CN107418022A - A kind of drainage by electroosmosis pipe and preparation method thereof - Google Patents
A kind of drainage by electroosmosis pipe and preparation method thereof Download PDFInfo
- Publication number
- CN107418022A CN107418022A CN201710361885.1A CN201710361885A CN107418022A CN 107418022 A CN107418022 A CN 107418022A CN 201710361885 A CN201710361885 A CN 201710361885A CN 107418022 A CN107418022 A CN 107418022A
- Authority
- CN
- China
- Prior art keywords
- electroosmosis
- drainage
- pipe
- raw material
- copper wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is applied to drainage by electroosmosis field of engineering technology, there is provided a kind of drainage by electroosmosis pipe, including conductive black, polyethylene, polypropylene, Tissuemat E, zinc stearate and lubricant；The copper wire being also wrapped in tube wall.A kind of preparation method of drainage by electroosmosis pipe is additionally provided, is comprised the following steps：A, mix as each component of raw material, heated after stirring；B, the raw material after heating enters double screw extruder and completes prilling；C, the raw material after granulation is poured into single screw extrusion machine, while is put into copper wire；D, raw material and copper wire are through mould extrusion molding；E, the drainage by electroosmosis pipe after being molded is actually needed according to user's request or scene to be blocked, and produces drainage by electroosmosis pipe finished product.The present invention by adjusting drainage by electroosmosis pipe formula and preparation method thereof, make drainage by electroosmosis pipe it is corrosion resistant simultaneously, improve drainage by electroosmosis efficiency.
Description
Technical field
The present invention relates to drainage by electroosmosis field of engineering technology, more particularly to a kind of drainage by electroosmosis pipe and preparation method thereof.
Background technology
Electro-osmosis method is exactly that metal electrode is inserted in soil, and passes to direct current, and under electric field action, water in soil is from anode
Flow to negative electrode, produce electric osmose, so as to reduce stream mud based on sticking grain, mud or Muddy Bottoms soil's water content or level of ground water,
To improve the reinforcement means of soil nature.Successful utilization is after railway excavation and cart-away first from nineteen thirty-nine for the method, and scholars are at it
Substantial amounts of research work is carried out in terms of reinforcement principle and iontophoresis device, and achievement in research is applied to fill out sea, fills out lake, marshland
Engineering, mine tailing, comprehensive useless mud, the processing of dangerous waste mud etc..
Drainage by electroosmosis pipe is that the technology that electro-osmosis method is achieved ensures, and obtains increasing extensive use, existing
In technology, drainage by electroosmosis pipe with two spelling formula electric osmose pipes be most widely used, two spell formula electric osmose pipes basic structures for electric osmose pipe with
The combination of electroosmosis board, the groove for grafting electroosmosis board is left on electric osmose pipe, is connected as electric osmose pipe with electroosmosis board by grafting
One, electric osmose work is completed as electroosmosis electrode, but the two spellings formula electric osmose pipe easily loosens in practice of construction, takes off electricity and construct
Time is grown, and because it has air interface without corrosion-resistant, application field is compared with being limited to, it is impossible to be used in ooze draining.
A kind of drainage by electroosmosis pipe is invented by our company, and it is realized single by the water discharging hard pipe and filtrate hose that fuse together
Pipe, integrated construction, it is easy to operate, the construction period is not only shortened, is also solved and is easily loosened, takes off existing for two spelling formula electric osmose pipes
The problems such as electric, perishable.
The present invention is illustrated for the factory formula and preparation method of this drainage by electroosmosis pipe.
The content of the invention
For it is above-mentioned the defects of, it is an object of the invention to provide a kind of drainage by electroosmosis pipe and preparation method thereof, it passes through
Adjust drainage by electroosmosis pipe formula and preparation method thereof, make drainage by electroosmosis pipe it is corrosion resistant simultaneously, improve drainage by electroosmosis efficiency.
To achieve these goals, the present invention provides a kind of drainage by electroosmosis pipe, including conductive black, polyethylene, polypropylene,
Tissuemat E, zinc stearate and lubricant；
The copper wire being also wrapped in tube wall.
According to the drainage by electroosmosis pipe of the present invention, the mass ratio between each component is (with terms of solids)：Conductive black：
(polyethylene and polypropylene)：Tissuemat E：Zinc stearate：Lubricant=29:45:15:8:3.
