is made up of following components：
    Stearic acid 18%-21%
    Vaseline 23%-27%
    Aluminum oxide 30%-35%
    Surplus is auxiliary material.
  2. A kind of 2. screw lubricating wax according to claim 1, it is characterised in that：Described auxiliary material and dosage be：Paraffin 4%- 6%, water soluble wax 3%-4.5%, microwax 4%-6.5%, Graphene powder 9%-11%.
  3. A kind of 3. screw lubricating wax according to claim 1, it is characterised in that：From different moulds, screw lubricating wax The product of different shapes such as bulk, column, tabular can be made by user's requirement.
  4. A kind of 4. preparation method of screw lubricating wax according to claim 1, it is characterised in that：Comprise the following steps：
    Step 1：High temperature wax, Graphene powder are taken, stirring is heated to 90 110 DEG C, is all dissolved to it, stir to obtain A liquid；
    Step 2：Stearic acid is added into A liquid, stir to obtain B liquid；
    Step 3：Vaseline is added into B liquid, stir to obtain C liquid；
    Step 4：Aluminum oxide is added into C liquid, stirred, then C liquid is recorded in model, is cooled down 30 minutes at normal temperatures, Take out shaping and form screw lubricating wax.
  5. A kind of 5. application of screw lubricating wax according to claim 1, it is characterised in that：Several fasteners with it is some Individual screw lubricating wax is put into roller, drum rotation speed 3000r/min, after rotating 20 minutes, makes fastener surface is viscous to affix one The very thin screw lubricating wax of layer.
CN201710674095.9A 2017-08-09 2017-08-09 Screw lubricating wax and preparation method thereof, application Pending CN107418683A (en)