CN107384554A - A kind of environment-friendly type mechanical lubrication agent and preparation method thereof - Google Patents

A kind of environment-friendly type mechanical lubrication agent and preparation method thereof Download PDF

Info

Publication number
CN107384554A
CN107384554A CN201710667686.3A CN201710667686A CN107384554A CN 107384554 A CN107384554 A CN 107384554A CN 201710667686 A CN201710667686 A CN 201710667686A CN 107384554 A CN107384554 A CN 107384554A
Authority
CN
China
Prior art keywords
parts
lubrication agent
mechanical lubrication
preparation
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710667686.3A
Other languages
Chinese (zh)
Inventor
伊婕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710667686.3A priority Critical patent/CN107384554A/en
Publication of CN107384554A publication Critical patent/CN107384554A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of environment-friendly type mechanical lubrication agent and preparation method thereof, mechanical lubrication agent component includes 20 40 parts of vegetable oil in parts by weight, 5 10 parts of acetate butyl, 8 18 parts of chlorinated paraffin, 5 12 parts of graphite, 38 parts of sodium citrate, 28 parts of sorb furfuryl alcohol acid anhydride monoleate, 16 parts of sodium benzoate, 38 parts of polyoxyethylene APEO, 10 20 parts of rosin resin, 5 12 parts of diatomite, 7 17 parts of nano organic montmorillonite, preparation method of the present invention is simple, obtained lubricant is environment-protecting and non-poisonous, high lubricating effect, also there is antirust simultaneously, corrosion-resistant effect, can effectively lubricating machinery all parts, and it can significantly extend the service life of apparatus.

