CN107385286A - 一种压铸铝合金 - Google Patents

一种压铸铝合金 Download PDF

Info

Publication number
CN107385286A
CN107385286A CN201710622634.4A CN201710622634A CN107385286A CN 107385286 A CN107385286 A CN 107385286A CN 201710622634 A CN201710622634 A CN 201710622634A CN 107385286 A CN107385286 A CN 107385286A
Authority
CN
China
Prior art keywords
pack alloy
alloy
present
pack
percentage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710622634.4A
Other languages
English (en)
Inventor
王婷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710622634.4A priority Critical patent/CN107385286A/zh
Publication of CN107385286A publication Critical patent/CN107385286A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种压铸铝合金，所述压铸铝合金包括以下重量百分比的组分：Si：8.5％～10.5％；Cu：2.2％～4.2％；Mg：0.15％～0.25％；Zn：0.5％～0.8％；Fe：0.2％～0.8％；Mn：0.1％～0.3％；Ni：0.1％～0.3％；Sn：0.1％～0.2％；Sr：1.5％～2.5％；Ti：0.05％～0.08％；Al：余量。所述一种压铸铝合金中的Si与Al所形成Al‑Si共晶体具有很好的塑性，加入的Mg、Mn元素能够提高合金的机械强度，此外，辅以有Sr、Ti等元素的协同作用，进而可对铝合金组织起到细化作用，使铝合金组织各部位的晶粒平均尺寸更细小，分布各均匀，大大提高了韧性和延伸率。

Description

一种压铸铝合金
技术领域
本发明涉及一种压铸铝合金。
背景技术
随着人们对产品轻质化的要求日益强烈，铝合金愈发受到重视。压铸铝合金鉴于其可实现复杂结构的一次成型，在工序的简易性方面有很大的优势，使得压铸铝合金的应用极为普遍。
然而，现有压铸铝合金多存在机械强度低，韧性差，延伸率低的问题，极大的限制了其在结构方面的应用，由此，急需解决。
发明内容
本发明的目的在于针对上述问题，提供一种压铸铝合金，以解决现有压铸铝合金机械强度低，韧性差，延伸率低的问题。
本发明的目的是通过以下技术方案来实现：
一种压铸铝合金，所述压铸铝合金包括以下重量百分比的组分：
Si：8.5％～10.5％；
Cu：2.2％～4.2％；
Mg：0.15％～0.25％；
Zn：0.5％～0.8％；
Fe：0.2％～0.8％；
Mn：0.1％～0.3％；
Ni：0.1％～0.3％；
Sn：0.1％～0.2％；
Sr：1.5％～2.5％；
Ti：0.05％～0.08％；
Al：余量。
作为本发明的一种优选方案，所述压铸铝合金包括以下重量百分比的组分：Si：9.5％；Cu：3.2％；Mg：0.2％；Zn：0.6％；Fe：0.6％；Mn：0.2％；Ni：0.2％；Sn：0.15％；Sr：2％；Ti：0.06％；Al：余量。
本发明的有益效果为，所述一种压铸铝合金中的Si与Al所形成Al-Si共晶体具有很好的塑性，加入的Mg、Mn元素能够提高合金的机械强度，此外，辅以有Sr、Ti等元素的协同作用，进而可对铝合金组织起到细化作用，使铝合金组织各部位的晶粒平均尺寸更细小，分布各均匀，大大提高了韧性和延伸率。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。可以理解的是，此处所描述的实施例仅仅用于解释本发明，而非对本发明的限定。
实施例1
于本实施例中，一种压铸铝合金，所述压铸铝合金包括以下重量百分比的组分：
Si：8.5％；
Cu：2.2％；
Mg：0.15％；
Zn：0.5％；
Fe：0.2％；
Mn：0.1％；
Ni：0.1％；
Sn：0.1％；
Sr：1.5％；
Ti：0.05％；
Al：余量。
实施例2
于本实施例中，一种压铸铝合金，所述压铸铝合金包括以下重量百分比的组分：
Si：10.5％；
Cu：4.2％；
Mg：0.25％；
Zn：0.8％；
Fe：0.8％；
Mn：0.3％；
Ni：0.3％；
Sn：0.2％；
Sr：2.5％；
Ti：0.08％；
Al：余量。
实施例3
于本实施例中，一种压铸铝合金，所述压铸铝合金包括以下重量百分比的组分：
Si：9.5％；
Cu：3.2％；
Mg：0.2％；
Zn：0.6％；
Fe：0.6％；
Mn：0.2％；
Ni：0.2％；
Sn：0.15％；
Sr：2％；
Ti：0.06％；
Al：余量。
本实施例为本发明的优选方案，本实施例中的压铸铝合金，其机械强度、韧性、延伸率等指标最优。
以上实施例只是阐述了本发明的基本原理和特性，本发明不受上述实施例限制，在不脱离本发明精神和范围的前提下，本发明还有各种变化和改变，这些变化和改变都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书界定。

Claims (2)

1.一种压铸铝合金，其特征在于：所述压铸铝合金包括以下重量百分比的组分：
Si：8.5％～10.5％；
Cu：2.2％～4.2％；
Mg：0.15％～0.25％；
Zn：0.5％～0.8％；
Fe：0.2％～0.8％；
Mn：0.1％～0.3％；
Ni：0.1％～0.3％；
Sn：0.1％～0.2％；
Sr：1.5％～2.5％；
Ti：0.05％～0.08％；
Al：余量。
2.根据权利要求1所述的一种压铸铝合金，其特征在于：所述压铸铝合金包括以下重量百分比的组分：Si：9.5％；Cu：3.2％；Mg：0.2％；Zn：0.6％；Fe：0.6％；Mn：0.2％；Ni：0.2％；Sn：0.15％；Sr：2％；Ti：0.06％；Al：余量。
CN201710622634.4A 2017-07-27 2017-07-27 一种压铸铝合金 Pending CN107385286A (zh)