CN107417245A - A kind of dalle of containing diatomite and preparation method thereof - Google Patents
A kind of dalle of containing diatomite and preparation method thereof Download PDFInfo
- Publication number
- CN107417245A CN107417245A CN201710842876.4A CN201710842876A CN107417245A CN 107417245 A CN107417245 A CN 107417245A CN 201710842876 A CN201710842876 A CN 201710842876A CN 107417245 A CN107417245 A CN 107417245A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- dalle
- raw material
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dalle of containing diatomite and preparation method thereof, the dalle of the containing diatomite, count, be made up of following raw material in parts by weight：50 80 parts of 100 150 parts of diatomite, 50 70 parts of kaolin, 30 50 parts of titanium dioxide, 50 90 parts of oyster shell whiting, 80 120 parts of corn stalk powder, 40 80 parts of polyvinyl chloride, 15 30 parts of glass fibre, 5 20 parts of foaming control agent, 5 15 parts of stearic acid and water.It the dalle of containing diatomite prepared by the present invention, can effectively purify the air of a room, remove the harmful substances such as formaldehyde, benzene and dimethylbenzene, and energy being capable of effective degradation of formaldehyde.
Description
Technical field
It is more particularly to a kind of to contain diatomaceous environment-friendly type decoration sheet material the invention belongs to dalle preparing technical field
And preparation method thereof.
Background technology
Dalle is a kind of artificial board, and it is with a variety of special paper after chemical treatment, with HTHP glue
Thermoset layer depositing plastic material made of mixture, the space of a whole page has various patterns, bright smooth, in beautiful color, while has higher
The good physical properties such as wear-resisting, heat-resisting, cold-resistant, fire prevention.The wall, roof, cabinet, table, bed etc. in many advanced rooms is mostly
Using this novel decorative plate.Existing decorative panel can release formaldehyde, benzene, dimethylbenzene, trichloro ethylene, ether during use
The harmful substances such as esters, propylene cyanogen, long-term life under such circumstances can the sizable harm of human body generation.
Diatomaceous main component is silicic acid matter, has the characteristics such as superfluorescent fiber, Porous, when humidity indoors rises,
Diatomaceous ultra micro pore can be in automatic absorption air moisture content, stored, avoid indoor environment mouldy, rotten.
If the moisture content in room air is reduced, humidity declines, kieselguhr wall material can just release the moisture content being stored in ultra micro pore
Release.Secondly, diatomite application study and test result indicates that, diatomite can play a part of deodorant, have eliminate it is different
The function of taste, decompose the harmful chemical such as harmful substance such as formaldehyde, benzene, dimethylbenzene, trichloro ethylene, ether-ether class, propylene cyanogen with
And pet body odor, smoking, peculiar smell caused by house refuse etc., it can effectively keep indoor cleaning；3rd, diatomite is to moisture
Absorption and release can produce water fall effect, by water-molecule dissociation into negative ions, negative ions group, then using hydrone to carry
Body, swim everywhere in atmosphere, run into the harmful substance such as allergin and other bacteriums, mould, can just be carried out immediately
Surround and isolate, and the most active hydroxide ion of performance in negative ions group is carried out violent chemistry instead with harmful substance
Should, they are finally completely decomposed into the harmless objects such as hydrone so as to produce medical effect, possesses sterilizing ability.
The content of the invention
In order to solve the above problems, there is provided a kind of dalle of containing diatomite and preparation method thereof, the application contain diatom
The dalle of soil is environment protection type sheet material, is added in manufacturing process without any harmful substance, green, improves Interior Space makings
Amount.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of dalle of containing diatomite, by weight
Number meter, is made up of following raw material：
Diatomite：100-150 parts；
Kaolin：15-25 parts；
Titanium dioxide：30-50 parts；
Oyster shell whiting：50-90 parts；
Corn stalk powder：80-120 parts；
Polyvinyl chloride：40-80 parts；
Glass fibre:15-30 parts；
Foaming control agent：5-20 parts；
Stearic acid:5-15 parts；
Water：50-80 parts.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Preferably, a kind of dalle of containing diatomite, is counted in parts by weight, is made up of following raw material：
Diatomite：100 parts；
Kaolin：25 parts；
Titanium dioxide：50 parts
Oyster shell whiting：90 parts；
Corn stalk powder：120 parts；
Polyvinyl chloride：40 parts；
Glass fibre：30 parts；
Foaming control agent：20 parts；
Stearic acid：15 parts；
Water：50 parts.
