CN107399802A - A kind of stainless steel acid cleaning waste water metal chelating agent - Google Patents
A kind of stainless steel acid cleaning waste water metal chelating agent Download PDFInfo
- Publication number
- CN107399802A CN107399802A CN201710669663.6A CN201710669663A CN107399802A CN 107399802 A CN107399802 A CN 107399802A CN 201710669663 A CN201710669663 A CN 201710669663A CN 107399802 A CN107399802 A CN 107399802A
- Authority
- CN
- China
- Prior art keywords
- parts
- stainless steel
- waste water
- cleaning waste
- chelating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stainless steel acid cleaning waste water metal chelating agent, include the component of following mass parts:1 ~ 2 part of diethanol amine, 2 ~ 5 parts of diallyldimethylammonium chloride, 0.5 ~ 1 part of diethylenetriamine pentacarboxylic acid salt, 2 ~ 5 parts of activated carbon, 1 ~ 3 part of polyacrylamide, 2 ~ 3 parts of chitosan, silica 1 ~ 2 part.The preparation method of the present invention is simple, and easy to operate, cost is cheap, containing diatomite, kaolin wide material sources in metal chelating agent, has the effect for removing metal ion in stainless steel acid cleaning waste water well.
Description
Technical field
The invention belongs to stainless steel manufacturing technology field, and in particular to a kind of stainless steel acid cleaning waste water metal chelating agent.
Background technology
Stainless steel is widely used because of its excellent corrosion resistance and good outward appearance.Stainless steel in process of production,
Inevitably the oxide skin of black can be produced often by process, surfaces such as annealing, normalizing, quenching, welding.Oxygen
Changing skin not only influences the presentation quality of stainless steel, can also have a negative impact to the following process of product, therefore before following process
The surface treatment methods such as pickling, polishing must be used to be removed.All the time, it is caused a large amount of in producing stainless steel process
The processing of pickling waste waters is the problem of iron and steel enterprise.As steel and iron industry progressively develops, people gradually recognize pickling waste waters pair
Environment is particularly the harm to mankind itself, and stainless steel acid cleaning waste water is containing Cr6+ 、Cr3+With metallic iron, the spent acidic of nickel
Water, Cr3+Belong to trace element in human body, participate in glucose and lipid metabolism.But Cr6+There are very big stimulation and corrosivity.Stream
Row disease is learned research and shown:Cr 6+Compound is common carcinogen, and inhaling people's abstracting moiety oxygen into blood becomes hemoglobin
Into ferrihemoglobin, red blood cell takes gas dysfunction, and interior suffocate occurs.When iron content waste water is discharged into water body, due to taking by force from water
Oxygen has been removed, has just destroyed fish, animal and the life condition for participating in the microorganism of auto purification of water etc., has caused fish dead.Fluorine member
Element can have an effect with a variety of enzymes in animals and plants, cause metabolic disorder, cytomorphosis, necrosis.Also sclerotin can be caused excessive
There is spur, spinal canal stenosis, and this method processing stainless steel acid cleaning waste water of carcinogenesis in calcification, although to Cr6+Carry out
Neutralize, reduce, precipitation process, the chromium sludge after filter press press filtration, still containing a small amount of Cr6+、Cr 3+, still have to environment
Larger harm, antiseepage can only be used to fill.Because the toxicity of Cr VI is stronger, and can exist steadily in the long term, antiseepage fills simultaneously
The potential danger that high valence chrome damages to environment can not be thoroughly eliminated, and landfill can increase processing cost, take the soil of preciousness
Ground resource.Therefore, seeking more reasonably processing approach has important theoretical and practical values.
The content of the invention
Technical problem:A kind of processing method of stainless steel acid cleaning waste water is provided.
Technical scheme:A kind of stainless steel acid cleaning waste water metal chelating agent, include the component of following mass parts:
1 ~ 2 part of diethanol amine, 2 ~ 5 parts of diallyldimethylammonium chloride, 0.5 ~ 1 part of diethylenetriamine pentacarboxylic acid salt, activated carbon 2
~ 5 parts, 1 ~ 3 part of polyacrylamide, 2 ~ 3 parts of chitosan, silica 1 ~ 2 part.
