CN107418128A - A kind of compound mat proper of high resilience - Google Patents
A kind of compound mat proper of high resilience Download PDFInfo
- Publication number
- CN107418128A CN107418128A CN201710736763.6A CN201710736763A CN107418128A CN 107418128 A CN107418128 A CN 107418128A CN 201710736763 A CN201710736763 A CN 201710736763A CN 107418128 A CN107418128 A CN 107418128A
- Authority
- CN
- China
- Prior art keywords
- parts
- compound mat
- mat proper
- high resilience
- proper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high compound mat proper of resilience, it is made up of by weight following components：100 ~ 130 parts of styrene analog thermoplastic elastomer；50 ~ 60 parts of polypropylene；SEBS20 ~ 50 part；8 ~ 25 parts of polyurethane；10 ~ 25 parts of butyl rubber；1 ~ 2 part of coupling agent；1 ~ 2 part of antioxidant；2 ~ 5 parts of dispersant；1 ~ 2 part of antiseptic；2 ~ 6 parts of fire retardant；The material of the present invention has preferable resilience, resistance to ag(e)ing and anti-flammability, improves the feel, security and service life of mat proper, is worth promoting.
Description
Technical field
The present invention relates to sports equipment field, specifically a kind of compound mat proper of high resilience.
Background technology
Wrestling is acknowledged as athletic sports earliest in the world, Greece, Egypt, China and Japan and other countries
There is the literature record of wrestling in ancient civilization.When B.C. 776 years are born, wrestling is exactly therein one for ancient Olympics
Item match, and the always event of all previous Olympic Games.
Wrestling is a most ancient and spectacular athletics event in the world.Just generated early in ancient times generation simplest
Wrestle method.Its generation and development is connected each other with the various laboring forms of the mankind, for example ball with other sports events
Etc. different, for example, it is ball in the generation of basketball, football, handball be in somewhere, certain country, and tumble and almost produce
Among nationality of the world, because in primitive society, people of all nationalities are in order to obtain existence in the world, in the struggle with nature,
The method for having the self-defence of oneself and obtaining the means of existence, wrestling are exactly one of them.Its development be in practice process,
Update flexible skill and gain in strength, make it more quickly to defeat one's opponents and win the victory.
Mat proper is equipment important in modern wrestling motion, and the place of good safety can be provided for wrestling.
A kind of Application No. CN201410469817.3 patent of invention " composite tae kwon do using XPE as sandwich
Pad " discloses " a kind of composite tae kwon do pad using XPE as sandwich, including the anti-skidding table from top to bottom set gradually
Face, intermediate layer and slip-resistant bottom surface；The non skid matting is the anti-skidding composite beds of PVC with anti-skid design；The slip-resistant bottom surface is
The anti-skidding composite beds of PVC with anti-skid design or the embossing XPE layers with raised and concave figures, the intermediate layer include multilayer XPE layers,
The density of the XPE layers being disposed adjacent is identical or different.Intermediate layer of the present invention be by multi-layer phase with or different densities XPE layers
It is combined by heat seal process, the mat so made has the advantages that comfort level is good, neither too hard, nor too soft, strong shock resistance；
Non skid matting adds the frictional force of whole mat with slip-resistant bottom surface anti-skid design, is further added by ensureing user on the basis of friction
Comfortableness.Tae kwon do place is laid using the present invention, its overall leveling is good, safe, and using effect is good, resistance to
It is strong with property, stationarity and security during Athletess is effectively ensured, suitable for wide popularization and application ".
Existing mat proper is mostly polyethylene foam-material or is combined as shown in above patent by itself and other materials,
Although with certain resilience, its bill of materials one, resilience is not high, and is easily influenceed and reduce bullet by aoxidizing
Property, do not possess anti-flammability in addition, security is poor.
The content of the invention
It is an object of the invention to provide the compound mat proper of high resilience that a kind of resilience is higher, anti-oxidant, anti-flammability is strong,
To solve the problems mentioned in the above background technology.
To achieve the above object, the present invention provides following technical scheme：
A kind of compound mat proper of high resilience, is made up of following components by weight：
100 ~ 130 parts of styrene analog thermoplastic elastomer；
50 ~ 60 parts of polypropylene；
20 ~ 50 parts of SEBS；
8 ~ 25 parts of polyurethane；
10 ~ 25 parts of butyl rubber；
1 ~ 2 part of coupling agent；
1 ~ 2 part of antioxidant；
2 ~ 5 parts of dispersant；
1 ~ 2 part of antiseptic；
2 ~ 6 parts of fire retardant.