Description

A kind of environment-friendly type mechanical lubrication agent and preparation method thereof
Technical field
The present invention relates to technical field of lubricant preparation, specially a kind of environment-friendly type mechanical lubrication agent and preparation method thereof.
Background technology
As industry is continuously increased to lubricant demand, the species of lubricant is also more and more, and people are from lubrication During agent, motion conditions, material, surface roughness, working environment and the condition of work of friction pair, and lubricant must be typically considered The many factors such as performance, in plant equipment, lubricant mostly by lubricating system transmission ＆ distribution to each position for needing to lubricate, The using effect that existing lubricant has is unstable, and some contains noxious material, and human body is caused serious injury.
The content of the invention
It is an object of the invention to provide a kind of environment-friendly type mechanical lubrication agent and preparation method thereof, to solve above-mentioned background skill The problem of being proposed in art.
To achieve the above object, the present invention provides following technical scheme：A kind of environment-friendly type mechanical lubrication agent, mechanical lubrication agent Component includes vegetable oil 20-40 parts, acetate butyl 5-10 parts, chlorinated paraffin 8-18 parts, graphite 5-12 parts, lemon in parts by weight Sour sodium 3-8 parts, sorb furfuryl alcohol acid anhydride monoleate 2-8 parts, sodium benzoate 1-6 parts, polyoxyethylene APEO 3-8 parts, rosin Resin 10-20 parts, diatomite 5-12 parts, nano organic montmorillonite 7-17 parts.
Preferably, the preferable composition proportion of mechanical lubrication agent component includes 30 parts of vegetable oil, 8 parts of acetate butyl, chlorination stone 13 parts of wax, 8 parts of graphite, 5 parts of sodium citrate, 5 parts of sorb furfuryl alcohol acid anhydride monoleate, 4 parts of sodium benzoate, polyoxyethylene polyoxyethylene 6 parts of ether, 15 parts of rosin resin, 8 parts of diatomite, 12 parts of nano organic montmorillonite.
Preferably, its preparation method comprises the following steps：
A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
Compared with prior art, the beneficial effects of the invention are as follows：Preparation method of the present invention is simple, obtained lubricant environmental protection Nontoxic, high lubricating effect, while also there is antirust, corrosion-resistant effect, can effectively lubricating machinery all parts, and can show Write the service life that ground extends apparatus；Wherein, graphite, diatomite, the nano organic montmorillonite added in the present invention, it is possible to increase The high temperature resistant and antiseptic property of lubricant；And the sorb furfuryl alcohol acid anhydride monoleate and polyoxyethylene APEO of addition, energy The antioxygenic property of lubricant is enough improved, the parts for ensureing to scribble the mechanical lubrication agent will not be oxidized；In addition, the present invention adopts Preparation method is simple to operate, it can be ensured that various material components are sufficiently mixed, and are improved the stability of lubricant, are further prolonged Its long service life.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects Enclose.
The present invention provides following technical scheme：A kind of environment-friendly type mechanical lubrication agent, mechanical lubrication agent component is in parts by weight Including vegetable oil 20-40 parts, acetate butyl 5-10 parts, chlorinated paraffin 8-18 parts, graphite 5-12 parts, sodium citrate 3-8 parts, sorb Furfuryl alcohol acid anhydride monoleate 2-8 parts, sodium benzoate 1-6 parts, polyoxyethylene APEO 3-8 parts, rosin resin 10-20 parts, silicon Diatomaceous earth 5-12 parts, nano organic montmorillonite 7-17 parts.
Embodiment one：
Mechanical lubrication agent component includes 20 parts of vegetable oil, 5 parts of acetate butyl, 8 parts of chlorinated paraffin, 5 parts of graphite, lemon in parts by weight 3 parts of lemon acid sodium, 2 parts of sorb furfuryl alcohol acid anhydride monoleate, 1 part of sodium benzoate, 3 parts of polyoxyethylene APEO, rosin resin 10 Part, 5 parts of diatomite, 7 parts of nano organic montmorillonite.
The preparation method of the present embodiment comprises the following steps：
A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
Embodiment two：
Mechanical lubrication agent component includes 40 parts of vegetable oil, 10 parts of acetate butyl, 18 parts of chlorinated paraffin, graphite 12 in parts by weight Part, 8 parts of sodium citrate, 8 parts of sorb furfuryl alcohol acid anhydride monoleate, 6 parts of sodium benzoate, 8 parts of polyoxyethylene APEO, rosin tree 20 parts of fat, 12 parts of diatomite, 17 parts of nano organic montmorillonite.
The preparation method of the present embodiment comprises the following steps：
A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
Embodiment three：
Mechanical lubrication agent component in parts by weight include 25 parts of vegetable oil, 6 parts of acetate butyl, 10 parts of chlorinated paraffin, 6 parts of graphite, 4 parts of sodium citrate, 3 parts of sorb furfuryl alcohol acid anhydride monoleate, 2 parts of sodium benzoate, 4 parts of polyoxyethylene APEO, rosin resin 12 parts, 6 parts of diatomite, 8 parts of nano organic montmorillonite.
The preparation method of the present embodiment comprises the following steps：
A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
Example IV：
Mechanical lubrication agent component in parts by weight include 38 parts of vegetable oil, 9 parts of acetate butyl, 16 parts of chlorinated paraffin, 11 parts of graphite, 7 parts of sodium citrate, 7 parts of sorb furfuryl alcohol acid anhydride monoleate, 5 parts of sodium benzoate, 7 parts of polyoxyethylene APEO, rosin resin 18 parts, 11 parts of diatomite, 15 parts of nano organic montmorillonite.
The preparation method of the present embodiment comprises the following steps：
A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
Embodiment five：
Mechanical lubrication agent component in parts by weight include 28 parts of vegetable oil, 8 parts of acetate butyl, 15 parts of chlorinated paraffin, 9 parts of graphite, 7 parts of sodium citrate, 4 parts of sorb furfuryl alcohol acid anhydride monoleate, 5 parts of sodium benzoate, 7 parts of polyoxyethylene APEO, rosin resin 16 parts, 10 parts of diatomite, 10 parts of nano organic montmorillonite.
The preparation method of the present embodiment comprises the following steps：
A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
Embodiment six：
Mechanical lubrication agent component in parts by weight include 30 parts of vegetable oil, 8 parts of acetate butyl, 13 parts of chlorinated paraffin, 8 parts of graphite, 5 parts of sodium citrate, 5 parts of sorb furfuryl alcohol acid anhydride monoleate, 4 parts of sodium benzoate, 6 parts of polyoxyethylene APEO, rosin resin 15 parts, 8 parts of diatomite, 12 parts of nano organic montmorillonite.
The preparation method of the present embodiment comprises the following steps：
A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
Preparation method of the present invention is simple, and obtained lubricant is environment-protecting and non-poisonous, high lubricating effect, while also has antirust, prevents Rotten effect, can effectively lubricating machinery all parts, and can significantly extend the service life of apparatus；Wherein, this hair Graphite, diatomite, the nano organic montmorillonite of bright middle addition, it is possible to increase the high temperature resistant and antiseptic property of lubricant；And add The sorb furfuryl alcohol acid anhydride monoleate and polyoxyethylene APEO added, it is possible to increase the antioxygenic property of lubricant, ensure to apply The parts for having the mechanical lubrication agent will not be oxidized；Obtained through overtesting, using traditional lubricant, lubricant effect is poor, resistance to High temperature can only achieve 70 DEG C, and easily etching part surface, and use the lubricant of the present invention, and high temperature resistant can reach 180 DEG C, And will not etching part surface；In addition, the preparation method that the present invention uses is simple to operate, using first stirring at low speed, again high-speed stirring Mix, finally carry out heat mixing preparation process be able to ensure that various material components are sufficiently mixed, improve the stability of lubricant, Further extend its service life.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding And modification, the scope of the present invention is defined by the appended.