Preferably, a kind of dalle of containing diatomite, is counted in parts by weight, is made up of following raw material：
Diatomite：110 parts；
Kaolin：20 parts；
Titanium dioxide：45 parts
Oyster shell whiting：80 parts；
Corn stalk powder：110 parts；
Polyvinyl chloride：50 parts；
Glass fibre：25 parts；
Foaming control agent：18 parts；
Stearic acid：13 parts；
Water：60 parts.
Preferably, a kind of dalle of containing diatomite, is counted in parts by weight, is made up of following raw material：
Diatomite：120 parts；
Kaolin：15 parts；
Titanium dioxide：40 parts
Oyster shell whiting：70 parts；
Corn stalk powder：100 parts；
Polyvinyl chloride：60 parts；
Glass fibre：20 parts；
Foaming control agent：15 parts；
Stearic acid：10 parts；
70 parts of water.
Preferably, a kind of dalle of containing diatomite, is counted in parts by weight, is made up of following raw material：
Diatomite：130 parts；
Kaolin：15 parts；
Titanium dioxide：35 parts
Oyster shell whiting：50 parts；
Corn stalk powder：90 parts；
Polyvinyl chloride：70 parts；
Glass fibre：15 parts；
Foaming control agent：10 parts；
Stearic acid：5 parts；
Water：80 parts.
Preferably, a kind of dalle of containing diatomite, is counted in parts by weight, is made up of following raw material：
Diatomite：150 parts；
Kaolin：20 parts；
Titanium dioxide：30 parts
Oyster shell whiting：85 parts；
Corn stalk powder：80 parts；
Polyvinyl chloride：80 parts；
Glass fibre：20 parts；
Foaming control agent：16 parts；
Stearic acid：12 parts；
Water：65 parts.
The present invention also provides a kind of preparation method of the dalle of containing diatomite, comprises the following steps：
Step 1：Based on raw material weight number, following raw material is taken：
Diatomite 100-150 parts, kaolin 50-70 parts, titanium dioxide 30-50 parts, oyster shell whiting 50-90 parts, maize straw
Powder 80-120 parts, polyvinyl chloride 40-80 parts, glass fibre 15-30 parts, foaming control agent 5-20 parts, stearic acid 5-15 parts and water
50-80 parts；
Step 2：Diatomite, oyster shell whiting, titanium dioxide, corn stalk powder, polyvinyl chloride, glass fibre, foaming control agent,
Mixer stirring is added after stearic acid and water mixing, first stirring at low speed 30-60 minutes, rotating speed is 800 revs/min, then high-speed stirring
Mix 30-60 minutes, rotating speed 4000/ minute, obtain mixed slurry A；
Step 3：Mixture A is added and heated in extruder 30-60 minutes, temperature is 60-80 DEG C, obtains mixed slurry B；
Step 4：Intermixture B is extruded into modular system, it is compressing；
Step 5：By the compressing sheet material of step 4 using dry kiln drying, temperature is 50-65 DEG C, and the time is that 10-12 is small
When, when wet weight is less than 3.5%, turn into semi-finished product；
Step 6：Semi-finished product polish flat after drying, and surface is smooth, by products application design using coating, baking vanish,
It is UV plated films, silk-screen, gold stamping, packed after its surface cure, produce the dalle for containing diatomite.
Compared with prior art, the beneficial effects of the invention are as follows：
Diatomite main component is silicic acid matter, and there are a countless pores on surface, adsorbable, decompose peculiar smell in air, has and adjusts
Wet, deodorization functions.The building materials for using diatomite to be produced for raw material, not only with non-ignitable, dehumidifying, deodorization, bactericidal and
The characteristics of permeability is good, but also air, sound insulation, waterproof and heat-insulated can be purified；Kaolin has strong acid resistance, high-quality
Kaolin also has good electrical insulating property and various ions and impurity can be adsorbed from surrounding medium；Tripolite loading two
Titanium oxide being capable of effective absorption degradation formaldehyde；Oyster shell whiting is oyster shell whiting pulverized powder, and its 95% main component is calcium carbonate,
Also a small amount of amino acid and polysaccharide material, have purification air, eliminate peculiar smell, antibacterial bacteriostatic, antistatic, adjusting air humidity,
The premium properties such as fire protection flame retarding.Containing lignin, string in corn stalk powder, original raw material wood powder can be substituted,
Corn stalk powder it is cheap, it is green.