According to the drainage by electroosmosis pipe of the present invention, the conductive black is Colombia's conductive black.
According to the drainage by electroosmosis pipe of the present invention, the polypropylene is isotactic polypropylene, and the mass ratio of itself and polyethylene is
1.5:2.5。
According to the drainage by electroosmosis pipe of the present invention, the area of section of the copper wire is 1~1.5mm2, quantity 4.
According to the drainage by electroosmosis pipe of the present invention, the lubricant is A6 lubricants.
The present invention also provides a kind of preparation method of drainage by electroosmosis pipe, comprises the following steps：
A, mix as each component of raw material, heated after stirring；
B, the raw material after heating enters double screw extruder and completes prilling；
C, the raw material after granulation is poured into single screw extrusion machine, while is put into copper wire；
D, raw material and copper wire are through mould extrusion molding；
E, the drainage by electroosmosis pipe after being molded is actually needed according to user's request or scene and blocked, produce drainage by electroosmosis pipe into
Product.
According to the preparation method of the drainage by electroosmosis pipe of the present invention, the heating-up temperature in the step A is 90~120 °.
According to the preparation method of the drainage by electroosmosis pipe of the present invention, the mould in the step D is circular for oval inner sleeve, described
Circular diameter is equal with the minor axis length of ellipse.
The present invention is obtained a kind of new by limiting each part and its proportions and quantity of drainage by electroosmosis pipe
Drainage by electroosmosis pipe, the drainage by electroosmosis pipe specifically include：Conductive black, polyethylene, polypropylene, Tissuemat E, zinc stearate and profit
Lubrication prescription；The copper wire being additionally wrapped in tube wall.Drainage by electroosmosis pipe in the present invention while conductive discharge rate is improved,
Accommodation is wider, particular for ooze draining, the characteristics of shaping due to the content and single tube of its each component, makes it more resistant to corruption
Erosion.In addition, present invention also offers a kind of preparation method of drainage by electroosmosis pipe, mix, stir using as each component of raw material first
Heated after mixing uniformly；Raw material after heating enters double screw extruder and completes prilling；Then the raw material after granulation is poured into
Single screw extrusion machine, while it is put into copper wire；Raw material is with copper wire through mould extrusion molding；Finally by the drainage by electroosmosis pipe root after shaping
It is actually needed and blocks according to user's request or scene, produces drainage by electroosmosis pipe finished product.The preparation method is simple, quick, effective, and energy
According to the different demands of client, implement customized production.
Brief description of the drawings
Fig. 1 is the flow chart of preparation method in the present invention；
Fig. 2 is mould Structure of cross section schematic diagram in the present invention；
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is right below in conjunction with drawings and Examples
The present invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and
It is not used in the restriction present invention.
The invention provides a kind of drainage by electroosmosis pipe.The drainage by electroosmosis pipe includes conductive black, polyethylene, polypropylene, poly-
6 kinds of ethylene waxes, zinc stearate and lubricant components.
Specifically, with terms of solids, the mass ratio of each component is：Conductive black：(polyethylene and polypropylene)：Polyethylene
Wax：Zinc stearate：Lubricant=29:45:15:8:3.
Wherein, because polyethylene and polyacrylic similitude and hardness, draftability etc. are distinguished, both mixtures are made
Be that entirety calculates, and be the isotactic polypropylene that accounting is larger in industrial production used herein of polypropylene, its with it is poly-
The mass ratio of ethene preferably 1.5:2.5.
It should also be noted that, the preferred electric conductivity of conductive black in the drainage by electroosmosis pipe it is good Colombia it is conductive
Carbon black；The preferred A6 lubricants of lubricant.
The drainage by electroosmosis pipe is also wrapped in the copper wire in tube wall；Consider the electric conductivity of copper wire and its caused
The specification of the factors such as electric field level, preferably copper wire is that area of section is 1~1.5mm2Copper wire, quantity 4.
Referring to Fig. 1, present invention also offers a kind of preparation method of drainage by electroosmosis pipe.The preparation method includes following step
Suddenly：
Step 1: being mixed as each component of raw material, heated after stirring.
In order to facilitate the processing of subsequent handling, after raw material is mixed evenly, heated, it is contemplated that each component melts
Point, preferably 90~120 ° of heating-up temperature.