As the further scheme of the present invention：The coupling agent is silane resin acceptor kh-550.
As the further scheme of the present invention：The antioxidant is hindered phenol anti-oxidants.
As the further scheme of the present invention：The fire retardant is non-halogen fragrance organic phosphates fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
As the further scheme of the present invention：Six silicon carbides of double screw extruder are respectively in the step 3：One
220~235 DEG C of section, two 230~235 DEG C of sections, three, four, five 240~245 DEG C of sections, six 225~235 DEG C of sections；Extrusion
Machine rate of feeding is 24Hz, engine speed 350Hz.
As the further scheme of the present invention：The high compound mat proper of resilience is sandwich construction, and top surface is provided with layer of silica gel, and bottom surface is set
There is rubber layer.
As the further scheme of the present invention：The high compound mat proper of resilience and layer of silica gel, rubber layer heat seal.
As the further scheme of the present invention：The two sides of the high compound mat proper of resilience is equipped with netted projection.
Compared with prior art, the beneficial effects of the invention are as follows：The material of the present invention has preferable resilience, resistance to ag(e)ing
And anti-flammability, the feel, security and service life of mat proper are improved, is worth promoting.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment one
A kind of compound mat proper of high resilience, is made up of following components by weight：
115 parts of styrene analog thermoplastic elastomer；
55 parts of polypropylene；
30 parts of SEBS；
20 parts of polyurethane；
15 parts of butyl rubber；
1.5 parts of coupling agent；
1.5 parts of antioxidant；
3 parts of dispersant；
1.5 parts of antiseptic；
4 parts of fire retardant.
Preferably, coupling agent is silane resin acceptor kh-550.
Preferably, antioxidant is hindered phenol anti-oxidants.
Preferably, fire retardant is non-halogen fragrance organic phosphates fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Preferably, six silicon carbides of double screw extruder are respectively in step 3：One 220~235 DEG C of section, two sections
230~235 DEG C, three, four, five 240~245 DEG C of sections, six 225~235 DEG C of sections；Extruder rate of feeding is 24Hz, main frame
Rotating speed is 350Hz.
Embodiment two
A kind of compound mat proper of high resilience, is made up of following components by weight：
100 parts of styrene analog thermoplastic elastomer；
50 parts of polypropylene；
20 parts of SEBS；
8 parts of polyurethane；
10 parts of butyl rubber；
1 part of coupling agent；
1 part of antioxidant；
2 parts of dispersant；
1 part of antiseptic；
2 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Embodiment three
A kind of compound mat proper of high resilience, is made up of following components by weight：
100 parts of styrene analog thermoplastic elastomer；
50 parts of polypropylene；
35 parts of SEBS；
20 parts of polyurethane；
15 parts of butyl rubber；
1 part of coupling agent；
1 part of antioxidant；
3 parts of dispersant；
1.5 parts of antiseptic；
5 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Example IV
A kind of compound mat proper of high resilience, is made up of following components by weight：
110 parts of styrene analog thermoplastic elastomer；
50 parts of polypropylene；
35 parts of SEBS；
20 parts of polyurethane；
15 parts of butyl rubber；
1.5 parts of coupling agent；
1.5 parts of antioxidant；
3 parts of dispersant；
1.5 parts of antiseptic；
5 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Embodiment five
A kind of compound mat proper of high resilience, is made up of following components by weight：
120 parts of styrene analog thermoplastic elastomer；
50 parts of polypropylene；
35 parts of SEBS；
20 parts of polyurethane；
20 parts of butyl rubber；
1.5 parts of coupling agent；
1.5 parts of antioxidant；
3 parts of dispersant；
1.5 parts of antiseptic；
5 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Embodiment six
A kind of compound mat proper of high resilience, is made up of following components by weight：
125 parts of styrene analog thermoplastic elastomer；
55 parts of polypropylene；
40 parts of SEBS；
20 parts of polyurethane；
20 parts of butyl rubber；
1.5 parts of coupling agent；
1.5 parts of antioxidant；
3 parts of dispersant；
1.5 parts of antiseptic；
5 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Embodiment seven
A kind of compound mat proper of high resilience, is made up of following components by weight：
125 parts of styrene analog thermoplastic elastomer；
55 parts of polypropylene；
40 parts of SEBS；
20 parts of polyurethane；
20 parts of butyl rubber；
2 parts of coupling agent；
2 parts of antioxidant；
5 parts of dispersant；
2 parts of antiseptic；
6 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Embodiment eight
A kind of compound mat proper of high resilience, is made up of following components by weight：
130 parts of styrene analog thermoplastic elastomer；
58 parts of polypropylene；
40 parts of SEBS；
20 parts of polyurethane；
20 parts of butyl rubber；
2 parts of coupling agent；
2 parts of antioxidant；
5 parts of dispersant；
2 parts of antiseptic；
6 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Embodiment nine
A kind of compound mat proper of high resilience, is made up of following components by weight：
130 parts of styrene analog thermoplastic elastomer；
60 parts of polypropylene；
50 parts of SEBS；
25 parts of polyurethane；
25 parts of butyl rubber；
2 parts of coupling agent；
2 parts of antioxidant；
5 parts of dispersant；
2 parts of antiseptic；
6 parts of fire retardant.