What the present invention was prepared is a kind of cheap, green decorative panel containing diatomaceous dalle
The harmful substance such as material, formaldehyde that can not only be in adsorption-decomposition function air, benzene, dimethylbenzene, also has that to remove air peculiar smell, regulation empty
The premium properties such as air humidity degree, fire-proof and thermal-insulation, electric insulation.
Embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
HL-100 foaming control agents used in the embodiment of the present invention are purchased from Shandong Suzhou office of Ke Group Co., Ltd.
Embodiment 1
A kind of preparation method of the dalle of containing diatomite, comprises the following steps：
Step 1：Based on raw material weight number, following raw material is taken：
100 parts of diatomite, 25 parts of kaolin, 50 parts of titanium dioxide, 90 parts of oyster shell whiting, 120 parts of corn stalk powder, polychlorostyrene second
50 parts of 40 parts of alkene, 30 parts of glass fibre, 20 parts of HL-100 foaming control agents, 15 parts of stearic acid and water；
Step 2：Diatomite, oyster shell whiting, titanium dioxide, corn stalk powder, polyvinyl chloride, glass fibre, foaming control agent,
Mixer stirring is added after stearic acid and water mixing, first stirring at low speed 30 minutes, rotating speed is 800 revs/min, then high-speed stirred 30
Minute, rotating speed 4000/ minute, obtain mixed slurry A；
Step 3：Mixture A is added in extruder and heated 60 minutes, temperature is 60 DEG C, obtains mixed slurry B；
Step 4：Intermixture B is extruded into modular system, it is compressing；
Step 5：By the compressing sheet material of step 4 using dry kiln drying, temperature is 50 DEG C, and the time is 12 hours, when
When wet weight is less than 3.5%, turn into semi-finished product；
Step 6：Semi-finished product polish flat after drying, and surface is smooth, by products application design using coating, baking vanish,
It is UV plated films, silk-screen, gold stamping, packed after its surface cure, produce the dalle for containing diatomite.
Embodiment 2
A kind of preparation method of the dalle of containing diatomite, comprises the following steps：
Step 1：Based on raw material weight number, following raw material is taken：
110 parts of diatomite, 20 parts of kaolin, 45 parts of titanium dioxide, 80 parts of oyster shell whiting, 110 parts of corn stalk powder, polychlorostyrene second
60 parts of 50 parts of alkene, 25 parts of glass fibre, 18 parts of HL-100 foaming control agents, 13 parts of stearic acid and water；
Step 2：Diatomite, oyster shell whiting, titanium dioxide, corn stalk powder, polyvinyl chloride, glass fibre, foaming control agent,
Mixer stirring is added after stearic acid and water mixing, first stirring at low speed 60 minutes, rotating speed is 800 revs/min, then high-speed stirred 60
Minute, rotating speed 4000/ minute, obtain mixed slurry A；
Step 3：Mixture A is added in extruder and heated 60 minutes, temperature is 60 DEG C, obtains mixed slurry B；
Step 4：Intermixture B is extruded into modular system, it is compressing；
Step 5：By the compressing sheet material of step 4 using kiln drying is dried, temperature is 65 DEG C, and the time is 10 hours, when
When wet weight is less than 3.5%, turn into semi-finished product；
Step 6：Semi-finished product polish flat after drying, and surface is smooth, by products application design using coating, baking vanish,
It is UV plated films, silk-screen, gold stamping, packed after its surface cure, produce the dalle for containing diatomite.