Preferably, include the component of following mass parts:
It is 1 part of diethanol amine, 2 parts of diallyldimethylammonium chloride, 0.5 part of diethylenetriamine pentacarboxylic acid salt, 2 parts of activated carbon, poly-
1 part of acrylamide, 2 parts of chitosan, silica 1 part.
Preferably, include the component of following mass parts:
2 parts of diethanol amine, 3 parts of diallyldimethylammonium chloride, 1 part of diethylenetriamine pentacarboxylic acid salt, 4 parts of activated carbon, poly- third
3 parts of acrylamide, 3 parts of chitosan, 2 parts of silica.
The preparation method of above-mentioned stainless steel acid cleaning waste water metal chelating agent, comprises the following steps:
(1) chitosan, activated carbon are ground respectively, sieving, 1 ~ 2h are calcined at 100 ~ 150 DEG C;
(2) by chitosan, activated carbon, silica, water according to mass ratio for mixing, add NaOH, regulation pH be 5.5 ~
6.5, obtain mixture;
(3) diethanol amine, diallyldimethylammonium chloride, diethylenetriamine pentacarboxylic acid salt, polypropylene are added into mixture
Acid amides, 1h is reacted under high temperature;Obtain stainless steel acid cleaning waste water metal chelating agent.
In 5 steps (3), the temperature of pyroreaction is 60 ~ 70 DEG C.
The stainless steel acid cleaning waste water metal network that the preparation method of above-mentioned stainless steel acid cleaning waste water metal chelating agent is prepared
Mixture.
Application of the above-mentioned stainless steel acid cleaning waste water metal chelating agent in stainless steel acid cleaning waste water processing.
Beneficial effect:
The preparation method of the present invention is simple, and easy to operate, cost is cheap, comes in metal chelating agent containing silica, activated carbon
Source is extensive, has the effect for removing metal ion in stainless steel acid cleaning waste water well.
Embodiment
According to following embodiments, the present invention may be better understood.It is however, as it will be easily appreciated by one skilled in the art that real
Apply the content described by example and be merely to illustrate the present invention, without should be also without limitation on sheet described in detail in claims
Invention.
Embodiment 1:
A kind of stainless steel acid cleaning waste water metal chelating agent, include the component of following mass parts:
It is 1 part of diethanol amine, 2 parts of diallyldimethylammonium chloride, 0.5 part of diethylenetriamine pentacarboxylic acid salt, 2 parts of activated carbon, poly-
1 part of acrylamide, 2 parts of chitosan, silica 1 part.
The preparation method of above-mentioned stainless steel acid cleaning waste water metal chelating agent, comprises the following steps:
(1) chitosan, activated carbon are ground respectively, sieving, 1 ~ 2h are calcined at 100 ~ 150 DEG C;
(2) by chitosan, activated carbon, silica, water according to mass ratio for mixing, add NaOH, regulation pH be 5.5 ~
6.5, obtain mixture;
(3) diethanol amine, diallyldimethylammonium chloride, diethylenetriamine pentacarboxylic acid salt, polypropylene are added into mixture
Acid amides, 1h is reacted under high temperature;Obtain stainless steel acid cleaning waste water metal chelating agent.
Embodiment 2:
A kind of stainless steel acid cleaning waste water metal chelating agent, include the component of following mass parts:
2 parts of diethanol amine, 3 parts of diallyldimethylammonium chloride, 1 part of diethylenetriamine pentacarboxylic acid salt, 4 parts of activated carbon, poly- third
3 parts of acrylamide, 3 parts of chitosan, 2 parts of silica.