Claims (3)

  1. A kind of 1. environment-friendly type mechanical lubrication agent, it is characterised in that：Mechanical lubrication agent component includes vegetable oil 20-40 in parts by weight Part, acetate butyl 5-10 parts, chlorinated paraffin 8-18 parts, graphite 5-12 parts, sodium citrate 3-8 parts, sorb furfuryl alcohol acid anhydride monoleate 2-8 parts, sodium benzoate 1-6 parts, polyoxyethylene APEO 3-8 parts, rosin resin 10-20 parts, diatomite 5-12 parts, nanometer Organo montmorillonite 7-17 parts.
  2. A kind of 2. environment-friendly type mechanical lubrication agent according to claim 1, it is characterised in that：Mechanical lubrication agent component is preferable Composition proportion includes 30 parts of vegetable oil, 8 parts of acetate butyl, 13 parts of chlorinated paraffin, 8 parts of graphite, 5 parts of sodium citrate, sorb furfuryl alcohol 5 parts of acid anhydride monoleate, 4 parts of sodium benzoate, 6 parts of polyoxyethylene APEO, 15 parts of rosin resin, diatomite 8 part, nanometer have 12 parts of machine montmorillonite.
  3. 3. realize a kind of preparation method of environment-friendly type mechanical lubrication agent described in claim 1, it is characterised in that：Its preparation method Comprise the following steps：
    A, added after mixing vegetable oil, acetate butyl, chlorinated paraffin, graphite, sodium citrate 3, sorb furfuryl alcohol acid anhydride monoleate Stirring at low speed is carried out in stirred tank, speed is 300 revs/min, time 20min, and standing obtains mixture A；
    B, by sodium benzoate, polyoxyethylene APEO, rosin resin, diatomite, nano organic montmorillonite, added after mixing High-speed stirred is carried out in stirred tank, rotating speed is 4000 revs/min, time 10min, obtains mixture B；
    C, mixture A being added in mixture B, heating response is carried out after being sufficiently mixed, temperature is 80 DEG C, my 10min of time, it After be slowly cooled to room temperature, stand 3h, that is, obtain mechanical lubrication agent.
CN201710667686.3A 2017-08-07 2017-08-07 A kind of environment-friendly type mechanical lubrication agent and preparation method thereof Withdrawn CN107384554A (en)