Embodiment 3
A kind of preparation method of the dalle of containing diatomite, comprises the following steps：
Step 1：Based on raw material weight number, following raw material is taken：
120 parts of diatomite, 15 parts of kaolin, 40 parts of titanium dioxide, 70 parts of oyster shell whiting, 100 parts of corn stalk powder, polychlorostyrene second
70 parts of 60 parts of alkene, 20 parts of glass fibre, 15 parts of HL-100 foaming control agents, 10 parts of stearic acid and water；
Step 2：Diatomite, oyster shell whiting, titanium dioxide, corn stalk powder, polyvinyl chloride, glass fibre, foaming control agent,
Mixer stirring is added after stearic acid and water mixing, first stirring at low speed 45 minutes, rotating speed is 800 revs/min, then high-speed stirred 45
Minute, rotating speed 4000/ minute, obtain mixed slurry A；
Step 3：Mixture A is added in extruder and heated 45 minutes, temperature is 70 DEG C, obtains mixed slurry B；
Step 4：Intermixture B is extruded into modular system, it is compressing；
Step 5：By the compressing sheet material of step 4 using dry kiln drying, temperature is 60 DEG C, and the time is 11 hours, when
When wet weight is less than 3.5%, turn into semi-finished product；
Step 6：Semi-finished product polish flat after drying, and surface is smooth, by products application design using coating, baking vanish,
It is UV plated films, silk-screen, gold stamping, packed after its surface cure, produce the dalle for containing diatomite.
Embodiment 4
A kind of preparation method of the dalle of containing diatomite, comprises the following steps：
Step 1：Based on raw material weight number, following raw material is taken：
130 parts of diatomite, 15 parts of kaolin, 35 parts of titanium dioxide, 50 parts of oyster shell whiting, 90 parts of corn stalk powder, polychlorostyrene second
80 parts of 70 parts of alkene, 15 parts of glass fibre, 10 parts of HL-100 foaming control agents, 5 parts of stearic acid and water；
Step 2：Diatomite, oyster shell whiting, titanium dioxide, corn stalk powder, polyvinyl chloride, glass fibre, foaming control agent,
Mixer stirring is added after stearic acid and water mixing, first stirring at low speed 40 minutes, rotating speed is 800 revs/min, then high-speed stirred 50
Minute, rotating speed 4000/ minute, obtain mixed slurry A；
Step 3：Mixture A is added in extruder and heated 55 minutes, temperature is 75 DEG C, obtains mixed slurry B；
Step 4：Intermixture B is extruded into modular system, it is compressing；
Step 5：By the compressing sheet material of step 4 using dry kiln drying, temperature is 60 DEG C, and the time is 12 hours, when
When wet weight is less than 3.5%, turn into semi-finished product；
Step 6：Semi-finished product polish flat after drying, and surface is smooth, by products application design using coating, baking vanish,
It is UV plated films, silk-screen, gold stamping, packed after its surface cure, produce the dalle for containing diatomite.
Embodiment 5
A kind of preparation method of the dalle of containing diatomite, comprises the following steps：
Step 1：Based on raw material weight number, following raw material is taken：
150 parts of diatomite, 20 parts of kaolin, 30 parts of titanium dioxide, 85 parts of oyster shell whiting, 80 parts of corn stalk powder, polychlorostyrene second
65 parts of 80 parts of alkene, 20 parts of glass fibre, 16 parts of HL-100 foaming control agents, 12 parts of stearic acid and water；
Step 2：Diatomite, oyster shell whiting, titanium dioxide, corn stalk powder, polyvinyl chloride, glass fibre, foaming control agent,
Mixer stirring is added after stearic acid and water mixing, first stirring at low speed 50 minutes, rotating speed is 800 revs/min, then high-speed stirred 45
Minute, rotating speed 4000/ minute, obtain mixed slurry A；
Step 3：Mixture A is added in extruder and heated 50 minutes, temperature is 55 DEG C, obtains mixed slurry B；
Step 4：Intermixture B is extruded into modular system, it is compressing；
Step 5：By the compressing sheet material of step 4 using dry kiln drying, temperature is 55 DEG C, and the time is 12 hours, when
When wet weight is less than 3.5%, turn into semi-finished product；
Step 6：Semi-finished product polish flat after drying, and surface is smooth, by products application design using coating, baking vanish,
It is UV plated films, silk-screen, gold stamping, packed after its surface cure, produce the dalle for containing diatomite.
The purification that decorative panel made from 1-6 of the embodiment of the present invention is carried out to purifying formaldehyde efficiency, Degradation Formaldehyde ability, benzene is imitated
Rate, the purification efficiency of dimethylbenzene are shown in Table 1.
