CN1074159A - The method of composite stainless steel compound plate on continuous casting billet - Google Patents
The method of composite stainless steel compound plate on continuous casting billet Download PDFInfo
- Publication number
- CN1074159A CN1074159A CN 92110428 CN92110428A CN1074159A CN 1074159 A CN1074159 A CN 1074159A CN 92110428 CN92110428 CN 92110428 CN 92110428 A CN92110428 A CN 92110428A CN 1074159 A CN1074159 A CN 1074159A
- Authority
- CN
- China
- Prior art keywords
- compound
- plate
- compound plate
- stainless steel
- continuous casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of manufacture method of composite metal plate, especially about the method for composite stainless steel compound plate on continuous casting billet.It is on the basis of existing explosive welding (EW) connection, adopts layering compound, and selects between suitable explosive proportioning and compound plate and the substrate method such as gap, solves continuous casting billet bad mechanical property and prior art and can not carry out a big compound difficult problem more compound than corrosion resistant plate.Use the inventive method and created condition for the stainless steel clad plate of producing the big compound ratio of large tracts of land in enormous quantities.It can be widely used in the industries such as oil, chemical industry, light industry and space flight.
Description
The present invention relates to a kind of preparation method of composite metal plate.
Make the method for stainless steel clad plate at present, mainly contain following several: 1, on the finished product steel plate with the direct composite stainless steel plate of explosion method, because the corrosion resistant plate restriction of opening the width of cloth can only be adopted many corrosion resistant plates splicings, seam has caused surface smoothness poor, and crackle is easily arranged.2, with soldering and sealing around corrosion resistant plate and the steel billet, after vacuumizing,, make corrosion resistant plate and steel plate compound by heating rolling.This method combined strength bination is low, and shear strength is also very low.3, billet rolling is arrived 50-60mm thickness, eliminate the as-cast structure in the steel billet, with explosion method that corrosion resistant plate is compound then.Because single face uni-tension rolling, composite plate easily take place to curl, so two stainless one sides of composite plate are relative, the centre adds division board, carries out ply rolling.The composite plate of Zhi Zuoing in this way, surface smoothness is very poor, and area also is subjected to certain limitation.Along with the continuous development of producing, industries such as oil, chemical industry, light industry and space flight need the stainless steel clad plate of a large amount of big compound ratios of large tracts of land.Through effort in a few years, Shoudu Iron and Steel Co has solved single face uni-tension rolling (Asymmetric Rolling) difficult problem, and the single face uni-tension rolling can be produced the big specification composite plate of high-quality.Need for this reason on continuous casting billet, to realize that the stainless steel of big compound ratio is compound, the compound base of rolling needs is provided, the problem to be solved in the present invention that Here it is, its difficult point is: though 1, the electroforming base is through cogging, but still be in half as-cast structure, its poor mechanical properties; 2, the stainless steel double layer thickness is usually greater than 18mm, and it is compound to adopt existing explosive method to carry out, and is not that the continuous casting billet matrix is burst, and is exactly that combined strength bination is not enough, and recombination rate does not reach requirement.
The purpose of this invention is to provide a kind of decked explosion, and with suitable dose proportioning compound big thickness stainless steel compound plate on continuous casting billet, with the method for the stainless steel clad plate of making the big compound ratio of large tracts of land.
For achieving the above object; the present invention has taked following method: a kind of on continuous casting billet the method for composite stainless steel compound plate; it is that substrate is placed on the sand basis; between stainless steel compound plate and described substrate, place supporter; make both keep certain interval; place the buffer protection layer on described compound plate, explosive and detonator are placed on the described buffer protection layer, ignite described detonator.It is characterized in that: described substrate is a continuous casting billet, gap between described compound plate and the substrate is the doubly thickness of described compound plate of 1-1.2, the dose of described explosive is the doubly weight of described compound plate of 0.3-0.5, the thickness of described compound plate is during greater than 18mm, compound at twice, after for the first time compound, carry out 100% flaw detection, postwelding is repaiied at not compound place, and it is compound to carry out the second time again.
Be to guarantee composite quality, make wherein compound plate area greater than described substrate, its every limit goes out 10-30mm greatly, and on described compound plate by the size fluting of described substrate, described groove depth is the thickness of 50-70% compound plate, groove width is 4-6mm.
The present invention is owing to the method that adopts at the compound big thickness stainless steel compound plate of continuous casting billet higher slice, for the stainless steel clad plate of producing the big compound ratio of large tracts of land in enormous quantities has been created condition.Owing to adopt the design of suitable explosive consumption and compound plate greater than substrate, make continuous casting billet can produce neither that matrix damages or the edge is pulled, guarantee that again combined strength bination and recombination rate reach requirement, simultaneously owing to the design of having taked on compound plate, to slot, explode compound after, the redundance of compound plate can cut off automatically.The composite continuous casting base that adopts the present invention to make can be widely used in oil through rolling, and chemical industry is in the industries such as light industry and space flight.
