CN107416987A - Water softening agent and its preparation method and application - Google Patents
Water softening agent and its preparation method and application Download PDFInfo
- Publication number
- CN107416987A CN107416987A CN201710523325.1A CN201710523325A CN107416987A CN 107416987 A CN107416987 A CN 107416987A CN 201710523325 A CN201710523325 A CN 201710523325A CN 107416987 A CN107416987 A CN 107416987A
- Authority
- CN
- China
- Prior art keywords
- softening agent
- water
- layer
- diatomite
- filter paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to water treatment field, and in particular to a kind of water softening agent and its preparation method and application.Described water softening agent includes following weight percentage component:Diatomite 15 25%;Sodium carbonate 1 5%;Sodium hydroxide 1 2%;Activated carbon 10 20%;Deionized water surplus.The present invention completes the purification of running water and one step of softening, convenient and swift.The addition of activated carbon can effectively filter out the chlorine residue in running water, diatomite has been especially added with purification softening agent, abundant ratio surface makes it have good physical absorption performance, and the calcium ions and magnesium ions in running water can be very good by kieselguhr adsorption after forming precipitation with the sodium carbonate in purification softening agent, sodium hydroxide.The design of Filter column make it that the calcium ions and magnesium ions in running water are fully precipitated, and effectively filters out chlorine residue.
Description
Technical field
The invention belongs to water treatment field, and in particular to a kind of water softening agent and its preparation method and application.
Background technology
Hard water refers to the water containing a large amount of calcium ions and magnesium ion, and many harm are brought in being produced to life.Such as hard water adds
Incrustation scale is produced when hot, is contacted with soap and produces scum silica frost influence cleaning performance, drinking the larger water of hardness influences health, and
Loss is brought to industrial production, when hard water passes through pipeline, incrustation scale is easily sticked to the time on tube wall and has grown and be easily damaged equipment.Originally
Calcium ions and magnesium ions content in water is generally higher, while the chlorine residue in running water also has very major injury to human body health.At present, firmly
Water softening method has ion-exchange, membrane separation process, method for dosing medicine etc., but the method cost of investment that has is high, the method that has is dangerous.
The content of the invention
The shortcomings that it is an object of the invention to overcome in the prior art, there is provided a kind of water softening agent and preparation method thereof and
Using.
To achieve the above object, the technical solution adopted by the present invention is:
A kind of water softening agent, including following weight percentage component:
Present invention additionally comprises a kind of preparation method of described water softening agent, by described diatomite, sodium carbonate, hydrogen-oxygen
Change sodium and activated carbon stir after being dissolved in water, then drying and moulding.
Present invention additionally comprises a kind of application of described water softening agent, and one layer of filter paper is first put into glass adsorption column,
One layer of 5mm filter paper pulp layer is added, is then sequentially placed into the work of 1-5g diatomite, water softening agent, 1-2g described in 5-10g
Property charcoal, then above add one layer of 5mm filter paper pulp layer, then put last layer filter paper, finally drain.
Compared with prior art, the beneficial effects of the invention are as follows:
The present invention completes the purification of running water and one step of softening, convenient and swift.The addition of activated carbon can be filtered out effectively
Chlorine residue in running water, purify and diatomite has been especially added with softening agent, abundant ratio surface makes it have good physics and inhaled
Attached performance, the calcium ions and magnesium ions in running water can be very good after forming precipitation with the sodium carbonate in purification softening agent, sodium hydroxide
By kieselguhr adsorption.The design of Filter column make it that the calcium ions and magnesium ions in running water are fully precipitated, and effectively filters out chlorine residue.
Embodiment
In order that those skilled in the art more fully understand technical scheme, implement with reference to optimal
The present invention is described in further detail for example.