A kind of preparation method of the compound mat proper of high resilience, comprises the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
Embodiment ten
A kind of compound mat proper of high resilience is sandwich construction, and top surface is provided with layer of silica gel, and bottom surface is provided with rubber layer.
Preferably, the compound mat proper of high resilience and layer of silica gel, rubber layer heat seal.
Preferably, the two sides of the compound mat proper of high resilience is equipped with netted projection.Strengthen the combination between Rotating fields.
Layer of silica gel, which can exempt, re-lays sheet, and rubber layer can improve the intensity of mat proper.
Experimentation and its result
Experimental example is used as using the material of the formula of above-described embodiment one ~ ten respectively；
With a kind of Application No. Application No. CN201410469817.3 patent of invention " composite using XPE as sandwich
XPE materials in tae kwon do pad " are comparative example 1
Elastic testing standard is GB/T6670-2008
The testing standard of resistance to ag(e)ing is GB/T16422；
The testing standard of vertical combustion fire resistance is UL94
Experimental result such as following table：
As can be seen that resilience, resistance to ag(e)ing and the anti-flammability of the present invention will than common XPE materials from above-mentioned experimental data
By force.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be on the premise of this patent objective not be departed from one skilled in the relevant art's possessed knowledge
Various changes can be made.
Claims (9)
1. a kind of compound mat proper of high resilience, it is characterised in that be made up of by weight following components：
100 ~ 130 parts of styrene analog thermoplastic elastomer；
50 ~ 60 parts of polypropylene；
20 ~ 50 parts of SEBS；
8 ~ 25 parts of polyurethane；
10 ~ 25 parts of butyl rubber；
1 ~ 2 part of coupling agent；
1 ~ 2 part of antioxidant；
2 ~ 5 parts of dispersant；
1 ~ 2 part of antiseptic；
2 ~ 6 parts of fire retardant.
2. the compound mat proper of high resilience according to claim 1, it is characterised in that the coupling agent is silane coupler
KH-550。
3. the compound mat proper of high resilience according to claim 1, it is characterised in that the antioxidant is Hinered phenols antioxygen
Agent.
4. the compound mat proper of high resilience according to claim 1, it is characterised in that the fire retardant is that non-halogen fragrance is organic
Phosphorus type flame retardant.
5. the preparation method of the compound mat proper of high resilience according to claim 1, it is characterised in that comprise the following steps：
First, each constitutive material is compared by formulation weight to be weighed, it is separated；
2nd, styrene analog thermoplastic elastomer, polypropylene, SEBS, polyurethane, butyl rubber are mixed with mixer, at 60 DEG C
At a temperature of, 50min is stirred with 500r/min speed, the mixture after stirring is deposited at a temperature of being placed on 35 DEG C,
It is standby；
3rd, the mixture obtained in step 2 and coupling agent, antioxidant, dispersant, antiseptic and fire retardant are added at a high speed
10min is mixed under 50 DEG C~65 DEG C states in mixer, then melting extrusion is granulated on the twin screw extruder；
4th, finished product mat proper is made through extrusion molding in the particle obtained in step 3.
6. the preparation method of the compound mat proper of high resilience according to claim 5, it is characterised in that double in the step 3
Six silicon carbides of screw extruder are respectively：One 220~235 DEG C of section, two 230~235 DEG C of sections, three, four, five sections
240~245 DEG C, six 225~235 DEG C of sections；Extruder rate of feeding is 24Hz, engine speed 350Hz.
7. the compound mat proper of high resilience according to claim 1, it is characterised in that the high compound mat proper of resilience is multilayer
Structure, top surface are provided with layer of silica gel, and bottom surface is provided with rubber layer.
8. the compound mat proper of high resilience according to claim 7, it is characterised in that the compound mat proper of high resilience and silica gel
Layer, rubber layer heat seal.
9. the compound mat proper of high resilience according to claim 7, it is characterised in that the two sides of the high compound mat proper of resilience is equal
Provided with netted projection.