The diatomite dalle clean-up effect of table 1 tests table
As seen from the above table, the present invention contains diatomaceous dalle, can effectively purify the air of a room, removal formaldehyde,
The harmful substances such as benzene, dimethylbenzene, and energy being capable of effective degradation of formaldehyde.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (7)
1. a kind of dalle of containing diatomite, it is characterised in that count, be made up of following raw material in parts by weight：
Diatomite：100-150 parts；
Kaolin：15-25 parts；
Titanium dioxide：30-50 parts；
Oyster shell whiting：50-90 parts；
Corn stalk powder：80-120 parts；
Polyvinyl chloride：40-80 parts；
Glass fibre:15-30 parts；
Foaming control agent：5-20 parts；
Stearic acid:5-15 parts；
Water：50-80 parts.
A kind of 2. dalle of containing diatomite according to claim 1, it is characterised in that count in parts by weight, by with
Lower raw material composition：
Diatomite：100 parts；
Kaolin：25 parts；
Titanium dioxide：50 parts
Oyster shell whiting：90 parts；
Corn stalk powder：120 parts；
Polyvinyl chloride：40 parts；
Glass fibre：30 parts；
Foaming control agent：20 parts；
Stearic acid：15 parts；
Water：50 parts.
3. a kind of dalle of containing diatomite according to claim 1, it is characterised in that count in parts by weight, by following
Raw material forms：
Diatomite：110 parts；
Kaolin：20 parts；
Titanium dioxide：45 parts
Oyster shell whiting：80 parts；
Corn stalk powder：110 parts；
Polyvinyl chloride：50 parts；
Glass fibre：25 parts；
Foaming control agent：18 parts；
Stearic acid：13 parts；
Water：60 parts.
4. a kind of dalle of containing diatomite according to claim 1, it is characterised in that count in parts by weight, by following
Raw material forms：
Diatomite：120 parts；
Kaolin：15 parts；
Titanium dioxide：40 parts
Oyster shell whiting：70 parts；
Corn stalk powder：100 parts；
Polyvinyl chloride：60 parts；
Glass fibre：20 parts；
Foaming control agent：15 parts；
Stearic acid：10 parts；
70 parts of water.
5. a kind of dalle of containing diatomite according to claim 1, it is characterised in that count in parts by weight, by following
Raw material forms：
Diatomite：130 parts；
Kaolin：15 parts；
Titanium dioxide：35 parts
Oyster shell whiting：50 parts；
Corn stalk powder：90 parts；
Polyvinyl chloride：70 parts；
Glass fibre：15 parts；
Foaming control agent：10 parts；
Stearic acid：5 parts；
Water：80 parts.
6. a kind of dalle of containing diatomite according to claim 1, it is characterised in that count in parts by weight, by following
Raw material forms：
Diatomite：150 parts；
Kaolin：20 parts；
Titanium dioxide：30 parts
Oyster shell whiting：85 parts；
Corn stalk powder：80 parts；
Polyvinyl chloride：80 parts；
Glass fibre：20 parts；
Foaming control agent：16 parts；
Stearic acid：12 parts；
Water：65 parts.
7. a kind of preparation method of the dalle of containing diatomite, it is characterised in that comprise the following steps：
Step 1：Based on raw material weight number, following raw material is taken：
Diatomite 100-150 parts, kaolin 15-25 parts, titanium dioxide 30-50 parts, oyster shell whiting 50-90 parts, corn stalk powder 80-
120 parts, polyvinyl chloride 40-80 parts, glass fibre 15-30 parts, foaming control agent 5-20 parts, stearic acid 5-15 parts and water 50-80
Part；
Step 2：Diatomite, oyster shell whiting, titanium dioxide, corn stalk powder, polyvinyl chloride, glass fibre, foaming control agent, tristearin
Mixer stirring is added after acid and water mixing, first stirring at low speed 30-60 minutes, rotating speed is 800 revs/min, then high-speed stirred 30-
60 minutes, rotating speed 4000/ minute, obtain mixed slurry A；
Step 3：Mixture A is added and heated in extruder 30-60 minutes, temperature is 60-80 DEG C, obtains mixed slurry B；
Step 4：Intermixture B is extruded into modular system, it is compressing；
Step 5：The compressing sheet material of step 4 is used and dries kiln drying, temperature is 50-65 DEG C, and the time is 10-12 hours,
When wet weight is less than 3.5%, turn into semi-finished product；
Step 6：Semi-finished product polish flat after drying, and surface is smooth, are plated by products application design using coating, baking vanish, UV
It is film, silk-screen, gold stamping, packed after its surface cure, produce the dalle for containing diatomite.