Embodiments of the present invention is described in detail below in conjunction with accompanying drawing.
Accompanying drawing 1 is the relative position schematic diagram of various materials before the cap sensitive of the present invention
Accompanying drawing 2 is the schematic diagrames of slotting on the compound plate
As shown in Figure 1: a compound block length 1800mm on continuous casting billet, wide 1400mm, thickness are the stainless steel of 22mm.Earlier with the thickness pad on sand basis 2 to more than the 500mm, and do not have stone greater than φ 20.Continuous casting billet 1 is placed on the sand basis 2.On continuous casting billet 1, put the folding aluminium flake of several warps or other has certain rigidity but more frivolous supporter 4.On supporter 4, place the stainless steel compound plate 3 that 10mm is thick.The height of supporter 4, just the gap between compound plate 3 and the substrate 1 is 10mm.The staggered buffer protection layer of forming 6 of two-layer butter and two-layer malthoid is set above the compound plate 3.Placing weight on the second road malthoid is the ammonium nitrate-fuel oil mixture 7 that 79kg contains diesel oil 6%-10%, inserts detonator 8 on explosive 7, and detonating primer 8 then.Behind explosive charge, powerful explosive force will produce one powerful jet between compound plate 3 and substrate 1, promptly wash away the oxide layer on two-ply 3,1 apparent surface, and push supporter 4 open, and it is closely compound with substrate 1 to promote compound plate 3.Then the ground floor compound plate is carried out 100% flaw detection, if any not compound part, repairing postwelding, to carry out the second time more compound.Compound tense for the second time, the thickness of compound plate 3 is 12mm, and the gap between compound plate and the substrate is 12mm, and the consumption of explosive is 96kg, and all the other steps etc. are all compound identical with the first time.After twice compound finishing, in four jiaos of usefulness knot 506 welding rod sections weldering of compound base, to strengthen edge strength.
In the above-described embodiments, the gap 5 between stainless steel compound plate 3 and the continuous casting billet 1 can change in the scope of 1-1.2 times of compound plate 3 thickness.The buffer protection layer also can adopt alternate manner or material.The dose of explosive can change in the scope of 0.3-0.5 compound plate 3 weight doubly.Explosive 7 also can adopt 70% No. 2 rock explosive+30%No.l or other explosive.
The thickness that generally needs compound stainless steel compound plate 3 can adopt during less than 18mm and once explode compoundly, and when surpassing 18mm when thick, it is compound to explode at twice, and its lift height can be with reference to following numerical value:
Compound bed thickness is the composite thickness composite thickness second time for the first time
(mm) (mm) (mm)
18 8 10
20 10 10
22 10 12
24 10 14
26 12 14
Pull for preventing that the explosion time unloading from drawing with the edge, compound plate 3 areas should be greater than the area of substrate 1, and about every limit goes out 10-30mm greatly, and the size of pressing substrate 1 on compound plate 3 is with carbon arc air gouging fluting 9, groove 9 is the thickness of 50-70% compound plate 3 deeply, groove 9 is wide be 4-6mm(as shown in Figure 2).The redundance of compound plate 3 is excised automatically when blast is finished like this.
Claims (2)
1; a kind of on continuous casting billet the method for composite stainless steel compound plate; it is that substrate 1 is positioned on the sand basis 2; placing between stainless steel compound plate 3 and described substrate 1 makes both keep the supporter 4 of certain interval 5; on described compound plate 3, place buffer protection layer 6; explosive 7 and detonator 8 are placed on the described buffer protection layer 6; ignite described detonator 8; it is characterized in that: described substrate 1 is continuous casting billet; gap between described compound plate 3 and the substrate 1 is the thickness of the doubly described compound plate 3 of 1-1.2; the dose of described explosive 7 is the weight of the doubly described compound plate 3 of 0.3-0.5; the thickness of described compound plate 3 is during greater than 18mm; compound at twice, after for the first time compound, carry out 100% flaw detection; postwelding is repaiied at not compound place, and it is compound to carry out the second time again.
2, as claimed in claim 1 on continuous casting billet the method for composite stainless steel compound plate, it is characterized in that: compound plate 3 areas wherein are greater than described substrate 1, its every limit goes out 10-30mm greatly, and the size by described substrate 1 slots 9 on described compound plate 3, described groove 9 is the thickness of 50-70% compound plate 3 deeply, and groove 9 is wide to be 4-6mm.