Step 2: the raw material after heating, which enters double screw extruder, completes prilling.
Soften after raw material is heated, the raw material of softening is added in double screw extruder, double screw extruder is by raw material
Extruded in the form of raw material grain.
Step 3: the raw material after granulation is poured into single screw extrusion machine, while it is put into copper wire.
Raw material grain after extrusion pours into single screw extrusion machine, while is put into preprepared copper wire.
Step 4: raw material and copper wire are through mould extrusion molding.
Under the operation of single screw extrusion machine, one is extruded and formed into through mould with copper wire for raw material；Referring to Fig. 2, herein
Mould it is circular for oval inner sleeve, and circular diameter is equal with oval minor axis length, and the white space in figure is electric
Row's soakaway trench.
Step 5: the drainage by electroosmosis pipe after shaping is actually needed according to user's request or scene and blocked, drainage by electroosmosis is produced
Pipe finished product.
In summary, each part and its proportions and quantity of the invention by limiting drainage by electroosmosis pipe, is obtained
To a kind of new drainage by electroosmosis pipe, the drainage by electroosmosis pipe specifically includes：It is conductive black, polyethylene, polypropylene, Tissuemat E, hard
Resin acid zinc and lubricant；The copper wire being additionally wrapped in tube wall.Drainage by electroosmosis pipe in the present invention is improving busbar
While water rate, accommodation is wider, particular for ooze draining, due to its each component the shaping of content and single tube the characteristics of,
Make it more resistant to corrosion.In addition, present invention also offers a kind of preparation method of drainage by electroosmosis pipe, first using as each group of raw material
Divide mixing, heated after stirring；Raw material after heating enters double screw extruder and completes prilling；Then by after granulation
Raw material pours into single screw extrusion machine, while is put into copper wire；Raw material is with copper wire through mould extrusion molding；Finally by the electric osmose after shaping
Drainpipe is actually needed according to user's request or scene and blocked, and produces drainage by electroosmosis pipe finished product.The preparation method is simple, it is quick,
Effectively, and customized production can be implemented according to the different demands of client.
Certainly, the present invention can also have other various embodiments, ripe in the case of without departing substantially from spirit of the invention and its essence
Know those skilled in the art when can be made according to the present invention it is various it is corresponding change and deformation, but these corresponding change and become
Shape should all belong to the protection domain of appended claims of the invention.
Claims (9)
1. a kind of drainage by electroosmosis pipe, it is characterised in that including conductive black, polyethylene, polypropylene, Tissuemat E, zinc stearate
And lubricant；
The copper wire being also wrapped in tube wall.
2. drainage by electroosmosis pipe according to claim 1, it is characterised in that the mass ratio between each component is (with solid
Thing meter) be：Conductive black：(polyethylene and polypropylene)：Tissuemat E：Zinc stearate：Lubricant=29:45:15:8:3.
3. drainage by electroosmosis pipe according to claim 1, it is characterised in that the conductive black is Colombia's conduction charcoal
It is black.
4. drainage by electroosmosis pipe according to claim 2, it is characterised in that the polypropylene is isotactic polypropylene, and it is with gathering
The mass ratio of ethene is 1.5:2.5.
5. drainage by electroosmosis pipe according to claim 1, it is characterised in that the area of section of the copper wire is 1~1.5mm2、
Quantity is 4.
6. drainage by electroosmosis pipe according to claim 1, it is characterised in that the lubricant is A6 lubricants.
7. prepare the method for the drainage by electroosmosis pipe as described in any one of claim 1~6, it is characterised in that comprise the following steps：
A, mix as each component of raw material, heated after stirring；
B, the raw material after heating enters double screw extruder and completes prilling；
C, the raw material after granulation is poured into single screw extrusion machine, while is put into copper wire；
D, raw material and copper wire are through mould extrusion molding；
E, the drainage by electroosmosis pipe after being molded is actually needed according to user's request or scene to be blocked, and produces drainage by electroosmosis pipe finished product.
8. the preparation method of drainage by electroosmosis pipe according to claim 5, it is characterised in that the heating temperature in the step A
Spend for 90~120 °.
9. the preparation method of drainage by electroosmosis pipe according to claim 5, it is characterised in that the mould in the step D is
Oval inner sleeve is circular, and the circular diameter is equal with the minor axis length of ellipse.