The preparation method of above-mentioned stainless steel acid cleaning waste water metal chelating agent, comprises the following steps:
(1) chitosan, activated carbon are ground respectively, sieving, 1 ~ 2h are calcined at 100 ~ 150 DEG C;
(2) by chitosan, activated carbon, silica, water according to mass ratio for mixing, add NaOH, regulation pH be 5.5 ~
6.5, obtain mixture;
(3) diethanol amine, diallyldimethylammonium chloride, diethylenetriamine pentacarboxylic acid salt, polypropylene are added into mixture
Acid amides, 1h is reacted under high temperature;Obtain stainless steel acid cleaning waste water metal chelating agent.
Embodiment 3:
A kind of stainless steel acid cleaning waste water metal chelating agent, include the component of following mass parts:
1.5 parts of diethanol amine, 2.5 parts of diallyldimethylammonium chloride, 0.8 part of diethylenetriamine pentacarboxylic acid salt, activated carbon 3
Part, 2 parts of polyacrylamide, 2.5 parts of chitosan, silica 1 .5 parts.
The preparation method of above-mentioned stainless steel acid cleaning waste water metal chelating agent, comprises the following steps:
(1) chitosan, activated carbon are ground respectively, sieving, 1 ~ 2h are calcined at 100 ~ 150 DEG C;
(2) by chitosan, activated carbon, silica, water according to mass ratio for mixing, add NaOH, regulation pH be 5.5 ~
6.5, obtain mixture;
(3) diethanol amine, diallyldimethylammonium chloride, diethylenetriamine pentacarboxylic acid salt, polypropylene are added into mixture
Acid amides, 1h is reacted under high temperature;Obtain stainless steel acid cleaning waste water metal chelating agent.
Claims (7)
1. a kind of stainless steel acid cleaning waste water metal chelating agent, it is characterised in that include the component of following mass parts:
1 ~ 2 part of diethanol amine, 2 ~ 5 parts of diallyldimethylammonium chloride, 0.5 ~ 1 part of diethylenetriamine pentacarboxylic acid salt, activated carbon 2
~ 5 parts, 1 ~ 3 part of polyacrylamide, 2 ~ 3 parts of chitosan, silica 1 ~ 2 part.
2. stainless steel acid cleaning waste water metal chelating agent according to claim 1, it is characterised in that including following mass parts
Component:
It is 1 part of diethanol amine, 2 parts of diallyldimethylammonium chloride, 0.5 part of diethylenetriamine pentacarboxylic acid salt, 2 parts of activated carbon, poly-
1 part of acrylamide, 2 parts of chitosan, silica 1 part.
3. stainless steel acid cleaning waste water metal chelating agent according to claim 1, it is characterised in that including following mass parts
Component:
2 parts of diethanol amine, 3 parts of diallyldimethylammonium chloride, 1 part of diethylenetriamine pentacarboxylic acid salt, 4 parts of activated carbon, poly- third
3 parts of acrylamide, 3 parts of chitosan, 2 parts of silica.
4. the preparation method of the stainless steel acid cleaning waste water metal chelating agent according to claim 1 ~ 3, it is characterised in that including
Following steps:
(1) chitosan, activated carbon are ground respectively, sieving, 1 ~ 2h are calcined at 100 ~ 150 DEG C;
(2) by chitosan, activated carbon, silica, water according to mass ratio for mixing, add NaOH, regulation pH be 5.5 ~
6.5, obtain mixture;
(3) diethanol amine, diallyldimethylammonium chloride, diethylenetriamine pentacarboxylic acid salt, polypropylene are added into mixture
Acid amides, 1h is reacted under high temperature;Obtain stainless steel acid cleaning waste water metal chelating agent.
5. the preparation method of stainless steel acid cleaning waste water metal chelating agent according to claim 4, it is characterised in that step (3)
In, the temperature of pyroreaction is 60 ~ 70 DEG C.
6. the stainless steel acid that the preparation method of any stainless steel acid cleaning waste water metal chelating agent of claim 4 ~ 5 is prepared
Wash waste water metal complexing agent.
7. application of the stainless steel acid cleaning waste water metal chelating agent described in claim 6 in stainless steel acid cleaning waste water processing.