Embodiment 1:
Prepare water softening agent:Diatomite 1.5g, sodium carbonate 0.2g, sodium hydroxide 0.1g, activated carbon 1g are taken, is then added
7.2g deionized waters, after being well mixed, drying and moulding, that is, it is purified softening agent 1;
Prepare Filter column:One layer of filter paper is first put into adsorption column, adds one layer of 5mm filter paper pulp layer, then successively
2g diatomite, 5g purifications softening agent 1,2g activated carbon, then the filter paper pulp in one layer of 5mm of addition above are put into, then puts one
Layer filter paper, finally drains and obtains Filter column 1.
Embodiment 2:
Prepare water softening agent:Diatomite 1.5g, sodium carbonate 0.5g, sodium hydroxide 0.2g, activated carbon 2g are taken, is then added
5.8g deionized waters, after being well mixed, drying and moulding, that is, it is purified softening agent 2;
Prepare Filter column:One layer of filter paper is first put into adsorption column, adds one layer of 5mm filter paper pulp layer, then successively
1g diatomite, 8g purifications softening agent 2,1g activated carbon, then the filter paper pulp in one layer of 5mm of addition above are put into, then puts one
Layer filter paper, finally drains and obtains Filter column 2.
Embodiment 3:
Prepare water softening agent:Diatomite 2.5g, sodium carbonate 0.2g, sodium hydroxide 0.1g, activated carbon 1g are taken, is then added
6.2g deionized waters, after being well mixed, drying and moulding, that is, it is purified softening agent 3;
Prepare Filter column:One layer of filter paper is first put into adsorption column, adds one layer of 5mm filter paper pulp layer, then successively
4g diatomite, 10g purifications softening agent 3,1g activated carbon, then the filter paper pulp in one layer of 5mm of addition above are put into, then puts one
Layer filter paper, finally drains and obtains Filter column 3.
Purify softening process and measure of merit:Running water is tested into tap water purifying by above three Filter column respectively
The front and rear hardness of softening, as a result shows, using the method for the present invention, can making the hardness of running water, effectively to reduce efficiency very high.
Purify bating effect test:It is as follows with the total hardness in EDTA complexometric titration water, assay method:Take 25ml
Water sample, 2ml pH10 NH3-NH4Cl cushioning liquid is added, after being well mixed, the ethanol solution of 5 0.5% eriochrome black Ts of drop is added dropwise,
It is in aubergine after shaking up, is titrated with 0.0102mol/L EDTA-Na2 solution (being demarcated with Zn2+ benchmark liquid), it is extremely molten
Liquid becomes au bleu then into titration end-point by aubergine, calculates total hardness X (mg/L, in terms of CaCO3) as follows:
Wherein:EDTA standard liquids consumption volume, ml when V- is titrated;M-EDTA concentration of standard solution, mol/L;VW- water samples
Volume, ml;100.08- calcium carbonate molal weight, g/mol.
Table 1 shows that different embodiments purify front and rear influence to hard water.
Table 1
Hardness (mg/L) before filtering | Hardness (mg/L) after filtering | |
Embodiment 1 | 726 | 126 |
Embodiment 2 | 720 | 112 |
Embodiment 3 | 731 | 98 |
Chlorinty is tested:The water after the Filter column filtering of the present invention is detected into free chlorine according to GB/T5750.11-2006 to contain
Amount.Table 2 showed test period 10 days, respectively at the 1st day, the 5th day, the 10th day free chlorine contents tested;
Table 2
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (3)
1. a kind of water softening agent, it is characterised in that including following weight percentage component:
2. the preparation method of the water softening agent described in a kind of claim 1, it is characterised in that by described diatomite, carbonic acid
Sodium, sodium hydroxide and activated carbon stir after being dissolved in water, then drying and moulding.
3. the application of the water softening agent described in a kind of claim 1, it is characterised in that one layer is first put into glass adsorption column
Filter paper, one layer of 5mm filter paper pulp layer is added, be then sequentially placed into 1-5g diatomite, the water softening agent described in 5-10g, 1-
2g activated carbon, then the filter paper pulp layer in one layer of 5mm of addition above, then put last layer filter paper, finally drain.